• Restorative Dentistry and Endodontics
• /
• 제18권1호
• /
• pp.1-26
• /
• 1993

The purpose of this study was to investigate the effect of acid etching on the surface appearance and fracture toughness of five glass ionomer cements. Five kinds of commercially available glass ionomer cements including chemical curing filling type, chemical curing lining type, chemical curing metal reinforced type, light curing tilling type and light curing lining type were used for this study. The specimens for SEM study were fabricated by treating each glass ionomer cement with either visible light curing or self curing after being inserted into a rubber mold (diameter 4mm, depth 1mm). Some of the specimens were etched with 37% phosphoric acid for 0, 15, 30, 60, go seconds, at 5 minutes, 1 hour and 1 day after mixing of powder and liquid. Unetched ones comprised the control group and the others were the experimental groups. The surface texture was examined by using scanning electron microscope at 20 kV. (S-2300, Hitachi Co., Japan). The specimens for fracture toughness were fabricated by curing of each glass ionomer cement previously inserted into a metal mold for the single edge notch specimen according to the ASTME399. They were subjected to a three-point bend test after etching for 0, 30, 60, and 90 seconds at 5 minutes-, 1 hour-and 1 day-lapse after the fabrication of the specimens. The plane strain fracture toughness ($K_{IC}$) was determined by three-point bend test which was conducted with cross-head speed of 0.5 mm/min using Instron universal testing machine (Model No. 1122) following seven days storage of the etched specimens under $37^{\circ}C$, 100% humidity condition. Following conclusions were drawn. 1. In unetched control group, crack was present, but the surface was generally smooth. 2. Deterioration of the surface appearance such as serious dissolving of gel matrix and loss of glass particles occured as the etching time was increased beyond 15 s following Immediate etching of chemical curing type of glass ionomer cements. 3. Etching after 1 h, and 1 d reduced surface damage, 15 s, and 30s etch gave rough surface appearance without loss of glass particle of chemical curing type of glass ionomer cements. 4. Light curing type glass ionomer cement was etched by acid, but there was no difference in surface appearances according to various waiting periods. 5. It was found that the value of plane stram fracture toughness of glass ionomer cements was highest in the light curing filling type as $1.79\;MNm^{-1.5}$ followed by the light curing lining type, chemical curing metal reinforced type, chemical curing filling type and chemical curing lining type. 6. The value of plane stram fracture toughness of the chemical curing lining type glass ionomer cement etched after 5 minutes was lower than those of the cement etched after 1 hour or day or unetched (P < 0.05). 7. Light curing glass ionomer cement showed Irregular fractured surface and chemical curing cement showed smooth fractured surface.

• The Journal of Advanced Prosthodontics
• /
• 제10권1호
• /
• pp.73-78
• /
• 2018

PURPOSE. The purpose of this study was to analyze the effects of two different implant surface treatments on initial bone connection by comparing the Removal Torque Values (RTQs) at 7 and 10 days after chemically modified, sandblasted, large-grit and acid-etched (modSLA), and Laser-etched (LE) Ti implant placements. MATERIALS AND METHODS. Twenty modSLA and 20 LE implants were installed on the left and right tibias of 20 adult rabbits. RTQs were measured after 7 and 10 days in 10 rabbits each. Scanning electron microscope (SEM) photographs of the two implants were observed by using Quanta FEG 650 from the FEI company (Hillsboro, OR, USA). Analyses of surface elements and components were conducted using energy dispersive spectroscopy (EDS, Horiba, Kyoto, Japan). RESULTS. The mean RTQs were $12.29{\pm}0.830$ and $12.19{\pm}0.713$ Ncm after 7 days (P=.928) and $16.47{\pm}1.324$ and $16.17{\pm}1.165$ Ncm after 10 days (P=.867) for LE and modSLA, respectively, indicating no significant inter-group differences. Pore sizes in the LE were $40{\mu}m$ and consisted of numerous small pores, whereas pore sizes in the modSLA were $5{\mu}m$. In the EDS analysis, Ti, O, and C were the only three elements found in the LE surfaces. Na, Ca, Cl, and K were also observed in modSLA, in addition to Ti, O, and C. CONCLUSION. The implants showed no significant difference in biomechanical bond strength to bone in early-stage osseointegration. LE implant can be considered an excellent surface treatment method in addition to the modSLA implant and can be applied to the early loading of the prosthesis clinically.

