• Journal of the Korea Institute of Building Construction
• /
• v.17 no.3
• /
• pp.235-243
• /
• 2017

Carbonation of concrete is being occurred due to interaction of atmospheric carbon dioxide with hydroxides. Reinforce concrete (RC) structure is getting collapse or accident due to corrosion of embedded steel rebar. The maintenance of reinforced concrete structure recently has the attention of researchers regarding durability of structure and its importance day by day is increasing. In order to study the carbonation progress of pre-repaired concrete, present study was carried out to measure the carbonation velocity for different repair materials up to 100% of carbonation. The obtained results have predicted the carbonation progress of repair materials in service condition. These results have been verified by FEM and FDM analysis. As a result, the carbonation depth can be predicted by using the carbonation prediction formula after the repair, and the analytical and the experimental values are almost similar when the initial $Ca(OH)_2$ concentration is assumed to be 40%.

• Corrosion Science and Technology
• /
• v.4 no.2
• /
• pp.69-74
• /
• 2005

The carbonation of concrete is one of the major factors that cause durability problems in concrete structures. The rate of carbonation depends largely upon the diffusivity of carbon dioxide in concrete. The purpose of this study is to identify the diffusion coefficients of carbon dioxide for various concrete mixtures. To this end, several series of tests have been planned and conducted. The test results indicate that the diffusion coefficient increases with the increase of water-cement ratio. The diffusion coefficient decreases with the increase of relative humidity at the same water-cement ratio. The diffusion of carbon dioxide reached the steady state within about five hours after exposure. The content of aggregates also influences the diffusivity of carbon dioxide in concrete. It was found that the diffusion coefficient of cement paste is larger then that of concrete or mortar. The quantitative values of diffusivity of carbon dioxide in this study will allow more realistic assessment of carbonation depth in concrete structures.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.05a
• /
• pp.23-24
• /
• 2015

As this study is an experiment for solving problem on the carbonation acceleration of high volume admixture concrete, the capillary pore getting filled up by saponification as cooking oil gets absorbed to the concrete surface in case of applying a cooking oil based coating agent to the concrete has been verified in the previous studies. Accordingly, this study has performed a comparative experiment on the cooking oil and the anticorrosive coating agent sold on the market while the result followed by this experiment has shown the fact of indicating similar carbonation penetration depth and porosity.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.158-159
• /
• 2021

When the porous concrete is exposed to the external environment, the internal relative humidity changes from time to time due to the inflow and outflow of moisture. This change in moisture is affected by temperature. The temperature and humidity of concrete is dominant in the carbonation rate, the largest cause of deterioration of concrete. In this study, actual weather data were used as boundary conditions. A carbonization model of concrete temperature and humidity and calcium hydroxide was constructed to perform long-term analysis. There is a slight error in the carbonation formula of the Japanese Academy of Architecture applying the Kishtani coefficient, a representative experimental formula related to carbonization, and the analysis result values. However, considering that it behaves very similarly, it is thought that a fairly reliable numerical analysis model has been established. A slight error is believed to be due to the fact that the amount of residual calcium hydroxide in the carbonated site has not yet been clearly identified.

• Journal of the Korea Concrete Institute
• /
• v.21 no.4
• /
• pp.449-455
• /
• 2009

The increase of industrial carbonic dioxide emissions has accelerated the carbonation of reinforced concrete structures, which drops off their durability. Although advanced countries have already taken safety control measures against the carbonation of RC structures, it is still difficult now to accurately predict the actual carbonation depth. Additionally, it requires much time and efforts. Recently, it is possible to get the data more rapidly through accelerated carbonation test with the $CO_2$ concentration of 100%. In this paper, the carbonation test results obtained by two test methods such as the normal carbonation test method and the accelerated carbonation test method, were compared to investigate the carbonation characteristics of fly ash concrete. The accelerated carbonation test on concrete specimens with the pre-curing age of 180 days was also carried out to examine the carbonation characteristics of fly ash concrete at long-term age. Consequently, fly ash concrete at early age was vulnerable to carbonation and however, its carbonation resistance at long-term ages was improved compared with OPC concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.5
• /
• pp.81-88
• /
• 2007

Among deteriorations of concrete due to environmental exposure, carbonation problems of concrete structures have increased in urban and underground structures. But conventional carbonation-prediction equations that were proposed by foreign references, can not be applied directly to the prediction of carbonation for domestic concrete structures. The purpose of this study is to propose a prediction equation of carbonation depth by considering domestic exposure conditions of concrete structures. For the derivation of the equation, conventional carbonation-prediction equations are analyzed. Through considering the relationship between results of prediction equation and those of various domestic field survey data, the so-called correction factors for different domestic exposure condition of concrete structures are derived. Finally, a carbonation-prediction equation of concrete structures under domestic exposure conditions is proposed with consideration for concrete strength in core and correction factors.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.793-801
• /
• 2005

