The properties of Ni/Au Ohmic contacts formed on nonpolar a-plane GaN grown on r-plane sapphire substrate with different tilt angles are investigated using current-voltage (I-V) measurements. To investigate the effects of pattern direction and size on Ohmic contact properties of a-plane GaN, transmission line method (TLM) patterns are formed either along c-axis and m-axis on nonpolar GaN surface with different size. I-V measurement results show that the size of TLM pattern and formation direction of electrode have an effect on the electrical properties of a-plane GaN. The large sized patterns show the relatively lower sheet resistance compared to the small sized patterns. In addition, the sheet resistance of a-plane GaN along m-axis shows lower values than that along the c-axis. Finally, the effects of miscut angle of r-sapphire substrate ($0.2^{\circ}$, 0.4oand $0.6^{\circ}$) on electrical properties of a-plane GaN will be discussed.
GaN 기반 반도체는 넓은 bandgap을 가지고 있어 가시광부터 자외선까지 다양한 광전소자에 유용하게 사용된다. 광전소자중 발광다이오드의 경우 대부분 사파이어 기판위에 성장된다. 하지만 사파이어와 GaN의 격자 불일치 및 열팽창 계수의 차이로 인해 고품질의 GaN를 성장하기가 어렵다. 특히 열팽창 계수의 차이는 GaN 성장 공정이 고온에서 이루어지기 때문에 성장후 상온으로 온도가 떨어질 때 웨이퍼의 bowing을 발생시키고 동시에 dislocation이나 crack과 같은 결함이 생성되 GaN 성장막의 품질을 떨어트린다. 웨이퍼의 크기가 커지면 커질수록 웨이퍼 bowing은 커져 이에 대한 연구는 중요하다. 본 논문에서 2인치 사파이어 기판위에 성장된 GaN의 bow특성을 알아보기 위해 먼저 simulation을 하였고 실제로 성장된 GaN 웨이퍼와 비교를 하였다. c-plane 사파이어 기판위에 성장된 c-plane GaN의 bow특성을 알아보기 위해 성장 온도 $1,100^{\circ}C$에서 GaN두께를 1 ${\mu}m$에서 10 ${\mu}m$까지 1 ${\mu}m$씩 변화시켜 가며 simulation을 하였다. GaN두께가 1 ${\mu}m$일때는 bow가 11 ${\mu}m$, 6 ${\mu}m$ 일때는 54.7 ${\mu}m$, 10 ${\mu}m$ 일때는 108 ${\mu}m$를 얻어 GaN두께가 1 ${\mu}m$씩 증가할 때 마다 bow가 약 10 ${\mu}m$씩 증가하였다. 성장온도에 대한 영향을 알아보기 위해 $700^{\circ}C$에서 $1,200^{\circ}C$까지 $100^{\circ}C$씩 증가시켜며 bow특성 simulation을 하였다. 6 ${\mu}m$성장된 GaN의 경우 성장온도가 $100^{\circ}C$ 씩 증가할 때 bow는 약 6 ${\mu}m$ 증가하였다. 실제 성장된 c-plane GaN웨이퍼와 비교하기 위해 GaN을 각각 3 ${\mu}m$와 6 ${\mu}m$를 성장시켰고 high resolution x-ray diffraction장비를 사용하여 bow를 측정한 결과 각각 28 ${\mu}m$와 61 ${\mu}m$ 였고 simulation결과는 각각 33 ${\mu}m$와 65.5 ${\mu}m$를 얻어 비슷한 결과를 보였다. c-plane 사파이어 기판위에 성장된 c-plane GaN는 방향에 무관하게 동일한 bow 특성을 가지는 반해 r-plane 사파이어 기판위에 성장된 a-plane GaN는 방향에 따라 다른 bow특성을 보인다. a-plane GaN 이방향성적인 bow 특성을 알아보기 위해 simulation을 하였다. $1,100^{\circ}C$에서 a-plane GaN을 성장할 때 두께가 1 ${\mu}m$ 증가할 때마다 bow가 c축 방향으로는 21.7 ${\mu}m$씩 증가하였고 m축 방향으로는 11.8 ${\mu}m$ 씩 증가하여 매우 큰 이방향성적인 bow 특성을 보였다. 실제 r-plane 사파이어 기판위에 성장된 a-plane GaN의 bow를 측정하였고 simulation 결과와 비교해 보았다.
