• Earthquakes and Structures
• /
• 제5권4호
• /
• pp.477-497
• /
• 2013

This paper reports extensive experimental study done to compare workability and bond strength of five different types of polymer-based bonding agents for reinforcing bars in pinning retrofit. In pinning retrofit, steel pins of 6 to 10 mm diameters are inserted into holes drilled diagonally from mortar joints. This technique is superior to other techniques especially in retrofitting historic masonry constructions because it does not change the appearance of constructions. With an ordinary cement paste as bonding agent, it is very difficult to insert reinforcing bars at larger open times due to poor workability and very thin clearance available. Here, open time represents the time interval between the injection of bonding agent and the insertion of reinforcing bars. Use of polymer-cement paste (PCP), as bonding agent, is proposed in this study, with investigation on workability and bond strengths of various PCPs in brick masonry, at open times up to 10 minutes, which is unavoidable in practice. Corresponding nonlinear finite element models are developed to simulate the experimental observations. From the experimental and analytical study, the Styrene-Butadiene Rubber polymer-cement paste (SBR-PCP) with prior pretreatments of drilled holes showed strong bond with minimum strength variation at larger open times.

• 대한치과기공학회지
• /
• 제31권4호
• /
• pp.15-23
• /
• 2009

The aim of this study was to evaluate the bond strength of using a Au bonding agent applied on cp-Ti and nonprecious metal-gold-ceramic system. Metallic frameworks(diameter: 5mm, height: 20mm)(N=56, n=7per group) cast in Ni-Cr alloy, Co-Cr alloy and cp-Ti were obtained using acrylic templates and airborne particle abraded with $110{\mu}m$ aluminum oxide. Au bonding agent was applied on wash opaque firing as intermediate layer. SEM and SEM/EDS line profile were performed on the cutting the cross-section of the metal substrate-porcelain with intermediate Au coating. Groups were tested using shear bond strength(SBS) testing at 0.5mm/min. The mean SBS values for the ceramic-Au layer-metal combination were significantly higher than those ceramic-metal combination. While ceramic-Au layer-cp-Ti combinations failed to increase bond strength instead of using a titanium bonding porcelain. The appication of using Au intermediate layer significantly improve the bond strength combination with metal-ceramic system.

• 대한치과보철학회지
• /
• 제19권1호
• /
• pp.61-73
• /
• 1981

The effects of the opaque porcelain firing temperature, the bonding agent and the degassing prior to the opaque firing On the bond strength were investigated by means of the tensile shear stIe$. The diffusional behaviours at the interface of the porcelain and the alloy, and .the microstructures of the ceramic and metal composite were studied for understanding the bonding mechanism. The results obtained in this experiment were summarizd as follow; 1. With no application of bonding agent, the tensile shear strength of the specimen firing at $1840^{\circ}F$ was higher than that of the specimen firing at $1760^{\circ}F$. 2. The highest bond strength was obtained by application of bonding agent without degassing prior to the opaque firing. 3. Application of bonding agent after the degassing showed the lowest bond strength. 4. The greater number of pores were observed at the firing temperature of $1840^{\circ}F$ than that of $1760^{\circ}F$ in the porcelain and the interface respectively.

• 한국콘텐츠학회논문지
• /
• 제10권10호
• /
• pp.219-225
• /
• 2010

티타늄 표면처리방법 중 gold 코팅, TiN 코팅, 그리고 전용결합재를 복합적으로 사용하여 티타늄과 세라믹의 결합강도에 미치는 영향을 분석하고자 하였다. 티타늄과 세라믹의 3점 굽힘 결합강도를 측정한 결과, TiN 코팅과 전용결합재로 처리한 SPTB군이 $72.20({\pm}5.25)MPa$로 가장 높게 나타났으며, 전용결합재로 처리한 SPB군($67.66({\pm}12.10)MPa$), gold 코팅과 전용결합재로 처리한 SPGB군($46.95({\pm}12.48)MPa$), 코팅과 전용결합재로 처리하지 않은 SP군$(43.80({\pm}5.12)MPa)$ 순으로 나타났다. 시편들의 결합강도를 통계 분석한 결과, 전용 결합재로 처리한 SPB군과 TiN코팅과 전용결합재로 처리한 SPTB군이 결합력이 유사하게 나타났으며, 전용결합재로 처리한 군(SPB)이 처리하기 않은 군(SP)에 비하여 결합력이 높게 나타났으며, TiN 코팅한 군(SPTB)이 gold 코팅한 군(SPGB)에 비하여 결합력이 높게 나타난 것으로 관찰되었다.

