• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.1
• /
• pp.65-72
• /
• 2011

Purpose: The purpose of this study was to evaluate the level of electro-chemical corrosion and surface roughness change for the cases of Ti abutment connected to restoration made of base metal alloys. Materials and methods: It was hypothesized that Ni-Cr alloys in different compositions possess different corrosion resistances, and thus the specimens ($13{\times}13{\times}1.5\;mm$) in this study were fabricated with 3 different types of metal alloys, commonly used for metal ceramic restorations. The electrochemical characteristics were evaluated with potentiostat (Parstat 2273A) and the level of surface roughness change was observed with surface roughness tester. Paired t-test was used to compare mean average surface roughness (Ra) changes of each specimen group. Results: All specimens made of nickel-chromium based alloys, average surface roughness was increased significantly (P < .05). Among them, the Ni-Cr-Be alloy ($0.016{\pm}.007\;{\mu}m$) had the largest change of roughness followed by Ni-Cr ($0.012{\pm}.003\;{\mu}m$) and Ni-Cr-Ti ($0.012{\pm}.002\;{\mu}m$) alloy. There was no significant changes in surface roughness between each metal alloys after corrosion. Conclusion: In the case of galvanic couples of Ti in contact with all specimens made of nickel-chromium based alloys, average surface roughness was increased.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.6
• /
• pp.545-559
• /
• 2002

There has been increasing use of IPS Empress $2^{(R)}$ owing to easy fabrication method, high esthetics similar to natural teeth, good marginal accuracy, and sufficient fracture strength. However, in clinical application, although a luting agent and the tooth cementation bonding procedure influence the marginal accuracy and fracture strength restoration, there has been a controversy in the selection of proper luting agent. This study was to measure the marginal fidelites and fracture strength of IPS Empress crowns according to three cement types, Protec $cem^{(R)}$, Variolink $II^{(R)}$ and Panavia $21^{(R)}$. After construction of 12 experimental dies for each group, IPS Empress $2^{(R)}$ crowns were fabricated and luted the metal master die prepartion of the maxillary right premolar. Marginal gaps before cementation and after cementation were measured. Buccal incline on the functional cusp of specimens were loaded until the catastrophic failure and fracture strength was measured. The results of this study were as follows: 1. The range of gap was $34.04{\pm}4.84{\mu}m$ before cementation and $37.88{\pm}5.00{\mu}m$ after cementation, which showed significant difference by paired t-test (p<0.05). The difference in the results from marginal accuracy according to measuring point proved to be not statistically significant by two-way ANOVA test (p>0.05). 2. The difference in the results from marginal accuracy according to three cement types Proved that The Variolink $II^{(R)}$ cement group had the least gap, $35.43{\pm}5.03{\mu}m$, and showed superior marginal accuracy while there existed statistic significance in Protec $cem^{(R)}$ cement group, $39.06{\pm}4.41{\mu}m$ or Panavia $21^{(R)}$ cement group, $39.16{\pm}4.39{\mu}m$ by two-way ANOVA test & multiple range test (p<0.05). 3. The difference in the results from fractures strength testing according to three cement type groups proved to be statistically significant (p<0.05). The Variolink $II^{(R)}$ cement group shows highest fracture strength of $1257.33{\pm}226.77N$, Panavia $21^{(R)}$ cement group has $1098.08{\pm}138.45N$, and Protec $cem^{(R)}$ cement group represents the lowest fracture strength of $926.75{\pm}115.75N$. 4. Three different cement groups of different components showed acceptable marginal fidelity and fracture strength. It is concluded that IPS Empress $2^{(R)}$ crowns luted using Variolink $II^{(R)}$ cement group had stronger fracture strength and smaller marginal gap than the other cement groups. Although Variolink $II^{(R)}$ resin cement seemed acceptable to clinical applications in IPS Empress $2^{(R)}$ system, the IPS Empress $2^{(R)}$ system still requires long-term research due to the lack of data in clinical applications.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.3
• /
• pp.319-324
• /
• 2003

Statement of problem. Adhesives in dentistry playa major role in the success of restorative treatments. In the treatment of all ceramic restoration it is needed to find the adequate bond strength between enamel and dentin. Purpose. The purpose of this study was to evaluate shear bond strength of resin cement bonded to extracted human uncut enamel, cut enamel, and dentin in vitro. Material and methods. Ten freshly extracted anterior teeth without any previous restorative treatments were chosen. The extracted teeth were embedded in PMMA cold acrylic in the shape of a cylinder, 25 mm in diameter by 25 mm in height. The bonding system used was as follow: Uni-Etch (32% phosphoric acid), One-Step adhesive, Duolink resin cement. The specimens were acid etched and rinsed with water. Two layers of One-Step adhesive were coated with a disposable brush on the uncut enamel. VIP curing light at $500mV/cm^2$ was used to cure the adhesive. For cut enamel shear bond test, the specimen used for uncut enamel was further reduced approximately $0.3{\sim}0.5mm$ using a laminate preparation diamond bur (0.3 mm in depth). The specimens were subsequently treated with 320-grit SiC paper followed by 600-grit SiC paper and cleaned with distilled water. The bonding procedure on the cut enamel was same as uncut enamel bonding procedure. For dentin bonding test, the specimen used for cut enamel was further reduced approximately $0.5mm{\sim}1.0mm$ using a laminate preparation diamond bur (0.5 mm in depth of diamond cutting). The amount of reduction was evaluated with the silicone mold. The specimens were subsequently treated with 320-grit SiC paper followed by 600-grit silicon carbon paper and cleaned in distilled water. The bonding procedure on the dentin was same as uncut enamel bonding procedure. All samples were mounted and secured on the Ultradent shear bond test sample holder, and Ultradent restricted shear bond testing device was used with Universal Instron machine until fracture. Analysis of variance (ANOVA) test was performed comparing the result at P<0.05. Multiple comparison (Tukey) was used to compare each groups. Result. The result showed that the mean value in shear bond strength of resin cement bonded to uncut enamel, cut enamel and dentin were 27.04 Mpa, 30.25 Mpa and 26.39 Mpa with respect. Conclusion. Within the limitation of this study, the mean value of the shear bond strength of cut enamel was higher than those of uncut enamel or dentin. However there existed no statistical differences between three different human dentition substrates due to increased adhesive characteristics.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.4
• /
• pp.495-505
• /
• 2019

