• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.159-160
• /
• 2022

The purpose of this study is to evaluate the adhesion in flexure depending on the cement type, polymer type, polymer-cement ratio, and silica fume ratio of the polymer-cement composites(PCCs) for crack repair in RC structures to induce optimal mix proportions. The adhesion in flexure of PCCs for crack repair of RC structure has a significant effect on the polymer type and polymer-cement ratio, and the adhesion in flexure is generally improved with mixing of silica fume as a mixture. The adhesion in flexure according to the type of polymer is slightly higher in the order of SAE, EVA, and SBR, and it is relatively high at the polymer-cement ratio of 60% or 80%. In addition, the adhesion in flexure of PCCs with silica fume ratio of 10% or 20% to the cement weight is higher than that without silica fume. In order to improve the adhesion in flexure of PCCs for repairing cracks in RC structures, the optimal mix design is to properly adjust the cement type, polymer type, polymer-cement ratio, and silica fume ratio.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.11a
• /
• pp.162-163
• /
• 2019

The purpose of this study is to evaluate the adhesion in flexure of SBR-modified mortar adding Fly Ash(FA). From the test results, the adhesion in flexure is seriously affected by polymer-binder ratios and adding content of FA. The maximum adhesion in flexure of SBR- modified mortar is about 1.46 times, the plain cement mortar. It is apparent that the adhesion in flexure of SBR-modified mortars by polymer-binder ratios is much more improved than that by adding contents of AF.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.1
• /
• pp.47-57
• /
• 2019

The purpose of this study is to evaluate the improvement effect of adhesion in tension and flexure of polymer cement mortars that have widely used as a repair-reinforcement material in construction field according to adding of polymer dispersions depending on different three types test methods. From the test results, the adhesion performance is improved with a raise in polymer-cement ratio irrespective of the type of polymer. The maximums of A type adhesion in tension, B type adhesion in tension and adhesion in flexure show 1.90 times, 2.17 times and 1.83 times, respectively that of plain cement mortar. The relative strength ratios, B type adhesion in tension and adhesion in flexure of polymer cement mortars to tensile and flexural strengths of plain mortar respectively are in ranges of 50.1% to 101.7% and 73.8% to 132.9% compared to 46.9% of plain mortar. It is apparent that polymer cement mortars with EVA and polymer cement ratios of 10% to 15% are recommended considering its adhesion performance and cost as a repair-reinforcement material in construction field.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.6
• /
• pp.485-494
• /
• 2019

This study is to evaluate the effect of admixtures such as blast-furnace slag and fly ash on adhesion in flexure and tension of polymer cement mortar(PCM) using SAE emulsion. The test specimens are prepared with five polymer-cement ratios and five admixture contents, and tested for flexural strength, adhesion in flexure, tensile strength and adhesion in tension. Based on the test results, no improvement of flexural strength and adhesion in flexure caused by admixtures in PCM can be indicated, but the tensile strength and adhesion in tension is improved due to mixing of the admixtures. In particular, the maximum of adhesion in tension of PCM with P/C 20% and BF content of 10% is 3.35MPa which is about 2.36 times higher than that of ordinary cement mortar, and 1.32 times that of PCM that does not contain any admixture. The average ratio of adhesion in tension to tensile strength of PCM was 48.7%. It is apparent that admixture contents of 5% or 10% could be proposed for improvement of tensile strength and adhesion in tension of PCM.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.11a
• /
• pp.179-180
• /
• 2023

The adhesion performance of PCCs for crack repair of RC structures was greater in the case of using ultra high-early strength cement than in the case of using ordinary Portland cement, and the effect of mixing silica fume was higher in the case of ordinary Portland cement than that of ultra high-early strength cement. On the other hand, 130% of W/C was more fluid than 80% of W/C in the same P/C 80%, which increased the fillability and improved the strength, but the strength improvement effect was the greatest in adhesion in flexure. Through this study, the basic characteristics of the adhesion performance of PCCs were identified, and based on this, it is necessary to induce an optimal mixing design that can increase adhesion performance through various mixing designs.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.301-304
• /
• 2006

The purpose of this study is to evaluate bonding properties of PMMA mortars using EPS with silane coupling agent. PMMA mortars are prepared with various silane coupling agent, and tested for flexural strength test, adhesion test in flexure and tensile strength in underwater and air. It is estimated that the application of silane coupling agent to PMMA mortar is more effective in underwater than air.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.601-610
• /
• 2007

