• Science of Emotion and Sensibility
• /
• v.25 no.4
• /
• pp.45-52
• /
• 2022

Recently, interest in and demand for sensors that recognize physical activity and their products are increasing. In particular, the development of wearable materials that are flexible, stretchable, and able to detect the user's biological signals is drawing attention. In this study, an experiment was conducted to improve the dip-coating efficiency of a single-walled carbon nanotube dispersion solution after fine holes were made in a hydrophobic material with a micro needle. In this study, dip-coating was performed with a material that was not penetrated, and comparative analysis was performed. The electrical conductivity of the sensor was measured when the sensor was stretched using a strain universal testing machine (Dacell Co. Ltd., Seoul, Korea) and a multimeter (Keysight Technologies, Santa Rosa, CA, USA) was used to measure resistance. It was found that the electrical conductivity of a sensor that was subjected to needling was at least 16 times better than that of a sensor that was not. In addition, the gauge factor was excellent, relative to the initial resistance of the sensor, so good performance as a sensor could be confirmed. Here, the dip-coating efficiency of hydrophobic materials, which have superior physical properties to hydrophilic materials but are not suitable due to their high surface tension, can be adopted to more effectively detect body movements and manufacture sensors with excellent durability and usability.

• Journal of the Korean Magnetics Society
• /
• v.25 no.3
• /
• pp.67-73
• /
• 2015

This is a basic research for improving soft magnetic property of Fe based nano crystalline alloy powder core. The main study is done around characteristics of permeability, core loss, and DC bias depending on amount of insulation coating agent and particle size. First, $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ amorphous alloy ribbon was fabricated by using the planar flow casting (PFC) device. Then, heat treatment and ball milling were done to obtain alloy powder. The amount of polyether imide (PEI) added to it was varied by 0.5, 1.0, 2.0, 2.5 wt% to have compression molding into $16ton/cm^2$. After going through crystalline heat treatment, the made toroidal nano crystalline powder core ($OD12.7mm^*ID7.62mm^*H4.75mm$) had smaller permeability as amount of insulation coating agent decreases. However, it was found out that core loss and DC bias characteristics have been improved. The reason for this results were expected to be because green density of power core decreases as amorphous alloy powder particles become smaller as amount of alloy powder insulation coating agent increases, it was determined that 1 wt% of insulation coating agent is appropriate. Also, for powder core made based on alloy powder size with amount of insulation coating agent fixed at 1 wt%, effective permeability and core loss were outstanding as particle size became bigger. However, characteristics of DC bias became worse as applied DC field increases. This is expected to be due to insulation effect, residual pores, or molding density of powder core resulting from thickness of coating on surface of alloy powder.

• Clean Technology
• /
• v.25 no.3
• /
• pp.256-262
• /
• 2019

Hydroxylammonium nitrate (HAN)-based liquid propellants are attracting attention as environmentally friendly propellants because they are not carcinogens and the combustion gases have little toxicity. The catalyst used to decompose the HAN-based liquid propellant in a thruster must have both low temperature activity and high heat resistance. The objective of this study is to prepare an Ru/alumina/metal foam catalyst by supporting alumina slurry on the surface of NiCrAl metal foam using a washing coating method and then to support a ruthenium precursor thereon. The decomposition activity of a HAN aqueous solution of the Ru/alumina/metal foam catalyst was evaluated. The effect of the number of repetitive coatings of alumina slurry on the physical properties of the alumina/metal foam was analyzed. As the number of alumina wash coatings increased, mesopores with a diameter of about 7 nm were well-developed, thereby increasing the surface area and pore volume. It was optimal to repeat the wash coating alumina on the metal foam 12 times to maximize the surface area and pore volume of the alumina/metal foam. Mesopores were also well developed on the surface of the Ru/alumina/metal foam catalyst. It was found that the metal form itself without the active metal and alumina can promote the decomposition reaction of the HAN aqueous solution. In the case of the Ru/alumina/metal foam-550 catalyst, the decomposition onset temperature was significantly lowered compared with that of the thermal decomposition reaction, and ${\Delta}P$ could be greatly increased in the decomposition of the HAN aqueous solution. However, when the catalyst was calcined at $1,200^{\circ}C$, the catalytic activity was lowered inevitably because the surface area and pore volume of the catalyst were drastically reduced and Ru was sintered. Further research is needed to improve the heat resistance of Ru/alumina/metal foam catalysts.

