• Journal of the Korean Wood Science and Technology
• /
• v.27 no.3
• /
• pp.31-38
• /
• 1999

This paper deals with a coating technique of hardening surface layer of softwood{Larix leptolepis) flooring board to improve its surface properties such as hardness and abrasion resisitance without spoiling its exellent qualities such as beautiful color tones and great strength. For surface hardening of the wood, polyurethane wood sealer was used as under coat, polyurethane sanding sealer as intermediate coat, and UV-curing epoxy acrylate and urethane acrylate varnishes as top coat. The hardness of the wood was improved by the coating treatment and it was similar to that of high density hardwood such as oak, keruing. The abrasion resistance of the coated wood was greatly improved by UV curing epoxy acrylate or urethane acrylate varnishes. Adhesion properties and impact resisitance of the coated wood surface were also good. It was suggested that the well-coated larch wood could be used as interior flooring board as substitute for hardwood such as keruing.

• Journal of Korean Ophthalmic Optics Society
• /
• v.5 no.2
• /
• pp.187-192
• /
• 2000

We prepared $SiO_2-Na_2O-R_mO_n$ thin films based on economics of water glass and investigated optical, mechanical properties of product thin films. Coating sol stabilized with 1 N HCl and 1 N $NH_4OH$, was fabricated by using water glass and calcium nitrate, and aluminum nitrate as starting materials. As-coated films on stainless steel, Si wafer and soda-lime-silica glass by spinning were finally annealed at 500, 750 and $900^{\circ}C$. Micro hardness and nitrogen content in film surface of annealed films were measured by Knoop hardness tester and EDX, respectively. Field Emission Scanning Electron Microscope (FE-SEM) and UV-VIS spectroscopy were adopted to analyze surface morphology and thickness and reflectance of our films.

• Journal of Surface Science and Engineering
• /
• v.49 no.6
• /
• pp.595-603
• /
• 2016

Rare-earth zirconates, including lanthanum zirconate and gadolinium zirconate, have been investigated as ones of the most promising candidates for next-generation thermal barrier coating (TBC) materials due to their excellent properties such as low thermal conductivity, chemical stability at high temperature and so on. In this study, TBCs with three compositions, in the $La_2O_3-Gd_2O_3-ZrO_2$ system with reduced rare-earth contents from $RE_2Zr_2O_7$ compositions, were fabricated by using suspension plasma spray with different suspension preparation methods. The phase formation, microstructure, and thermal properties of TBCs were examined. In particular, each coating exhibited single fluorite phase and a dense, vertically-separated microstructure. The potential of coatings with rare-earth zirconates for TBC applications was also discussed.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.120-120
• /
• 2016

Ti-6Al-4V alloy have been used for dental implant because of its excellent biocompatibility, corrosion resistance, and mechanical properties. However, the integration of such implant in bone was not in good condition to achieve improved osseointergraiton. For solving this problem, calcium phosphate (CaP) has been applied as coating materials on Ti alloy implants for hard tissue applications because its chemical similarity to the inorganic component of human bone, capability of conducting bone formation and strong affinity to the surrounding bone tissue. Various metallic elements, such as strontium (Sr), magnesium (Mg), zinc (Zn), sodium (Na), silicon (Si), silver (Ag), and yttrium (Y) are known to play an important role in the bone formation and also affect bone mineral characteristics, such as crystallinity, degradation behavior, and mechanical properties. Especially, Zn is essential for the growth of the human and Zn coating has a major impact on the improvement of corrosion resistance. Plasma electrolytic oxidation (PEO) is a promising technology to produce porous and firmly adherent inorganic Zn containing $TiO_2(Zn-TiO_2)$coatings on Ti surface, and the a mount of Zn introduced in to the coatings can be optimized by altering the electrolyte composition. In this study, corrosion behavior of Ti-6Al-4V alloy after plasma electrolytic oxidation in solutions containing Ca, P and Zn were studied by scanning electron microscopy (SEM), AC impedance, and potentiodynamic polarization test. A series of $Zn-TiO_2$ coatings are produced on Ti dental implant using PEO, with the substitution degree, respectively, at 0, 5, 10 and 20%. The potentiodynamic polarization and AC impedance tests for corrosion behaviors were carried out in 0.9% NaCl solution at similar body temperature using a potentiostat with a scan rate of 1.67mV/s and potential range from -1500mV to +2000mV. Also, AC impedance was performed at frequencies ranging from 10MHz to 100kHz for corrosion resistance.

• Composites Research
• /
• v.25 no.3
• /
• pp.70-75
• /
• 2012

Interfacial durability and electrical properties of CNT, ITO or xGnP coated PVDF nanocomposites were investigated for acoustic actuator applications. The xGnP coated PVDF nanocomposite exhibited better electrical conductivity than CNT and ITO case due to the unique electrical property of xGnP, and this nanocomposite also showed good sound characteristics. Interfacial adhesion durability between either neat CNT or plasma treated CNT and plasma treated PVDF were measured by static contact angle, surface energy, work of adhesion, and spreading coefficient tests. The optimum acoustic actuation performance of xGnP coated PVDF nanocomposite was measured using sound level meter with changing radius of curvature and coating conditions. As compared to CNT and ITO, the xGnP was known as more appropriate acoustic actuator due to the characteristic electrical property. It is the most appropriate condition when the radius of curvature is 15 degree. Although sound characteristics were different with various coating thicknesses, it is possible to manufacture transparent actuator with good sound quality.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.3
• /
• pp.40-43
• /
• 2017

