• 한국표면공학회지
• /
• 제45권1호
• /
• pp.8-14
• /
• 2012

The effects of the alkali surface modification process on the adhesion strength between electroless-plated Cu and polyimide films were investigated. The polyimide surfaces were effectively modified by alkali surface treatments from the hydrophobic to the hydrophilic states, and it was confirmed by the results of the contact angle measurement. The surface roughness increased by alkali surface treatments and the adhesion strength was proportional to the surface roughness. The adhesion strength of Cu/polyimide interface treated by KOH + EDA (Ethylenediamine) was 874 gf/cm which is better than that treated by KOH and KOH + $KMnO_4$. The results of XPS spectra revealed that the alkali treatment formed oxygen functional groups such as carboxyl and amide groups on the polyimide films which is closely related to the interfacial bonding mechanism between electroless-plated Cu and polyimide films. It could be suggested that the species and contents of functional group on polyimide films, surface roughness and contact angle were related with the adhesion strength of Cu/polyimide in combination.

• Journal of Periodontal and Implant Science
• /
• 제30권1호
• /
• pp.187-203
• /
• 2000

The precipitation of calcium phosphate on implant surface has been known to accelerate osseointegration and to enhance osseous adaptation. The present study was performed to examine whether the precipitation of calcium phosphate on Ti-6Al-4V alloy could be affected by the immersion in NaOH solution and heat treatment. Ti-6Al-4V alloy plates of $15{\times}3.5{\times}1mm$ in dimension were polished sequentially from #240 to #2,000 emery paper and one surface of each specimen was additionally polished with $0.1{\mu}m$ alumina paste. Polished specimens were soaked in various concentrations of NaOH solution(0.1, 1.0, 3.0, 5.0, 7.0, 10.0 M) at $60^{\circ}C$ for 24 hours for alkali treatment, and 5.0 M NaOH treated specimens were heated for 1 hour at each temperature of 400, 500, 600, 700, $800^{\circ}C$. After the alkali and heat treatments, specimens were soaked in the Hank's solution with pH 7.4 at $36.5^{\circ}C$ for 30days.The surface ingredient change of Ti-6Al-4V alloy was evaluated by thin-film X-ray diffractometer(TF-XRD) and the surface microstructure was observed by scanning electron microscope(SEM), and the elements of surface were analyzed by X-ray photoelectron spectroscopy(XPS). The results were obtained as follows ; 1. The precipitation of calcium phosphate on Ti-6Al-4V alloy was accelerated by the immersion in NaOH solution and heat treatment. 2. In Alkali treatment for the precipitation of calcium phosphate on Ti-6Al-4V alloy, the optimal concentration of NaOH solution was 5.0 M. 3. In heat treatment after alkali treatment in 5.0 M NaOH solution, the crystal formation on alloy surface was enhanced by increasing temperature. In heat treated alloys at $600^{\circ}C$, latticed structure and prominences of calcium phosphate layer were most dense. On heat treated alloy surface at the higher temperature(${\geq}700^{\circ}C$), main crystal form was titanium oxide rather than apatite. The above results suggested that the precipitation of calcium phosphate on the surface of Ti-6Al-4V alloy could be induced by alkali treatment in 5.0 M-NaOH solution and by heat treatment at $600^{\circ}C$.

• 한국세라믹학회지
• /
• 제32권3호
• /
• pp.385-393
• /
• 1995

Akali-resistant porous glass was prepared by phase separation in Na2O-B2O3-SiO2 system containing ZrO2 and MgO. ZrO2 was added for alkali-resistance and MgO for anti-cracking during leaching. Optimal content of ZrO2 for alkali-resistance was 7wt% and devitrification by heat treatment resulted from further addition. Pore size and pore volume were decreased and specific surface area was increased with ZrO2 addition due to depression in phase separation. Addition of 3mol% MgO to mother glass containing 7wt% ZrO2 was effective for anti-crack during leaching. In this case, with phase separation at 55$0^{\circ}C$ and 5$25^{\circ}C$ for 20 hrs. crack-free porous glasses could be prepared. The relation between pore size r and heat treatment time t at 55$0^{\circ}C$ was D=25.58＋18.16t. According to measurement of gas permeability, the mechanism of gas permeation was Knudsen flow. N2 and He permeability of porous glass which was prepared by heat treatment at 55$0^{\circ}C$ for 20 hrs. were 0.843$\times$10-7mol/$m^2$.s.Pa and 2.161$\times$10-7mol/$m^2$.s.Pa respectively.