• Korean Journal of Materials Research
• /
• v.21 no.2
• /
• pp.115-119
• /
• 2011

Si Nanowire (NW) field effect transistors (FETs) were fabricated on hard Si and flexible polyimide (PI) substrates, and their electrical characteristics were compared. Si NWs used as channels were synthesized by electroless etching method at low temperature, and these NWs were refined using a centrifugation method to get the NWs to have an optimal diameter and length for FETs. The gate insulator was poly(4-vinylphenol) (PVP), prepared using a spin-coating method on the PI substrate. Gold was used as electrodes whose gap was 8 ${\mu}m$. These gold electrodes were deposited using a thermal evaporator. Current-voltage (I-V) characteristics of the device were measured using a semiconductor analyzer, HP-4145B. The electrical properties of the device were characterized through hole mobility, $I_{on}/I_{off}$ ratio and threshold voltage. The results showed that the electrical properties of the TFTs on PVP were similar to those of TFTs on $SiO_2$. The bending durability of SiNWs TFTs on PI substrate was also studied with increasing bending times. The results showed that the electrical properties were maintained until the sample was folded about 500 times. But, after more than 1000 bending tests, drain current showed a rapid decrease due to the defects caused by the roughness of the surface of the Si NWs and mismatches of the Si NWs with electrodes.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.236-241
• /
• 2011

Polysilazane and silazane-based precursor films were deposited on stacked TiN/Ti/TEOS/Si-substrate by spin-coating, then annealed at $150{\sim}400^{\circ}C$, integrated further to form the top electrode and pad, and finally characterized. The precursor solutions were composed of 20% perhydro-polysilazane ($SiH_2NH$)n, and 20% hydropolymethyl silazane ($SiHCH_3NH$)n in dibutyl ether. Annealing of the precursor films led to the compositional change of the two chemicals into silicon (di)oxides, which was confirmed by Fourier transform infrared spectroscopy (FTIR) spectra. It is thought that the different results that were obtained originated from the fact that the two precursors, despite having the same synthetic route and annealing conditions, had different chemical properties. Electrical measurement indicated that under 0.6MV/cm, a larger capacitance of $2.776{\times}10^{-11}$ F and a lower leakage current of 0.4 pA were obtained from the polysilazane-based dielectric films, as compared to $9.457{\times}10^{-12}$ F and 2.4 pA from the silazane-based film, thus producing a higher dielectric constant of 5.48 compared to 3.96. FTIR indicated that these superior electrical properties are directly correlated to the amount of Si-O bonds and the improved chemical bonding structures of the spin-on dielectric films, which were derived from a precursor without C. The chemical properties of the precursor films affected both the formation and the electrical properties of the spin-on dielectric film.

• Corrosion Science and Technology
• /
• v.7 no.5
• /
• pp.269-273
• /
• 2008

It is known that the fluoric resin has the most outstanding properties in the extremely acidic environment of high temperature. However, this resin is the thermal hardening type that needs long time heat treatments above $250^{\circ}C$. It's impossible to use in situ in the extremely acidic environment such as a huge FGD ductworks or industrial chemical tanks. Furthermore, even the natural hardening type fluoric coatings which can be hardened less than $120^{\circ}C$ can not be applied to the highly acidic environmental plants because of its chemical resistance. In this study, new fluoric coatings that has excellent thermal resistance, chemical resistance and corrosion resistance has been developed in order to solve above problems and to be applied to the large plant structures in the field. These newly developed coatings are organic and inorganic composite type that have fluoric rubber(100 wt%), fluoric resin(5~50 wt%), oxalates(5~30 wt%), inorganic fillers mixed with plate-type and bulk-type solids(20~150 wt%), hardeners(0.5~5 wt%), and hardening hasteners(0.1~3 wt%). The best chemical and physical properties of these coatings are acquired by variation of adhesive reinforcement agents, dispersants, leveling agents. Mixing ratios of plate-type and bulk-type inorganic fillers influence the thermal properties, abrasive resistance and chemical infiltration properties of coatings. The mixing control is also very important to have homogeneous surface and removing inner voids of coatings.