• 대한치과보철학회지
• /
• 제38권3호
• /
• pp.328-335
• /
• 2000

Statement of the problem. Recently an innovative method of fabricating indirect restorations by gold electroforming has been developed. But the bond quality and strength of the gold coping to the porcelain is uncertain. Purpose of study. The purpose of this study is to analyze and evaluate the electroformed gold surface for mechanical bonding between the gold and the ceramic veneering. Methods/material. Electroformed disks were made using electroforming technique. And the surface of the electroformed coping was analyzed after sandblasting, heat-treatment, bonding agent application, opaque porcelain firing with scanning electron microscopy and energy dispersive x-ray analysis. Results. In the analysis with SEM, Sandblasting made the sharp edges and undercuts on the electroformed surface, and after bonding agent application, net-like structure were created on the electroformed surface. In the energy dispersive x-ray analysis it is confirmed that electroformed surface contains some impurities. Conclusion. With the use of sandblasting and bonding agent, electroformed surface seems to be enough to bond with veneering porcelain.

• Restorative Dentistry and Endodontics
• /
• 제21권1호
• /
• pp.187-201
• /
• 1996

The purpose of this study was to evaluate the sealing ability of a calcium hydroxide plug treated with a bonding agent. Ninety extracted human anterior teeth and premolars with single canal were used in this study. Crowns were removed. the canal's were instrumented. and the roots were randomly divided into three groups of 30 each. In control group. a single apical seat was prepared with #60 K file 1mm short of the apex and the root canal was obturated with Gutta-percha and Sealapex by the lateral condensation method. In experimental group 1 and group 2. to prepare an apical isthmus of 1mm in length. the first apical seat was prepared with a #45 K file 1mm short of the anatomical apex and with a #60 K file 2mm short for the second apical seat. Dry calcium hydroxide powders were packed in the apical isthmus with a hand plugger and #60 K file and then. the root canal was obturated with Gutta-percha and Seal apex by the lateral condensation method. In experimental group 2. following an application of the bonding agent to the plug. the root canal was obturated in the same way. The teeth of each group were immersed in a 2% methylene blue dye solution. for 1, 2, and 4 weeks. The distance from the tip of the cone to the deepest penetration was measured using the Tool maker's microscope. The results were as follows : 1. The teeth having the calcium hydroxide plug treated with the dentin bonding agent (experimental group 2) showed the lowest leakage with 1.4705mm and the control group without apical plug(no apical isthmus) showed the highest leakage with 3.1735mm. 2. The control group without apical plug showed higher leakage than experimental group 1 having the calcium hydroxide plug treated without the dentin bonding agent(p>0.05). 3. The control group without apical plug and experimental group 1, having the calcium hydroxide plug treated without the dentin bonding agent. showed higher leakage than experimental group 2. having the calcium hydroxide plug treated with the dentin bonding agent(p<0.001). 4. The immersion time had no significant effect on the degree of leakage. In conclusion, the results showed that the calcium hydroxide plug treated with the dentin bonding agent could decrease the microleakage from the root apex effectively.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.301-304
• /
• 2006

The purpose of this study is to evaluate bonding properties of PMMA mortars using EPS with silane coupling agent. PMMA mortars are prepared with various silane coupling agent, and tested for flexural strength test, adhesion test in flexure and tensile strength in underwater and air. It is estimated that the application of silane coupling agent to PMMA mortar is more effective in underwater than air.

• Restorative Dentistry and Endodontics
• /
• 제22권1호
• /
• pp.470-478
• /
• 1997

The purpose of this study was to investigate the effects of moistening mechods of dentin on the morphologic states of hybrid layers and on the interfacial bond strength between dentin and composite. Specimens were divided into 6 groups based on the surface moistening methods and materials used. After the dentin surface was conditioned with 10 % phoporic acid and irrigated: 1. The dentin surface was dried. Then bonding agent and composite were applied. 2. The dentin surface was blot-dryed. Then primer, bonding atent and composite were applied. 3. The dentin surface was dryed first. Within 20 seconds, the surface was rewetted, then primer, bonding agent and composite were applied. 4. The dentin surface was dryed. Then primer, bonding agnent and composite were applied. 5. The dentin surface was dryed first. Atter 24hrs, the surface was rewetted, and then primer, bonding agent and composite were applied. 6. The surface was conditioned with NaOCl for 5min. Then primer, bonding agent and composite were applied. To reveal the hybrid layer, scanning electron microscopy was used after the samples were ion beam etched. The shear bond strength of each group was tom pared by ANOVA. In groups 2, 3 and 4, the hybrid layer was clearly visible, but the width was more limited in group 4. In group 1 and 5, the hybrid layer was not found, and a gap was formed between dentin and composite. In group 6, the hybrid layer was not found, but the interface between the dentin and composite was intimate. The shear bond strength of each group was as follows: Group 1 : 4MPa, Group 2 : 14MPa, Group 3 : 12MPa, Group 4 : 14MPa, Group 5 : 5MPa, Group 6 : 9MPa.

