• 구강회복응용과학지
• /
• 제16권1호
• /
• pp.1-11
• /
• 2000

Dental temporary resin should have adequate strength and similar esthetics as natural teeth. Recently esthetics has become a high priority in clinical dentistry. Thus the evaluation of color stability of dental temporary resin has become an important part in dental research. The purpose of this study was to evaluate the difference in color stability of 3 resins($Snap^{(R)}$, Temporary bridge $resin^{(R)}$, Trim $II^{(R)}$) according to polymerizing methods and stainning. The resins were divided into groups by 2 types of polymerizing methods ( air or pressure and heat curing) The resins were dyed with coffee, chlorhexidine and artificial saliva and then the color stability was evaluated with a spectrophotometer(CM-503i, Minolta, Japan). The results were as follows ; 1. In the color stability according to polymerizing method, pressure and heat polymerizing method was higher than air polymerizing method. 2. The color stability according to staining fluid decreased in the order of I, II, III group, there was significant difference among the groups of staining fluid. 3. The color stability according to resins decreased in the order of $Snap^{(R)}$, Trim $II^{(R)}$, Temporary Bridge $resin^{(R)}$, The $Snap^{(R)}$ resin was highest color stability, there was significant difference among the 3 resins.

• 대한소아치과학회지
• /
• 제45권2호
• /
• pp.137-143
• /
• 2018

본 실험의 목적은 초기 우식 부위에 레진 침투법과 불소 적용 후 탈회 저항성을 비교하기 위함이다. 인공 우식을 유발한 시편을 대조군, 1.23% 산성불화인산염(Acidulated phosphate fluoride(APF))군, 레진 침투군으로 분류하고 각 재료를 적용 후 재탈회시켰다. 이후 공초점 레이저 현미경(Confocal Laser Scanning Microscope(CLSM))을 이용하여 탈회 깊이를 측정하였고 주사전자현미경(SEM)을 이용하여 법랑질 표면 거칠기를 관찰하였다. CLSM을 이용하여 탈회 깊이를 측정하였을 때 대조군, 1.23% 산성불화인산염군, $Icon^{(R)}$ caries infiltrant군 순으로 감소하였다. 탈회 깊이는 1.23% 산성불화인산염군, $Icon^{(R)}$ caries infiltrant군이 대조군에 비해서는 유의성 있는 차이를 보이지만 두 군 간의 차이가 없었다(p < 0.05). 표면거칠기는 대조군에서 매우 거칠고 표면이 불규칙한 양상을 보였고 1.23% 산성불화인산염군, $Icon^{(R)}$ caries infiltrant 군으로 갈수록 표면 거칠기와 불규칙성은 감소하였다.

• 대한치과보철학회지
• /
• 제38권3호
• /
• pp.310-320
• /
• 2000

Statement of the problem. The record base in fabricating procedures of the complete denture, as a temporary form for reproducing denture base, is used to record upper and lower jaw relation and to align artificial teeth and try-in it in the mouth. The accuracy of jaw relation record is affected by the accuracy, stiffness and stability of the record base. So, the accuracy of record base is the most important requirements of jaw relation records. Purpose of study. The purpose of this study was to evaluate the gap that occurred over the palatal area of a maxillary record base fabricated with autopolymerizing resin and light-curing resin. Methods/material. The maxillary record bases were fabricated out of autopolymerizing resin that is used the most frequently in clinics and light-curing resin that attracts special attention for its several merits. The light-curing resin was made by two kinds of polymerization methods, which are one step curing method and multiple step curing method. All record bases were cut in certain positions of the master cast 1 hour and 1 day later after fabrication and the accuracy of the master cast was measured and analyzed with a microscope. Results. A pattern of gap formation between the record base and the maxillary cast was observed in all specimens. According to kinds of resins, autopolymerizing resin was significantly more accurate than light-curing resin. There was no statistical difference according to time lapse, and in all three groups, the maximum discrepancy occurred at the posterior border in the mid-palatal region. Conclusion. The autopolymerizing resin is better than light-curing resin, and multiple step curing method is more accurate than one step curing method when using light-curing resin.

