• Journal of the Korean Wood Science and Technology
• /
• 제43권2호
• /
• pp.206-213
• /
• 2015

This study was carried out to use carbonized medium density fiberboard (MDF) for the replacement of sound absorbing material. Carbonization treatment was performed to improve sound absorption property for MDF at carbonizing temperatures of $500^{\circ}C$, $700^{\circ}C$, $900^{\circ}C$ and $1100^{\circ}C$. As the carbonization temperature increased, the results of the observation by scanning electron microscope (SEM) demonstrated that the fibers exhibited a more compressed morphology within the surface section of the MDF than those within the middle section of MDF. As the carbonizing temperature increased, the cavity increased. The sound absorption coefficient increased between the temperatures of $500^{\circ}C$ and $900^{\circ}C$, but decreased at a temperature of $1100^{\circ}C$. The sound absorption properties of the carbonized MDF and the non-carbonized MDF were compared. The maximum sound absorption coefficient of the carbonized MDF was 12.38%. This was almost double of the value of the non-carbonized MDF.

• Journal of the Korean Wood Science and Technology
• /
• 제37권3호
• /
• pp.208-215
• /
• 2009

포름알데히드 등 유해 휘발성유기화합물(VOC)의 제거성능을 지닌 MDF 탄화보드를 개발하기 위한 기초연구의 일환으로 MDF를 여러 온도에서 탄화하여 주사전자현미경법 및 X선회절법에 의하여 특성을 조사하였다. 주사전자현미경 관찰 결과, 탄화 된 MDF의 내층부 보다 표층부에서, 측면내층부에 비해 측면표층부에서 압착된 섬유의 형태가 나타났으며, 다수의 이물질도 관찰되었다. 그러나 탄화온도가 상승함에 따라서 이물질이 제거되었고 공극의 증가가 관찰되었다. 섬유벽 표면과 내강측에서 주름형태가 관찰되었고 세포내강측 보다 외부 표면의 주름형태가 더욱 뚜렷하였다. 또한 벽공의 손상은 크지 않았고 벽공이 존재하는 부위에서 주름형태가 적게 나타났다. X선회절 결과, 셀룰로오스 결정은 탄화온도 $400^{\circ}C$에서 배향성을 잃으며 붕괴되었으나 약간의 결정성은 남아있는 것이 확인되었다. 그러나, $1,000^{\circ}C$에서 탄화한 MDF는 셀룰로오스 결정이 모두 붕괴되었고 탄소원자에 의한 비결정성 회절강도곡선을 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• 제44권3호
• /
• pp.424-429
• /
• 2016

본 연구에서는 중밀도섬유판, 파티클보드, 배향성스트랜드보드, 합판을 이용하여 탄화보드를 제조하고 각각의 흡방습 특성을 살펴보았다. 탄화보드는 $600^{\circ}C$에서 2시간 동안 열분해하는 조건으로 제조되었다. 그 결과, 탄화합판, 탄화OSB, 탄화MDF, 탄화파티클보드 순으로 높은 흡방습 성능을 나타내었다. 흡습률 및 방습률은 탄화파티클보드를 제외한 나머지 탄화보드들 간에 큰 차이는 발견하지 못했다. 이것은 목질재료가 탄화됨으로서 탄소로 변환되어 수분을 흡착하는데 높은 능력을 가졌지만 수분이 내부구조로까지의 이동에 있어서는 목재 본래의 구조에 영향을 받는다는 것을 의미한다. 따라서 목재의 구조의 특성을 살려 탄소화 했을 때 높은 흡방습 특성을 가진 탄화보드를 제조할 수 있다.