• Restorative Dentistry and Endodontics
• /
• 제22권1호
• /
• pp.447-463
• /
• 1997

The purpose of this study was to evaluate the effectiveness of copal varnish and five bonding agents(Scotchbond Multi-Purpose Plus Dental Adhesive System, Panavia 21, All Bond 2, Superbond D-Liner II plus, Fuji Duet) in reducing microleakage under amalgam restorations. Class V cavity were prepared on both buccal and lingual surface of sixty extracted human molars with cementum margin and were filled with different kinds of liners and amalgam. All teeth were stored at $37^{\circ}C$ in physiologic saline solution. After 1 week they were thermally stressed for 500 cycles between 5 and $55^{\circ}C$ in baths containing 0.5 % basic fuchsin dye. The dye penetrations were observed with a stereomicroscope. Scanning electron micrographs were taken of representative tooth sections from each group to assess the nature of the tooth/liner/amalgam interface. The statistical test were applied to the results using a one way analysis variance (ANOVA) and Duncan's multiple range test. The results were as follows ; 1. In all groups, the enamel margin showed significantly lower leakage value than the cementum margin (p<0.05). 2. At the dentin and enamel margins, the leakage value of Copalite-lined group showed significantly higher than that of no liner group (p<0.05), but showed significantly lower than that of bonding agent lined-groups (p<0.05). 3. There was no significant difference between the bonding agent lined-groups (p>0.05). 4. On the backscattered scanning electron microscopy observation, discontinuous gaps were observed between amalgam and dentin in the bonding agent-lined amalgam restorations and the bonding agents appeared to fill the gap space and were mixed with amalgam particles. At the amalgam/tooth interface, unsealed dentin and continuous gaps were found in both unlined and Copalite-lined restorations.

• Restorative Dentistry and Endodontics
• /
• 제20권2호
• /
• pp.699-720
• /
• 1995

본 연구는 양이온 계면활성효과를 가져 소독제로 사용되고 있는 benzalkonium chloride 수용액을 상아질 표면에 대한 습윤용 처리제로 적용시킬 경우 상아질접착제의 접착성능에 미치는 영향을 관찰하기 위해 시행되었다. 소의 하악전치 80개를 8개군으로 분류하여 순면의 상아질을 노출시켜서 산처리한 후 물로 습윤 상태를 유지시킨 대조군과 0.1%, 0.5% 및 1% 농도의 benzalkonium chloride 수용액으로 습윤시킨 실험군으로 나누어 NTG-GMA/BPDM계 상아질접착제인 All-bond 2와 DSDM 계 상아질접착제인 Aelitebond를 각각 접착시킨 후 접착시험을 시행하였다. 상아질 표면을 10% 인산수용액으로 처리한 후 습윤과정을 거친 시편을 각 접착시스템의 primer와 bonding resin을 도포하고 Aelitefil 복합레진으로 접 착시 킨후 항온조에서 24시간 방치한 뒤 인장접착강도를 측정하고, 상아질표면 및 파단면의 양상을 주사전자 현미경으로 관찰하였으며 FT-IR을 사용하여 전처리 전후의 상아질 표면을 분석하여 다음의 결과를 얻었다. 1. NTG-GMA/BPDM 계 상아질접착제 (All-bond 2)로 접착시킨 경우 물로 습윤시킨 대조군에 비해 0.1 % benzalkonium chloride 수용액으로 습윤시킨 군에서 유의하게 높은 인장접착강도를 보였으나(p<0.05), 0.5% 및 1.0 % benzalkonium chloride 수용액으로 습윤시킨 군에서는 유의한 차이가 나타나지 않았다. 2. DSDM계 상아질접착제 (Aelitebond) 로 접착시킨 경우 물로 습윤시킨 대조군과 0.1 %, 0.5% 및 1.0 % benzalkonium chloride 수용액으로 습융시킨 군 간의 인장접착강도의 유의한 차이는 없었다(p>0.05). 3. Benzalkonium chloride 수용액의 적용과 관계 없이 전체적으로 NTG-GMA/ BPDM계 상아질접착제로 접착시킨 경우가 DSDM계 상아질접착제로 접착시킨 경우보다 인장접착강도가 높았으며, 파단양상의 관찰결과에서도 NTG-GMA /BPDM계 상아질접착제를 사용한 경우는 응집성 및 혼합성 파단양상이, DSDM 계 상아질접착제를 사용한 경우는 부착성 파단양상이 우세하였다. 4. 주사전자 현미경적 관찰상에서 benzalkonium chloride 수용액 적용 유무에 따른 각 상아질 표면의 primer 도포양상의 뚜렷한 차이는 관찰되지 않았으나, 상아질 표면에 대한 benzalkonium chloride 수용액 적용 전후의 FT-IR 분석결과 에서는 0.1 % benzalkonium chloride 수용액으로 습윤 처리 시킨 군이 대조군에 비해 NTG-GMA/ BPDM 및 DSDM primer의 도포효과를 다소 향상시킨 소견이었다.