• Restorative Dentistry and Endodontics
• /
• v.12 no.2
• /
• pp.45-53
• /
• 1987

The purpose of this study was to evaluate the tensile bond strength between composite resin and the human enamel. Three composite resin systems, two chemical (Clearfil Posterior, and Clearfil Posterior-3) and one light cure (Photo Clearfil-A), used with and without an intermediate resin (clearfil bonding agent), were evaluated under different amounts of load (10g, 200g and 200g for a moment) for in vitro tensile bond strength to acid-eched human enamel. Clinically intact buccal or lingual surfaces of 144 freshly extracted human permanent molars, embedded in acrylic were flattened with No #600 carborundum discs. Samples were randomly assigned to the different materials and treatments using a table of random numbers. Eight samples were thus prepared for each group(Table 2) these surfaces were etched with an acid etchant (Kurarey Co. Japan) in a mode of etching for 30 seconds, washing for 15 seconds, and drying for 30-seconds. During the polymerization of composite resin on the acid-etched enamel surfaces with and without bonding agent 10-gram, 200 gram and temporary 200 gram of load were applied. The specimens were stored in 50% relation humidity at $37^{\circ}C$ for 24 hours before testing. An universal Testing machine (Intesco model No. 2010, Tokyo, Japan) was used to apply tensile loads in the vertical directed (fig 5), and the force required for separation was recorded with a cross head speed of 0.25 mm/min and 20 kg in full scale. The results were as follow: 1. The tensile bond strength was much greater in applying a bonding agent than in not doing that. 2. The tensile bond strength of chemical cure composite resin was higher than that of light cure composite resin with applying on bonding agent on the acid-etched enamel. 3. In case of not applying a bonding agents on the acid-etching enamel, the highest tensile bond strength under 200 gram of load was measured in light cure composite resin. 4. The tensile bond strength under 200-gram of load has no relation with applying the bonding agent. 5. Under the load of 10-gram, There was significant difference in tensile bond strength as applying the bonding agent.

• Composites Research
• /
• v.23 no.4
• /
• pp.21-27
• /
• 2010

In most engineering structures, fracture often takes place due to fatigue. Therefore, many studies about the effect of the various mode-mixities on fatigue characteristics have been performed. However, most of the former studies only address metal/metal interfaces or delamination of composite. In this study, the fatigue characteristics of composite/metal interfaces are investigated. The fatigue tests were performed using single leg bending(SLB)specimens that comprise composite and steel bonded to each other using co-cure bonding method. This paper focuses on fatigue characteristics depending on different mode ratios$(G_{II}/G_T$. The overall results obtained in this study show that the crack propagation rate increases with the mode II loading component.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.36 no.3
• /
• pp.211-216
• /
• 2016

In several industrial fields, epoxy resin is widely used as an adhesive for co-curing and manufacturing various structures. Controlling the manufacturing process is required for ensuring robust bonding performance and the stability of the structures. A fiber optic sensor is suitable for the cure monitoring of epoxy resin owing to the thready shape of the sensor. In this paper, a fiber Bragg grating (FBG) sensor was applied for the cure monitoring of epoxy resin. Based on the experimental results, it was demonstrated that the FBG sensor can monitor the status of epoxy resin curing by measuring the strain caused by volume shrinkage and considering the compensation of temperature. In addition, two types of epoxy resin were used for the cure-monitoring; moreover, when compared to each other, it was found that the two types of epoxy had different cure-processes in terms of the change of strain during the curing. Therefore, the study proved that the FBG sensor is very profitable for the cure-monitoring of epoxy resin.

• Journal of the Korean Society of Safety
• /
• v.12 no.4
• /
• pp.57-62
• /
• 1997

The combined structure of hybrid composite made through the bonding process of materials of different properties greatly defines its mechanical characteristics, as the results of the experiments on materials of different properties show much dissimilarity. When carbon/epoxy materials are applied to hybrid composite, the carbon materials helps to improve the mechanical properties of the hybrid composite, and the epoxy reduces its fracture strain and impact resistance. Carbon fiber which is now in general commercialization is classified as high modulus or high strength system, and its manufacturing methods are various. The study of the materials having combined structure is focused on the numerical analysis of the layers of bonding surface in materials with difference modulus. The hybrid composite made through the multilayered bonding of reinforced aluminium sheets with aramid fiber now faces the marketing phase, and especially its excellent fatigue resistance and mechanical properties promote active researches on the similar products of hybrid composite. This study aims to investigate the effects of CFRP volume ratio and fiber's orientation over the properties of mechanical strength and fatigue life of the hybrid composite, AI7075/CFRP. To carry out this study, static tensile and fatigue tests were given to some of the panels which, made through the co-cure processing in an autoclave, have different CFRP volume ratio and carbon fiber orientations.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.4
• /
• pp.189-196
• /
• 2020