• Journal of the Korean Wood Science and Technology
• /
• 제38권3호
• /
• pp.185-190
• /
• 2010

중밀도섬유판(MDF)에 글씨나 그림을 새김질한 목판을 제조하고, 이를 탄화하여 서각작품을 제작하는 방법을 개발하였다. 섬유판의 탄화에 따른 외형적 및 조직학적 변화를 검토하고 제작된 탄화보드 서각작품에 대한 미학적 특징을 고찰하였다. 서각한 MDF를 $850^{\circ}C$에서 탄화한 결과, 할열이나 뒤틀림은 관찰되지 않았으며, 치수는 가로 21.8%, 세로 18.8%, 두께 43.5% 줄어들었고, 중량은 69.2%, 밀도는 14.8% 감소하였다. 탄화보드의 전자 현미경에 의한 관찰 결과, 당초 섬유의 표면과 벽공을 둘러싸고 있던 접착제가 탄화되면서 목질섬유의 표면이 매끄럽게 변하고 벽공이 개열되며 섬유의 크기가 균일화되고 조직이 치밀화되는 현상을 나타내었다. 수작업에 의한 서각기법과 무할열 탄화기법의 융합에 의해 새로운 탄화보드 서각작품의 제작이 가능하였다. 탄화보드 서 각작품은 목탄의 기능성과 서각의 아름다움을 부여하는 새로운 친환경 예술영역의 한 분야로서 이용될 수 있을 것이다.

• Journal of the Korean Wood Science and Technology
• /
• 제42권6호
• /
• pp.714-722
• /
• 2014

선행연구에서 다양한 목질 보드류를 열분해하여 다공질 탄화보드 제조에 성공하였고, 높은 난연성, 전자파차폐성, 원적외선방사, 폼알데하이드 흡착성, 흡음성능을 확인하였다. 본 연구에서는 경제성과 흡음성이 뛰어난 탄화 중밀도 섬유판(MDF)을 선택하여 보다 높은 흡음성능을 부여하기 위해 다른 흡음재료에도 사용 중인 샌딩처리와 타공기법을 시도하였다. 또한 개선된 흡음성능을 바탕으로 실제 음향판을 제작하여 그 음향적 효과를 파악하였다. 탄화 MDF를 십자모양(타공 5개), 직사각형모양(타공 9개), 일자모양(타공 5개)으로 타공 처리한 후, 흡음률을 측정한 결과, 무처리 탄화 MDF의 흡음률은 14% 정도를 나타내었고, 직사각형모양 타공 시편이 16.01%로 흡음률이 가장 높았고 십자모양 타공 시편이 15.68%, 일자 타공 시편은 14.25%의 흡음률을 나타내어 그 효과가 미미하였다. 반면에, 탄화 MDF의 표면을 각 1, 2, 3 mm로 표면샌딩 처리후 흡음률을 측정한 결과, 무처리 시편(13%)에 비해 65% 증가한 21.7% (1 mm 샌딩), 21.83% (2 mm 샌딩), 19.37% (3 mm 샌딩)를 확인하였다. 이 결과를 바탕으로 실대형 탄화보드 복합 음향판을 제작하였으며 잔향실법으로 흡음시험한 결과 감음계수 0.45로 높은 흡음성능을 발휘하여 상업화도 가능할 것으로 판단된다.

• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.555-562
• /
• 2014

Characteristics of carbonized fiberboard such as chemical materials absorption, electromagnetic shielding, and electrical and mechanical performance were determined in previous studies. The carbonized board therefore confirmed that having excellent abilities of these characteristics. In this study, the effect of density on physical properties and sound absorption properties of carbonized fiberboards at $800^{\circ}C$ were investigated for the potential use of carbonized fiberboards as a replacement of conventional sound absorbing material. The thickness of fiberboards after carbonization was reduced 49.9%, 40.7%, and 43.3% in low density fiberboard (LDF), medium density fiberboard (MDF), and high density fiberboard (HDF), respectively. Based on SEM images, porosity of carbonized fiberboard increased by carbonization due to removing adhesives. Moreover, carbonization did not destroy structure of wood fiber based on SEM results. Carbonization process influenced contraction of fiberboard. The sound absorption coefficient of carbonized low density fiberboard (c-LDF) was higher than those of carbonized medium density fiberboard (c-MDF) and carbonized high density fiberboard (c-HDF). This result was similar with original fiberboards, which indicated sound absorbing ability was not significantly changed by carbonization compared to that of original fiberboards. Therefore, the sound absorbing coefficient may depend on source, texture, and density of fiberboard rather than carbonization.