• 대한치과보철학회지
• /
• 제46권5호
• /
• pp.490-499
• /
• 2008

생체 활성 재료는 생체 내에서 자가적으로 인회석 층 (apatite layer)을 형성하여, 골과의 생화학적 결합이 가능해야 한다. 알칼리와 열처리를 통하여 생체 활성 표면을 얻을 수 있는 것으로 보고되고 있다. 본 실험에서는 알칼리 및 열처리를 시행한 임플란트들의 안정성을 평가하고자 하였다. 실험군의 분류로 1군은 대조군인 선반 가공 임플란트군, 2, 3군은 $60^{\circ}C$, 5 M의 NaOH 용액에 24시간 처리한 후, 각각 대기 중 및 진공 상태 $600^{\circ}C$에서 1시간 동안 열처리하였다. 처리된 시편은 FESEM, XPS, TF-XRD 및 AFM을 이용하여 표면 특성을 관찰하고, 임플란트의 안정성을 위해 공진 주파수와 페리오테스트 및 역 토오크를 측정하고, 골유착 안정성에 관한 차이를 비교 분석하여 다음과 같은 결과를 얻었다. 1. 표면 특성: 알칼리 및 열처리를 시행한 2, 3군은 비슷한 양상의 거친 표면을 보여주었다. 알칼리 처리를 시행한 2군과 3군에서 1군과는 달리 높은 함량의 나트륨 이온이 검출되었으며, 결정구조 분석 결과 2군에서 예추석 (antase)과 금홍석 (rutile)이 혼재된 상태로 금홍석이 우세한 양상을 보여주었다. 2. 공진 주파수 분석: 군간 비교에서 12주에 2군이 1, 3군에 비해 통계적으로 유의하게 높은 측정치를 보였다. 주간 비교시, 1, 2군은 4주 이후에 유의한 증가를 보여주었고, 3군은 2주와 4주에서 각각 유의한 증가를 보여주었다 (P < .05). 3. 페리오테스트 분석: 주간 비교에서 1, 2군은 4주 이후에 유의하게 감소를, 3군은 2주와 4주에서 각각 유의한 감소를 보여주었다 (P< .05). 4. 역 토오크 분석: 군간 비교에서는 2, 4, 8주에서는 2군이 1, 3군에 비해 유의하게 높은 측정값을 보여주었다. 주간 비교에서는 1, 3군은 4주, 12주에서 유의한 증가를 보여주었고, 2군은 4주부터 유의한 증가를 보여주었다 (P < .05). 이상의 결과로 볼 때, 알칼리 및 대기 중 열처리를 통해서 적절한 결정 구조의 산화막을 가진 생체 활성화된 무정형의 나트륨 티탄산염 층을 얻을 수 있었고, 알칼리 및 진공 상태 열처리만으로도 나트륨이 함유된 생체 활성화된 표면을 얻을 수 있었다고 사료된다. 또한 이런 처리 과정으로 형성된 표면층들은 임플란트의 초기 골유착에 도움을 줄 수 있는 유용한 방법 중 하나라고 사료된다.

• 한국해양공학회지
• /
• 제31권3호
• /
• pp.248-255
• /
• 2017

Many rivers and seas have been affected by environmental contamination. Therefore, city water supplies often require a high-degree purification treatment to provide safe drinking water. However, in order to achieve a high-degree purification treatment, a large amount of chlorine has to be added to sterilize city drinking water. The added chlorine reacts chemically with water and forms hypochlorous and chlorine ions. The hypochlorous ionizes with hypochlorous ions and hydrogen ions. As a result, the city water contains a large amount of chlorine ion. As such, when city water is used with domestic boilers, many kinds of heat exchangers, and the engines of vehicle and ships, there are often corrosion problems. In this study, alkali water was electrochemically made by electrolysis of city water, and corrosion properties between alkali and city water were investigated with an electrochemical method. Most of the chlorine ions are thought to not be contained in the alkali water because the alkali water is created in the cathodic chamber with an electrolysis process. In other words, the chlorine ion can be mostly removed by its migration from a cathodic chamber to an anodic chamber. Moreover, the alkali water also contains a large amount of hydroxide ion. The alkali water indicated relatively good corrosion resistance compared to the city water and the city water exhibited a local corrosion pattern due to the chlorine ion created by a high-degree purification treatment. In contrast, the alkali water showed a general corrosion pattern. Consequently, alkali water can be used with cooling water to inhibit local corrosion by chlorine ions in domestic boilers, various heat exchangers and the engine of ships and for structural steel in a marine structure.

• 폴리머
• /
• 제39권1호
• /
• pp.99-106
• /
• 2015

나노케냐프 섬유가 포함된 셀룰로스 섬유를 알카리(NaOH)로 처리 후 PP 수지에 첨가하여 물성에 미치는 영향에 대하여 조사하였다. 알카리를 섬유에 처리한 효과로는 M.I., 신장율, 충격강도가 증가하는 반면 인장강도, 휨모듈러스, 열변형온도가 처리하지 않은 섬유에 비해 감소하였다. 알카리를 나노섬유에 처리하였을 때 섬유표면의 불순물과 화학물질을 제거하여 섬유표면의 특성을 변화시켜서 나노섬유와 PP 수지간의 계면간 접착력을 감소시키고 PP의 특성을 변화시키는 것으로 보인다.