Statement of problem: The adhesion between titanium and ceramic is less optimal than conventional metal-ceramic bonding, due to reaction layer form on cast titanium surface during porcelain firing. Purpose: This study characterized the effect of titanium-ceramic adhesion after gold and TiN coating on cast and wrought titanium substrates. Material and method: Six groups of ASTM grade II commercially pure titanium and cast titanium specimens$(13mm{\times}13mm{\times}1mm)$ were prepared(n=8). The conventional Au-Pd-In alloy served as the control. All specimens were sandblasted with $110{\mu}m\;Al_2O_3$ particles and ultrasonically cleaned for 5min in deionized water and dried in air before porcelain firing. An ultra-low-fusing dental porcelain (Vita Titankeramik) was fused on titanium surfaces. Porcelain was debonded by a biaxial flexure test at a cross head speed of 0.25mm/min. The excellent titanium-ceramic adherence was exhibited by the presence of a dentin porcelain layer on the specimen surface after the biaxial flexure test. Area fraction of adherent porcelain (AFAP) was determined by SEM/EDS. Numerical results were statistically analyzed by one-way ANOVA and Student-Newman-Keuls test at ${\alpha}=0.05$. Results: The AFAP value of cast titanium was greatest in the group 2 with TiN coating, followed by group 1 with Au coating and the group 3 with $Al_2O_3$ sandblasting. Significant statistical difference was found between the group 1, 2 and the group 3 (p<.05). The AFAP value of wrought titanium was greatest in the group 5 with TiN coating, followed by the group 4 with Au coating and the group 6 with $Al_2O_3$ sandblasting. Conclusion: No significant difference was observed among the three groups (p>.05). The AFAP values of the cast titanium and the wrought titanium were similar. However the group treated with $Al_2O_3$ sandblasting showed significantly lower value (p<.05).

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.6
• /
• pp.176-181
• /
• 2018

Concrete structures are degraded physically and chemically due to various reasons after construction. Because the deterioration of concrete structure reduces the service life, reasonable repair and maintenance techniques are needed. Recently, in order to efficiently repair concrete structures, many researches on hybrid repair materials having improved adhesion performance have been carried out actively. In this study, we developed a hybrid repair material containing rapid hardening cement, PVA powder, nylon fiber, and latex to improve adhesion and water-tightness of existing concrete. The compressive strength, drying shrinkage and the adhesion strength test were carried out to evaluate the performance of the repair material. In addition, the flexure bond performance was evaluated before and after repair. From the results, the bending strength was 110% ~ 150% in all specimens except for the specimen containing only the rapid hardening cement, and all the specimens behaved with the existing concrete in the crack pattern generated by the bending strength.

• Journal of dental hygiene science
• /
• v.9 no.4
• /
• pp.405-412
• /
• 2009

The purpose of this study investigated the effect of Au coating on adhesion between porcelain matrix and metal substructure interface. Titanium, Ni-Cr alloy and Co-Cr alloy are well known as proper metal for the dental restorations. The success of a porcelain fused to metal (PFM) restoration depends upon the quality of the porcelain-metal bond. However, adhesion between dental alloys and porcelain is related to diffusion of oxygen during ceramic firing. The excessive oxidized layers make hard adhesion between dental alloy and ceramic. Ni-Cr and Co-Cr specimens were divided into test and a control group and Titanium specimens were divided into three test groups and a control group. Each group had 20 specimens. The adhesion characteristics of porcelain and metal with Au coating layer and without Au coating layer were observed with scanning electron microscopy(SEM). The adhesion was evaluated by a biaxial flexure test and volume fraction of adherent porcelain was determined by SEM/EDS analysis. Result of this study suggest that Au coating layer is effective barrier to diffuse oxide layer completely protect non-precious alloys from oxidation during the porcelain firing. The SEM photomicrographs of cross-section specimens showed a smooth interface between Au coating layer and metals and porcelain which suggested proper chemical bonding, and no gap, porosity were observed. The mode of failure was mainly adhesive for Ti tested specimens, but mixed failures with adhesive and cohesive were observed in Ni-Cr and Co-Cr specimens. The adhesion between non-precious metals and porcelain would not be improved by Au coating agent. However, It is suggested that the continuous study is required further investigation and development.

• Composites Research
• /
• v.21 no.4
• /
• pp.7-14
• /
• 2008

Prediction of the load-bearing capacity of an adhesive-bonded Joint is of practical importance for engineers. This paper introduces interface fracture mechanics approach to predict the load-bearing capacity of composite metal bonded joints. The adhesion strength of composite/steel bonding is evaluated in terms of the energy release rate of an interfacial crack and the fracture toughness of the interface. Virtual track closure technique (VCCT) is used to calculate energy release rates, and hi-material end-notched flexure (ENF) specimens are devised to measure the interfacial fracture toughness. Bi-material ENF specimens gave consistent mode II fracture toughness $(G_{IIc})$ values of the composite/steel interface regardless of the thickness of specimens. The critical energy release rates of double-lap joints showed a good agreement with the measured fracture toughness. Therefore. the energy-based interfacial fracture characterization can be a practical engineering tool for predicting the load-bearing capacity of bonded joints.