• 한국도로학회논문집
• /
• 제20권4호
• /
• pp.7-13
• /
• 2018

PURPOSES : In order to apply high-speed weigh-in-motion (HS WIM) systems to asphalt pavement, three high-durability asphalt concrete mixtures installed with a WIM epoxy are evaluated. METHODS : In this study, dynamic stability, number of loading repetitions to reach the rut depth of 1 mm, and rut depth measurements of three asphalt mixtures at $60^{\circ}C$ were compared using an Asphalt Pavement Analyzer (APA). Laboratory-fabricated material and field core samples were prepared and tested according to KS F2374. RESULTS : Through the laboratory tests, it was found that all three modified asphalt mixtures (stone-mastic, porous, and semi-rigid) with WIM epoxy showed favorable permanent deformation results and passed the dynamic stability criterion of 3000 loading repetitions per 1 mm. In addition, it was confirmed that the modified SMA mixtures cored from the field construction yields satisfactory rutting testing results using the APA. Finally, the epoxy used for the HS WIM installation shows good adhesion with the three asphalt mixtures and permanent deformation resistance.

• 대한토목학회논문집
• /
• 제28권1D호
• /
• pp.35-43
• /
• 2008

본 연구는 지난 4년간 한국도로공사 시험도로 아스팔트 포장의 주요 손상인자의 정량화와 그 변화를 다루고 있다. 포장상태조사 장비인 ARAN(Automatic Road Analyzer)을 이용하여 준공 직후인 2002년 12월부터 2006년 10월까지 총 5차례에 걸쳐 아스팔트 전단면에 대해 노면상태를 측정하고 소성변형, 균열손상, 그리고 종단평탄성을 중심으로 그 결과를 분석하였다. 실내시험을 통해 시험도로의 아스팔트 혼합물의 온도와 하중 재하속도에 대한 선형점탄성 거동을 비교하고, 표층용 혼합물인 ASTM 19mm에 대해서는 동탄성계수에 미치는 공극률의 영향도 검토하였다. 일반 밀입도 표층 단면의 차륜부에서 추출한 시편의 공극률을 측정하여 시험도로 포장의 다짐도 변화를 추정하였으며 이를 바탕으로 다짐도-포장 손상의 관계를 검토하였다. 교통하중과 포장 손상과의 연관성 분석 결과 소성변형과 균열을 포함한 노면 손상의 증가는 교통하중이 재하되는 시기와 바로 일치하지는 않았으며 오히려 온도와 같은 환경에 더 영향을 받는 것으로 관측되었다. 반면에 노면 평탄성은 공용년수가 증가 하면서 교통하중에 민감하게 반응하였으며 환경인자와의 상관성은 매우 낮은 것으로 나타났다.

• 한국농공학회논문집
• /
• 제61권3호
• /
• pp.43-53
• /
• 2019

It is well-known fact that the stone-mastic asphalt (SMA) mixture has shown superior rut resistance, compared with the dense-graded asphalt (DGA) mixture in highway pavements. However, the SMA is measured to be inferior to DGA mixes when tested by well-known high-temperature test methods, such as the wheel tracking (WT), asphalt pavement analyzer, the Marshall Stability and Kim Test. Therefore, this study examined the reasons why it was measured to be inferior, and devised a potential procedure by which the superiority of SMA could be measured at $60^{\circ}C$. The strength against deformation ($S_D$), which was known to show very high correlation with WT results for DGA mixes, was measured by the Kim Test on the specimen confined in the compacted mold. In standard Kim Test, which used the specimen without confinement, the DGA was measured to show higher $S_D$ than the SMA. But by confining specimen, it was found that the $S_D$ of SMA was measured to be higher than that of DGA. Therefore, the confined static test protocol devised in this study was found to be feasible for evaluating rut resistance of SMA mix.

