• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.350-356
• /
• 2006

In order to investigate the effect of the composition of weather-resistant coatings on physical properties, three different weather-resistant coatings were prepared by varying the ratio of a mill-base silicone/acrylic resin and let-down silicone/acrylic resin in weight ratios of 2 : 8, 3 : 7, and 4 : 6. The physical properties and weather-resistance of the prepared coatings were tested. It was found that the thermal stability, salt spray exposure, and weather-resistance were improved with increasing the amount of silicone. The optimum mixing ratio of mill-base silicone/acrylic resin to the let-down silicone/acrylic resin was 2 : 8. The coating containing silicone component of 30 wt% was found to be suitable as high weather-resistant coatings.

• Journal of the Korean Institute of Gas
• /
• v.9 no.4 s.29
• /
• pp.26-29
• /
• 2005

In this paper, the solvent sensing properties of the metallophthalocyanine macrocyclic compounds(ZnPc) have been deposited as thin films by the spin-coated method and evaporated methods onto alumina substrates and quartz substrates. And then the spin-coated materials of Zinc phthalocyanine solutions blended with $N,N'-diphenyl-N,N'-bis(1-naphthyl)-1,\;1-biphenyl-4,4'-diamine\;and/or\; Poly[2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenylene-vinylene]$ solutions. The influences of the blended metallophthalocyanine macrocyclic compounds on the resistance have been measured and analysed in five different vapour organic compounds.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.4
• /
• pp.226-231
• /
• 2014

Thin thermistor films of solutions with nickel and manganese oxides were prepared by metal-organic decomposition (MOD). The structural properties of the thin films were investigated as a function of annealing temperature. Field emission scanning electron microscope (FE-SEM) results indicated that the thin films had a thin thickness, smooth and dense surface. The crystallization temperature of $414.9^{\circ}C$ was confirmed from thermogavimetric-differential thermal analysis (TG-DTA) curve. A single phase of cubic spinel structure was obtained for the thin film annealed from $700^{\circ}C$ to $800^{\circ}C$, which was confirmed from the X-ray diffraction (XRD). From the selected area electron diffraction (SAED) in high resolution transmission electron microscope (HRTEM), the nano grains (2~3 nm) of spinel phase with (311) and (222) planes were detected for the thin film annealed at $500^{\circ}C$, which could be applicable to read-out integrated circuit (ROIC) substrate of the uncooled microbolometer with low processing temperature.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.5
• /
• pp.193-196
• /
• 2011

Lead zirconate titanate (PZT)/ bismuth ferrite (BFO) multilayer thin films have been fabricated by the spin-coating method on Pt(200 nm)/Ti(10 nm)/$SiO_2$(100 nm)/p-Si(100) substrates using $BiFeO_3$ and $Pb(Zr_{0.52}Ti_{0.48})O_3$ metal alkoxide solutions. The PZT/BFO multilayer thin films show a uniform and void-free grain structure, and the grain size is smaller than that of PZT single films. The reason for this is assumed to be that the lower BFO layers play an important role as a nucleation site or seed layer for the formation of homogeneous and uniform upper PZT layers. The dielectric constant and dielectric losses decreased with increasing number of coatings, and the six-layer PZT/BFO thin film has good properties of 162 (dielectric constant) and 0.017 (dielectric losses) at 1 kHz. The remnant polarization and coercive field of three-layer PZT/BFO thin films were 13.86 ${\mu}C/cm^2$ and 37 kV/cm respectively.

• Textile Coloration and Finishing
• /
• v.28 no.1
• /
• pp.40-47
• /
• 2016

As a coating material for loudspeaker dampers, resilient polyurethane/epoxy hybrid resins were synthesized to replace conventional phenol resin and examined the physical properties, which are not only environmentally friendly but also not harmful to human. Five types of polyurethane resins were synthesized in the step-shot method using methylene diisocyanate, three polyols such as poly tetramethylene ether glycol(PTMEG, MW:2000), poly(1,4-buthylene adipate(PBAP, MW:2000), and poly carbonatediol(PCD, MW:2000), and three chain extenders such as ethylene glycol(EG), neopentyl glycol(NPG), and 1,4-buthandiol(1,4-BD). The five types of synthesized polyurethane resins and commercially available bisphenol A type epoxy resin were blended in weight ratios of 90:10, 70:30, and 50:50 to synthesize 15 types of polyurethane/epoxy hybrid resins. Among the polyurethane resins, the one that was synthesized using PCD and 1,4-BD showed excellent tensile strength, 100% modulus, low extension, and relatively high viscosity. Polyurethane/epoxy hybrid resins with higher epoxy resin contents showed better thermal properties and water resistance while those with higher polyurethane contents showed higher flexibility. The polyurethane/epoxy hybrid resin made by blending the polyurethane based on PCD and 1,4-BD with a bisphenol A type epoxy resin in a weight ratio of 70:30 was identified to be the most suitable to be used in speaker dampers.