Carbon coating approach is used to prepare carbon-doped $MgB_2$ bulk samples using low-cost naphthalene ($C_{10}H_8$) as a carbon source. The coating of carbon (C) on boron (B) powders was achieved by direct pyrolysis of naphthalene at $120^{\circ}C$ and then the C-coated B powders were mixed well with appropriate amount of Mg by solid state reaction method. X-ray diffraction analysis revealed that there is a noticeable shift in (100) and (110) Bragg reflections towards higher angles, while no shift was observed in (002) reflections for $MgB_2$ doped with carbon. As compared to un-doped $MgB_2$, a systematic enhancement in $J_c(H)$ properties with increasing carbon doping level was observed for naphthalene-derived C-doped $MgB_2$ samples. The substantial enhancement in $J_c$ is most likely due to the incorporation of C into $MgB_2$ lattice and the reduction in crystallite size, as evidenced by the increase in the FWHM values for doped samples.

• Fire Science and Engineering
• /
• v.27 no.4
• /
• pp.41-46
• /
• 2013

The present study has been conducted to investigate the reaction kinetics and pyrolysis parameters for flame propagation analysis of furniture material components. TGA measurement for component materials such as MDF (medium density fiberboad) panel including coating material, synthetic leather and foam cushion are performed under maximum temperature of $600^{\circ}C$ and heating rate of $10^{\circ}C/min$. The results of TGA have shown that the peak temperature of MDF panel was $324^{\circ}C$ and the initial peak temperature of coating material decreased by $270{\sim}280^{\circ}C$. In the case of synthetic leather and foam materials, the reference temperature and reference rate depend on the type of polymer consisting the sample, the initial kinetic characteristics was classified into 2 categories of about $270^{\circ}C$ and $420^{\circ}C$ of reference temperature for the tested synthetic materials. The present study showed the pyrolysis parameters of reference temperature and reference rate proposed by Lyon to evaluate the pre-exponential factor and activation energy. The present study can contribute to improve the reliability of computational fire analysis and enhance the understanding of fire propagation phenomena based on the thermal properties study of material.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1850-1852
• /
• 2005

$SrTiO_3$ and $BaTiO_3$ sol-liquids and powders were prepared by the sol-gel method. $SrTiO_3/BaTiO_3$ heterolayered thin/thick films have been prepared on the $Al_2O_3$ substrates by screen printing and spin-coating method. The thin films were sintered at $750^{\circ}C$ in the air for 1 hour and the thick films sintered at $1325^{\circ}C$ in the air for 2 hours, respectively. The $SrTiO_3/BaTiO_3$ thin/thick films's structural and dielectric properties were investigated. Increasing the spin-coating times, (110), (200), (211) peaks of the $SrTiO_3$ were increased. The X-ray diffraction(XRD) patterns and SEM photographs indicated that the $SrTiO_3$ phase were formed in the surface of $BaTiO_3$ thick films. The average thickness of a $BaTiO_3$ thick films and $SrTiO_3$ thin films were $50{\mu}m$ and 400nm, respectively The dielectric constant and dielectric loss of the $SrTiO_3/BaTiO_3$ thin/thick films with $SrTiO_3$ coated 5 times were 1598 and 0.0436 at 10KHz.

• Journal of Surface Science and Engineering
• /
• v.50 no.5
• /
• pp.339-344
• /
• 2017

Highly corrosion resistance performance of CrAlSiN coatings were obtained by applying ultrathin $Al_2O_3$ thin films using atomic layer deposition (ALD) method. CrAlSiN coatings were prepared on Cr adhesion layer/SUS304 substrates by a hybrid coating system of arc ion plating and high power impulse magnetron sputtering (HiPIMS) method. And, ultrathin $Al_2O_3$ passivation layer was deposited on the CrAlSiN/Cr adhesion layer/SUS304 sample to protect CrAlSiN coatings by encapsulating the whole surface defects of coating using ALD. Here, the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX) analysis revealed that the ALD $Al_2O_3$ thin films uniformly covered the inner and outer surface of CrAlSiN coatings. Also, the potentiodynamic and potentiostatic polarization test revealed that the corrosion protection properties of CrAlSiN coatings/Cr/SUS304 sample was greatly improved by ALD encapsulation with 50 nm-thick $Al_2O_3$ thin films, which implies that ALD-$Al_2O_3$ passivation layer can be used as an effect barrier layer of corrosion.

• Journal of Conservation Science
• /
• v.37 no.3
• /
• pp.302-311
• /
• 2021

This study uses traditional lacquer techniques to coat the metal surface and evaluates its physical properties to check the applicability of the lacquer coating. For this purpose, a total of six specimens were produced by setting the variation conditions for the number of times (1, 2, 3) and the heating temperature (120℃, 150℃) using SS275 metal(60*60 mm) and 'Wonju lacquer'. For analysis, chromaticity measurements, contact angle/surface energy measurements, Chemical Resistance, and cross-cut tests were used. The analysis showed that the corrosivity was improved and the adhesion of lacquer to the metal surface was excellent. There was no significant change in contact angle/surface energy. Also, there was no significant difference in color. Through this study, it was confirmed that lacquer on metal surfaces improves waterproofing and has a anticorrosion effect. We could also check the proper number of lacquer and heating temperature. Additional physical characteristics such as hardness and wear rate should be studied. It is also necessary to study how lacquer can be painted with a certain thickness.