• 한국도로학회논문집
• /
• 제9권4호
• /
• pp.193-204
• /
• 2007

변형강도($S_D$)는 고온에서 아스팔트 혼합물의 소성변형특성과 상관관계가 높은 특성이며, APA 시험기는 아스팔트 혼합물의 소성변형저항성 평가에 널리 이용된다. 따라서 $S_D$를 이용한 아스팔트 혼합물의 소성변형저항성 추정에 상응하는 값으로 APA 시험 결과가 사용되었으며 $S_D$와 APA의 상관관계를 설정하기 위하여 많은 데이터가 수집되었다. 아스팔트 공시체를 $60^{\circ}C$에 30분간 수침한 후 50mm/min의 하중을 가하여 최대하중 P와 그때의 수직변형 y로 부터 $S_D$를 계산하였다. 같은 혼합물에 대하여 APA 시험도 수행되었다. APA 침하깊이와 $S_D$간의 회귀분석을 수행하여 $R^2=0.76$이 얻어졌다. 이는 변형강도 시험이 아스팔트 혼합물의 고온변형 저항성을 추정 가능한 시험법임을 암시하는 것이다. 또한 회귀분석 모델을 이용하여 특정 등급도로의 표층 및 기층 혼합물 $S_D$의 임계값을 설정할 수 있음을 보였다. 이를 더 정교하게 연구하면 이 임계치는 특정층 포장혼합물의 하한치로 이용될 수 있을 것이다.

• 한국도로학회논문집
• /
• 제5권1호
• /
• pp.11-18
• /
• 2003

포장의 평탄성은 자동차 주행시의 승차감 안전성 및 포장파손의 직접적인 영향인자로서, 도로 이용자 입장에서 도로상태를 평가하는 가장 중요한 사항이다. 이러한 포장의 평탄성은 포장 공용성 평가요소 중 가장 중요한 사항으로서 포장의 품질관리나 유지관리시에 중요하게 다루어져야 하나, 국가별로 각기 고유의 측정장비나 계산방법이 사용됨으로 인해 국제적으로 통일된 관리기준이 확립되어 있지 않은 실정이다. 국내의 경우 신설포장에 대해 포장평탄성의 관리기준을 적용하고 있으며, 관리 기준값은 7.6m CP 장비를 이용한 PrI를 사용하고 있는 실정이다. 그러나 이 장비는 수동식으로서 현장조사시 교통차단이 불가피하며, 측정 및 계산을 인력에 의존하고 있기 때문에 시간이 많이 소요되고 개인오차가 발생하는 문제점이 있다. 따라서 80km의 속도로 평탄성을 측정할 수 있는 자동식 평탄성 장비인 APL에서 IRI 값을 도입하여 수동식 장비의 문제점을 해결코자 하고 있다. 본 연구에서는 기존의 PrI 관리기준을 이용하여 IRI 관리기준을 정립하기 위해, 7.6m CP에 의한 PrI와 APL에 의한 IRI의 상관관계를 시험을 통해 규명하였다. 시험결과 분석에 따르면 아스팔트 및 시멘트 콘크리트 포장 모두는 신뢰 할 만한 상관관계가 나타남을 알 수 있었다.

• 한국도로학회논문집
• /
• 제9권1호
• /
• pp.57-67
• /
• 2007

최근 아스팔트 혼합물의 VMA 혹은 그 외 다른 체적요소의 기준값을 대체하기 위해 유효아스팔트 함량(film thickness)에 대해 논의되어 왔다. 이들 중 일부는 유효 아스팔트 함량의 기준값을 제안하였으며, 일부는 새로운 개념 또는 계산 방법을 포함하는 새로운 모델을 즉, 인덱스 모델(index model) 또는 가상 모델(virtual model)을 소개하였다. 각각의 모델은 아스팔트혼합물의 체적특성을 설명하는데 있어서 형상, 크기 등 골재의 체적특성을 정량화하는 방법을 이용한다. 본 연구에서는 인덱스 모델과 가상 모델의 장점을 결합한 개선된 가상 모델 (modified virtual model)을 제안하였다. 개선된 가상 모델을 기존의 두 가지 모델과 비교평가하기 위하여 DASR 개념에 근거하여 제작된 총 8개의 혼합물을 대상으로 IDT 시험과 APA 시험을 수행하였다. 시험 결과, 아스팔트 혼합물의 공용성과 유효 아스팔트 함량의 관계를 계산함에 있어서 본 연구에서 제안된 가상 모델은 기존의 모델들에 비해 더 적절함을 알 수 있었다.