EFFECT OF BENZALKONIUM CHLORIDE ON DENTIN BONDING WITH NTG-GMA/BPDM AND DSDM SYSTEM

Benzalkonium Chloride가 NTG-GMA/BPDM계 및 DSDM계 상아질접착제의 접착성능에 미치는 영향

  • Shin, Il (Dept. of Conservative Dertistry, School of Dentistry, Kyungpook National University) ;
  • Park, Jin-Hoon (Dept. of Conservative Dertistry, School of Dentistry, Kyungpook National University)
  • 신일 (경북대학교 치과대학 보존학교실) ;
  • 박진훈 (경북대학교 치과대학 보존학교실)
  • Published : 1995.09.10

Abstract

This study was conducted to evaluate the effect of benzalkonium chloride solution as a wetting agent instead of water on dentin bonding with NTG-GMA/BPDM system (All-bond 2, Bisco.) and DSDM system (Aelitebond, Bisco.). Benzalkonium chloride solution is a chemical disinfectant widely used in medical and dental clinics for preoperative preparation of skin and mucosa due to its strong effect of cationic surface active detergent. Eighty freshly extracted bovine lower incisor were grinded labially to expose flat dentin surface, and then were acid-etched with 10 % phosphoric acid for 15 second, water-rinsed, and dried for 10 second with air syringe. The specimens were randomly divided into 8 groups of 10 teeth. The specimens of control group were remoistured with water and the specimens of experimental groups were remoistured with 0.1 %, 0.5 %, and 1.0 % benzalkonium chloride solution respectively. And then, the Aelitefil composite resin was bonded to the pretreated surface of the specimens by use of All-bond 2 dentin bonding system or Aelitebond dentin bonding system in equal number of the specimens. The bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured, the mode of failure was observed, the fractured dentin surface were examined under scanning electron microscopy, and FT-IR spectroscopy was taken for the purpose of investigating the changes of the dentin surface pretreated with benzal konium chloride solution followed by each primer of the dentin bonding systems. The results were as follows : In the group of bonding with NTG-GMA/BPDM dentin bonding agent(All-bond 2), higher tensile bond strength was only seen in the experimental group remoistured with 0.1 % benzal konium chloride solution than that in water-remoistured control group(p<0.05). In the group of bonding with DSDM dentin bonding agent (Aelitebond), no significant differences were seen between the control and each one of the experimental group(p<0.05). Higher tensile bond strength were seen in NTG-GMAIBPDM dentin bonding agent group than in DSDM dentin bonding agent group regardless of remoistur ization with benzal konium chloride solution. On the examination of failure mode, cohesive and mixed failure were predominantly seen in the group of bonding with NTG-GMAIBPDM dentin bonding agent, while adhesive failure was predominantly seen in the group of bonding with DSDM dentin bonding agent. On SEM examination of fractured surfaces, no differences of findings of primed dentin surface between the groups with and without remoisturization with benzal konium chloride solution. FT-IR spectroscopy taken from the control and the experimental group reve::.led that some higher absorbance derived from the primers binding to dentin surface was seen at the group pretreated with 0.1 % benzal konium chloride solution than at the control group of remoisturizing with water.

본 연구는 양이온 계면활성효과를 가져 소독제로 사용되고 있는 benzalkonium chloride 수용액을 상아질 표면에 대한 습윤용 처리제로 적용시킬 경우 상아질접착제의 접착성능에 미치는 영향을 관찰하기 위해 시행되었다. 소의 하악전치 80개를 8개군으로 분류하여 순면의 상아질을 노출시켜서 산처리한 후 물로 습윤 상태를 유지시킨 대조군과 0.1%, 0.5% 및 1% 농도의 benzalkonium chloride 수용액으로 습윤시킨 실험군으로 나누어 NTG-GMA/BPDM계 상아질접착제인 All-bond 2와 DSDM 계 상아질접착제인 Aelitebond를 각각 접착시킨 후 접착시험을 시행하였다. 상아질 표면을 10% 인산수용액으로 처리한 후 습윤과정을 거친 시편을 각 접착시스템의 primer와 bonding resin을 도포하고 Aelitefil 복합레진으로 접 착시 킨후 항온조에서 24시간 방치한 뒤 인장접착강도를 측정하고, 상아질표면 및 파단면의 양상을 주사전자 현미경으로 관찰하였으며 FT-IR을 사용하여 전처리 전후의 상아질 표면을 분석하여 다음의 결과를 얻었다. 1. NTG-GMA/BPDM 계 상아질접착제 (All-bond 2)로 접착시킨 경우 물로 습윤시킨 대조군에 비해 0.1 % benzalkonium chloride 수용액으로 습윤시킨 군에서 유의하게 높은 인장접착강도를 보였으나(p<0.05), 0.5% 및 1.0 % benzalkonium chloride 수용액으로 습윤시킨 군에서는 유의한 차이가 나타나지 않았다. 2. DSDM계 상아질접착제 (Aelitebond) 로 접착시킨 경우 물로 습윤시킨 대조군과 0.1 %, 0.5% 및 1.0 % benzalkonium chloride 수용액으로 습융시킨 군 간의 인장접착강도의 유의한 차이는 없었다(p>0.05). 3. Benzalkonium chloride 수용액의 적용과 관계 없이 전체적으로 NTG-GMA/ BPDM계 상아질접착제로 접착시킨 경우가 DSDM계 상아질접착제로 접착시킨 경우보다 인장접착강도가 높았으며, 파단양상의 관찰결과에서도 NTG-GMA /BPDM계 상아질접착제를 사용한 경우는 응집성 및 혼합성 파단양상이, DSDM 계 상아질접착제를 사용한 경우는 부착성 파단양상이 우세하였다. 4. 주사전자 현미경적 관찰상에서 benzalkonium chloride 수용액 적용 유무에 따른 각 상아질 표면의 primer 도포양상의 뚜렷한 차이는 관찰되지 않았으나, 상아질 표면에 대한 benzalkonium chloride 수용액 적용 전후의 FT-IR 분석결과 에서는 0.1 % benzalkonium chloride 수용액으로 습윤 처리 시킨 군이 대조군에 비해 NTG-GMA/ BPDM 및 DSDM primer의 도포효과를 다소 향상시킨 소견이었다.

Keywords