• Transactions on Electrical and Electronic Materials
• /
• v.4 no.2
• /
• pp.24-28
• /
• 2003

(Ba,Sr,Ca)TiO$_3$ powders, prepared by the sol-gel method, were mixed with organic binder and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. All the BSCT thick films, sintered at 1420$^{\circ}C$, showed the typical XRD patterns of a perovskite polycrystalline structure. The average grain sizes decreased with increasing amounts of ZrO$_2$, and the BSCT(40/40/20) thick films doped with 2wt% MnO$_2$ showed a value of 8$\mu\textrm{m}$. The thickness of thick films by four-cycle on printing/drying was approximately 951$\mu\textrm{m}$. The relative dielectric constant decreased with increasing Ca content and MnO$_2$ doping amount. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) thick films doped with 2.0wt% ZrO$_2$ were 772, 0.184％ and 15.62%, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.123-124
• /
• 2006

The sandwiched PZT/$BaTiO_3$/PZT thick films were fabricated by two different methods thick films of the PZT by screen printing method on alumina substrateselectrodes with Pt, thin films of $BaTiO_3$ by the spin-coating method on the PZT thick films and once more thick films of the PZT by the screen printing method on the $BaTiO_3$ layer. The structural and the dielectric properties were investigated for effect of various stacking sequence of sol-gel prepared $BaTiO_3$ coating solution at interface of the PZT thick films, The insertion of BaTi03 interlayer yielded the PZT thick films with homogeneous and dense grain structure with the number of $BaTiO_3$ layers. The leakage current density of the $PZT/BaTiO_3-1$ film is less that $4.41{\times}10^{-9}A/cm^2$ at 5 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.12
• /
• pp.956-960
• /
• 2010

CuO doped $WO_3-SnO_2$ thick film gas sensors were fabricated by screen printing method on alumina substrates and heat-treated at $350^{\circ}C$ in air. The effects of mixing ratio of $WO_3$ with $SnO_2$ on the structural and morphological properties of $WO_3-SnO_2$ were investigated X-ray diffraction and Scanning Electron Microscope. The structural properties of the $WO_3-SnO_2$:CuO thick film by XRD showed that the monoclinic of $WO_3$ and the tetragonal of $SnO_2$ phase were mixed. Nano CuO was coated on the $WO_3-SnO_2$ surface and then the surface of $WO_3$ was coated with $SnO_2$ particles with $1\sim1.5{\mu}m$ in diameters, as confirmed form the SEM image. The sensitivity of the $WO_3-SnO_2$:CuO sensor to 2000 ppm $CO_2$ gas and 50 ppm $H_2S$ gas for the various ratio of $WO_3$ and $SnO_2$ was investigated. The 4 wt% CuO doped $WO_3-SnO_2$(75:25) tkick films showed the highest sensitivity to $CO_2$ gas and $H_2S$ gas.

• Korean Journal of Materials Research
• /
• v.12 no.12
• /
• pp.930-934
• /
• 2002

Nanosized $WO_3$ powders were synthesized by the sol-precipitation process using $WCl_{6}$ as the starting material, ethanol as a solvent and $NH_4$OH solution as a precipitant, followed by a washing-drying treatment and calcination. The effects on the powder crystallinity and microstructure of calcination temperature were investigated with XRD and FE-SEM. The $WO_3$ powders calcined at $500^{\circ}C$ and $700^{\circ}C$ showed good crystallinity and their mean particle size was 30nm and 70nm, respectively. These powders were used for the preparation of pastes which were printed as thick films on alumina substrates with comb-type Pt electrodes. The particle size strongly influenced the $NO_2$ gas sensing property of the thick films. A significant reduction in the $NO_2$ sensitivity was observed for the film prepared from larger particle size, having thus a larger grain size. For the film having a smaller grain size, on the other hand, the higher $NO_2$ sensitivity was observed and the sensitivity increased with $NO_2$ concentration.

• Tribology and Lubricants
• /
• v.33 no.5
• /
• pp.220-227
• /
• 2017

In this work, carbon nanotube and nano-size alumina particle are exploited as additive for lubrication experiment. We used pin-on-disk type tribometer to investigate the tribological characteristics of lubricants with respect to additives and rotational speed. We conducted more than 15 trials of tribotests for two hours for each specimen to obtain stable and accurate frictional force and to create measurable wear track on the substrate. We conducted tests at the boundary/mixed lubrication regime to evaluate the influence of additives on the tribological characteristics. We found that the friction coefficient decreased as the rotational speed increased and as additives were added. In particular, the reduction of friction by adding additives was more significant at low rotational speed than at high rotational speed. We speculate that the additives helped to separate and protect the two contacting surfaces at low speed, while the influence of additives was not significant at high speed since sufficiently thick lubricant film was formed. The wear of the substrate was also reduced by adding additives to the lubricant. However, in contrast to friction, the amount of wear at high rotational speed was less when alumina particles were added to the lubricant than the amount of wear at low speed. We speculate that the increased wear at low rotational speed is as a result of the intermittent abrasive wear caused by alumina particles with uneven shape, while the reduced wear at high speed is as a result of sufficient film thickness which prevented the abrasive wear.