본 연구에서는 HVPE(Hydride Vapor Phase Epitaxy)를 이용하여 각각 다른 V/III ratio를 가지는 multi-step의 성장 시간 변화에 따라 r-plane 사파이어 위에 성장되는 a-plane GaN 에피층의 결정성에 대하여 연구하였다. 또한 이번 연구의 결과를 선행 연구에서 single-step으로 r-plane 사파이어 위에 성장시킨 a-GaN 에피층의 결과와 비교하였다. Multi-step으로 r-plane 사파이어 위에 a-plane GaN 에피층을 성장시켰을 때, source HCl의 유량과 성장 시간이 증가함에 따라 a-plane GaN 에피층에 대한 rocking curve의 FWHM(Full Width at Half Maximum) 값이 감소하였다. 높은 source HCl의 유량을 갖는 first step과 second step의 성장 시간과 source HCl의 유량이 증가할수록 a-plane GaN 에피층 내부의 void가 감소하였다. 결과적으로 first step과 second step의 성장 시간이 가장 긴 조건에서 성장된 a-plane GaN 에피층이 가장 낮은 FWHM 값인 584 arcsec을 가지며, azimuth angle의 의존도가 가장 적은 것으로 확인되었다.
R-plane 사파이어 위에 a-plane GaN층이 성장된 기판에 혼합소스 HVPE(mixed-source hydride vapor phase epitaxy) 방법으로 GaN/InGaN의 이종접합구조(heterostructure)를 구현하였다. GaN/InGaN 이종접합구조는 GaN, InGaN, Mg-doped GaN 층으로 구성되어 있다. 각 층의 성장온도는 GaN층은 $820^{\circ}C$, InGaN 층은 $850^{\circ}C$, Mg-doped GaN 층은 $1050^{\circ}C$에서 성장하였다. 이때의 $NH_3$와 HCl 가스의 유량은 각각 500 sccm, 10 sccm 이었다. SAG-GaN/InGaN 이종접합구조의 상온 EL (electroluminescence) 특성은 중심파장은 462 nm, 반치폭(FWHM : full width at half maximum) 은 0.67eV 이었다. 이 결과로부터 r-plane 사파이어 기판위에 multi-sliding boat system의 혼합소스 HVPE 방법으로 이종접합구조의 성장이 가능함을 확인하였다.
Ga source 채널의 HCl flow가 700 sccm, 그리고 V/III족 비가 10으로 고정되었을 때, r-면 사파이어 위에 HVPE로 성장된 a-면 GaN 에피층 특성에 대한 성장 온도 영향을 연구하였다. 추가적으로 성장온도가 $1000^{\circ}C$, 그리고 Ga source 채널의 HCl flow가 700 sccm으로 고정되었을 때, 공급가스에 대한 V/III족 비 영향에 대하여 연구하였다. 성장온도가 높아지면서, a-면 GaN 에피층에 대한 (11-20) 면의 Rocking curve(RC)의 반치폭 값이 감소하였고 a-면 GaN 에피층의 성장두께는 증가하였다. $1000^{\circ}C$에서 V/III족 비가 높아짐에 따라, (11-20) 면의 RC의 반치폭 값이 감소하였고, a-면 GaN 에피층의 성장두께가 증가하였다. $1000^{\circ}C$와 V/III족 비=10에서 성장된 a-면 GaN 에피층이 (11-20) 면에서 가장 낮은 RC 반치폭인 734 arcsec을 보이며, RC측정을 통한 (11-20) 면의 방위각 가장 작은 영향을 보여준다.
