• Corrosion Science and Technology
• /
• v.21 no.4
• /
• pp.282-289
• /
• 2022

Aluminum 1000 series alloy, a pure aluminum with excellent workability and weldability, is mainly used in the ship field. Aluminum alloy can combine with oxygen in the atmosphere and form a natural oxide film with high corrosion resistance. However, its corrosion resistance and durability are decreased when it is exposed to a harsh environment for a long period of time. For solving this problem, a porous oxide film can be formed on the surface using an anodizing treatment method, a typical surface technique among various methods. In this study, aluminum 1050 alloy was anodized for 2 minutes, 6 minutes, and 10 minutes. The structure and shape of the oxide film were then analyzed to determine the corrosion resistance according to the thickness of the oxide film that changed depending on working condition using 15 wt% NaCl. After it was immersed in NaCl solution for 1, 5, and 10 days, corrosion damage was observed. Results confirmed that the thickness of the oxide film increased as the anodization time became longer. The depth of surface damage due to corrosion became deeper when the film was immersed in the 15 wt% NaCl solution for a longer period of time.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.121-128
• /
• 2008

High strength 7xxx aluminum alloys have been applied to automotive bump back beam of the some limited model for light weight vehicle. The aluminum bump back beam is manufactured through extrusion, bending and welding. The residual stress given on these processes combines with the corrosive atmosphere on the road spreaded with corrosive chemicals to melt snow to occur the stress corrosion cracking. The composition of commercial 7xxx aluminum has Zn/Mg ratio about 3 and Cu over 2 wt% for better strength and stress corrosion cracking resistivity. But this composition isn't adequate for appling to the automotive bump back beam with high resistance to extrusion and bad weldability. In this study the composition of 7xxx aluminum alloy was modified to high Zn/Mg ratio and low Cu content for better extrusion and weldability. To estimate the resistivity against stress corrosion cracking of this aluminum alloy by slow strain rate test, the corrosion atmosphere and strain rate separate the stress corrosion cracking from conventional corrosion must be investigated. Using 0.6 Mol NaCl solution on slow strain rate test the stress corrosion cracking induced fracture was not observed. By adding 0.3% $H_2O_2$ and 0.6M $Na_2SO_4$ to 1M NaCl solution, the corrosion potential and current density of polarization curve moved to active potential and larger current density, and on the slow strain rate test the fracture energy in solution was lower than that in pre-exposure. These mean the stress corrosion cracking induced fracture can be estimated in this 1M NaCl + 0.3% $H_2O_2$ + 0.6M $Na_2SO_4$ solution. When the strain rate was below $2{\times}10^{-6}$, the stress corrosion cracking induced fracture start to be observed.

• Journal of the Korean Chemical Society
• /
• v.58 no.1
• /
• pp.85-91
• /
• 2014

The corrosion behavior of aluminum and mild steel in hydrochloric acid medium was studied using a nicotinic acid hydrazide as inhibitor by potentiodynamic polarization, electrochemical impedance spectroscopy technique and gravimetric methods. The effects of inhibitor concentration and temperature were investigated. The experimental results suggested, nicotinic acid hydrazide is a good corrosion inhibitor for both aluminum and mild steel in hydrochloric acid medium and the inhibition efficiency increased with increase in the inhibitor concentration. The polarization studies revealed that nicotinic acid hydrazide exhibits mixed type of inhibition. The inhibition was assumed to occur via adsorption of the inhibitor molecules on the aluminum and mild steel surface and inhibits corrosion by blocking the reaction sites on the surface of aluminum.

• Corrosion Science and Technology
• /
• v.20 no.2
• /
• pp.85-93
• /
• 2021

The corrosion damage of materials in marine environment mainly occurs by Cl^- ions due to the breakdown of passive films. Additionally, various characteristics in seawater such as salinity, temperature, immersion time, flow rate, and biological activity also affect corrosion characteristics. In this study, the corrosion characteristics of stainless steels (STS 304 and STS 316L) and anodized aluminum alloys (AA 3003 and AA 6063) were evaluated with seawater temperature parameters. A potentiodynamic polarization experiment was conducted in a potential range of -0.25 V to 2.0 V at open circuit potential (OCP). Corrosion current density and corrosion potential were obtained through the Tafel extrapolation method to analyze changes in corrosion rate due to temperature. Corrosion behavior was evaluated by measuring weight loss before/after the experiment and also observing surface morphology through a scanning electronic microscope (SEM) and 3D microscopy. Weight loss, maximum damage depth and pitting damage increased as seawater temperature increased, and furthermore, the tendency of higher corrosion current density with an increase of temperature attributed to an increase in corrosion rate. There was lower pitting damage and lower corrosion current density for anodized aluminum alloys than for stainless steels as the temperature increased.

• Corrosion Science and Technology
• /
• v.18 no.1
• /
• pp.24-32
• /
• 2019

The effects of zinc coating and heat treatment on the corrosion resistance of aluminum alloys including A1100 and the modified A3003, used as heat exchanger tube were investigated in this study. The grain size of the heat-treated specimen is larger than that of the specimen without heat treatment, but the grain size did not significantly affect the corrosion behavior. The concentration of zinc was noted at 11.3 ~ 31.4 at.% for the as-received Zn-coated samples and reduced to 1.2 ~ 2.4 at.% after the heat treatment, as measured by the scanning electron microscopy (SEM) with an energy dispersive spectrometer (EDS) on the surface. The concentration of oxygen is 22 ~ 46 at.% for the zinc coated specimens while noted at 7.4 ~ 12.8 at.% for the specimens after the removal of the coating. The corrosion behavior depended largely on the concentrations of zinc, aluminum, and oxygen on the specimen surface, but not on the Mo content. The corrosion potential was high and the corrosion rate was low for a specimen with a low zinc content, a high aluminum content, and a high oxygen content.

