• Journal of the Korean Ceramic Society
• /
• v.55 no.1
• /
• pp.61-66
• /
• 2018

In this study, fabrication method of inorganic insulation were studied to reduce $CO_2$ from buildings. Main materials for inorganic insulation were used cement, blast furnace slag and aluminum powder as foaming agent. Mixing ratio of cement and slag was controlled and physical properties of inorganic insulation were analyzed. When inorganic insulation was fabricated using cement and slag, expanded slurries were not sunken and hardened normally. Pore size was 0.5 - 2 mm; mean pore size was about 1mm in inorganic insulation. Compressive strength of inorganic insulation increased with curing time and increased slightly with cement fineness. However, specific gravity decreased slightly with curing time; this phenomenon was caused by evaporation of adsorptive water. When inorganic insulation was dried at $60^{\circ}C$, compressive strength was higher than that of undried insulation. The highest compressive strength was found with a mixture of cement (50%) and slag (30%) in inorganic insulation. Compressive strength was 0.32 MPa, thermal conductivity was 0.043 W/mK and specific gravity was $0.12g/cm^3$.

• Nuclear Engineering and Technology
• /
• v.40 no.6
• /
• pp.497-504
• /
• 2008

In a study of the optimum operational condition for a melting decontamination, the effects of the basicity, slag type and slag composition on the distribution of depleted uranium were investigated for radioactively contaminated metallic wastes of iron-based metals such as stainless steel (SUS 304L) in a direct current graphite arc furnace. Most of the depleted uranium was easily moved into the slag from the radioactive metal waste. The partitioning ratio of the depleted uranium was influenced by the amount of added slag former and the slag basicity. The composition of the slag former used to capture contaminants such as depleted uranium during the melt decontamination process generally consists of silica ($SiO_2$), calcium oxide (CaO) and aluminum oxide ($Al_2O_3$). Furthermore, calcium fluoride ($CaF_2$), magnesium oxide (MgO), and ferric oxide ($Fe_2O_3$) were added to increase the slag fluidity and oxidative potential. The partitioning ratio of the depleted uranium was increased as the amount of slag former was increased. Up to 97% of the depleted uranium was captured between the ingot phase and the slag phase. The partitioning ratio of the uranium was considerably dependent on the basicity and composition of the slag. The optimum condition for the removal of the depleted uranium was a basicity level of about 1.5. The partitioning ratio of uranium was high, exceeding $5.5{\times}10^3$. The slag formers containing calcium fluoride ($CaF_2$) and a high amount of silica proved to be more effective for a melt decontamination of stainless steel wastes contaminated with depleted uranium.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.95-102
• /
• 2015

In this paper, the effects of sodium hydroxide (NaOH) and aluminum potassium sulfate ($AlK(SO_4)_2{\cdot}12H_2O$) dosage on strength properties were investigated. For evaluating the property related to the dosage of alkali activator, sodium hydroxide (NaOH) of 4% (N1 series) and 8% (N2 series) was added to 1~5% (K1~K5) dosage of aluminum potassium sulfate ($AlK(SO_4)_2{\cdot}12H_2O$) and 1% (C1) and 2% (C2) dosage of calcium oxide (CaO). W/B ratio was 0.5 and binder/ fine aggregate ratio was 0.5, respectively. Test result clearly showed that the compressive strength development of alkali-activated slag cement (AASC) mortars were significantly dependent on the dosage of NaOH and $AlK(SO_4)_2{\cdot}12H_2O$. The result of XRD analysis indicated that the main hydration product of $NaOH+AlK (SO_4)_2{\cdot}12H_2O$ activated slag was ettringite and CSH. But at early ages, ettringite and sulfate coated the surface of unhydrated slag grains and inhibited the hydration reaction of slag in high dosage of $NaOH+AlK(SO_4)_2{\cdot}12H_2O$. The $SO_4{^{-2}}$ ions from $AlK(SO_4)_2{\cdot}12H_2O$ reacts with CaO in blast furnace slag or added CaO to form gypsum ($CaSO_4{\cdot}2H_2O$), which reacts with CaO and $Al_2O_3$ to from ettringite in $NaOH+AlK(SO_4)_2{\cdot}12H_2O$ activated slag cement system. Therefore, blast furnace slag can be activated by $NaOH+AlK(SO_4)_2{\cdot}12H_2O$.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11a
• /
• pp.32-37
• /
• 2005

The characteristics of the metal melting and radionuclide distribution of the radioactive has been investigated in a lab-scale arc furnace. The slag former based on the constituents of silica, calcium oxide, aluminum oxide, borate and calcium fluoride additions was used for melting of the stainless and carbon steel. In the melting of the stainless steel, the amount of slag formation increased with an increase of the concentration of the slag former. But the effects of the slag basicity on the amount of stag formation showed a local maximum value of the slag formation with an increase of the basicity index in the melting of the stainless steel as well as in the melting of the carbon steel. With an increase of the amount of slag former addition, the trends of the cobalt distribution into the ingot and the stag depended on the kind of slag former used in the melting of the stainless steel while the effect of the slag basicity on the distribution of the cobalt was not clarified in the melting of carbon steel. Tn the melting of the carbon steel, the strontium was captured at up to $50\%$ into the slag phase. Cesium was completely eliminated from the melt of the stainless steel as well as the carbon steel and distributed to the dust phase.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.1
• /
• pp.15-20
• /
• 2014

