• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.202-209
• /
• 2005

Phase evolution, microstructure and the electrical properties such as $k_p$ and $Q_m$ of $Pb(Mg_{1/3}Nb_{2/3})O_3[PMN]-Pb(Mn_{1/3}Nb_{2/3})O3[PM'N]-PbZrO_3[PZ]-PbTiO_3[PT]$ quaternary system were investigated within the compositional ranges $0{\leq}y{\leq}0.125$, y+z=0.125, and $0.39{\leq}x{\leq}0.54$ of the formula $Pb_{0.97}Sr_{0.03}[Mg_{1/3}Nb_{2/3})_y\;(Mn_{1/3}Nb_{2/3})_z\;(Zr_{x}Ti_{1-x})_{1-(y+z)}]O_3$. In the case of increasing Mn/(Mg+Mn) ratio for a fixed Zr/Ti ratio of 47.5/52.5, phase relation remained unchanged but the grain size drastically decreased, and the electrical properties changed as following: both $k_P$ and $Q_m$ reached the peak values at $Mn/(Mg+Mn)\cong0.3l7$ and gradually decreased; $\varepsilon33^T$ showed a monotonic decrease; P-E hysteresis loop gradually changed to asymmetrical one, and $E_i$ increased in correspondence. With increasing Zr/Ti ratio for a fixed Mn/(Mg+Mn) ratio of 0.317, on the contrary, the cell parameter $(\alpha^2c)^{1/3}$ gradually increased, and tetragonal-rhombohedral morphotropic phase boundary appeared in the range of $51/49{\leq}Zr/Ti{\leq}54/46$. the meantime, the grain size substantially increased, and the electrical properties changed as following: $k_P$ and $\varepsilon33^T$ reached peak values at Zr/Ti=51/49 and 48/52, respectively, and then gradually decreased; change of $Q_m$ was adverse to $k_P$; both $E_C\;and\;E_i$ considerably decreased while $P_S$ moderately increased. For the system 0.125(PMN+PM'N)-0.875PZT studied, the composition Mn/(Mg+Mn)=0.3l7 and Zr/Ti=51/49 revealed some promising electrical properties for piezoelectric transformer application such as $k_P=0.58,\;Q_m\cong1000$, and $\varepsilon^T_{33}=970$, as well as dense and fine-grained microstructure.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.32 no.3
• /
• pp.224-230
• /
• 2008

In this article, $TiO_2$ nanoparticles were synthesized by using $O_2$-enriched coflow, hydrogen, diffusion flames. We investigated the thermal stability of the flame-synthesized $TiO_2$ nanoparticles by examining the crystalline structures of the nanoparticles. Also, the results were compared with those of commercial P-25 nanoparticles. $TiO_2$ nanoparticles, which were spherical with diameters approximately ranging from 30 to 60nm, were synthesized. From the XRD analyses, about 96wt% of the synthesized nanoparticles were anatase-phase. After the heat-treatment at $800^{\circ}C$ for 30 minutes, the synthesized $TiO_2$ nanoparticles showed no significant changes of their shapes and crystalline phases. On the other hand, most of the commercial particles sintered with each other and changed to the rutile-phase. Based on the result of XRD analysis it is believed that the flame-synthesized $TiO_2$ nanoparticles have higher thermal stability at $800^{\circ}C$ than the commercial particles.

• Applied Chemistry for Engineering
• /
• v.8 no.5
• /
• pp.709-714
• /
• 1997

$TiO_2$ hydrate coating on mica in an aqueous solution of $TiOSO_4$ by the hydrolysis using ammonia water studied with emphasis on coating conditions for a uniform coating. For the uniform coating of $TiO_2$ film on mica surface, it was found that smaller mica particles were coated more uniformly compared to larger particles. It was necessary to suppress the rate of formation of hydrated $TiO_2$ particles in solution, which were deposited on mica and generate irregular coating. It was also necessary to control precipitation yield by varying the reaction temperature to obtain uniform coating. More uniform coating was obtained with higher precipitation yield. A uniform dense film was formed when mica particles of average size of $14.7{\mu}m$ is used for mica slurry solution, of which pH is 2.5, and the factor of acidity of $TiOSO_4$ solution is 291, and the solution was kept at $80^{\circ}C$ for 3 hours. The morphology of $TiO_2$ film formed on mica was little affected by firing at $900^{\circ}C$.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.56.2-56.2
• /
• 2011