• Restorative Dentistry and Endodontics
• /
• 제7권1호
• /
• pp.77-83
• /
• 1981

The purpose of this study was to observe the bonding strength between tooth surface (enamel and dentin) and restorative filling materials which are two composite resins (Clearfil and Concise) and Glass ionomer cement, after etching with 50% phoshoric acid and 37% citric acid. To measure the bonding strength in enamel, the labial surface of upper anterior tooth was cut flatly with using carborundum disk and polished with sand paper disk, and to measure in dentin, the dentin surface was prepared by grinding upper part of posterior tooth horizontally. After washing the tooth surface with water and drying with air blast, the prepared tooth surface was etched. In glass ionomer cement, 50% phosphoric acid and 37% citric acid were used, in Clearfil 40% phosphoric acid was used and in Concise, 50% phosphoric acid and 37% citric acid were used as etchant for 1 minute. After the copper band which is 5 mm in diameter and 5 mm in height was fixed on the prepared surface and each filling material was inserted into the copper band, the hooking loop was inserted into filled material in the copper band before setting to make it easily that the load is applied on the specimen. After all specimens were immersed in water at $37^{\circ}C$ for 1 week, this specimen was placed on the load cell of tensile test apparatus, and specimen was pulled at the cross-head speed of 0.8 mm per minute. The following results were obtained 1) In glass ionomer cement, the bond strength obtained by 37% citric acid was higher than one obtained by 50% phosphoric acid in enamel and dentin surfaces. The bond strength obtained in non-etched surface was much less than one by etchants in enamel and dentin surface. 2) In Clearfil, the bond strength obtained by 40% phosphoric acid was 4 times more than one obtained by non etch ant. 3) In Concise, the bond strength obtained by 50% phosphoric acid was almost same as one obtained by 37% citric acid, and the bond strength obtained by non etch ant was much less than one obtained by etchants.

• 대한치과교정학회지
• /
• 제42권1호
• /
• pp.32-38
• /
• 2012

Objective: The aim of this study was to compare the effects of different enamel conditioning techniques for bracket bonding. Methods: Ninety-one human premolars were randomly divided in six groups of 15 specimens each. The enamel surfaces of the teeth were etched with 35% orthophosphoric acid in Group 1, with a self-etching primer in Group 2, sandblasted in Group 3, sandblasted and etched with 35% orthophosphoric acid in Group 4, conditioned by Er:YAG laser in Group 5 and conditioned by Er:YAG laser and etched with 35% phosphoric acid gel respectively in Group 6. After enamel conditioning procedures, brackets were bonded and shear bonding test was performed. After debonding, adhesive remnant index scores were calculated for all groups. One tooth from each group were inspected by scanning electron microscope for evaluating the enamel surface characteristics. Results: The laser and acid etched group showed the highest mean shear bond strength (SBS) value ($13.61{\pm}1.14$ MPa) while sandblasted group yielded the lowest value ($3.12{\pm}0.61$ MPa). Conclusions: Although the SBS values were higher, the teeth in laser conditioned groups were highly damaged. Therefore, acid etching and self-etching techniques were found to be safer for orthodontic bracket bonding. Sandblasting method was found to generate inadequate bonding strength.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2001년도 추계학술대회(제116회) 및 13회 Workshop 제3회 한ㆍ일 치과보존학회 공동학술대회 초록집
• /
• pp.577-577
• /
• 2001