• 대한치과교정학회지
• /
• 제41권2호
• /
• pp.121-126
• /
• 2011

Objective: The purpose of this study was to evaluate shear bond strength (SBS) and failure site location of brackets bonded to enamel with or without desensitizer application. Methods: Sixty-six freshly extracted human premolar teeth were randomly divided into 3 groups of 22. Group 1 served as the control. Desensitizer was applied to the remaining teeth at two time intervals (Group 2, bonded immediately after Pro-$Relief^{TM}$ (Colgate-Palmolive Co., New York, NY, USA) application and Group 3, bonded 30 days after Pro-$Relief^{TM}$ application with the teeth stored in artificial saliva during the 30 days). Orthodontic brackets were bonded with a light cure composite resin and cured with a halogen light. After bonding, the SBS of the brackets was tested using a universal testing device. Adhesive remnant index (ARI) scores were determined after the brackets failed. Data were analyzed with analysis of variance, Tukey's HSD, and G tests. Results: The SBS was significantly lower in Group 2 than in Groups 1 (p = 0.024) and 3 (p = 0.017). Groups 1 and Group 3 did not differ (p = 0.991). ARI scores did not differ significantly among groups. Conclusions: The Pro-$Relief^{TM}$ desensitizer agent applied immediately before bonding significantly reduces bond strength, but the SBS values still exceed the minimum 5.9 - 7.8 MPa required for adequate clinical performance. Immersing the teeth in artificial saliva for 30 days after applying the Pro-$Relief^{TM}$ desensitizer agent and before bonding increased the SBS to control levels.

• Tribology and Lubricants
• /
• 제38권6호
• /
• pp.255-260
• /
• 2022

This research presents tetrahedral amorphous (ta-C) coating on the artificial tooth for improving the durability and functionality (esthtics, foreign body of tooth) by filtered cathodic vacuum arc (FCVA). A differentiated coating method is required for a ta-C coating on polymer owing to the low melting point of the polymer, inter-facial adhesion, low friction, and non-conductivity. Herein, ta-C coating is applied below 50℃, and the potential difference of the carbon plasma drawn to the substrate was controlled by applying a positive duct bias voltage without using a substrate bias voltage. Consequently, the ta-C coating with a thickness of 70nm using the duct bias condition of 20V with the highest plasma intensity satisfies the esthetics of the artificial tooth and had a 5B level of inter-facial adhesion. In addition, the composite hardness of ta-C/polymer is 380 MPa, and correlations with esthetics, sp³ bonding, and mechanical properties. The friction coefficient (CoF) of the ta-C coating in a water-lubricated environment is 0.07, showing a six-fold reduction in CoF compared with that of a polymer.

• 대한치과보철학회지
• /
• 제43권3호
• /
• pp.322-330
• /
• 2005

Statement of problem. In distal extension removable partial denture, the preservation of health of abutment teeth is very important, but abutment teeth are subjected to unfavorable stress. Purpose. The purpose of this study was to investigate the biomechanical effects of mandibular removable partial dentures with various prosthetic designs using strain gauge analysis. Material and methods. Artificial teeth of both canines were anchored bilaterally in a mandibular edentulous model made of resin. Bilateral distal extension removable partial dentures with splinted and unsplinted abutments were fabricated. Group 1 : Clasp-retained mandibular removable partial denture with unsplinted abuhnents Group 2 : Clasp-retained mandibular removable partial denture with splinted abutments by 6-unit bridge Group 3 : Bar-retained mandibular removable partial denture Strain gauges were bonded on the labial plate of the mandibular resin model, approximately 2 mm close to the abutments. Two vertical experimental loadings (100N and 200N) were applied subsequently via two miniature load cells that were placed at mandibular first molar regions. Strain measurements were performed and simultaneously monitored from a computer connected to data acquisition system. For within-group evaluations, t-test was used to compare the strain values and for between-group comparisons, a one-way analysis of variance (ANOVA) was used and Duncan test was used as post hoc comparisons. Results. Strain values increased as the applied load increased from 100N to 200N for all groups (p<.05). The strain values of group 1 and 2 were tensile under loadings. In contrast, strain values of group 3 were compressive in nature. Under 100N loading, group 1 showed higher strain values than group 3 in absolute quantity (p<.05). Under 200N loading, group 3 showed higher strain values than group 1 and 2 in absolute quantity (p<.05). Group 1 showed higher strain values than group 2 (p<.05). Conclusion. Splinting of two isolated abutments by bridge reduced the peri-abutment strain in comparison with unsplinted abutments. Strain of bar-retained removable partial denture increased much more as applied load increased, but was compressive in nature.