고효율 염료감응 태양전지를 제작하기 위해 Sol-gel법을 사용하여 $TiO_2$ 분말을 제조하였다. 제조 과정 중 다양한 양의 nitric acid를 첨가하여 pH를 조절하였다. Sol-gel법을 위한 출발 물질로 titanium (IV) isopropoxide(TTIP)와 DI water를 사용하였으며 nitric acid은 0, 0.05, 0.1, 0.15의 몰비(nitric acid/TTIP)로 첨가하였다. 첨가한 결과 pH는 $22^{\circ}C$에서 각각 5.52, 2.26, 1.68, 1.38이었다. 얻어진 $TiO_2$ 콜로이드 용액은 결정성 있는 분말로 제조 후 $5{\times}5[mm^2]$ 크기의 염료감응 태양전지를 제작하는데 사용 되였다. $TiO_2$의 결정구조 및 형태는 cell의 XRD와 FE-SEM으로 분석되었고 전기화학적 특성을 분석하기 위해 irradiation of AM 1.5 ($100mW/cm^2$) simulatedsunlight에서 I-V 곡선을 측정하였다. 측정 결과 몰비(nitric acid/TTIP) 0.05, pH가 2.26일 때 가장 우수한 효율 특성을 보였다.

• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.863-869
• /
• 2004

The purpose of this research is to investigate the mechanical property and ductile-brittle transition temperature of Ti-Nb-P added extra low carbon interstitial free steel having a tensile strength of 440 MPa. The mechanical property and transition temperature of hot rolled steel sheets were more influenced by the coiling temperature rather than by the small amount of alloying element. Further, at the same composition, the property of the specimen coiled at low temperature was superior to that obtained at higher coiling temperature. The fracture surface of 0.005C-0.2Si-1.43Mn steel coiled at $630^{\circ}C$ showed a ductile fracture mode at $-100^{\circ}C$, but coiling at $670^{\circ}C$ showed a transgranular brittle fracture mode at $-90^{\circ}C$. The galvannealed 0.006C-0.07Si-1.33Mn steel sheet annealed at $810^{\circ}C$ has tensile strength and elongation of 442.8 MPa and $36.6\%$, respectively. The transition temperature of galvannealed 0.006C-0.07Si-1.33Mn steel sheet was increased with a drawing ratio, and the transition temperature of the galvannealed 0.006C-0.07Si-1.33Mn steel was $-60^{\circ}C$ at a drawing ratio of 1.8

• Korean Journal of Materials Research
• /
• v.23 no.6
• /
• pp.334-338
• /
• 2013

In this study, $BaTiO_3$ thin films were grown by RF-magnetron sputtering, and the effects of the thin film thickness on the structural characteristics of $BaTiO_3$ thin films were systematically investigated. Instead of the oxide substrates generally used for the growth of $BaTiO_3$ thin films, p-Si substrates which are widely used in the current semiconductor processing, were used in this study in order to pursue high efficiency in device integration processing. For the crystallization of the grown thin films, annealing was carried out in air, and the annealing temperature was varied from $700^{\circ}C$. The changed thickness was within 200 nm~1200 nm. The XRD results showed that the best crystal quality was obtained for ample thicknesses 700 nm~1200 nm. The SEM analysis revealed that Si/$BaTiO_3$ are good quality interface characteristics within 300 nm when observed thickness. And surface roughness observed of $BaTiO_3$ thin films from AFM measurement are good quality surface characteristics within 300 nm. Depth-profiling analysis through GDS (glow discharge spectrometer) showed that the stoichiometric composition could be maintained. The results obtained in this study clearly revealed $BaTiO_3$ thin films grown on a p-Si substrate such as thin film thickness. The optimum thickness was 300 nm, the thin film was found to have the characteristics of thin film with good electrical properties.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.2
• /
• pp.69-75
• /
• 2008