This study investigates fundamental properties of recycled aggregate concrete which incorporated 100% recycled coarse aggregate and various amount of recycled fine aggregate. In addition, for the purpose of the improvement of long term strength and durability, a part of cement was replaced with fly ash. Compressive strength and resistance to chloride ion penetration and carbonation were investigated. When the coarse aggregate was completely replaced with the recycled the replacement ratio of the fine aggregate with the recycled was recommended to be limited below 60% in the consideration of strength. The strength of the steam-cured specimen was very comparable to the wet-cured at 28 days. As fly ash content increased the resistance to chloride ion penetration was increased. The chloride ion penetrability based on the charge passed was found to be low at 21 days and very low at 56 days, respectively. Carbonation depth and carbonation velocity coefficient increased as the fly ash content increased and the relationship between the carbonation depth and recycled fine aggregate replacement ratio was not clear. Up to 28days, however, the measured carbonation depth was mostly less than 10mm which could be considered as low.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.5
• /
• pp.391-397
• /
• 2020

This study is to compare and analyze the strength, drying shrinkage and carbonation properties of lightweight aggregate mortar using recycling water as prewetting water and mixing water. The flow, compressive strength, split tensile strength, drying shrinkage and carbonation depth of lightweight aggregate mortar with recycling water were measured. As test results, the mortar flow was similar in all mixes regardless of the recycling water content. The compresseive strength of the RW5 mix with 5% recycling water as prewetting water and mixing water was the highest value, about 53.9 MPa after 28 days. In addition, the tensile strength of lightweight mortar was about 3.4 to 3.8 MPa, indicating 7 to 9% of the compressive strength value regardless of recycling water content. In the case of drying shrinkage, the RW2.5 mix using 2.5% recycling water showed the lowest shrinkage rate as about 0.107% at 56 days. The drying shrinkage of the plain mix without recycling water was relatively higher than the RW2.5 and RW5 mix. The RW5 mix showed lowest carbonation depth compared to other mixes. In this study, the RW5 lightweight aggregate mortar with 5% recycling water exhibits excellent compressive strength and carbonation resistance. Therefore, it is considered that if the recycling water, a by-product of the concrete industry, is properly used as prewetting water and mixing water of lightweight mortar and concrete, it will be possible to increase the recycling rate of the by-product and contribute to improve the property of lightweitht aggregate mortar and concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.1
• /
• pp.53-60
• /
• 2024

Compressive strength in concrete has many affecting parameters and varies with exposure conditions. Although the concrete has same mix proportions, its properties are different with exposure conditions, and sea-environment can be classified into three groups such as tidal, atmospheric, and sea submerged region particularly. In this study, compressive strength was evaluated on 7-year-cured concrete and the results from previous equations (KDS, ACI, CEB, and JSCE) were compared with them. Furthermore the strength and carbonation progress were evaluated on concrete cured for 7 years exposed to three different sea environment. Three levels of w/c (water to cement) ratio (0.37, 0.42, and 0.47) and three different exposure conditions (tidal, atmospheric, and submerged) were considered. The results from wet-cured condition are all higher than those from the previously proposed equations, and the results from different sea exposure conditions (tidal, atmospheric, and submerged region) were lower than those from wet-cured condition. A reduction of strength was evaluated with increasing w/c ratio and the minimum strength was evaluated in the sea-submerged conditions. Several experimental constants applicable to the previous equations were obtained from regression analysis since the strength change with w/c ratios were not considered in those equations. Regarding carbonation depth with different exposure conditions, higher carbonation depth clearly was observed with increasing w/c ratios, and evaluated in the order of atmospheric, submerged, and tidal region. Considerable carbonation depth was observed in submerged and tidal region due to sulfate ion and dissloved carbon dioxide as well.

• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.577-584
• /
• 2012

Carbonation resistance is one of the most influencing factors on durability of concrete. Alkali activated slag (AAS) is known to have weaker resistance for carbonation than OPC due to the low calcium contents. In this paper, the carbonation characteristic of AAS mortar which is related to the basicity (CaO/$SiO_2$) was investigated. In order to give the various basicity conditions, SM (source material) was blended with quicklime (CaO) and silicon dioxide ($SiO_2$) by adopting mechano-chemical treatment method. Experiments including flow test, compressive strength test, carbonation depth test, together with XRD, FTIR and TGA were employed to evaluate the effects of basicity of SM on the carbonation characteristics. The test results showed that the carbonation resistance effectively increased with the increase of the basicity of SM.