• Journal of the Korean Wood Science and Technology
• /
• 제40권2호
• /
• pp.71-77
• /
• 2012

Cellulose nanowhisker (CNW) isolated from hardwood bleached kraft pulp (HW-BKP) using sulfuric acid hydrolysis was suspended in polyvinyl alcohol (PVA) and electrospun into composites nanofibers. Transmission electron microscopy (TEM) revealed the CNW to be rod-like, approximately of $16.1{\pm}4.6$ nm wide and $194{\pm}61$ nm long, providing an aspect ratio of about 12, with a particle size distribution range of $662.2{\pm}301.2$ nm. Uniform and high quality CNW/PVA composite nanofibers were successfully manufactured by the electrospinning method. As the CNW loading increases, the viscosity of CNW/PVA solutions shows a minimum at 1% CNW level which subsequently results in the smallest diameter (193 nm) of electrospun nanofibers. The average diameter of the nanofibers increased up to 284 nm with increasing CNW loading. These results suggest that the electrospinning method provides a great potential of manufacturing consistent and reliable nanofibers from CNW/PVA solution for the formation of scaffolds with potentials in future application.

• Elastomers and Composites
• /
• 제45권1호
• /
• pp.51-57
• /
• 2010

본 연구에서는 친환경적인 특징을 가지면서도 우수한 기계적 특성을 가지고 있어 고분자 복합재료의 보강제로 주목 받고 있는 Cellulose nanowhisker (CNW) 를 염산 혹은 황산을 사용한 산가수분해 방법을 이용하여 Microcrystalline cellulose (MCC) 로 부터 추출하였다. 염산 혹은 황산을 사용하여 추출된 CNW는 직경이 20 에서 30nm 정도였고, 길이가 200 에서 300 nm 로써, 형상학적 측면에서 유사한 특성을 가지는 것을 확인하였다. 또한 전해질 용액의 전기전도도를 이용한 적정 (conductometric titration) 결과 황산을 이용하여 제조되어진 CNW의 경우, 셀룰로오스 표면의 sulfate group 에 의해 나타나는 표면전하 값이 각각 140, 197.78 mmol/kg으로 나타났으며, 염산을 이용하여 제조되어진 CNW 의 경우 셀룰로오스 표면에 약한 전하 값을 가져 표면전하 값을 구할 수 없었다. 황산을 이용하여 추출된 CNW의 열중량 분석 결과 염산을 이용하여 추출된 CNW와 비교하여 열분해 온도가 급격히 감소하는 것을 확인할 수 있었으며, Broido's method를 이용하여 정의 되어진 열분해 거동에 대한 활성화 에너지 역시 상대적으로 낮음을 확인할 수 있었다.