• Korean Journal of Materials Research
• /
• v.32 no.12
• /
• pp.515-521
• /
• 2022

Various types of optical materials and devices used in special environments must satisfy durability and optical properties. In order to improve the durability of zinc sulfide multispectral (MS ZnS) substrates with transmission wavelengths from visible to infrared, Ge-Sb-Se-based chalcogenide glass was used as a sealing material to bond the MS ZnS substrates. Wetting tests of the Ge-Sb-Se-based chalcogenide glass were conducted to analyze flowability as a function of temperature, by considering the glass transition temperature (T_g) and softening temperature (T_s). In the wetting test, the viscous flow of the chalcogenide glass sample was analyzed according to the temperature. After placing the chalcogenide glass disk between MS ZnS substrates (20 × 30 mm), the sealing test was performed at a temperature of 485 ℃ for 60 min. Notably, it was found that the Ge-Sb-Se-based chalcogenide glass sealed the MS ZnS substrates well. After the MS ZnS substrates were sealed with chalcogenide glass, they showed a transmission of 55 % over 3~12 ㎛. The tensile strength of the sealed MS ZnS substrates with Ge-Sb-Se-based chalcogenide glass was analyzed by applying a maximum load of about 240 N, confirming its suitability as a sealing material in the far infrared range.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.9
• /
• pp.641-645
• /
• 2013

Chalcogenide glass has superior property of optical transmittance in the infrared region. Glass made using Ge-Se how many important optical applications. We have determined the composite formular of $Ge_{0.25}Se_{0.75}$ to be the GeSe chalcogenide glass composition appropriate for IR lenses. Also, the optical, thermal and physical characteristics of chalcogenide glass depended on the composition ratio. GeSe bulk sample is produced using the traditional melt-quenching method. The optical, structural, thermal and physical properties of the compound were measured by using Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), Differential scanning calorimeter (DSC), and Scanning electron microscope (SEM) respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.8
• /
• pp.624-628
• /
• 2013

With the recent development of less-costly uncooled detector technology, expensive optics are among the remaining significant cost drivers in the thermography camera. As a potential solution to this problem, the fabrication of IR lenses using chalcogenide glass has been studied in recent years. We report on the molding and evaluation of a ultra-precision chalcogenide-glass lens for the thermography camera for body-temperature monitoring. In addition, we fabricated prototype thermography camera using the chalcogenide-glass lens and obtained the thermal image from the camera. In this work, it was found out that thermography camera discerned body-temperature between 20 and $50^{\circ}C$ through the analysis of thermal image. It is confirmed that thermography camera using the chalcogenide-glass lens is applicable to the body-temperature monitoring system.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.8
• /
• pp.60-66
• /
• 2021

This study aimed at identifying and optimizing the heating-condition parameters that cause surface defects during the compression molding of chalcogenide glass (GeSbSe) lenses through thermal analysis. We derived the optimal heating conditions for molding chalcogenide glass lenses through thermal analysis and analyzed the surface defects. As a result, we observed a significant reduction in surface defects, which verified the analysis process.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.06a
• /
• pp.463-464
• /
• 2009

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.3
• /
• pp.183-189
• /
• 2013

The chalcogenide glass has superior optical properties in IR region transmittances. We have determined the composition of GeSbSe chalcogenide glass for the application of good IR lenses, resulting in the composite rate of $Ge_{19}Sb_{23}Se_{58}$. The optical, structural, thermal and physical properties were measured by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), Differential scanning calorimeter (DSC), X-ray computed tomography (X-ray CT) respectively. The fabrication of the chalcogenide glass lens for infrared optics applications was proposed using a diamond turning machining technology which is known as the suitable ways for the production cost reduction and the accurate fabrication process control.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.19 no.3
• /
• pp.388-393
• /
• 2010

In recent years the research has been focused on the preparation of special glasses, i.e., chalcogenide and heavy metal oxide ones that can transmit optical radiation above 2 um and also other optical parameters exceed those of silica based glasses. The attention in this paper is focused on chalcogenide glasses, on preparation of high quality base glass, for an application in infrared optical product design and manufacture. The amorphous materials of As-Se and Ge-As-Se chalcogenides were prepared by a standard melt-quenching technique. The compositions were mesaured by ICP-AES and EPMA, and structural and thermal properties were studied through various annealing processes. Several anomalies of glass transition and crystallization were observed in the DSC/DTA/TG results of the chalcogenide glass.

• Journal of the Korean Ceramic Society
• /
• v.33 no.8
• /
• pp.855-862
• /
• 1996

The nucleation and the crystal growth rates of Ge-Se-Te chalcogenide glass by two step heat-treatment and its effect on the mechanical optical properties and water-resistance were determined. The maximum nuclea-tion and crystal growth rate were 2.1$\times$103/mm3 .min at 28$0^{\circ}C$ and 0.4${\mu}{\textrm}{m}$/min at 33$0^{\circ}C$ respectively. When the crystal volume fraction with crystal size $1.5mutextrm{m}$ was about 4% the (hardness and fracture toughness were about 117kg/mm2 and 6.0 MPa.mm1/2)respectively. The weight loss of crystallized glass in water was lower than parent glass($25^{\circ}C$ for 32 hrs : 0.03% 8$0^{\circ}C$ for 16 hrs : 0.1%) as 0.01% at $25^{\circ}C$, 0.03% at 8$0^{\circ}C$ for 16 hrs : 0.1%) at $25^{\circ}C$ 0.03% at 8$0^{\circ}C$ respectively. The IR-transmittance decreased with increasing crystal size and crystal volume fraction. The IR-transmittance of crystallized glass with the crystal size of $1.5mutextrm{m}$ (crystal volume fraction : 4%) presented 56% which was about 4% lower than that of parent glass.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.06a
• /
• pp.193-194
• /
• 2009

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.6
• /
• pp.43-48
• /
• 2020

This study explores the compression molding of diffractive-aspheric lenses using GeSbSe chalcogenide glasses. A mold core with diffractive structure was prepared and a chalcogenide glass lens was molded at various temperatures using the corresponding core. The effect of molding temperature on the transcription characteristics of diffractive structure was examined, by measuring and comparing the diffractive structure between the mold core and the molded chalcogenide glass lens using a microscope and a white light interferometer. In addition, the applicability of the molded lens for thermal imaging was evaluated, by measuring the form error.