Effect of Soft Segment Length on the Dispersion and Physical Properties of Polyurethane Ionomer

Soft Segment 길이가 Polyurethane Ionomer의 분산특성 및 물리적 특성에 미치는 영향

Aqueous polyurethane(PU) anionomer dispersions were prepared from isophorone diisocyanate (IPDI), polytetramethylene adipate glycol(PTAd) and dimethylol propionic acid(DMPA) as potential anionic centers. The effects of polyol molecular weight(Mn) on the state of dispersion, thermal, mechanical, and viscoelastic properties and swelling of emulsion cast film were determined. With increasing Mn of PTAd, particle size of emulsion and soft segment T$_{g}$ decreased, and solvent swell, emulsion viscosity, and hard segment $T_{g}$ increased. Tensile strength showed minimum with PTAd 1000, and elongation at break generally increased with the Mn of PTAd. These results were possibly nterpreted in terms of soft segment-hard segment phase separation and crystallization of high molecular weight PTAd.

IPDI, PTAd 및 DMPA(음이온 중심)을 사용하여 폴리우레탄 아이오노머를 합성하고 여기에 물을 첨가하여 수분산 폴리우레탄을 제조하였다. 폴리올 분자량(Mn)이 분산상태 및 에멀젼 주사 필름의 열적, 기계적, 점탄성적 성질 및 팽윤에 미치는 영향을 측정하였다. 폴리올 분자량이 증가할수록 에멀젼 입경과 soft segment $T_{g}$는 감소하였으며, 용매팽윤, 에멀젼 점도, hard segment $T_{g}$는 증가하였다. 필름의 인장강도는 Mn = 1000에서 최소치를 나타냈으며, 파단신율은 폴리올 분자량 증가와 더불어 증가하였는데 이러한 결과는 soft-hard segment 상분리와 고분자량 PTAd의 결정화로 적절히 설명할 수 있었다.