This study reported the treatment of a patient with excessive worn dentition and limited maxillo-mandibular space for restoration, utilizing the computer-aided design and computer-aided manufacturing (CAD/CAM) technology. After the thorough examination of the patient's occlusal vertical dimension (OVD), full mouth rehabilitation was planned with increase of the OVD. The patient was satisfied with the provisional restorations establishing the increased OVD. The horizontal and vertical data of the patient's jaw relation that the provisional restorations contained were transferred to the definitive metal ceramic fixed prostheses by double scanning and three-dimensional printing. After the fixed restorations were cemented to the abutments, electronic surveying and three-dimensional printing were used to fabricate metal frameworks for the patient's removable partial dentures. The mandibular definitive removable prostheses were delivered to the patient's mouth and the full mouth rehabilitation procedures were completed. The digital technologies used for this case produced fixed and removable restorations satisfactory in masticatory, phonetic and aesthetic functions to both the patient and the dental clinician.

• The Journal of Korean Academy of Prosthodontics
• /
• v.54 no.3
• /
• pp.193-202
• /
• 2016

Purpose: This study was performed in order to assess the effect of the surface treatment methods and the use of bonding agent on the shear bond strength (SBS) between the aged CAD-CAM (computer aided design-computer aided manufacturing) hybrid materials and added composite resin. Materials and methods: LAVA Ultimate (LU) and VITA ENAMIC (VE) specimens were age treated by submerging in a $37^{\circ}C$ water bath filled with artificial saliva (Xerova solution) for 30 days. The surface was ground with #220 SiC paper then the specimens were divided into 9 groups according to the combination of the surface treatment (no treatment, grinding, air abrasion with aluminum oxide, HF acid) and bonding agents (no bonding, Adper Single Bond 2, Single Bond Universal). Each group had 10 specimens. Specimens were repaired (added) using composite resin (Filtek Z250), then all the specimens were stored for 7 days in room temperature distilled water. SBS was measured and the fractured surfaces were observed with a scanning electron microscope (SEM). One-way ANOVA and Scheffe test were used for statistical analysis (${\alpha}=.05$). Results: Mostly groups with bonding agent treatment showed higher SBS than groups without bonding agent. Among the groups without bonding agent the groups with aluminum oxide treatment showed higher SBS. However there was no significant difference between groups except two subgroups within LU group, which revealed a significant increase of SBS when Single Bond Universal was used on the ground LU specimen. Conclusion: The use of bonding agent when repairing an aged LAVA Ultimate restoration is recommended.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.1
• /
• pp.21-28
• /
• 2009

Purpose: The purpose of this study was to compare the wear characteristics of human enamel opposing 2 heat-pressed ceramics (e.max Press and Empress Esthetic), conventional feldspathic porcelain (Ceramco 3) and type III gold alloy. Material and methods: Intact cusps of extracted premolars were used for enamel specimens. Five disk samples were made for each of two heat-pressed ceramics groups, conventional feldspathic porcelain group and type III gold alloy group. Wear tests were conducted in distilled water using a pin-on-disk tribometer. The amount of enamel wear was determined by weighing the enamel specimens before and after wear tests, and the weight was converted to volumes by average density. The wear tracks were analyzed by scanning electron microscopy and surface profilometer to elucidate the wear characteristics. Results: 1. Ceramco 3 led to the greatest amount of enamel wear followed by Empress Esthetic, e.max Press and type III gold alloy. However, there was no significant difference between Ceramco 3 and Empress Esthetic (P>.05), and there were also no significant differences among Empress Esthetic, e.max Press and type III gold alloy (P>.05). 2. The average surface roughness of e.max Press after wear test was smallest followed by Empress Esthetic and Ceramco 3, but there was no significant difference between Empress Esthetic and Ceramco 3 (P>.05). 3. There were no significant differences among the depth of wear tracks of all the groups (P>.05). The group that showed the largest width of wear track was Ceramco 3 followed by Empress Esthetic, e.max Press and type III gold alloy. However, there was no significant difference between e.max Press and Empress Esthetic (P>.05), and there was also no significant difference between Empress Esthetic and Ceramco 3 (P>.05). Conclusion: Within the limits of this study, heat-pressed ceramics were not more abrasive than conventional feldspathic porcelain.