• Journal of Soil and Groundwater Environment
• /
• v.9 no.2
• /
• pp.20-27
• /
• 2004

Kinetic characteristics dependent on several factors such as iron mineral and organic solvents were investigated. When F $e^{0}$ , FeS and Fe $S_2$ were used as mediators, minerals affecting reaction rate were in the following order : $Fe_{0}$ 0/ ＞ FeS ＞ $FeS_2$ when in contact $C_2$C $l_{6}$ . The more chloride substituted, the higher reaction rate were observed. The reaction rates were dependent on pH, shaking rate, temperature and specific surface area. 1, 10-phenanthroline and EDTA degradation rates were fast, indicating that they adsorbed on the surface of the iron which makes the electron transfer reaction easy. Nitrate which has $\pi$＊ orbital of molecular can increase electron transfer rate because it is delocalized in its entity. The reaction rates were not affected by hydroquinone. Degradation rates were much enhanced with naturally occurring kaolinite because of the surface corrosion of Fe mineral. However, The reaction rate was not affected by F $e^{2+}$ or S $O_4$$^{2-}$ presented in solution.n.

• 한국문화재보존과학회:학술대회논문집
• /
• 2002.02a
• /
• pp.45-52
• /
• 2002

본 연구에서는 KaOH, $K_2CO_3$, Sodium, 그리고 1차 이온수 용액의 $Cl^-$ 이온 추출량과 부식생성물의 생성순위, 부식물 생성, 그리고 부식물 제거에 관하여 관찰하였으며 이 연구로 아래와 같은 결과를 얻었다. $Cl^-$ 이온 추출량에 대한 실험 결과 NaOH은 탈염 초기에는 Cl- 이온을 잘 추출시켰으나 탈염 횟수가 증가하면서 $Cl^-$ 이온의 추출량이 급감하였다. 또한 유물 중량 변화에도 감소폭이 가장 심하였다. $K_2CO_3$은 NaOH나 1차이온수 용액과 비교해 보면 이 방법은 탈염처리동안 $Cl^-$ 이온을 꾸준히 추출시켜 주었으며 다른 탈염용액에 비해 유물 중량변화가 거의 관찰되지 않았다. Sodium 용액은 $K_2CO_3$ 용액과 마찬가지로 탈염처리 동안 $Cl^-$ 이온을 꾸준히 추출시켰으며 다른 탈염 용액에 비해 $Cl^-$ 이온 추출량이 가장 많았다. 하지만 이 용액은 약품 내에 불순물인 $Cl^-$ 이온을 $3\~5\;ppm$을 기지고 있어 보존처리자가 탈염처리를 할 때 좀 더 신중하게 생각해야 할 것 같다. 1차 이온수 용액은 부식인자가 $Cl^-$이온을 완전하게 제거해주지는 못하였지만, pH가 $7.5\~7.9$로 다른 탈염 용액에 비해서 전위차가 낮으며, 별도로 탈알칼리 처리를 하지 않아도 되기 때문에 유물손상은 극소화할 수가 있다. 따라서 이 용액은 부식이 매우 심한 철제 유물이나 균열이 많은 주조 철편과 같은 유물을 처리할 때 적절한 용액이다. 부식생성물 관찰에서는 출토 철기 유물에 생성된 부식물은 주로 인철광$(\gamma-FeOOH)$, 침철광$(\alpha-FeOOH)$, 적금광$(\beta-FeOOH)$, 그리고 자철광$(Fe_3O_4)$이다. 인위적 부식에서는 전부 인철광의 부식물이 생성되었고 자연적 부식에서는 모두 침철광의 부식물이 생성되었다. 특히 철제 표면에 자연적으로 생성된 공식 녹을 XRD 분석한 결과 적금광으로 동정되었다. 이런 모든 시편들을 각 탈염방법에 따라 탈염처리한 후 XRD와 SEM-EDS으로 분석한 결과 인철광과 침철광은 어떠한 변화도 보이지 않았고, 다만 적금광으로 동정된 시편만이 잔존하지 않았다. 철기 제작별 $Cl^-$ 이온 추출량과 탈염효과에 대한 비교 실험은 이온 크로마토그래피 분석 결과와 마찬가지로 단조 철제유물이 주조 철제보다 $Cl^-$ 이온을 많이 가지고 있었으며, 탈염 처리 후에는 $Cl^-$ 이온은 전혀 발견되지 않았다. 이상의 결과 $K_2CO_3$와 Sodium 용액은 탈염처리에서 가장 적합한 탈염처리 용액으로 알수가 있었으며 특히 어떠한 탈염 용액으로 유물을 처리한다 해도 철제유물에 생성된 부식물은 제거되지 않는다는 것을 알게 되었다. 따라서 보존처리자는 유물 표면의 부식 상태만을 보고 처리하기 보다는 철기제작물로 고려하여 처리하는 것이 필요하다. 또한 금속에 부식을 야기시키는 $Cl^-$ 이온과 부식물을 완전하게 제거하여 탈염처리를 하는 것이 유물 부식을 최대한 지연시킬 수 있는 것이라 생각된다.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.641-650
• /
• 2010