The lastest concepts in bonding are "total etch", in which both enamel and dentin are etched with an acid to remove the smear layers, and "wet dentin" in which the dentin is not blown dry but left moist before application of the bonding primer. Ideally, the application of a bonding agent to tooth structure should be insensitive to minor contamination from oral fluids. Clinically contaminations such as saliva, gingival fluid, blood and handpiece lubricant are often encountered by dentists during preparation of a restoration. The aim of this study was to evaluate the effect of contamination by hem-ostatic agents on shear bond strength of compomer restorations. One hundred and ten extracted human maxillary and mandibular molar teeth were collected. The teeth were cleaned from soft tissue remnant and debris and stored in physiologic solution until they were used. Small flat area on dentin of the buccal surface were wet ground serially with 400, 800 and 1200 abrasive paper on automatic polishing machine. The teeth were randomly divided into 11 groups. Each group was conditioned as follows: Group 1 : Dentin surface was not etched and not contaminated by hemostatic agents. Group2 : Dentin surface was not etched but was contaminated by Astringedent (Ultradent product Inc., Utah, U.S.A.). Group3 : Dentin surface was not etched but was contaminated by Bosmin (Jeil Phann, Korea.). Group4 : Dentin surface was not etched but was contaminated by Epri-dent (Epr Industries, NJ, U.S.A.). Group5: Dentin surface was etched and not contaminated by hemostatic agents. Group 6 : Dentin surface was etched and contaminated by Astringedent. Group7 : Dentin surface was etched and contaminated by Bosmin. Group8 : Dentin surface was etched and contaminated by Epri-dent. Group9 : Dentin surface was contaminated by Astringedent. The contaminated surface was rinsed by water and dried by compressed air. Group10 : Dentin surface was contaminated by Bosmin. The contaminated surface was rinsed by water aud dried by compresfed air. Group 11 : Dentin surface was contaminated by Epri-dent. The contaminated surface was rinsed by water and dried by compresfed air. After surface conditioning, F2000 was applicated on the conditoned dentin surface. The teeth were thermocycled in distilled water at $5^{\circ}C\;and\;55^{\circ}C$ for 1000 cycles. The samples were placed on the binder with the bonded compomer-dentin interface parallel to the lmife-edge shearing rod of the Universal testing machine(Zwick 020, Germany) running at a cross head speed of 1.0mmimin. There were no significant differences in shear bond strength between groups 1 and group 3 and 4, but group 2 showed significant decrease in shear bond strength compared with group 1. There were no significant differences in shear bond strength between group 5 and group 7 and 8, but group 6 showed significant decrease in shear bond strength compared with group 5. There were no significant differences in shear bond strength between group 5 and group 9, 10 and 11.

• Restorative Dentistry and Endodontics
• /
• 제45권1호
• /
• pp.6.1-6.8
• /
• 2020

Objectives: This study investigated the effects of a hydrofluoric acid (HA; solution of hydrogen fluoride [HF] in water)-based smart etching (SE) solution at an elevated temperature on yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramics in terms of bond strength and morphological changes. Materials and Methods: Eighty sintered Y-TZP specimens were prepared for shear bond strength (SBS) testing. The bonding surface of the Y-TZP specimens was treated with 37% phosphoric acid etching at 20℃-25℃, 4% HA etching at 20℃-25℃, or HA-based SE at 70℃-80℃. In all groups, zirconia primers were applied to the bonding surface of Y-TZP. For each group, 2 types of resin cement (with or without methacryloyloxydecyl dihydrogen phosphate [MDP]) were used. SBS testing was performed. Topographic changes of the etched Y-TZP surface were analyzed using scanning electron microscopy and atomic force microscopy. The results were analyzed and compared using 2-way analysis of variance. Results: Regardless of the type of resin cement, the highest bond strength was measured in the SE group, with significant differences compared to the other groups (p < 0.05). In all groups, MDP-containing resin cement yielded significantly higher bond strength values than MDP-free resin cement (p < 0.05). It was also shown that the Y-TZP surface was etched by the SE solution, causing a large change in the surface topography. Conclusions: Bond strength significantly improved when a heated HA-based SE solution was applied to the Y-TZP surface, and the etched Y-TZP surface was more irregular and had higher surface roughness.

• 대한치과교정학회지
• /
• 제46권6호
• /
• pp.386-394
• /
• 2016

Objective: The objective of the study was to evaluate the practicality and the validity of different surface treatments of self-drilling orthodontic mini-implants (OMIs) by comparing bone cutting capacity and osseointegration. Methods: Self-drilling OMIs were surface-treated in three ways: Acid etched (Etched), resorbable blasting media (RBM), partially resorbabla balsting media (Hybrid). We compared the bone cutting capacity by measuring insertion depths into artificial bone (polyurethane foam). To compare osseointegration, OMIs were placed in the tibia of 25 rabbits and the removal torque value was measured at 1, 2, 4, and 8 weeks after placement. The specimens were analyzed by optical microscopy, scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). Results: The bone cutting capacity of the etched and hybrid group was lower than the machined (control) group, and was most inhibited in the RBM group (p < 0.05). At 4 weeks, the removal torque in the machined group was significantly decreased (p < 0.05), but was increased in the etched group (p < 0.05). In the hybrid group, the removal torque significantly increased at 2 weeks, and was the highest among all measured values at 8 weeks (p < 0.05). The infiltration of bone-like tissue surface was evaluated by SEM, and calcium and phosphorus were detected via EDS only in the hybrid group. Conclusions: Partial RBM surface treatment (hybrid type in this study) produced the most stable self-drilling OMIs, without a corresponding reduction in bone cutting capacity.

