• Journal of Korea Foundry Society
• /
• v.36 no.1
• /
• pp.18-23
• /
• 2016

Iron based amorphous ribbons with the nominal compositions of $(Fe_{79}C_{11}B_8Si_2)_{100-X}Cr_X$ (X = 0,2,4,6,8 at%) have been developed as reinforcements that can be applied to the concrete materials. Mechanical properties and glass forming ability of the ribbons can be enhanced by the optimum amounts of Cr additions that can also improve corrosion properties of the ribbons. Vein patterns typical of the fractured surface morphology of amorphous alloys have been observed on the surfaces of ribbons after tensile tests. It is inferred from the EDS analysis results of vein patterns that carbon segregations occur within the narrow shear band regions.

• Journal of the Korean Ceramic Society
• /
• v.45 no.4
• /
• pp.196-203
• /
• 2008

Metal-carbon/$TiO_2$ composite photocatalysts were thermally synthesized through the mixing of anatase to metal(Cu, Zn) containing phenol resin in an ethanol solvent coagulation method. The BET surface area increases, with the increase depending on the amount of metal salt used. From SEM images, metal components and carbon derived from phenol resin that contains metal was homogeneously distributed to composite particles with porosity. XRD patterns revealed that metal and titanium dioxide phase can be identified for metal-carbon/$TiO_2$ composites, however, the diffraction peaks of carbon were not observed due to the low carbon content on the $TiO_2$ surfaces and due to the low crystallinity of the amorphous carbon. The results of a chemical elemental analysis of the metal-carbon/$TiO_2$ composites showed that most of the spectra for these samples gave stronger peaks for C, O, treated metal components and Ti metal compared to that of any other elements. According to photocatalytic results, the MB degradation can be attributed to the three types of synergetic effect: photocatalysis, adsorptivity and electron transfer, according to the light absorption between the supporter $TiO_2$, metal species, and carbon layers.

• Journal of Digital Contents Society
• /
• v.18 no.6
• /
• pp.1199-1205
• /
• 2017

Global energy consumption is rapidly increasing yearly due to drastic industrial advances, requiring the development of new energy storage devices. For this reason, supercapacitors with fast charge-discharge, long life cycle and high power density is getting attention, and have been considered as one of the potential energy storage systems. In this research, we developed a supercapacitor that consists of amorphous manganese oxide($MnO_2$) electrodes deposited onto carbon cloth substrates using the hydrothermal method. The Fe-doped amorphous $MnO_2$ samples were characterized by X-ray diffraction(XRD), Energy Dispersive X-ray spectroscopy(EDX), as well as scanning electron microscopy(SEM). The electrochemical analysis of the prepared samples were performed using cyclic voltammetry and galvanostatic charge-discharge measurements in 1M $Na_2SO_4$ electrolyte. The test results demonstrate that the supercapacitor based on the Fe-doped amorphous $MnO_2$ electrodes has a specific capacitance as high as 163F/g at 1A/g current density, and good cycling stability of 87.34% capacitance retention up to 1000 cycles.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.1
• /
• pp.32-36
• /
• 2021

This study was investigated in carbon diffusion behavior of laser-carburized TiZrN coating layer and the changes of mechanical properties. The carbon paste was deposited on TiZrN coatings, and the laser was irradiated to carburize into the coatings. The XRD peak corresponding to the (111) plane shifted to a lower angle after the carburization, showing the lattice expansion by doped carbon. The decreased grain size implied the compression by the grain boundary diffusion of carbon. The XPS spectra for the bonding states of carbon was analyzed that carbon was substitute to nitrogen atoms in TiZrN, as carbide, through the thermal energy of laser. In addition, the combination of sp2 and sp3 hybridized bonds represented the formation of an amorphous carbon. The cross-sectional TEM image and the inverse FFT of the TiZrN coating after carburizing were observed as the wavy shape, confirming the amorphous phase located in grain boundaries. After the carburization, the hardness increased from 34.57 GPa to 38.24 GPa, and the friction coefficient decreased by 83 %. In particular, the ratio of hardness and elastic modulus (H/E) which is used as an index of the elastic recovery, increased from 0.11 to 0.15 and the wear rate improved by 65 %.

