• Clean Technology
• /
• v.21 no.3
• /
• pp.200-206
• /
• 2015

In order to investigate the effect of cerium oxide addition, Cu-ZnO-CeO₂ catalysts were prepared using co-precipitation method for water gas shift (WGS) reaction. A series of Cu-ZnO-CeO₂ catalyst with fixed Cu Content (50 wt%, calculated as CuO) and a given ceria content (e.g., 0, 5, 10, 20, 30, 40 wt%, calculated as CeO₂) were tested for catalytic activity at a GHSV of 95,541 h^-1, and a temperature range of 200 to 400 ℃. Cu-ZnO-CeO₂ catalysts were characterized by using BET, SEM, XRD, H₂-TPR, and XPS analysis. Varying composition of Cu-ZnO-CeO₂ catlysts led the difference characteristics such as Cu dispersion, and binding energy. The optimum 10 wt% doping of cerium facilitated catalyst reduction at lower temperature and improved the catalyst performance greatly in terms of CO conversion. Cerium oxide added catalyst showed enhanced activities at higher temperature when it compared with the catalyst without cerium oxide. Consequently, ceria addition of optimal composition leads to enhanced catalytic activity which is attributed to enhanced Cu dispersion, lower binding energy, and hindered Cu metal agglomeration.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.104-104
• /
• 1999

Cerium dioxide 박막의 포토루미네슨에 관해서는 Cerium 4f band에서 oxygen 2p band로의 transition에 의한 발광(400nm) 현상이 보고되었다. 또한 Indium Oxide 박막의 발광(637nm0 현상이 보고되었다. 본 연구에서는 3족인 Indium을 Si/In/CeO2/Si 구조와 CeO2/Si 구조에 도핑하여 포토루미네슨스 현상을 관찰하였다. E-beam evaporator를 사용하여 Silicon(111) 기판에 Cerium dioxcide 박막을 성장시킨 경우의 두가지 시료를 분석하였다. 포토루미네슨스 관찰을 위해서 Ge-Cd laser (325nm)가 사용되었으며 Indium의 도핑양과 분포 상태를 알기 위해 SIMS와 ADP를 이용하여 분석하였다. Indium양에 대한 포토루미네슨스 변화와 열처리 후의 indium의 분포의 변화에 의한 포토루미네슨스 변화를 관찰하였다. 상온에서 In/CeO2/Si 시료와 Si/In/CeO2/Si 시료에 대한 포토루미네슨스 현상을 관찰한 결과 Si/In/CeO2/Si 시료에서만 500nm(2.5eV)에서 발광 현상이 관찰되었다. 도핑된 indium은 ADP에서는 검출되지 않고 SIMS에서만 검출되어 ADP의 detection range(1-0.1%) 이하의 양이 도핑된 것으로 추측된다. 도핑된 Indium의 양이 증가할수록 포토루미네슨스의 Intensity가 증가하였다. 또한 열처리(110$0^{\circ}C$, 1min) 후 포토루미네슨스의 peak위치가 390nm(3.18eV)로 변화하였다. Si/In/CeO2/Si에서 포토루미네슨스 현상이 관측되고 Intensity가 indium의 양에 의존하므로 완전하지 못한 Cerium dioxide의 CeOx 구조와 indium과의 결합이 포토루미네슨스의 원인으로 추측된다. 열처리 후 SIMS의 분석결과 indium의 분포가 변화하였으며 이는 포토루미네슨스의 변화의 원인으로 판단된다.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.29.2-29
• /
• 2003

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.08a
• /
• pp.64.4-64
• /
• 1998

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.9
• /
• pp.803-809
• /
• 2005

Cerium ammonium nitrate (CAN) and nitric acid was used an etchant and an additive for Ru etching and polishing. pH and Eh values of the CAN and nitric acid added chemical solution satisfied the Ru etching condition. The etch rate increased linearly as the concentration of CAN increased. Nitric acid added solution had the high etch rate. But micro roughness of etched surfaces was not changed before and after etching, The removal rate of Ru film was the highest in $1wt\%$ abrasive added slurry, and not increased despite the concentration of alumina abrasive increased to $5wt\%$. Even Ru film was polished by only CAN solution due to the friction. The highest removal rate of 120nm/min was obtained in 1 M nitric acid and $1wt\%$ alumina abrasive particles added slurry. The lowest micro roughness value was observed in this slurry after polishing. From the XPS analysis of etched Ru surface, oxide layer was founded on the etched Ru surface. Therefore, Ru was polished by chemical etching of CAN solution and oxide layer abrasion by abrasive particles. From the result of removal rate without abrasive particle, the etching of CAN solution is more dominant to the Ru CMP.

• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.6-13
• /
• 2004

The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of Alloy 600(UNS N06600) was evaluated in 10% sodium hydroxide solution at $315^{\circ}C$. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours with and without inhibitors such as titanium oxide, titanium boride and cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in no inhibitor solution. It was found that the changes of the active-passive transition potentials and the film compositions were related to the resistance to stress corrosion cracking in high temperature caustic solution.

• Proceedings of the KAIS Fall Conference
• /
• 2010.11a
• /
• pp.318-322
• /
• 2010

NaZSM 5 was synthesized in an alkaline medium and impregnated with cerium oxide by wet method using cerium nitrate as the source for cerium. There TGA results shows decomposition of nitrate at $200^{\circ}C$. The ceria impregnated ZSM 5 materials were designated as NaZSM 5 (X) where X is the percent ceria impregnated (3, 5, 7, 11, 19%). They were characterized by XRD, SEM, EDAX, BET techniques. XRD analysis showed decrease in intensity of the patterns with the increase in the ceria loading but crystallization of ceria to larger size is evident for 11 and 19% loading. The surface area and pore volume decreased with increase in ceria loading. The maximum adsorption capacity of NaZSM 5 (5%) is 100.2 mg/g of sorbent. The ceria impregnated NaZSM 5's were found to be regenerable, selective and recyclable.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.9
• /
• pp.611-615
• /
• 1999

Piezoelectric properties of PMN-PZT ceramics with $CeO_2$ impurity were investigated. Mechanical quality factor, $Q_m$ of 1792, 1285 and the electromechanical coupling coefficient, $k_p$ of 0.52, 0.54 were obtained from the specimen with 0.25 and 0.5 mole % $CeO_2$ respectively. Curie temperature was decreased with the addition of $CeO_2$ while the electric coercive field was proportional to the amount of impurity. Based on the system ceramics with 0.5 mole % cerium oxide, a Rosen type piezoelectric transformer was fabricated and tested. Voltage step-up ratios of 230 and 13 were obtained from the transformer at no load and $100 k\Omega$ resistance, respectively. Experimental results showed a potential of the transformer for the practical use coupled with the expected strength increase by the grain size refinement.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.1
• /
• pp.1-5
• /
• 2019

The physical properties of ceramic materials including oxides are greatly influenced by the material density. Therefore, various efforts have been made to increase the material density. One of the most popular strategies is to use sintering additives in sintering materials. The conventional sintering additive was a spherical powder having a three-dimensional structure. In this study, sintering additive with 2-dimensional (2D) layer structure was used to increase the sintering density of cerium oxide and its effect was confirmed. In this study, 1 nm-thick $TiO_x$ and $MnO_x$ nanosheets were used as sintering additives.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.49-52
• /
• 2007

We investigated hydrogen storage and production properties using redox system of iron oxide($Fe_{3}O_{4}$ + $4H_{2}$ ${\leftrightarrows}$ 3Fe + $4H_{2}O$) modified with rhodium, ceria and zirconia under atmospheric pressure. Reduction of iron oxide with hydrogen(hydrogen storage) and re-oxidation of reduced iron oxide with steam(hydrogen evolution) was carried out using a temperature programmed reaction(TPR) technique. On the temperature programmed studies, the effects of amounts of cerium and zirconium on the re-oxidation rate of partial reduced iron oxides were increased with increasing metal additives amount, but the rhodium amount showed little effect on the re-oxidation rate. On the thermal studies, the re-oxidation rates were enhanced with increasing temperature(300 $^{\circ}C$ < 350 $^{\circ}C$).