• Corrosion Science and Technology
• /
• v.21 no.6
• /
• pp.487-494
• /
• 2022

Anodizing is a typical electrochemical surface treatment method that can improve the corrosion and insulating properties of aluminum alloys. The anodization process can obtain a dense structure. It can be used to artificially grow the thickness of an anodization film. Aluminum 3003 alloy used in this study is the most commonly used alloy for batteries due to its high strength and excellent formability as well as its weldability and corrosion resistance. Aluminum 3003 alloy was anodized at 0 ℃ with 0.3 M oxalic acid at 20 V, 40 V, or 60 V for 1 hour, 6 hours, or 12 hours. As a result of analyzing the composition of each specimen with an Energy Dispersive Spectrometer (EDS), aluminum was converted into an oxide film. The thickness of the formed anodization film increased when the applied voltage and anodization time increased. High corrosion potential values and low corrosion current density values were observed for the thickest oxide layer. The anodization film formed by anodization acted as a protective layer. The electrical resistance increased as the applied voltage and anodization time increased.

• Corrosion Science and Technology
• /
• v.21 no.4
• /
• pp.290-299
• /
• 2022

Anodizing is an electrochemical surface treatment method conferring corrosion resistance and durability by forming a thick anodization film on the metal surface. Aluminum has a long service life and high thermal conductivity and formability, as well as excellent corrosion resistance. Aluminum 3003 alloy has improved formability, strength, and corrosion resistance due to the addition of a small amount of manganese. However, corrosion occurs in seawater and environments polluted with corrosion-inducing substances, which reduce corrosion resistance. Therefore, it is necessary to artificially form a thick anodized film to improve corrosion resistance. In this study, the anodization treatment time was 4 minutes, and voltages of 10 V, 20 V, 30 V, 40 V, 50 V, 60 V, 70 V, 80 V, 90 V, and 100 V were applied. The thickness and pore size of the oxide film increased according to the applied voltage. A barrier film was formed under voltage conditions from 10 V to 50 V, and a porous film was formed under voltage conditions from 60 V to 100 V. After anodizing, coating was applied. Wettability and corrosion resistance were observed before and after coating according to the surface shape and thickness of the oxide film.

• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.292-299
• /
• 2019

The hull material of a high-speed ship may cause erosion damage from fluid impact. When physical erosion and electrochemical corrosion combine, erosion corrosion damage occurs. The aluminum ship is vulnerable to erosion corrosion because it can be operated at high speed. Thus, in this study, Al5052-O and Al6061-T6 aluminum alloys for the marine environment were selected as experimental materials. The erosion corrosion resistance of Al5052-O and Al6061-T6 aluminum alloys in seawater was investigated by an erosion test and potentiodynamic polarization test at the various flow rate (0 m/s, 5 m/s, 10 m/s, 15 m/s, 20 m/s). Erosion corrosion characteristics were evaluated by surface analysis, 3D analysis, SEM analysis, and the Tafel extrapolation method. The results of surface damage analysis after the erosion test showed that Al6061-T6 presented better erosion resistance than Al5052-O. The results of the potentiodynamic polarization test at the various flow rate, corrosion current density by Tafel extrapolation presented lower values of Al6061-T6 than Al5052-O. Al5052-O showed more surface damage than Al6061-T6 at all flow rates. Consequently, Al6061-T6 presented better erosion corrosion resistance than Al5052-O. The results of this study are valuable data for selecting hull material for an aluminum alloy vessel.

• Journal of Power System Engineering
• /
• v.20 no.3
• /
• pp.17-21
• /
• 2016

The corrosion behavior of aluminum alloys in the $H_2SO_4$ solution was investigated based on potentiodynamic techniques. Electrochemical properties, such as corrosion potential($E_c$), passive potential($E_p$), corrosion current density($I_c$), corrosion rate(mpy), of Al-Mg-Si, Al-Cu-Si and Al-Si alloys were characterized at room temperature. Passive aluminum oxide film, which including $Al_2(SO_4)_3$ and $3Al_2O_34SO_38H_2O$, were uniformly formed on the surface via the reaction of Al with $SO{_3}^{2-}$ or $SO{_4}^{2-}$ ions in the $H_2SO_4$ solution and the dependence of the corrosion behavior on the alloying element was discussed. The selective leaching of alloy element increased with increasing Cu content in the aluminum alloys.

• Corrosion Science and Technology
• /
• v.16 no.3
• /
• pp.128-140
• /
• 2017

Aluminum alloy matrix may be used for manufacturing lighter automobiles. However, galvanic corrosion may occur between the rivet joint combining aluminum alloy matrix and a CFRP (carbon fiber reinforced plastic) laminate. The possibility of galvanic corrosion may be investigated by measuring galvanic couple currents. Two types of galvanic current measuring methods were used. One method is to use potentiodynamic polarization curves and the other is the ZRA (zero resistance ammeter) method. For galvanic corrosion experiments graphite, a major component of CFRP, was used with carbon steel (rivets) and 6061 aluminum alloys. Regardless of carbon steel, Ni deposited carbon steel, and 316L stainless steels we also investigated the possibility of reduction in galvanic corrosion. Results revealed that even though Ni deposited carbon steel or 316L stainless rivet may slightly increase galvanic current density between those and Al matrix, substitute rivets for carbon steel may be considerably useful for reducing overall galvanic corrosion.