• Journal of Radiation Industry
• /
• v.9 no.1
• /
• pp.15-20
• /
• 2015

Carbon fiber has received much attention owing to its properties, including a large surface-to-volume ratio, chemical and thermal stability, high thermal and electrical conductivity, and high mechanical strengths. In particular, magnetic nanopowder dispersed carbon fiber has been attractive in technological applications such as the electrochemical capacitor and electromagnetic wave shielding. In this study, the nickel-oxide-nanoparticle dispersed polyacrylonitrile (PAN) fibers were prepared through an electrospinning method. Electron beam irradiation was carried out with a 2.5 MeV beam energy to stabilize the materials. The samples were then heat-treated for stabilization and carbonization. The nanofiber surface was analyzed using a field emission scanning electron microscope (FE-SEM). The crystal structures of the carbon matrix and nickel nanopowders were analysed using X-ray diffraction (XRD). In addition, the magnetic and electrical properties were analyzed using a vibrating sample magnetometer (VSM) and 4 point probe. As the irradiation dose increases, the density of the carbon fiber was increased. In addition, the electrical properties of the carbon fiber improved through electron beam irradiation. This is because the amorphous region of the carbon fiber decreases. This electron beam effect of PAN fibers containing nickel nanoparticles confirmed their potential as a high performance carbon material for various applications.

• Korean Journal of Materials Research
• /
• v.23 no.3
• /
• pp.190-193
• /
• 2013

Spatial distributions of alloying elements of an Fe-based amorphous ribbon with a nominal composition of $Fe_{75}C_{11}Si_2B_8Cr_4$ were analyzed through the atom probe tomography method. The amorphous ribbon was prepared through the melt spinning method. The macroscopic amorphous natures were confirmed using an X-ray diffractometer (XRD) and a differential scanning calorimeter (DSC). Atom Probe (Cameca LEAP 3000X HR) analyses were carried out in pulsed voltage mode at a specimen base temperature of about 60 K, a pulse to base voltage ratio of 15 %, and a pulse frequency of 200 kHz. The target detection rate was set to 5 ions per 1000 pulses. Based on a statistical analyses of the data obtained from the volume of $59{\times}59{\times}33nm^3$, homogeneous distributions of alloying elements in nano-scales were concluded. Even with high carbon and strong carbide forming element contents, nano-scale segregation zones of alloying elements were not detected within the Fe-based amorphous ribbon. However, the existence of small sub-nanometer scale clusters due to short range ordering cannot be completely excluded.

• Journal of the Korean Chemical Society
• /
• v.34 no.5
• /
• pp.396-403
• /
• 1990

We describe how to design and construct a LPCVD (Low Pressure Chemical Vapor Deposition) apparatus which can be applicable to the study of reaction mechanism in general CVD experiments. With this apparatus we have attempted to make diamond like carbon films on the p-type (111) Si wafer from (H$_2$ ＋ CH$_4$) gas mixtures. Two different methods have been tried to get products. (1)The experiment was carried out in the reactor with two different inlet gas tubes. One coated with phosphoric acid was used for supplying microwave discharged hydrogen gas stream, and methane has been passed through the other tube without the microwave discharge. In this method we got only amorphous carbon cluster products. (2) The gas mixture (H$_2$ ＋ CH$_4$) has been passed through the discharge tube with the Si wafer located in and/or near the microwave plasma. In this case diamond-like carbon products could be obtained.

