The purpose of this study is to evaluate the mix design of pH reducing cement concrete which can be used for environment-friendly concrete. Cement pastes and concretes are prepared with water-binder ratios and various admixtures such as blast-furnace slag, fly ash and recycled cement, and tested for compressive strength and pH. pH is measured through pore solution expressed from hydrated cement paste by special apparatus. From the test results, regardless of water-binder ratio, The pH of expressed pore solution from hydrated cement paste which is made of ordinary portland cement with blast-furnace slag, fly ash is decreased with increasing of admixtures content, and compressive strength is also slightly improved. The compressive strength of cement paste made of recycled cement which is burnt at $1000^{\circ}C$, for 2 hours is considerably increased compared with that of none-burnt recycled cement due to restoration of hydraulic property, but pH is a little higher. Porous concrete with ordinary portland cement has high pH in the range of 12.22 to 12.59, however, that is reduced to the range of 8.95 to 10.39 by carbonation at the surface of porous concrete. The pH reduction of porous concrete is possible by various admixture addition, however their degrees are very slight. Therefore, to reduce the pH considerably, carbonation method of porous concrete is better in pH reduction methods for plant survival condition of pH of 9.0 or less. In this study, it is apparent that pH for the environment-friendly porous concrete products used in the construction field can be suppressed by this carbonation method and various admixtures addition.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.41 no.4
• /
• pp.357-364
• /
• 2021

The present study investigated the hydration properties and NO_x-removal performances of the cement pastes containing three different types of TiO₂. Two commercially available TiO₂ (P-25 and NP-400) and refined TiO₂ (GST) obtained from waste sludge were incorporated to cement paste at levels of 0, 5, 10, and 20 wt%. Isothermal calorimetry test results indicated that the TiO₂ incorporation induced a notable influence on the reaction kinetics of cement paste, showing the highest cumulative heat release in the samples containing P-25, followed by NP-400 and GST. Quantitative X-ray diffractometry as calculated by the Rietveld method identified that the incorporated TiO₂ promoted the formation of C-S-H, ultimately leading to the enhancement in the 28 day-compressive strength of cement pastes. As revealed by SEM/EDS analysis, the content of distributed Ti elements on the surface of the samples was in the order of P-25, GST, and NP-400. Regardless, the NO_x-removal performance was the highest in the sample containing P-25, followed by NP-400 and GST.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.5
• /
• pp.133-142
• /
• 2008

This paper studies the early-aged chloride binding capacity of various blended concretes including OPC(ordinary Portland cement), PFA(pulversied fly ash), GGBFS(ground granulated blast furnace slag) and SF(silica fume) cement paste. Cement pastes with 0.4 of a free water/binder ratio were cast with chloride admixed in mixing water, which ranged from 0.1 to 3.0% by weight of cement and different replacement ratios for the PFA, GGBFS and SF were used. The content of chloride in each paste was measured using water extraction method after 7 days curing. It was found that the chloride binding capacity strongly depends on binder type, replacement ratio and total chloride content. An increase in total chloride results in a decrease in the chloride binding, because of the restriction of the binding capacity of cement matrix. For the pastes containing maximum level of PFA(30%) and GGBFS(60%) replacement in this study, the chloride binding capacity was lower than those of OPC paste, and an increase in SF resulted in decreased chloride binding, which are ascribed to a latent hydration of pozzolanic materials and a fall in the pH of the pore solution, respectively. The chloride binding capacity at 7 days shows that the order of the resistance to chloride-induced corrosion is 30%PFA > 10%SF > 60%GGBFS > OPC, when chlorides are internally intruded in concrete. In addition, it is found that the binding behaviour of all binders are well described by both the Langmuir and Freundlich isotherms.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.829-834
• /
• 2002

Carbonation of concrete used impregnation alkalization agent construction reinforcement, recovery of pH, elevation improve, in which efficiency decline mternal force of number and durability because of impregnation alkalization agent applyment general standard, used concrete. Material quality not understanding lack of study and stadard. This study investigate change of PH. recovery depth of impregnation alkalization agent, recovery depth belong a mount of aggregate that comparision, analysis parity.