• Journal of Periodontal and Implant Science
• /
• 제38권4호
• /
• pp.595-602
• /
• 2008

Purpose: Ti-6Al-4V alloy is widely used as an implant material because of its good biocompatibility and good mechanical property compared with commercial pure titanium. Otherwise, toxicity of aluminum and vanadium in vivo has been reported. Ti-8Ta-3Nb alloy is recently developed in the R&D Center for Ti and Special Alloys and it was reported that this alloy has high mechanical strength, no cytotoxicity and similar biocompatibility to commercial pure titanium, but many studies are needed for its clinical use. In these experiment, we carried out different surface treatment on each Ti-8Ta-3Nb alloy disks, then cultured cell on it and assessed biological response. Materials and Methods: cpTi, Ti-6Al-4V, Ti-8Ta-3Nb alloy disks were prepared and carried out sandblasting and acid etching (SLA) or alkali-heat treatment (AH) on the Ti-8Ta-3Nb alloy disks. We cultured primary rat calvarial cells on each surface and assessed early cell attachment and proliferation by scanning electron microscopy, cell proliferation, alkaline phosphatase activity. Result: The rates of cell proliferation on the cpTi, Ti-8Ta-3Nb AH disks were higher than others (p<0.05) and alkaline phosphatase activity was significantly enhanced on the Ti-STa-8Nb AH disks(p<0.05). Conclusion: Most favorable cell response was shown on the Ti-8Ta-3Nb AH surfaces. It is supposed that alkali-heat treatment of the Ti-8Ta-3Nb alloy could be induced earlier bone healing and osseointegration than smooth surface.

• 한국의류산업학회지
• /
• 제13권6호
• /
• pp.972-982
• /
• 2011

The purpose of this study is to improve the method of color developing with alkali solution as a promotor of color developing for feasible use. Cotton fabric was dyed with persimmon extract ranged with 0~3% alkali component with 5 types of strong to mild alkali solution. Heat treatment for color developing was applied to fabric dyed with persimmon extract and alkali mixing solution. Tests were carried out to analyze the change of surface color, ${\Delta},Ea^*b^*$, and water repellent of the dyed cotton fabric. The alkali mixing sample showed higher ${\Delta},Ea^*b^*$ value than control one without alkali mixing on the base of dyed fabric due to high color developing by alkali in the initial step of dyeing process. As alkali concentration increased, deeper dark color appeared on the fabric. The fabric color was changed to more dark in the application of sodium hydroxide, sodium carbonate, potassium carbonate in the initial step of dyeing process but color was not changed by increased heating time. However, the fabric showed a slight dark color with sodium acetate and more color change than that of the fabric dyed with persimmon extract without alkali. Therefore, sodium acetate seemed to a suitable promotor for color developing in persimmon extract dyeing. Property of water repellent was showed after color developing by heating with low concentration of alkali treatment.

• 구강회복응용과학지
• /
• 제25권3호
• /
• pp.293-306
• /
• 2009

본 연구에서는 알카리 열처리 티타늄 임플란트상에서 백서 태자 두개관 세포의 생물학적 반응을 알아보고자 하여 다음과 같은 결과를 얻었다. 알카리 열처리 티타니움 표면에서 Ti-6Al-4V 합금 표면에서보다 세포증식도가 유의하게 높았다 (p<0.01). 면역효소 분석에서 interleukin $(IL)-1{\beta}$와 IL-6의 합성은 배양 시간이 길수록 증가하였다. Herbimycin으로 전처치한 경우에는 세포 배양 7일 째에 IL-6의 합성이 유의하게 억제되었다(p<0.01). 알카리인산 분해 효소 활성은 알카리 열처리 임플란트에서 타이타늄, Ti-6Al-4V 합금 표면에서 보다 유의하게 더 높았다 (p<0.001). 유전자 분석에서 알카리 열처리 임플란트에서 배양된 세포들의 alkaline phosphatase, bone sialoprotein, receptor activated nuclear factor ligand 유전자의 발현이 증가하였다. Herbimycin과 SB203580으로 전처치시 $IL-1{\beta}-induced$ IL-6 유전자의 발현이 감소하였다. 이상의 결과는 알카리 열처리된 티타늄 임플란트가 조골세포의 분화를 자극하고 골개조를 촉진시킴을 시사한다.

• 한국세라믹학회지
• /
• 제31권11호
• /
• pp.1337-1345
• /
• 1994

Glasses in the system of 45CaO-25TiO2-30P2O5 containing 1 mole% of M2O(M=Li, Na, K) were melted and crystallized. And their crystal phases were Ca3(PO4)2, CaTi4(PO4)6, and TiO2. Porous glass-ceramics with skeleton of two crystal phase CaTi4(PO4)6 and TiO2 were prepared by selective leaching of Ca3(PO4)2 with 0.1 N-HCl. Glass transition temperature(Tg) and crystallization temperature(Tc) were decreased by addition of 1 mole% alkali metal oxide. Pore size of porous glass-ceramics was increased with increasing heat treatment temperature and its dependence on heat treatment temperature was decreased with addition of Na2O and K2O. It was found that porous glass-ceramics of parent glass and containing 1mole% M2O(M=Li, Na, K) composition had maximum specific surface area, porosity and maximum of crystallzed phase by heat treatment at 80$0^{\circ}C$, 76$0^{\circ}C$, 78$0^{\circ}C$, 80$0^{\circ}C$ respectively.