• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.159-160
• /
• 2022

The purpose of this study is to evaluate the adhesion in flexure depending on the cement type, polymer type, polymer-cement ratio, and silica fume ratio of the polymer-cement composites(PCCs) for crack repair in RC structures to induce optimal mix proportions. The adhesion in flexure of PCCs for crack repair of RC structure has a significant effect on the polymer type and polymer-cement ratio, and the adhesion in flexure is generally improved with mixing of silica fume as a mixture. The adhesion in flexure according to the type of polymer is slightly higher in the order of SAE, EVA, and SBR, and it is relatively high at the polymer-cement ratio of 60% or 80%. In addition, the adhesion in flexure of PCCs with silica fume ratio of 10% or 20% to the cement weight is higher than that without silica fume. In order to improve the adhesion in flexure of PCCs for repairing cracks in RC structures, the optimal mix design is to properly adjust the cement type, polymer type, polymer-cement ratio, and silica fume ratio.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.162-163
• /
• 2019

The purpose of this study is to evaluate the adhesion in flexure of SBR-modified mortar adding Fly Ash(FA). From the test results, the adhesion in flexure is seriously affected by polymer-binder ratios and adding content of FA. The maximum adhesion in flexure of SBR- modified mortar is about 1.46 times, the plain cement mortar. It is apparent that the adhesion in flexure of SBR-modified mortars by polymer-binder ratios is much more improved than that by adding contents of AF.

• 한국건축시공학회지
• /
• 제19권1호
• /
• pp.47-57
• /
• 2019

폴리머 종류에 상관없이 폴리머 시멘트비의 증가에 따라 접착성능은 크게 개선되었으며, A타입 인장접착강도는 1.90배, B 타입 인장(접착)강도는 2.17배, 휨(접착)강도는 1.83배 보통 시멘트 모르타르 보다 높게 나타났으며, 보통 시멘트 모르타르의 B 타입 인장(접착)강도에 대한 인장강도비와 휨(접착)강도에 대한 휨강도비인 상대강도비가 각각 46.9%, 72.6%를 나타냈으며, 폴리머 시멘트 모르타르의 경우에는 각각 50.1%~101.7%, 73.8%~132.9% 범위를 나타내, 폴리머 시멘트 모르타르가 높은 강도회복율을 보였다. 폴리머 종류에 따라서는 EVA를 사용하고, 폴리머 시멘트비로서는 접착성능과 경제성을 고려하면, P/C 10%~15% 범위를 제안할 수 있다.

• 한국건축시공학회지
• /
• 제19권6호
• /
• pp.485-494
• /
• 2019

본 연구는 고로슬래그 미분말 및 플라이애쉬를 혼입한 SAE 에멀젼 기반 폴리머 시멘트 모르타르의 휨과 인장특성에 대하여 실험하여 혼화재의 혼입효과를 평가하고자 하였다. PCM은 폴리머 시멘트비와 혼화재의 혼입율을 변화시켜 시험편을 제작하였으며, 휨강도, 휨접착강도, 인장강도 및 인장접착강도 시험을 실시하였다. 연구결과, 혼화재의 혼입에 따른 휨강도 및 휨접착강도 개선은 거의 발현되지 않았으나, 인장강도 및 인장접착강도에서는 혼화재의 혼입에 따른 강도개선 효과를 얻을 수 있었다. 특히 PCM의 인장 접착강도는 P/C 20%, 고로슬래그 미분말 혼입율 10%에서 최대 3.35MPa로 보통시멘트 모르타르의 약 2.36배, 혼화재를 혼입하지 않은 PCM의 약 1.32배의 높은 강도를 나타냈으며 인장접착강도/인장강도비는 평균 48.7%를 나타냈다. 본 연구를 통하여 PCM의 인장 및 인장접착강도 개선을 위해서는 혼화재 혼입율 5% 또는 10%를 제안할 수 있었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.179-180
• /
• 2023

The adhesion performance of PCCs for crack repair of RC structures was greater in the case of using ultra high-early strength cement than in the case of using ordinary Portland cement, and the effect of mixing silica fume was higher in the case of ordinary Portland cement than that of ultra high-early strength cement. On the other hand, 130% of W/C was more fluid than 80% of W/C in the same P/C 80%, which increased the fillability and improved the strength, but the strength improvement effect was the greatest in adhesion in flexure. Through this study, the basic characteristics of the adhesion performance of PCCs were identified, and based on this, it is necessary to induce an optimal mixing design that can increase adhesion performance through various mixing designs.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.301-304
• /
• 2006

The purpose of this study is to evaluate bonding properties of PMMA mortars using EPS with silane coupling agent. PMMA mortars are prepared with various silane coupling agent, and tested for flexural strength test, adhesion test in flexure and tensile strength in underwater and air. It is estimated that the application of silane coupling agent to PMMA mortar is more effective in underwater than air.