PURPOSE. The aim of the present study was to investigate the effects of surface treatments on the bond strengths between polymer-containing restorative materials and two dual-cure resin cements. MATERIALS AND METHODS. In the present study, rectangular samples prepared from Lava Ultimate (LU) and Vita Enamic (VE) blocks were used. The specimen surfaces were treated using CoJet sandblasting, 50 ㎛ Al₂O₃ sandblasting, % 9 HF (hydrofluoric) acid, ER,Cr:YSGG laser treatment, and Z-Prime. Dual-cure resin cements (TheraCem and 3M RelyX U 200) were applied on each specimen's treated surface. A micro-tensile device was used to evaluate shear bond strength. Statistical analysis was performed using the SAS 9.4v3. RESULTS. While the bond strength using TheraCem with LU or VE was not statistically significant (P=.164), the bond strength using U200 with VE was statistically significant (P=.006). In the TheraCem applied VE groups, Z-Prime and HF acid were statistically different from CoJet, Laser, and Sandblast groups. In comparison of TheraCem used LU group, there was a statistically significant difference between HF acid and other surface treatments. CONCLUSION. The bonding performance between the restorative materials and cements were material type-dependent and surface treatment had a large effect on the bond strength. Within the limitations of the study, the use of both U200 and TheraCem may be suggested if Z-prime was applied to intaglio surfaces of VE. The cementation of LU using TheraCem is suitable after HF acid conditioning of the restoration surfaces.

• The korean journal of orthodontics
• /
• v.41 no.2
• /
• pp.121-126
• /
• 2011

Objective: The purpose of this study was to evaluate shear bond strength (SBS) and failure site location of brackets bonded to enamel with or without desensitizer application. Methods: Sixty-six freshly extracted human premolar teeth were randomly divided into 3 groups of 22. Group 1 served as the control. Desensitizer was applied to the remaining teeth at two time intervals (Group 2, bonded immediately after Pro-$Relief^{TM}$ (Colgate-Palmolive Co., New York, NY, USA) application and Group 3, bonded 30 days after Pro-$Relief^{TM}$ application with the teeth stored in artificial saliva during the 30 days). Orthodontic brackets were bonded with a light cure composite resin and cured with a halogen light. After bonding, the SBS of the brackets was tested using a universal testing device. Adhesive remnant index (ARI) scores were determined after the brackets failed. Data were analyzed with analysis of variance, Tukey's HSD, and G tests. Results: The SBS was significantly lower in Group 2 than in Groups 1 (p = 0.024) and 3 (p = 0.017). Groups 1 and Group 3 did not differ (p = 0.991). ARI scores did not differ significantly among groups. Conclusions: The Pro-$Relief^{TM}$ desensitizer agent applied immediately before bonding significantly reduces bond strength, but the SBS values still exceed the minimum 5.9 - 7.8 MPa required for adequate clinical performance. Immersing the teeth in artificial saliva for 30 days after applying the Pro-$Relief^{TM}$ desensitizer agent and before bonding increased the SBS to control levels.

• Journal of the Korean Chemical Society
• /
• v.46 no.3
• /
• pp.233-240
• /
• 2002

In this work, the cure kinetics and rheological and mechanical properties of diglycidylether of bispheonol A (DGEBA, EP)/polyurethane (PU) blends were investigated. The 1 wt% N-benzylpyrazinium hexafluoroantiminate (BPH) was used as a latent thermal catalyst. Latent properties were performed by measurement of the conversion as a function of reaction temperature using DSC. And the rheological properties of the blend systems were investigated under isothermal conditions using a rheometer. Crosslinking activating energies (Ec) were also determined from the Arrhenius equation based on gel time and curing temperature. The impact strengths were measured as mechanical properties of the casting specimens. The BPH in the blend systems could be an excellent latent thermal catalyst without any co-initiator. The rheological results showed that Ec was highest when PU content was 30 wt% which was in good agreement with the impact strengths. This was probably due to the intermolecular hydrogen bonding between the hydroxyl group in PU and EP, resulting in increasing the crosslinking density.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2004.04a
• /
• pp.404-409
• /
• 2004

To maximize the productivity in machining molds and dies, machine tools should operate at high speeds. During the high speed operation of moving frames or spindles, vibration problems are apt to occur if the machine tool structures are made of conventional steel materials with inferior damping characteristics. However, self-excited vibration or chatter is bound to occur during high speed machining when cutting speed exceeds the stability limit of machine tool. Chatter is undesirable because of its adverse effect on surface finish, machining accuracy, and tool life. Furthermore, chatter is a major cause of reducing production rate because, if no remedy can be found, metal removal rates have to be lowered until vibration-free performances is obtained. Also, the resonant vibration of machine tools frequently occurs when operating frequency approaches one of their natural frequencies because machine tools have several natural frequencies due to their many continuous structural elements. However, these vibration problems are closely related to damping characteristics of machine tool structures. The polymer concrete has high potential for machine tool bed due to its good damping characteristics with moderate stiffness. This paper presents the use of polymer concrete and sandwich structures to overcome vibration problems. Also, co-cure bonding method for functional part mounting was exhibited experimentally, by which manufacturing time and cost for polymer concrete bed will be remarkably reduced.