In this research, the geopolymer was fabricated using municipal solid waste incineration ash (denoted as MSWIA) slag and alkali activator, NaOH and its properties were analyzed. Particularly, the effects of NaOH molarity, particle size of MSWIA, and liquid/solids ratio on the compressive strength of geopolymers were investigated. The compressive strength of geopolymers fabricated increased with finer grain size of MSWIA, and optimum value of the liquid/solids ratio was identified as 0.13. As the molarity of the NaOH increased, the compressive strength of geopolymers was increased. Even more the 20 M of NaOH, but the strength was not increased. The calcium aluminum silicate and calcium aluminum silicate hydrate zeolites were generated in the geopolymer fabricated with more than 20 M of NaOH, with some unreacted silica and unknown crystals remained. The highest compressive strength, 163 MPa, of geopolymer was appeared at conditions of curing temperature $70^{\circ}C$, and 20 M of NaOH, indicating that the high concentration of NaOH accelerates the geopolymer reaction and dense microstructure. The high-strength geopolymer fabricated in the present study is expected to contribute significantly to develop the field of cement alternative substances and to improve the recycling rate of MSWIA slag.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.9 no.2
• /
• pp.135-141
• /
• 1989

Blast furnace slag presents coarse surface for microbes to grow on and high calcium and magnesium contents to neutralize acid to be produced during anaerobic digestion. Also, slag contains aluminum and iron oxides which would promote biological flocculation, and minerals which would stimulate microbial growth. Acid wastes like dairy waste, carbohydrate waste, sanitary landfill leachate and molases wastes were applied without neutralization to laboratory reactors to examine the applicability of blast furnace slag as media. The study results indicated slag media was effective to neutralize pH and maintain microbial population in the system. Particularly, COD removal efficiency was greater than those from plastic media operations treating dairy waste at higher loading rates.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.333-336
• /
• 2005

The reduction behavior of $Nb_2O_5$ in aluminum containing self-reducing briquettes(SRNB) was investigated. The time required for slag/metal equilibrium was estimated as about 20 minutes from the addition of SRNB on to the surface of molten steel. The maximum yield of Nb was expected with the slag composition of $60\%CaO-40\%Al_2O_3$. When $CaCO_3$ was used as a flux, the oxidation loss of Al by $CO_2$ should be compensated, and the chemical equivalent ratio of Al to $Nb_2O_5$ of about 1.43 was required to maximize the yield of Nb.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.450-457
• /
• 2017

This study is to develop high quality floor mortar which can be applied in construction sites using EXFG(Expansive admixdure Flue Gas desulfurization gypsum). First, as the substitution rate of ALS(Aluminum Slag) increased, the flow is increased proportionally. EXFG showed a tendency to decrease with increasing substitution rate. Also, in the case of the setting time of 5% of ALS replacement rate, the setting time of Plain compared to EXFG was decreased by 5~20%. The compressive strength increased with the ALS replacement ratio at 0%, 5% and the EXFG replacement ratio at 1%. The strength was increased when the ALS replacement ratio was more than 10%. In the case of ALS replacement rate of 0% and 5%, drying shrinkage compared to plain was decreased by about 10~25% regardless of EXFG replacement rate.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.4
• /
• pp.143-150
• /
• 2022

Geopolymers were made by mixing IGCC slag and aluminum smelted waste and their properties were compared with those of IGCC slag based geopolymers. When two raw materials were mixed, the highest compressive strength was obtained at 1.78 of Si/Al ratio. Because the change in compressive strength and density was not so sensitive by the change in Si/Al ratio; that is, the permissible range of Si/Al ratio mixing ratio is broad, it was speculated this broad permissible range would be advantageous for commercialization. The Compressive strength of geopolymers including red mud was higher than that of IGCC based ones and the safety was confirmed by TCLP test. Therefore, it was concluded that the making geopolymers by mixing red mud not only enhances the properties of geopolymers but also gives a recyclability as safe construction materials.

• Journal of the Korea Concrete Institute
• /
• v.24 no.6
• /
• pp.745-752
• /
• 2012

This paper studies the effect of the compressive strength for combined alkali-activated slag mortars. The effect of activators such as alkali type and dosage factor on the strength was investigated. The alkalis combinations made using five caustic alkalis (sodium hydroxide (NaOH, A series), calcium hydroxide ($Ca(OH)_2$, B series), magnesium hydroxide ($Mg(OH)_2$, C series), aluminum hydroxide ($Al(OH)_3$, D series), and potassium hydroxide (KOH, E series)) with sodium carbonate ($Na_2CO_3$) were evaluated. The mixtures were combined in different dosage at 1M, 2M, and 3M. The study results showed that the compressive strength of combined alkali-activated slag mortars tended to increase with increasing sodium carbonate. The strength of combined alkali-activated slag mortars was better than that of control cases (without sodium carbonate). The result from scanning electron microscopy (SEM) analysis confirmed that there were reaction products of calcium silicate hydrate (C-S-H) and alumina-silicate gels from combined alkali-activated slag specimens.