• 대한치과보철학회지
• /
• 제45권5호
• /
• pp.601-610
• /
• 2007

Statement of problem: The adhesion between titanium and ceramic is less optimal than conventional metal-ceramic bonding, due to reaction layer form on cast titanium surface during porcelain firing. Purpose: This study characterized the effect of titanium-ceramic adhesion after gold and TiN coating on cast and wrought titanium substrates. Material and method: Six groups of ASTM grade II commercially pure titanium and cast titanium specimens$(13mm{\times}13mm{\times}1mm)$ were prepared(n=8). The conventional Au-Pd-In alloy served as the control. All specimens were sandblasted with $110{\mu}m\;Al_2O_3$ particles and ultrasonically cleaned for 5min in deionized water and dried in air before porcelain firing. An ultra-low-fusing dental porcelain (Vita Titankeramik) was fused on titanium surfaces. Porcelain was debonded by a biaxial flexure test at a cross head speed of 0.25mm/min. The excellent titanium-ceramic adherence was exhibited by the presence of a dentin porcelain layer on the specimen surface after the biaxial flexure test. Area fraction of adherent porcelain (AFAP) was determined by SEM/EDS. Numerical results were statistically analyzed by one-way ANOVA and Student-Newman-Keuls test at ${\alpha}=0.05$. Results: The AFAP value of cast titanium was greatest in the group 2 with TiN coating, followed by group 1 with Au coating and the group 3 with $Al_2O_3$ sandblasting. Significant statistical difference was found between the group 1, 2 and the group 3 (p<.05). The AFAP value of wrought titanium was greatest in the group 5 with TiN coating, followed by the group 4 with Au coating and the group 6 with $Al_2O_3$ sandblasting. Conclusion: No significant difference was observed among the three groups (p>.05). The AFAP values of the cast titanium and the wrought titanium were similar. However the group treated with $Al_2O_3$ sandblasting showed significantly lower value (p<.05).

• 한국구조물진단유지관리공학회 논문집
• /
• 제22권6호
• /
• pp.176-181
• /
• 2018

콘크리트 구조물은 시공 후 다양한 원인에 의해 물리적, 화학적 변형을 통해 물리적인 성능이 저하된다. 이러한 콘크리트 구조물의 성능저하는 사용수명을 감소하기 때문에 합리적인 보수보강이 필요하다. 최근 콘크리트 구조물의 효율적인 보수을 위해, 부착성능을 향상시킨 하이브리드 보수재료에 대한 연구가 활발히 수행되어오고 있다. 본 연구에서는 기존콘크리트와의 부착성능 및 수밀성을 향상시키기 위해 초속경 시멘트에 PVA 분말수지, 나일론 섬유, 라텍스를 혼입 한 하이브리드 보수재를 개발하였다. 보수재료의 성능평가를 위해 압축강도, 건조수축, 부착강도 실험을 수행하였다. 또한 미리 손상이 발생한 시험체를 제작한 후 보수 전후의 휨부착 성능평가를 수행하였다. 휨강도 평가결과, 기존의 초속경시멘트만 혼입한 시험체를 제외한 모든 실험체에서 110%~150%정도 휨강도가 크게 나타났고, 휨강도에 의해 발생된 균열패턴은 모든 실험체가 기존 콘크리트와 일체 거동하는 것으로 나타났다.

• 치위생과학회지
• /
• 제9권4호
• /
• pp.405-412
• /
• 2009

본 연구는 도재소부용 비귀금속에 Au 코팅 층을 형성하고, Au 코팅 층이 금속-도재의 결합력에 미치는 영향을 알아보고자 2출 굴곡 시험 후에 SEM/EDS 방법으로 조사하여 비교하였다. 1. Ni-Cr ally 군과 Co-Cr alloy 군, 그리고 Ti 군의 절단면 시편의 전자현미경 사진에서 Au 코팅 층은 산화층의 확산을 제어하는 것으로 관찰되었다. 2. 2축 굴곡 시험 후에 EDS 분석 결과 Ni-Cr alloy 군과 Co-Cr alloy 군에서 Si 함량은 Au 코팅 층을 형성한 시편에서 약간 감소하였고, 결합실패의 형태는 cohesive failure와 adhesive failure가 혼재된 양상으로 관찰되었다. 3. Ni-Cr alloy 군과 Co-Cr alloy 군에서 Au 코팅 층은 도재-금속 결합력에 미치는 영향은 미미하였다. 4. Ti 군의 결합실패 형태는 Ni-Cr alloy 군과 Co-Cr alloy 군에 비해서 adhesive failure 양상이 두드러지게 관찰되었고, Au 코팅 층은 도재-금속 결합력에 영향을 미치지 않았다. 이상의 결과 비귀금속에 적용한 Au 코팅은 산화층의 확산을 제어 하는 것으로 관찰 되었으나, 금속-도재 간의 결합력 증징에 미치는 효과는 미미하였다. Au 코팅을 이용하여 금속-도재 간의 결합력 증진을 위해서는 많은 연구가 지속되어야 할 것으로 사료된다.

• Composites Research
• /
• 제21권4호
• /
• pp.7-14
• /
• 2008

접착제 이용 결합 조인트의 하중지지 능력 예측 기법은 점착제를 이용한 접합 조인트 설계에 있어서 가장 중요한 기술이다. 본 연구 계면 파괴역학을 이용하여 복합재료/금속 접착 조인트의 하중지시 능력을 예측하는 기법을 소개한다. 구체적으로 복합재료/탄소강 결합의 접착 강도를 계면 균열의 에너지 방출률과 계면 파괴인성치 개념을 사용하여 평가하는 방법을 제시 검증하였다. 계면 균열의 에너지 방출률은 유한요소해선 결과를 이용한 가상 균열 닫음 기법 (VCCT)을 사용하여 계산하였으며, 게면 파괴인성치는 이종재료 ENF (end-notched flexure) 시편을 고안하여 측정하였다. 고안된 이종 재료 ENF 시편을 사용하여 시편의 두께에 상관없이 일관된 Mode II 계면 파괴인성치를 측정할 수 있음과 양면 겹치기 접합 조인트의 특성 에너지 방출률이 측정된 계면 파괴인성치와 일치함을 확인하였다. 따라서 에너지 방출률에 근거한 계면 균열 진전 기준은 접착 조인트의 하중지지 능력을 신뢰성 있게 예측하는 실제적인 설계 도구로서 활용될 수 있다.