• 한국농공학회지
• /
• 제20권1호
• /
• pp.4599-4613
• /
• 1978

This study was intended to investigate the effects of bituminous material content of soil-cement mixtures on their durability. For the purpose, unconfined compressive strength test, Freeze-thaw test, and wet-dry test were performed with three types of soil. Each type of soil was mixed with three levels of cement content and each soil-cement mixture was mixed with four levels of bituminous material content. For the unconfined compressive strength test, Freeze-thaw test and wet-dry test, 324, 108, and 108-specimens were prepared respectively. Unconfined compressive strength was measured at age of 7-days, 14-days and 28-days using 108-specimens in each age. The soil-cement loss rate due to freeze-thaw and wet-dry were calculated after 12 cycles of test using 108-specimens in each test. The results are summarized as follows : 1. Optimum moisture content was increased with increase of cement content, but maximum dry density was changed irregulary with increase of the cement content. 2. The unconfined compressive strength was increased with increase of cement content, bituminous material content and curing age. Cement is more effective factor than bituminous material on unconfined compressive strength of soil-cement Mixture. 3. It is estimated as the most economical cement content that the recommended cement content of A.S.T.M. because increasing rate of unconfined compressive strength at age of 28-days was low when cement content is above the recommanded cement content of A.S.T.M. among all types of soil. 4. Although a portion of cement content is substituted for bituminous material, the necessary unconfined compressive strength can be obtained. 5. The soil-cement loss was more influenced by wet-dry than Freeze-thaw 6. The bituminous material is more effective on the decrease of soil-cement loss than increase of unconfined compressive strength 7. The void ratio of soil-cement mixture was changet irregularly with increase of cement content, but that was decreased in proportion to the increase of bituminous material content. 8. The regression equation between the unconfined compressive strength and soil-cement loss rate were obtained as table 7.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 1999년도 연약지반처리위원회 학술세미나
• /
• pp.84-95
• /
• 1999

Laboratory experiments were performed to evaluate the strength characteristics of solidified sandy soils by portland cement with mixing conditions. Factors considered in the experiments were the fine content(<#200, %), cement content(%) and water-cement ratio and unconfined compressive strength tests were performed on samples at 7 and 28 cured day. Results of tests showed that for a low cement content(7%∼10%) the fine content was very important while for a high cement content the water-cement ratio was very important. For 7%∼10% cement content, the optimum fine content which gained maximum strength was about 30%. But for 13% cement content, low fine content and water-cement ratio were more useful than others. In the multi regression analysis, significant equation was gained.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 봄 학술발표회 논문집
• /
• pp.24-29
• /
• 1996

The purpose of this study is to propose new estimation method of unit cement content in hardened concrete. In general, the quantity of cement in hardened concrete is tested by hydrochlonic acid dissolving cement paste, however, hydrochloric acid dissolves sea shell contained in sea sand and lime stone in concrete. Therefore, the tested cement content is apt to estimate greater than actual cement content. The sodium gluconate solution dissolves only cement in concrete, it is hard to dissolve sea shell and lime stone as CaCo3. The effects of the quantity, concentration and temperature of sodium gluconate solution, the ignition temperature, the ignition loss of cement on the cement content and the percentage of dissolution of cement were investigated to establish a test method. From the results of these tests, the fundamental test method for cement content of hardened concrete by sodium gluconate is proposed.

• 한국농공학회지
• /
• 제17권1호
• /
• pp.3685-3701
• /
• 1975

This study was conducted to investigate the strength of soil cements for varied molding water content and cement content(3,6,9,12%) in four cementstabilized soils(KY: sand, MH: sad, SS: sandy loam, JJ: loam). The eoperimental results obtainedfrom unconfined compressive strength tests are asfollows: 1. The optimum moisture content increased in accordance with the increase of the cement while maximum dry density didn't change uniformly. 2. The moisture content for maximum strength was higher than the optimum moisture content in the higher cement content. Moisture-density curves showed a dull peak in the higher cement contents, on the other hand, a sharp peak in the lower cement contents. 3. In molding the specimen with the approximate optimum moisture content, the maximum strength showed at the wet side of the optimum moisture content. 4. SS and JJ maybe used as cement-stabilized base of road to require 300PSI of compressive strength cured seven days, but MH and KY may be not adequate. 5. In soil cement, the better the grain size distribution was, the stronger the compressive strength was itn general. 6. The relation between 28-day strengh and 7-day strength in the cementstabilized four soils may be expressed as follows: q28=1.55q7+1.5 in which q28:28-day strength. q7:7-day strength.

• 한국농공학회지
• /
• 제17권2호
• /
• pp.3778-3783
• /
• 1975

The objective of this study is to determine an appropriate cement of soil-cement in which silty soil of salty tidal flat with low plasticity was used. Physical, chemical and mechanical tests were conducted to find out the standard properties of the soil to be used. Various cement contents used in this test were 8%, 10%, 12%, and 14%, and the compressive strength was tested after 7 days and 28 days of standard curing in the above each cement content respectively. The results obtaind are summarized as follows. 1. As the cement content was increased from 8% to 14%, Maximum dry density (M.D.D.) and optimum moisture content (O.M.C.) were not changed remarkably. 2. Density of soil-cement was directly proportional to cement content and inversely proportional to water content. 3. OMC was generally decreased in proportion to the increase of cement content. 4. Compressive stranth was directly proportional to centent and inversely proportional to water content. 5. In freezing and thawing test, maximum loss of 10% in the total Weight was found on the 8% cement mixture. and This loss was rapidly decreased to 2% when the Cement content of the mixture was more than 10%.