• Restorative Dentistry and Endodontics
• /
• v.15 no.1
• /
• pp.107-119
• /
• 1990

The purpose of this study was to evaluate the marginal adaptability of the amalgam restorations in applying the cavity varnish (Copalite$^{(R)}$) and dentin bonding agent (Scotchbond 2$^{(R)}$) under the scanning electron microscope. For this study, eighteen sound extracted human molars were selected. Class I cavities in 12 teeth and class V cavities in 6 teeth were prepared using an air turbine with No. 701 tungsten carbide bur and finished using a low speed handpiece with No. 557 fissure bur. The prepared specimens were then divided into three groups including 4 class I cavities and 2 class V cavities in each group and restored as follows ; Group I. All the prepared cavities were restored with amalgam only (Control). Group II. Two layers of Copalite$^{(R)}$ cavity varnish were applied to the cavities with a gentle stream of air after each application and cavities were restored with amalgam. Group III. The enamel cavity margins were etched with 37% phosphoric acid gel for 60 sec., rinsed for 30 sec. and dried. One layer of visible lightcured Scotchbond Dental Adhesive$^{(R)}$ was applied and immediately cured for 20 seconds with visible light-cure unit and cavities were restored with amalgam. All the specimens were cut at the neck of the teeth and the occlusal halves of specimens were sectioned buccolingually in the longitudinal axis centering the amalgam restorations, using the disk. The cut specimens were ground with sandpapers (400, 600, 800, 1000 grit), and cleaned for 5 minutes in the ultrasonic cleaner (Brason Co. U.S.A.). In the cut surfaces, the amalgam - tooth interfaces were examined under the scanning electron microscope (JSM, 35C type, JEOL). The obtained results were as follows ; 1. The amalgam-tooth interfaces were reduced more significantly in the Copalite$^{(R)}$ and Scotchbond 2$^{(R)}$ application group than in the control group. 2. In the class I cavities, the Scotchbond 2$^{(R)}$ application group showed the findings similar to the Copalite$^{(R)}$ application group in the cavity floor, and the marginal adaptability was better in the side wall than in the cavity floor. 3. In the class I cavities, the Scotchbond 2$^{(R)}$ application group showed better marginal adaptability in the occlusal margin than in the gingival margin. 4. The marginal adaptability was in the order of the Scothbond 2$^{(R)}$ application group, the Copalite$^{(R)}$ application group and the control group.

• The korean journal of orthodontics
• /
• v.38 no.4
• /
• pp.275-282
• /
• 2008

Objective: The purpose of this study was to investigate the effect of using laser for ceramic bracket bonding of porcelain surfaces and to compare it with conventional treatment of porcelain surfaces. Methods: Ninety feldspathic porcelain specimens were divided into 9 groups of 10, with each group having different surface treatments performed. Surface treatment groups were orthophosphoric acid, orthophosphoric acid with silane, hydrofluoric acid, hydrofluoric acid with silane, sandblasted, sandblasted with silane, laser etched, laser etched with silane, and glazed surface served as a control group. In the laser etched groups, the specimens were irradiated with 2-watt superpulse carbon dioxide ($CO_2$) laser for 20 seconds. Ceramic brackets were bonded with light-cure composite resin and all specimens were stored in water at $37^{\circ}C$ for 24 hours. Shear bond strength was determined in megapascals (MPa) by shear test at 1 mm/minute crosshead speed and the failure pattern was assessed. For statistical analysis, one-way ANOVA and tukey test were used. Results: Statistical analysis showed significant differences between the groups. The HFA + S group showed the highest mean shear bond strength ($13.92{\pm}1.94\;MPa$). This was followed by SB + S ($10.16\;{\pm}\;1.27\;MPa$), HFA ($10.09\;{\pm}\;1.07\;MPa$), L + S ($8.25\;{\pm}\;1.24\;MPa$), L ($7.86\;{\pm}\;0.96\;MPa$), OFA + S ($7.22\;{\pm}\;1.09\;MPa$), SB ($3.41\;{\pm}\;0.37\;MPa$), OFA ($2.81\;{\pm}\;0.37\;MPa$), G ($2.46\;{\pm}\;1.36\;MPa$), Bond failure patterns of HFA and silane groups, except L + S, were cohesive modes in porcelain while adhesive failure was observed in the control group and the rest of the groups. Conclusions : A 2-watt superpulse $CO_2$ laser etching of porcelain surfaces can provide a satisfactory result for porcelain surface treatment for ceramic bracket bonding. Laser irradiation may be an alternative conditioning method for the treatment of porcelain surfaces.