• Korean Journal of Materials Research
• /
• v.20 no.8
• /
• pp.439-443
• /
• 2010

Nano sized SiC particles (270 nm) are easily agglomerated in nickel sulfamate electrolytic bath during a composite electrodeposition process. The agglomeration of nano particles in composite coatings can significantly reduce the mechanical properties of the composite coatings. In this study, Ni-SiC nano composite coatings were fabricated using a conventional electrodeposition process with the aid of ultrasound. Nano particles were found to be distributed homogeneously with reduced agglomeration in the ultrasonicated samples. Substantial improvements in mechanical properties were observed in the composite coatings prepared in presence of ultrasound over those without ultrasound. Ni-SiC composite coatings were prepared with variable ultrasonic frequencies ranging from 24 kHz to 78 kHz and ultrasonic powers up to 300 watts. The ultrasonic frequency of 38 kHz with ultrasonic power of 200 watt was revealed to be the best ultrasonic conditions for homogeneous dispersion of nano SiC particles with improved mechanical properties in the composite coatings. The microstructures, phase compositions, and mechanical properties of the composite coatings were observed and evaluated using SEM, XRD, Vickers microhardness, and wear test. The Vickers microhardness of composite coatings under ultrasonic condition was significantly improved as compared to the coatings without ultrasound. The friction coefficient of the composite coating prepared with an ultrasonic condition was also smaller than the pure nickel coatings. A synergistic combination of superior wear resistance and improved microhardness was found in the Ni-SiC composite coatings prepared with ultrasonic conditions.

• Elastomers and Composites
• /
• v.6 no.1
• /
• pp.71-81
• /
• 1971

The intention of this study is to investigate the properties of polymer blend, NBR/PVC vulcanizates and blending procedures such as roll-mixing temperatures and sequences for polymer blending of NBR and PVC(resin type). The results obtained are as follows: 1. The roll temperature applied for polymer blending is around $150^{\circ}C$. At this temperature region, the degradation of rubber stock, which may be caused by heat, can be minimized and mill processing in practical application in industries can also be facilitated. 2. It is obviously necessary that a small amount of plasticizers should be added to the stock for improving processibility of roll mixing and physical properties. 3. On roll-mixing sequence, it is more effective that PVC compounded with plasticizer is added to NBR milled on hot roll. 4. The vulcanizates of the blends with different degree of polymerization of PVC ale similar to one another in properties. 5. NBR/PVC(70/30) blends shows the better physical characters than eve,-made foreign latex blend except abrasion-resistance. 6. As PVC addition ratio is increased, the physical properties such as resistance to ozone, tear, heat and oil and tensile strength, modulus, hardness have also improved, on the other hand, tension set and rebound character decreased. 7. The curve of ultimate elongation have point of inflection at the ratio of $30\sim40$ part of PVC. 8. While CR is blended, the physical properties such as brittle point, rebound and resistance to oil in high temperature have improved. 9. Polymer blend of NBR and domestic PVC is applied for the industrial utility such as rubber sole and heel, electric wire cover and oil-resistant packing, coating and gasket, printing roll, film for food packing etc.

• Textile Coloration and Finishing
• /
• v.29 no.2
• /
• pp.97-103
• /
• 2017

Polyketone fiber, a newly developed high strength fiber, has a tenacity and modulus similar to the p-aramid fiber, and can be used for reinforcing mechanical rubber goods(MRG), such as tires, hoses, and technical textiles. It will be expected for replacement of super fiber such as aramids and increasing the technical textile market share. This paper surveys the mechanical properties of polyketone fiber for technical textiles. For this purpose, dyed polyketone fabric is prepared, mechanical properties of coated and uncoated polyketone fabrics such as tensile strength, elongation and tear strength were examined before and after weather resistance test(temperature $63{\pm}3^{\circ}C$, humidity 60%, amount of power $0.35w/m^2$). The differences of mechanical properties between uncoated and coated fabrics for high functional technical textiles and composite materials are estimated through this study. The UV-stability of polyketone fabric showed obvious improvement after coating. After 168h(7day) of UV exposure, the coated fabric showed less deterioration in mechanical properties with the retained tensile strength and elongation at break greater than 22 and 17% of the uncoated polyketone fabrics values, respectively.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.10 no.8
• /
• pp.2026-2031
• /
• 2009

Because the stone cultural properties located outdoors, they have been altered and deteriorated in external appearance due to environmental factors. Damage to stone cultural properties is accelerated particularly due to recent industrial development and environmental pollution. When fresh granite was dipped into the seawater, the mineral compositions(Ca, K) of the granite surface were lower then those of the fresh granite and density of the weathered granite was steadily decreased from $2.600 g/cm^3$ to $2.580-2.582 g/cm^3$. Also, absorption capacity of the weathered granite was steadily increased from 0.392% to $0.526{\sim}0.616%$. In the case of $TiO_2$ was coated to the granite, the change of density and absorption ratio of $TiO_2$ coated granite were decreased. Therefore, the $TiO_2$ coating considered to be a viable method to assist in the conservation of stone cultural properties from environmental contaminants.