• Journal of the Korean Ceramic Society
• /
• v.46 no.1
• /
• pp.58-68
• /
• 2009

In this study, rheological properties of ternary system cement containing ground fly ash(F3, Blaine specific surface area $8,100\;cm^2/g$) were investigated using mini slump, coaxial cylinder viscometer and conduction calorimeter. In the results, the segregation resistance was observed at high W/B and PC area while the replacement ratio of F3 was increasing. The 2:5:3 system was shown in higher fluidity and lower hydration heat than 3:4:3 system. The segregation range of cement pastes occurred over 175 mm in average diameter by mini slump and below $10\;dynesec/cm^2$ of the plastic viscosity or below 50 cP of the yield stress by coaxial cylinder viscometer. It was observed that even if BFS and FA blended together admixture properties would remaine as they were separately. The properties of admixture would not be changed. On the above results, the decreased replacement ratio of OPC and increased replacement ratio of admixtures would be possible.

• Journal of the Korean Ceramic Society
• /
• v.50 no.2
• /
• pp.149-156
• /
• 2013

This study examines the effects of limestone's factors on the fluidity of cement paste when of up to 15%. As the substitution ratio of limestone powder increases, the fluidity of the paste is also improved; however, it has no correlation to the $CaCO_3$ content of the limestone, fineness of the limestone, and fluidity of the pastes. Regardless of clay content of the limestone, it showed a similar mini-slump, so there was no correlation between the clay content and the fluidity of the paste. Also, the total organic carbon content of the limestone and the fluidity of the paste showed no correlation. Regardless of the limestone's grade or fineness, n value of powder gained by using the Rosin-Rammler distribution function showed that the fluidity of the paste increased as the n value reduced. It was also shown that particle size distribution of ordinary Portland cement with limestone powder had a major effect on the fluidity of the paste.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.230-231
• /
• 2017

The addition of a limestone filler(LF) to fill into the voids between cement and aggregate particles can reduce the cementitious paste volume. This paper aim to evaluate the influence of LF contents on the hydration kinetics and compressive strength. Hydration kinetics were evaluate using heat of hydration, ignition loss and thermal analysis. The heat of hydration was measured using Isothermal Calorimetry. The degree of hydration was measured using ignition loss. Hydration product analysis was carried out by Thermal Gravimetric and Differential Thermal Analysis. The results show that the addition of LF reduces not only the initial setting time and heat of hydration peak, also degree of hydration and rate of strength development at early age increase with the addition of LF. It can be concluded the LF fills the pore between cement particles due to formation of carboaluminate, which may accelerate the setting of cement pastes.

• Computers and Concrete
• /
• v.6 no.4
• /
• pp.343-356
• /
• 2009

Experiments were designed to investigate the flow behavior of portland cement paste and concrete incorporating superplasticizers. The paste and concrete mixtures were subjected to prolonged mixing for up to 110 min at high temperature. The yield stress values of concrete and that of the corresponding cement paste were measured using a rotating rheometer and viscometer, respectively. The results reveal a weak linear correlation between the yield stress of concrete mixtures and that of the corresponding cement pastes. Results also indicate that the yield stress of concrete varies in a linear fashion with the elapsed time, while its variations with the temperature and superplasticizer dosage follow power and inverse power functions, respectively. In this study, the genetic algorithms (GA) technique was used to predict the yield stress of concrete considering various parameters, such as the mixing time, ambient temperature, and superplasticizer dosage. A sensitivity study was conducted to evaluate the ability of the GA equations thus developed to capture the effects of test parameters on the yield stress of concrete. It was found that the GA equations were sensitive to the effects of test parameters and provided yield stress predictions that compared well with corresponding experimental data.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.26-27
• /
• 2017

In this study, the cracking characteristics of cured pastes at 800℃ were investigated by X-ray CT. The test specimens were fabricated with and without aggregate, and the heating rate condition was applied at rapid heating (10.0℃/min). It is considered that the rapid heating condition does not cause a temperature gradient phenomenon because the temperature difference between the surface and the center of the sample is small due to a low heating rate unlike an actual fire. The cracking condition of the specimens without aggregate was more severe than that of specimens with aggregate.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.137-138
• /
• 2016

Palm Oil Fuel Ash(POFA),which is burned in palm oil factories to get energy and gathered, has been studied in many countries due to its chemical properties. However POFA has high value of LOI and lots of pores on its particle surface. Therefore, in this study, POFA's fluidity were confirmed by mini-slump test and plastic viscosity test. Through the results, fluidity of POFA reduced according to the replacement ratio of POFA because of high value of LOI and its pores on surface and plastic viscosity of POFA increased. In addition, when superplasticizer was added, fluidity increased due to the steric effect of polycarboxylate superplasticizer.