• Journal of Electrical Engineering and Technology
• /
• v.12 no.5
• /
• pp.2007-2013
• /
• 2017

In order to give hydrophobic surface properties on carbon steel, the fluorinated amorphous carbon films were prepared by using linear 2.45GHz microwave PECVD device. Two different process approaches have been tested. One is direct deposition of a-C:H:F films using admixture of $Ar/CH_4/CF_4$ working gases and the other is surface treatment using $CF_4$ plasma after deposition of a-C:H film with $Ar/CH_4$ binary gas system. $Ar/CF_4$ plasma treated surface with high $CF_4$ gas ratio shows best hydrophobicity and durability of hydrophobicity. Nanometer scale surface roughness seems one of the most important factors for hydrophobicity within our experimental conditions. The properties of a-C:H:F films and $CF_4$ plasma treated a-C:H films were investigated in terms of surface roughness, hardness, microstructure, chemical bonding, atomic bonding structure between carbon and fluorine, adhesion and water contact angle by using atomic force microscopy (AFM), nano-indentation, Raman analysis and X-ray photoelectron spectroscopy (XPS).

• Journal of the Korean Applied Science and Technology
• /
• v.23 no.1
• /
• pp.77-84
• /
• 2006

Modified polyesters (TTBA-10C, -20C, -30C) that contain phosphorus and chlorine were synthesized by the condensation polymerization of tetramethylene bis(orthophosphate), neohexanediol trichlorobenzoate, 1,4-butanediol and adipic acid, in which tetramethylene bis(orthophosphate) and neohexanediol trichlorobenzoate were prepared previously in our laboratory. In this study, two-component flame-retardant polyurethane coatings (TTBA-10C/HDI-trimer=TTHD-10C, TTBA-20C/ HDI-trimer= TTHD-20C, TTBA-30C/HDI-trimer= TTHD-30C) were obtained by curing at room temperature with the synthesized TTBAs and hexamethylene diisocyanate (HDI)-trimer as a curing agent. The obtained TTHDs were made into coating samples and used as test samples for various physical properties. The physical properties of the flame-retardant coatings containing chlorine and phosphorus groups were generally inferior to those containing only phosphorus group. Flame retardancy was tested by vertical and horizontal combustion method, and $45_{\circ}$ Meckel burner method. Since the retardancy of flame-retardant coatings containing chlorine and phosphorus groups was better than that containing only phosphorus group, it could be concluded that the retardancy by the synergism effect of chlorine and phosphorus groups exhibited.

• Journal of Adhesion and Interface
• /
• v.18 no.3
• /
• pp.134-140
• /
• 2017

In this study, we made UV cured acrylic pressure sensitive adhesive containing silicone-urethane-acrylate (SUA) oligomer for a coating on protective film and investigated the effect of SUA oligomer content and UV-dose on adhesion properties. The results illustrated that peel strength decreases with increasing oligomer content and UV-dose, while holding power increases. The gel fractions sharply increased after UV irradiation and then remain constant with prolonged UV exposure. From peel-off test, sample S70 (70% oligomer content) shows the best peelability and removability without remaining any mark or adhesive material on the test substrate than S50 (50% oligomer content) and S60 (60% oligomer content). Sample S70 also showed a surface energy lower than $26mJ/m^2$ and a transmittance higher than 95% at UV-dose 1857 and $2270mJ/cm^2$ which met the required properties for protective film application.

• Polymer(Korea)
• /
• v.34 no.5
• /
• pp.424-429
• /
• 2010

The hybrid composites of aliphatic polyester-silica were prepared via a sol-gel reaction and their potential application using as a buffer coating layer in the thermoelectric device were investigated. When aliphatic polyesters were thermally treated at a high temperature of $240^{\circ}C$, the polymer showed an increases in thermal degradation temperature by $30{\sim}90^{\circ}C$ according to the thermal treatment time. The polyester-silica composites showed an increases in thermal degradation temperature by $30{\sim}50^{\circ}C$ according to the content of the added silica. Polyester-silica composite showed neither discoloration nor change in optical properties because Knoevenagel condensation reaction was hindered by silica structure. The thermal conductivity of the composites increased linearly according to the content of added silica.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.3
• /
• pp.229-236
• /
• 1998

Ferroelectric $Sr_xBi_yTa_2O_{9+\alpha}$/(0.7$\leqSr\leq1.0,\; 2.0\leqBi\leq2.6)$ solutions were prepared by MOD (Metalorganic Deposition) process. These solutions were made into thin films with thickness ranging from 1500~2000${\AA}$ by spin coating. The phase transformation of the SBT thin films by variation of annealing temperature and annealing time were observed using high temperature XRD and SEM. The crystallization and grain growth of SBT thin film were accomplished at $800^{\circ}C$ for 30 minutes after deposition of Pt top electrode by sputtering to prevent electrical breakdown. Ferroelectric properties of the SBT thin films were measured in the range of $\pm$3V\; and\; \pm5V$. The specimen with composition ratio of Sr/Bi/Ta (0.8/2.4/2.0) has the excellent ferroelectric properties ; $2P_r = 10.5,\; 13.2\muC/cm^2 \;at\; \pm3V\; and\; \pm5V$ respectively. Observing the post annealed Pt/SBT/Pt interface by SEM, it was found that Pt electrode sputtered on to the SBT thin film penetrated into the hollow on the SBT thin film, thus decreasing the effective insulation thickness. The effective insulation thickness recovered by post annealing, and this was confirmed by leakage current density measurement.