• 대한치과교정학회지
• /
• 제43권3호
• /
• pp.141-146
• /
• 2013

Objective: Bonding forces of brackets to enamel surfaces may be affected by the procedures used for bleaching and enamel etching. The aim of this study was to investigate the bonding strength of orthodontic brackets to laser-etched surfaces of bleached teeth. Methods: In a nonbleached control group, acid etching (group A) or Er:YAG laser application (group B) was performed prior to bracket bonding (n = 13 in each group). Similar surface treatments were performed at 1 day (groups C and D; n = 13 in each subgroup) or at 3 weeks (groups E and F; n = 13 in each subgroup) after 38% hydrogen peroxide bleaching in another set of teeth. The specimens were debonded after thermocycling. Results: Laser etching of bleached teeth resulted in clinically unacceptable low bonding strength. In the case of acid-etched teeth, waiting for 3 weeks before attachment of brackets to the bleached surfaces resulted in similar, but not identical, bond strength values as those obtained with nonbleached surfaces. However, in the laser-etched groups, the bonding strength after 3 weeks was the same as that for the nonbleached group. Conclusions: When teeth bleached with 38% hydrogen peroxide are meant to be bonded immediately, acid etching is preferable.

• 대한치과교정학회지
• /
• 제26권4호
• /
• pp.389-399
• /
• 1996

치과교정장치의 장착을 위하여 치아법랑질표면을 산부식하는 것은 일반화된 술식이며, 산부식된 법랑질표면은 재석회화되어 자연적으로 정상상태를 회복하는 연구보고되어 왔다. 이 연구의 목적은 산부식된 법랑질표면의 재석회화에 불소가 미치는 영향을 실험적으로 관찰하여 재석희화의 일면을 구명하는데 있다. 교정치료목적으로 발거한 사람 제1소구치 치관을, 불소함유 석회화용액과 불소무함유 석회화용액에 12시간, 1일, 3일, 7일, 14일, 28일, 42일간 담구어 보관한후, 법랑질표면의 미세경도측정과 주사전자현미경관찰을 통하여 법랑질 표면의 변화들을 경시적으로 관찰하여 다음의 결과를 얻었다. 1) 표면미세경도는 불소함유 여부에 관계없이 시간경과에 따라 증가하였으며, 불소함유군 은 12시간부터, 불소무 함유군은 3일경과후부터 현저히 증가하였으나, 시간경과에 따라 그 차이는 감소하였다. 2) 주사전자현미경 관찰에서 불소함유용군은 12시간후부터 법랑질표면에 침상물질이 침착되기 시작하여 42일 후에는 편평한 표면으로 되었으나, 불소무함유용군은 전실험기간동안 산부식직후보다 약간 더 거칠어졌으나, 산부식 된 법랑질표면이 그대로 관찰되었다. 이상의 결과로부처 불소는 산부식된 법랑질표면의 재석회화 시기를 앞당기는 효과가 있으며, 재석회화의 소요시간도 단축하는 효과가 있음이 확인하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.594-594
• /
• 2012

Al doped ZnO (AZO) thin films were deposited on textured glass substrate by magnetron sputtering method. Also, AZO films on textured glass were etched by hydrochloric acid (HCl). Average thickness of etched AZO films are 90 nm. We observed morphology of AZO film by AFM with various etchant concentration and etching time. Etched AZO films have low resistivity and high haze. The surface RMS roughness of AZO film was increased from 53.8 nm to 84.5 nm. The haze ratio was also enhanced in above 700 nm of wavelength due to light trapping effect was increased by rough AZO surface. The etched AZO films on textured glass are applicable to fabricate solar cell.