• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.677-680
• /
• 2008

The surface of particles was energetically modified by inter-grinding OPC and BFS in vibration mill for improvement of the early strength and low-heat evolution of concretes. BFS was pre-grinding in ball-mill to 2535(BS2) and 3245 $cm^2/g$(BS3), in blaine surface area. The inter-grinding time in vibration mill was changed from 10 minutes to 30 minutes. And Mixing ration of BFS to OPC was changed in 60, 70, 80%. After inter-grinding, the change of specific surface area, particle size distribution, hydration heat of cement and compressive strength of mortar were measured. As the result of comparison test with LHC, it was found that the mixture and inter-grinding time satisfying the value of over 100% of compressive strength for 7 days and under 170J/g of heat of hydration for 72 hours. and it was confirmed that the possibility of low heat slag cement utilizing blast furnace slag(BS2, BS3) with the low fineness in high volumes.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.96-102
• /
• 2019

When GGBFS(Ground Granulated Blast Furnace Slag) with high blaine is incorporated in concrete, compressive strength in the initial period is improved, but several engineering problems arise such as heat of hydration and quality control. In this paper, compressive strength and durability performance of concrete with 3,000 Grade-low fineness slag are evaluated. Three conditions of concrete mixtures are considered considering workability, and the related durability tests are performed. Although the strength of concrete with 3,000 Grade slag is slightly lower than the OPC(Ordinary Portland Cement) concrete at the age of 28 days, but insignificant difference is observed in long-term compressive strength due to latent hydration activity. The durability performances in concrete with low fineness slag show that the resistances to carbonation and freezing/thawing action are slightly higher than those of concrete with high fineness slag, since reduced unit water content is considered in 3,000 Grade slag mixture. For the long-term age, the chloride diffusion coefficient of the 3000-grade slag mixture is reduced to 20% compared to the OPC mixture, and the excellent chloride resistance are evaluated. Compared with concrete with OPC and high fineness GGBFS, concrete with lower fineness GGBFS can keep reasonable workability and durability performance with reduced water content.