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.4
• /
• pp.149-152
• /
• 2007

[ $(Ba_{0.6}Sr_{0.3}Ca_{0.1})TiO_3$ ](BSCT) thick films doped with 0.1 mol% $MnCO_3\;and\;Yb_2O_3(0.1{\sim}0.7mol%)$ were fabricated by the screen printing method on the alumina substrates. And the structural and electrical properties as a function of $Yb_2O_3$ amount were investigated. The exothermic peak was observed at around $680^{\circ}C$ due to the formation of the poly crystalline perovskite phase. The lattice constants of the BSCT thick film doped with 0.7 mol% is 0.3994 nm. The specimen doped with 0.7 mol% $Yb_2O_3$ showed dense and uniform grains with diameters of about $4.2{\mu}m$. The average thickness of all BSCT thick films was approximately $70{\mu}m$. Relative dielectric constant and dielectric loss of the specimen doped with 0.7 mol% $Yb_2O_3$ were 2823 and 3.4%, respectively. The Curie temperature of the BSCT thick films doped with 0.1 mol% $Yb_2O_3$ was $46^{\circ}C$.

• Proceedings of the KIEE Conference
• /
• 2004.11a
• /
• pp.58-60
• /
• 2004

The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated on alumina substrate by screening printing method. The obtained films were sintered at $1400^{\circ}C$ with bottom electrode of Pt for 2 hours. The structural and electrical properties of $BaTiO_3/SrTiO_3$ heterolayered thick films were compared with pure $BaTiO_3$ and $SrTiO_3$ films. The (Ba,Sr)$TiO_3$ phase was appeared at the $BaTiO_3/SrTiO_3$ heterolayered thick films. The thickness of $BaTiO_3/SrTiO_3$ heterolayered thick film, obtained by one printing, was about $50{\mu}m$. The dielectric constant and dielectric loss of the $BaTiO_3/SrTiO_3$ heterolayered thick films were about 1964, 5.5% at 1KHz, respectively.

• Journal of the Korean Ceramic Society
• /
• v.41 no.5
• /
• pp.375-380
• /
• 2004

Pb(Ni$\_$1/3/Nb$\_$2/3/)O$_3$-PbZrO$_3$-PbTiO$_3$ thick films were screen-printed on platinized alumina substrates and fired at 800-1000$^{\circ}C$. Two kinds of powders with different particle size were prepared by attrition and ball milling methods. Effects of particle size of starting material on the microstructure and electrical properties of the thick films were investigated. Average particle size of attrition milled-powder (0.44 ${\mu}$m) was much smaller than that of ball milled-powder (2.87 ${\mu}$m). Average grain size of the thick film prepared from attrition-milled powder was smaller than that of the thick film prepared from ball-milled powder at the sintering temperature of 800$^{\circ}C$. However, the difference in average particle size became smaller with increasing the sintering temperature. Thick films prepared from attrition-milled powders showed more uniform and denser microstructures at all firing temperatures. Thick films prepared from attrition-milled powders had better electrical properties at the firing temperature above 900$^{\circ}C$ than thick films prepared from ball-milled powders. Dielectric constant, remanent polarization and coercive field of the thick film prepared from attrition-milled powders and fired at 900$^{\circ}C$ were 559, 16.3 ${\mu}$C/cm$^2$, and 51.3 kV/cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.81-81
• /
• 2009

Non-sintered Alumina films were fabricated via inkjet printing processes without a high temperature sintering process. The packing density of these inkjet-printed alumina films measured around 60%. Polymer resin was infiltrated thru these non-sintered films in order to fill out the 40% of voids constituting the rest of the inkjet-printed films. The concept of inkjet-printed Alumina-Resin hybrid materials was designed in order to be applicable to the ceramic package substrates for 3D-system module integration which may possibly substitute LTCC-based 3D module integration. So, the dielectric properties of these inkjet-printed $Al_2O_3$ hybridmaterialsareofourgreatinterest. We have measured dielectric constant and dissipation factor of the inkjet-printed $Al_2O_3$-resinhybridfilmsbyvaryingtheamountofresininfiltratedthruthe$Al_2O_3$films.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.07a
• /
• pp.151-156
• /
• 2001

Using the photoimageable thick film conductors, $25\mu\textrm{m}$ line widths and $25\mu\textrm{m}$ spaces can be obtained. Test patterns are made by green tape lamination, paste printing, exposing to UV light, developing in an aqueous process and cofiring. Postfiring method using alumina substrate can be also applied to fine line formation. Series gap resonator formed by photopatterning process showed the improved signal transmission characteristics compared to that obtained by conventional screen printing.