• 한국농공학회지
• /
• 제43권6호
• /
• pp.135-142
• /
• 2001

Laboratory experiment was performed to evaluate the influence of mixing conditions to the strength of solidified sandy soils with cement. The major physical factors considered in this experiment were the fine particles content(<$\sharp200%$), cement content(%) and water-cement ratio, and unconfined compressive strength test was performed on the samples at 7 and 28 cured day. The results of tests shows that when the cement content is relatively low (7~10 percents) the fine content in the sandy soils is very important, but when cement content is high the water-cement ratio became more important. It was appeared that in the range of the cement content of 7~10 percents, about 20~30 percents of fine content to the total sample weight is the optimum condition to get the maximum strength. In the case of the cement content of 13 percents, the strength of sample was considerably affected by the water-cement ratio rather than the fine content. In this paper, empirical equations were also developed and evaluated to verify the relationship among three factors by the multi-regression analysis.

• Geomechanics and Engineering
• /
• 제29권1호
• /
• pp.13-23
• /
• 2022

Peat soil has the characteristics of high moisture content, large void ratio and low shear strength. In this study, unconfined compressive strength and SEM tests are conducted to investigate the effects of ultrahigh moisture content, cement content, organic content and pH value on the strength of solidified peat. As an increase in the cement content and curing period, the failure mode of solidified peat soil changes from ductile failure to brittle failure. The influence of moisture content on the strength of solidified peat is greater than the cement content. As cement content increases from 10% to 30%, strength of solidified peat at a curing age of 28 days increases by 161%~485%. By increasing water content by 100%, decreases of solidified peat at a curing age of 28 days is 42%~79%. Compared with the strength of solidified peat with a pH value of 5.5, the strength of peat with a pH value of 3.5 reduces by 10% ~ 46%, while the strength of peat with a pH value of 7.0 increases by 8% ~ 38%. It is recommended to use filler materials for stabilizing peat soil with moisture content greater than 200%. Because of small size of clay particles, clay added in the cement solidified peat can improve much higher strength that that of sand.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1997년도 가을 학술발표회 논문집
• /
• pp.196-202
• /
• 1997

The objective of this study is characterize of Mortar and Concrete mae with Cement made with Cement containing Fly ash as an additive. Cement samples were prepared using tow kinds of Fly ash, which containing unburnt Carbon content 3.5% and 4.5%. Fly ash content in cement was in range 3wt% to 13wt%. In consequence of various experiments, these cement samples satisfied specification of Type I cement, and it is possible to use Fly ash as an additive to Type I cement in this content.

• 한국농공학회지
• /
• 제16권3호
• /
• pp.3533-3538
• /
• 1974

This study was attempted in order to search for physical properties of sail cement. In this study, soil samples were specified according to soil particle analysis and used for compaction, strength, abrasion, absorption tests respectively according to different cement contents. Cement content sused in each treatment were 6%, 8%, 10% and 12% of total weight of soil-consent mixture. In the test, compressise strengths of the specimens were measured at the following ages; 3 days, 7-days, 14-days, 21-days and 28-days. Abrasion and absorption tests of the specimens were carried out at the 7-days age only. The results obtained from the tests are summarized as follows; 1. As the cement contents were in creased, the compressive strengths of soil-cement were almost proportionally increased. 2. The Compressive strength of soil-cement was not always proporportional to ages. The gradient of compressive strength of the soil-cement was steeper as the cement content was rucreased. 3. As the cement content was increased, the amount of the weight loss of the samples due to the abrasion was decreased remarkably, giving no abrasion for about 8% of the cement content. 4. As the cement content was increased, the absorption ratio of the specimens was not changed remarkably.

• Geomechanics and Engineering
• /
• 제12권6호
• /
• pp.935-948
• /
• 2017

An experimental program was conducted to investigate the effects of the static compaction pressure, cement content, water/cement ratio, and curing time on unconfined compressive strength (UCS) of the cement treated sand. UCS were conducted on samples prepared with 4 different cement/sand ratios and were compacted under the lowest and highest static pressures (8 MPa and 40 MPa). Each sample was cured for 7 and 28 days to observe the impact of curing time on UCS of cement treated samples. Results of the study showed the unconfined compressive strength of sand increased as the cement content (5% to 10%) of the cement-sand mixture and compaction pressure (8 MPa to 40 MPa) increased. UCS of sand soil increased 30% to 800% when cement content was increased from 2.5% to 10%. Impact of compaction pressure on UCS decreased with a reduction in cement contents. On the other hand, it was observed that as the water content the cement-sand mixture increased, the unconfined compressive strength showed tendency to decrease regardless of compaction pressure and cement content. When the curing time was extended from 7 days to 28 days, the unconfined compressive strengths of almost all the samples increased approximately by 2 or 3 times.