• Korean Chemical Engineering Research
• /
• v.56 no.3
• /
• pp.303-308
• /
• 2018

Silicon/Carbon (Si/C) composite as anode materials for lithium-ion batteries was synthesized to find the effect of binders and an electrolyte additive. Si/C composites were prepared by two step method, including magnesiothermic reduction of SBA-15 (Santa Barbara Amorphous material No. 15) and carbonization of phenol resin. The electrochemical performances of Si/C composites were investigated by charge/discharge, cyclic voltammetry and impedance tests. The anode electrode of Si/C composite with PAA binder appeared better capacity (1,899 mAh/g) and the capacity retention ratio (92%) than that of other composition coin cells during 40 cycles. Then, Vinylene carbonate (VC) was tested as an electrolyte additive. The influence of this additive on the behavior of Si/C anodes was very positive (3,049 mAh/g), since the VC additive is formed passivation films on Si/C surfaces and suppresses irreversible changes.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.460-460
• /
• 2012

반도체 Device가 Shrink 함에 따라 Pattern Size가 작아지게 되고, 이로 인해 Photo Resist 물질 자체만으로는 원하는 Patterning 물질들을 Plasma Etching 하기가 어려워지고 있다. 이로 인해 Photoresist를 대체할 Hard Mask 개념이 도입되었으며, 이 Hardmask Layer 중 Amorphous Carbon Layer 가 가장 널리 사용되고 지고 있다. 이 Amorphous Carbon 계열의 Hardmask를 Etching 하기 위해서 기본적으로 O2 Plasma가 사용되는데, 이 O2 Plasma 내의 Oxygen Species들이 가지는 등 방성 Diffusion 특성으로 인해, 원하고자 하는 미세 Pattern의 Vertical Profile을 얻는데 많은 어려움이 있어왔다. 이를 Control 하기 인해 O2 Plasma Parameter들의 변화 및 Source/Bias Power 등의 변수가 연구되어 왔으며, 이와 다른 접근으로, N2 및 CO, CO2, SO2 등의 여러 Additive Gas 들의 첨가를 통해 미세 Pattern의 Profile을 개선하고, Plasma Etching 특성을 개선하는 연구가 같이 진행되어져 왔다. 본 논문에서 VLSI Device의 Masking Layer로 사용되는, Carbon 계 유기 층의 Plasma 식각 특성에 대한 연구를 진행하였다. Plasma Etchant로 사용되는 O2 Plasma에 새로운 첨가제 가스인 카르보닐 황화물 (COS) Gas를 추가하였을 시 나타나는 Plasma 내의 변화를 Plasma Parameter 및 IR 및 XPS, OES 분석을 통하여 규명하고, 이로 인한 Etch Rate 및 Plasma Potential에 대해 비교 분석하였다. COS Gas를 정량적으로 추가할 시, Plasma의 변화 및 이로 인해 얻어지는 Pattern에서의 Etchant Species들의 변화를 통해 Profile의 변화를 Mechanism 적으로 규명할 수 있었으며, 이로 인해 기존의 O2 Plasma를 통해 얻어진 Vertical Profile 대비, COS Additive Gas를 추가하였을 경우, Pattern Profile 변화가 개선됨을 최종적으로 확인 할 수 있었다.

• Tribology and Lubricants
• /
• v.38 no.3
• /
• pp.101-108
• /
• 2022

The structure and properties of tetrahedral amorphous carbon (ta-C) coatings depend on the main process parameters and bending angles of the magnetic field filter used in the filtered cathodic vacuum arc (FCVA). During the process, it is possible to effectively control the plasma flux of carbon ions incident on the substrate by controlling the arc discharge current, thereby influencing the mechanical properties of the coating film. Furthermore, we can control the size and amount of large particles mixed during carbon film formation while conforming with the bending angle of the mechanical filter mounted on the FCVA; therefore, it also influences the mechanical properties. In this study, we consider tribological characteristics for filtered bending angles of 45° and 90° as a function of arc discharge currents of 60 and 100 A, respectively. Experiment results indicate that the frictional behavior of the ta-C coating film is independent of the bending angle of the filter. However, its sliding wear behavior significantly changes according to the bending angle of the FCVA filter, unlike the effect of the discharge current. Further, upon changing the bending angle from 45° to 90°, abrasive wear gets accelerated, thereby changing the size and mixing amount of macro particles inside the coating film.