• 구강회복응용과학지
• /
• 제18권4호
• /
• pp.313-320
• /
• 2002

The purpose of the present study was to evaluate the marginal discrepancy and topography of artificial crown on teeth extracted due to severe periodontal disease. Twenty specimens were invested into metamethylacrylate resin and cutted into vertical slices along with the long axis of tooth. The selected marginal discrepancy between the outer edge of the crown and the finishing line of abutment was examined by stereo- microscope(Olympus, PM-VSP-3, Japan) at magnification of up to 10, and the topography of finishing margin on crown was observed by stereomicroscopeat magnification of up to $70{\times}$. The results were as follows. (1) The mean marginal discrepancy between extracted tooth and artificial crown were $50.82{\mu}m$. (2) There was a considerable difference in the microstructure of finishing margins among specimens. Microscopic Structure on finishing margin showed indefinite line, poor fit (open, underextended and overextended), distorted margin, and surface roughness. This study suggested that there could be necessary to consider the response of periodontium to the emergence profile of natural tooth and precision of marginal geometry while establishing treatment planning for the reconsruction of the artificial crown.

• 대한소아치과학회지
• /
• 제50권4호
• /
• pp.396-408
• /
• 2023

이 연구의 목적은 유구치를 재현한 인공치를 대상으로 인접면 복합레진 수복 시 매트릭스 시스템에 따른 인접면의 외형, 접촉면의 크기 및 수복 전과 후의 부피 차이를 비교해 보는 것이다. 네 가지 종류의 인공치에 Circumferential 매트릭스 시스템에 해당하는 Tofflemire Matrix System과 Sectional 매트릭스 시스템에 해당하는 Palodent V3 Sectional Matrix System, myJunior Kit를 이용하여 복합레진을 수복하고 3D 모델링 과정을 거쳐 분석되었다. Sectional 매트릭스 시스템을 사용한 경우에서 오목한 인접면 외형이 형성될 확률이 높았으며 더 큰 접촉 면적과 부피가 형성되었다. 이는 Sectional 매트릭스 시스템에 사용되는 매트릭스 밴드의 완전 연질(Dead soft) 특성에 의한 변형으로 인해 접촉점 주변으로 과량의 레진이 적용될 수 있기 때문이다. 게다가 Sectional 매트릭스 시스템에 포함된 고무 웨지가 매트릭스 밴드를 와동에 잘 적합 시키지 못할 가능성이 있다. 따라서 이번 연구의 결과를 바탕으로 유구치 인접면을 Sectional 매트릭스 시스템을 이용해 복합레진 수복하는 경우, 형태학적 관점을 고려한 신중한 사용이 요구된다.

• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.46-55
• /
• 2000

During bonding procedure of composite resin, the prepared cavity can be contaminated by saliva. In this study, marginal microleakage and shear bond strength of a composite resin to primed enamel and dentin treated with artificial saliva(Taliva$^{(R)}$) were evaluated. For the marginal microleakage test, Class V cavities were prepared in the buccal surfaces of fifty molars. The samples were randomly assigned into 5 groups with 10 samples in each group. Control group was applied with a bonding system (Scotchbond$^{TM}$ Multi-Purpose plus) according to manufacture's directions without saliva contamination. Experimental groups were divided into 4 groups and contaminated with artificial saliva for 30 seconds after priming: Experimental 1 group ; artificial saliva was dried with compressed air only, Experimental 2 group ; artificial saliva was rinsed and dried. Experimental 3 group ; cavities were etched with 35% phosphoric acid for 15 seconds after rinsing and drying artificial saliva. Experimental 4 group ; cavities were etched with 35% phosphoric acid for 15 seconds and primer was reapplied after rinsing and drying artificial saliva. All the cavities were applied a bonding agent and filled with a composite resin (Z-100$^{TM}$). Specimens were immersed in 0.5% basic fuschin dye for 24 hours and embedded in transparent acrylic resin and sectioned buccolingually with diamond wheel saw. Four sections were obtained from one specimen. Degree of marginal leakage was scored under stereomicroscope and their scores were averaged from four sections. The data were analyzed by Kruscal-Wallis test and Fisher's LSD. For the shear bond strength test, the buccal or occlusal surfaces of one hundred molar teeth were ground to expose enamel(n=50) or dentin(n=50) using diamond wheel saw and its surface was smoothed with Lapping and Polishing Machine(South Bay Technology Co., U.S.A.). Samples were divided into 5 groups. Treatment of saliva-contaminated enamel and dentin surfaces was same as the marginal microleakage test and composite resin was bonded via a gelatin capsule. All specimens were stored in distilled water for 48 hours. The shear bond strengths were measured by universal testing machine (AGS-1000 4D, Shimaduzu Co., Japan) with a crosshead speed of 5 mm/minute. Failure mode of fracture sites was examined under stereomicroscope. The data were analyzed by ANOVA and Tukey's studentized range test. The results of this study were as follows : 1. Enamel marginal microleakage showed no significant difference among groups. 2. Dentinal marginal microleakages of control, experimental 2 and 4 groups were lower than those of experimental 1 and 3 groups (p<0.05). 3. The shear bond strength to enamel was the highest value in control group (20.03${\pm}$4.47MPa) and the lowest value in experimental 1 group (13.28${\pm}$6.52MPa). There were significant differences between experimental 1 group and other groups (p<0.05). 4. The shear bond strength to dentin was higher in control group (17.87${\pm}$4.02MPa) and experimental 4 group (16.38${\pm}$3.23MPa) than in other groups, its value was low in experimental 1 group (3.95${\pm}$2.51 MPa) and experimental 2 group (6.72${\pm}$2.26MPa)(p<0.05). 5. Failure mode of fractured site on the enamel showed mostly adhesive failures in experimental 1 and 3 groups. 6. Failure mode of fractured site on the dentin did not show adhesive failures in control group, but showed mostly adhesive failure in experimental groups. As a summary of above results, if the primed tooth surface was contaminated with artificial saliva, primer should be reapplied after re-etching it.

• 대한치과기공학회지
• /
• 제39권1호
• /
• pp.25-33
• /
• 2017

Purpose: The aim of this study was to evaluate accuracy of glass fiber mesh complete denture of before and after curing. Methods: Edentulous model was selected as the master model. Ten study models were made by Type IV stone. Wax complete dentures were produced by the denture base and artificial teeth. CD and GD groups were measured six measurement distance before curing. The wax complete denture was investment after measurement is completed. Using a heat polymerization resin was injected resin. After injecting the resin it was curing. A complete denture was re-measured after curing. The measured data was verified by paired t-test. Results: Overall CD group was larger the value of the measured length. In the CD group, A-D point was larger. The smallest point was the B-D point. However, there was no statistically significant difference only C-D point(p>0.05). In the GD group, A-B point was larger. but B-D point was the smallest. A-D and B-C statistically points showed significant differences(p<0.05). Conclusion: Glass fiber mesh resin complete denture can be clinically applied to the edentulous patient.