• Textile Coloration and Finishing
• /
• v.5 no.4
• /
• pp.60-66
• /
• 1993

Aqueous polyurethane(PU) anionomer dispersions were prepared from isophorone diisocyanate (IPDI), polytetramethylene adipate glycol(PTAd) and dimethylol propionic acid(DMPA) as potential anionic centers. The effects of polyol molecular weight(Mn) on the state of dispersion, thermal, mechanical, and viscoelastic properties and swelling of emulsion cast film were determined. With increasing Mn of PTAd, particle size of emulsion and soft segment T$_{g}$ decreased, and solvent swell, emulsion viscosity, and hard segment $T_{g}$ increased. Tensile strength showed minimum with PTAd 1000, and elongation at break generally increased with the Mn of PTAd. These results were possibly nterpreted in terms of soft segment-hard segment phase separation and crystallization of high molecular weight PTAd.

• Applied Chemistry for Engineering
• /
• v.20 no.3
• /
• pp.258-265
• /
• 2009

An anionic polyurethane dispersions (PUDs) were synthesized from the poly (tetramethylene glycol) (PTMG, Mw = 2000 g/mol), mixed isocyanate of dicyclohexylmethane-4,4'-diisocyanate $(H_{12}-MDI)$ and 4,4'-diphenylmethane diisocyanate (MDI), and dimethylol propionic acid (DMPA) as anionic site, following a prepolymer mixing process. Triethylamine (TEA) was used as a neutralization agent and the ethylenediamine (EDA) as the chain extender of the prepolymer. The effects of the DMPA molar ratio and aromatic diisocyanate content in the mixed isocyanate on the particle size and viscosity of PUD were studied. Also, the mechanical and thermal properties of the PUD cast films were discussed according to the molar ratio of DMPA and aromatic isocyanate content. It was found that the particle size and the viscosity of an anionic PUD decreased with increasing DMPA molar ratio but increased with increasing aromatic isocyanate (MDI) content in the mixed isocyanate at the constant DMPA content. Tensile strength of the PUD cast films increased and elongation at break decreased with increasing DMPA content at the constant mixed isocyanate molar ratios. In thermal degradation temperature of PUD cast films, the effect of DMPA contents was great but the effect of aromatic isocyanate contents at the low DMPA content was very slight respectively.