Electrochemical behaviors of surface modified and MC3T3-E1 cell cultured Ti-30Ta alloys have been investigated using various electrochemical methods. The Ti alloys containing Ta were melted by using a vacuum furnace and then homogenized for 6 hrs at $1000^{\circ}C$. MC3T3-E1 cell culture was performed with MC3T3-E1 mouse osteoblasts for 2 days. The microstructures and corrosion resistance were measured using FE-SEM, XRD, EIS and potentiodynamic test in artificial saliva solution at $36.5{\pm}1^{\circ}C$. Ti-Ta alloy showed the martensite structure of ${\alpha}+{\beta}$ phase and micro-structure was changed from lamellar structure to needle-like structure as Ta content increased. Corrosion resistance increased as Ta content increased. Corrosion resistance of cell cultured Ti-Ta alloy increased predominantly in compared with non cell cultured Ti- Ta alloy due to inhibition of the dissolution of metal ion by covered cell. $R_p$ value of MC3T3-E1 cell cultured Ti-40 Ta alloy showed $1.60{\times}10^6{\Omega}cm^2$ which was higher than those of other Ti alloy. Polarization resistance of cell-cultured Ti-Ta alloy increased in compared with non-cell cultured Ti alloy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.43-46
• /
• 2002

Ferroelectric Mg-doped SBT and Ti-doped SBT were successfully deposited on Pt/Ti/$SiO_2/Si$ substrate by using a sol-gel solution coating method. The solutions were prepared through out adding the metal alkoxide solutions to SBT solution. The typical hysteresis loop of the films was obtained at 5V. The measured $2P_r$ value were $16.50{\mu}C/cm^2$ for SBT, $18.98{\mu}C/cm^2$ and for Mg-doped SBT, and $17.10{\mu}C/cm^2$ for Ti-doped SBT at an applied voltage of 5V, respectively. And it is found that the leakage current densities are less than $10^{-7}A/cm^2$ when applied voltage is less than 10.8MV/cm, which indicates the excellent insulating characteristics.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.192-202
• /
• 1996

In Li0.4Ca0.05AlP0.5Si0.75O4.5 composition glass, glass-ceramic having a near 100% crystallinity after nucleation heat treatment of 74$0^{\circ}C$/2 h and crystallization heat treatment of 90$0^{\circ}C$/2 h and in-situ TiO2 whisker reinforced glass-ceramic after heat treatment of 105$0^{\circ}C$ for 20 h were fabricated with the addition of 4% TiO2 as a nucleating agent. With these materials a ball-on-disc type wear test was conducted in order to examine the effect of TiO2 whisker prepcipitation on ambient and high temperature wear properties of the glass-ceramic. Wear test results indicated that all specimens exhibited micro-fracture wear mechanism in ambient temperature. As temperature increased the wear rates of the materials were increased. However the in-situ TiO2 whisker reinforced glass-ceramic exhibited the lowest wear rate over the test temperature range. This resulted from the improvement of harness and fracture toughness of the material as the glass converted into the glass-ceramic followed by precipitation of TiO2 whiskers throughout the glass-ceramic matrix.

• Journal of Industrial Technology
• /
• v.32 no.A
• /
• pp.95-102
• /
• 2012

To advance luminance efficiency of Titania at visible range, N-doped $TiO_2$ was prepared by using ammonium hydroxide as a source of nitrogen. The photoactivities of the synthesized $TiO_2$ were evaluated on the basis of degradation of humic acid in aqueous solutions with different light sources, UV-C, UV-A and fluorescent lamp. As a result, at UV-C is high efficiency $UV_{254}$ decrease and TOC removal. In this study, the best synthetic conditions of N-doped $TiO_2$ were 5.0 M of ammonium hydroxide concentration and calcination temperature of $550^{\circ}C$. The degradation rate of humic acid as an evaluation of photoactivities of the catalysts were conducted with pH variation, decrease rate of molecular absorption, removal rate of total organic carbon and fluorescece evolution for humic acid solution. XRD and SEM were applied for analysis of surface analysis of the catalysts.