The concrete cracking from the restrained stress caused by the shrinkage may play significant cause of deterioration of concrete structures by allowing the permeation of sulphate and chloride ions which in turn triggers corrosion of steel reinforcement. In particular, the cracking becomes more critical as water binder ratio (W/B) is reduced and concrete strength increases. Therefore, it needs to evaluate correctly the comprehensive shrinkage behavior of concrete with high strength: high-strength concrete (HSC), ultra-highstrength concrete (UHSC). The unrestrained shrinkage tests, however, cannot estimate the net shrinkage effectively which affects cracking after full development of strength and stiffness because it does not consider the degree of restraint, strength development, stress relaxation, and so on. Therefore, in this study, both free and restrained shrinkage tests with variables of W/B (W/B of 30, 25 and 16%) and admixtures (fly ash (FA) and granulated blast-furnace slag (BFS)) for HSC, very-high-strength concrete (VHSC) and UHSC were performed. The test results indicated that the autogenous shrinkage and total shrinkage at drying condition were reduced as W/B increased and FA, BFS were added, and the cracking behavior was suppressed as W/B increased and FA was added.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.1
• /
• pp.67-72
• /
• 2022

Concrete prevents corrosion of reinforcing bars due to its strong alkalinity. However, in the sea, strong alkali components with a pH of 12 to 13 are eluted, which adversely affects the ecological environment and growth of marine organisms. In this study, the mechanical properties and durability of the low alkali mortar were evaluated for the development of a low alkali mortar for the 3D printed artificial reefs. As a result of evaluation of strength characteristics, the α-35 mixture, which were produced with fly ash, silica fume and α-hemihydrate gypsum, satisfied the strength requirement 27 MPa in terms of compressive strength. As a result of pH measurement, it was found that mixing with alpha-type hemihydrate gypsum resulted in minimizing pH due to the the formation of calcium sulfate instead of calcium hydroxide production. As a result of the chloride ion penetration resistance test, the α-35 mixture exhibited the best performance, 3844C. As a result of measuring the length change over time, the α-35 mixture showed the shrinkage 33.5% less compared to the Plain mix.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.482-488
• /
• 2022

In this study, the durability of ultra rapid hardening mortar for sewage pipe was evaluated by type of mortar binder. As a result of analyzing the internal structure for each type of mortar, it was confirmed that Al₂(OH)₃ was generated in the internal structure of the CAC-based mortar, and its corrosion resistance was superior to that of other types of mortar. As a result of the compressive strength test, OPC had the tsmallest strength, followed by CAC100 > CAC100P > CAC80. This trend was similar to the previous study results. Chloride ion penetration resistance and freeze-thaw test showed similar trends. That is, CAC and C12A7 were better than OPC, and CSA was worse than OPC. This is mostly beacuse of cracks caused by expansion of CSA-based mortar. CAC100P mix showed the best chemical resistance. It is thought that this is because the alumina gel formed inside the mortar and the polymer combine to make the internal structure more dense.