• Journal of the Korean Wood Science and Technology
• /
• 제45권3호
• /
• pp.327-334
• /
• 2017

본 연구에서는 각종 건축재료의 폼알데하이드 방출 특성 및 탄화보드에 의한 이들의 저감 효과를 알아보기 위하여 챔버법으로 성능을 분석하였다. 그 결과, 약 12일간 소형 챔버 내에서의 폼알데하이드 저감 성능은 탄화보드(90%), 죽탄보드(84%), 규조토판넬(82%), 알로펜타일(78%), 소나무판재(58%), MDF (54%), 석고보드(46%)의 순으로 나타났다. 또한 파티클보드(PB)로 채워진 $1.9m^3$ 크기의 챔버 내 폼알데하이드 방출량을 68일간 조사한 결과, 탄화보드 투입량이 증가함에 따라 폼알데하이드 방출량은 크게 감소하는 것으로 나타났다. 특히 챔버의 크기 및 PB 면적 대비 탄화보드를 각각 약 10% 및 30% 투입하면 폼알데하이드를 약 40% 및 75% 이상 저감시킬 수 있는 것으로 조사되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제45권5호
• /
• pp.511-518
• /
• 2017

최근의 단열 재료에 대한 관심과 연구는 단열성능 이외의 복합적 성능을 요구하는 추세이다. 본 연구에서는 구조적인 성능을 가지는 왕겨숯 보드 개발을 위한 목재 섬유대 왕겨숯의 최적 비율을 찾고자 하였다. 왕겨숯을 활용하여 구조적 성능을 지니는 친환경 단열재를 개발하고자 기초 연구를 실시하여 다음과 같은 결론을 얻었다. 최종 왕겨숯 보드의 함수율은 3.2~4.1%로 얻어졌으며, 밀도는 0.58~0.68로 우수한 구조재료로서의 가능성을 보였다. 휨강도는 길이방향으로 9.1-32.6 MPa, 그리고 폭방향으로는 9.2-34.1 MPa로 나타났다. 통상적으로 사용되는 MDF 수준의 휨강도를 얻을 수 있어 구조적 성질을 가지는 단열재 개발의 가능성을 찾을 수 있었다.

• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.615-623
• /
• 2014

Increases of public attention on healthy environment lead to the regulation of indoor air quality such as Clean Healthy House Construction Standard. This standard covers emission of total volatile organic compounds (TVOCs) (e.g., formaldehyde, benzene, and toluene), ventilation, and use of environmentally-friendly products or functional products. Moisture absorption and desorption abilities are a recommended functionality for improving indoor air quality. In this study, moisture absorption and desorption capacities of carbonized board from wood-based panels and other materials were determined by using UNT-HEAT-01 according to ISO 24358:2008. Pine had higher moisture absorption and desorption capacities ($49.0g/m^2$ and $35.3g/m^2$, respectively) than hinoki cypress, cement board, gypsum board, oriented strand board, and medium density fiberboard (MDF). The moisture absorption and desorption capacities differed considerably according to the wood species. After carbonization process at $400^{\circ}C$, the absorption and desorption ability of MDF increased to 38% and 60%, respectively. However, moisture absorption and desorption capacities decreased with increasing carbonization temperature, but they were still higher than original MDF. Therefore, it is suggested that carbonization below $600^{\circ}C$ can improve moisture absorption/desorption capacities.

• Journal of the Korean Wood Science and Technology
• /
• 제41권2호
• /
• pp.105-110
• /
• 2013

A repeated impregnation and carbonization process was performed to prepare high-density woodceramics using MDF. The physical properties were estimated to further confirm morphologically structurally occurred changes of one-time and two-time phenolic resin treated and carbonized woodceramics. As compare one-time and two-time carbonized woodceramics, the increasing rate of weight and density declined after second carbonization as the resin impregnation ratio grew higher, and when the resin impregnation ratio was 40 percent, the weight and density of the second carbonization increased more than in the first step by 20.5% and 33.9% respectively which were the highest rates.