We report a high crystalline nonpolar a-plane (11-20) GaN on r-plane (1-102) sapphire substrates with $+0.15^{\circ}$, $-0.15^{\circ}$, $+0.2^{\circ}$, $-0.2^{\circ}$ and $+0.4^{\circ}$ misoriented by metalorganic chemical-vapor deposition (MOCVD). The multi-quantum wells (MQWs) active region is consists of 5 periods the nonpolar a-plane InGaN/GaN (a-InGaN/GaN) on a high quality a-plane GaN (a-GaN) template grown by using the multibuffer layer technique. The full widths at half maximum (FWHMs) of x-ray rocking curve (XRC) obtained from phiscan of the specimen that was grown up to nonpolar a-plane GaN layers with double crystal x-ray diffraction. The FWHM values of $+0.4^{\circ}$ misoriented sapphire substrate were decreased down to 426 arc sec for $0^{\circ}$ and 531 arc sec for $-90^{\circ}$, respectively. Also, the samples were characterized by photoluminescence (PL).
일반적으로 LED 제작에 사용되는 c-plane GaN는 c축 방향으로 발생하는 분극의 영향을 받게 된다. 분극은 LED내 양자우물의 밴드를 기울게 하여 그 결과 전자와 홀의 재결합 확률을 감소시켜 낮은 내부양자효율을 가지게 된다. 이러한 문제를 해결하기 위한 여러 가지 방법들이 제시되었는데 그 중에서도 특히 a-plane 혹은 m-plane면과 같은 무분극 면을 사용하는 GaN LED가 주목받고 있다. 그 이유는 무분극 면은 분극이 발생하는 c축과 수직이기 때문에 분극의 영향을 받지 않아 높은 내부 양자효율을 가질수 있다. 본 연구에서는 MOCVD 장비를 사용하여 2인치 r-plane 사파이어 기판위에 3um두께의 a-plane GaN을 성장하였다. 그위에 2um정도로 Si을 도핑하여 n-type GaN 형성한후 단일 양자우물, 그리고 Mg을 도핑하여 p-type GaN을 성장하였다. 장파장대역의 a-plane LED의 특성을 알아보기 위해서 양자우물 형성시 In의 조성비를 높였다. 일반적인 포토리소그래피 공정과 Dry etching 공정을 사용하여 메사구조를 형성하였으며 Ti/Al/Pt/Au와 Ni/Au를 각각 n-type과 p-type의 전극 물질로 사용하였다. 제작된 LED의 특성을 파악하기 위해서 인가전류를 0부터 100mA까지 출력 스펙트럼을 측정하였으며 orange대역의 파장을 갖는 LED를 얻었다. 인가전류별 Peak 파장의 변화와 반측폭의 변화를 파악하여 장파장 대역의 a-plane LED의 특성을 확인하였다.
본 연구에서는 HVPE(hydride vapor phase epitaxy) 방법으로 r-plane 사파이어 기판 위에 무극성의 (11-20) a-plane GaN을 성장하여 구조적인 특성을 관찰하였다. HVPE 방법으로 저온($500/550/600/660^{\circ}C$)에서 성장한 AIN 버퍼층이 고온의 a-GaN에 미치는 영향을 확인하였다. 또한, AIN 버퍼층과의 비교를 위하여 저온에서 성장한 GaN 버퍼층과 InGaN 버퍼층 같은 다양한 버퍼층을 이용하여 a-plane GaN의 성장도 실시하였다. 고온에서 성장된 a-GaN의 구조적 형상은 저온버퍼층의 성장 조건에 크게 영향을 받음을 알 수 있었다. $GaCl_3$ 전 처리를 실시하고 $820^{\circ}C$에서 성장한 경우에 가장 평탄한 표면을 가지는 a-GaN을 얻을 수 있었다.
The crystals of group-Ⅲ nitride semiconductors with wurtzite structure exhibit a strong polarity. Especially, GaN has characteristics of different growth rate, anisotropic electrical and optical properties due to the polarity. In this work, GaN epilayer was grown and the polarities of the crystals were observed by the chemical wet etching and SP-EFM. GaN thin films were deposited on c-plane A1₂O₃ substrate under the variations of growth conditions by HVPE such as the deposition temperature of the buffer layer, the deposition time, the ratio of Group-V and Ⅲ and the deposition temperature of the film. The adquate results were obtained under the conditions of 500℃, 90 seconds, 1333 and 1080℃, respectively. It is observed that the GaN layer grown without the buffer layer has N-polarity and the GaN layer grown on the buffer layer has Ga-polarity. Fine crystal single particles were grown on c-plane A1₂O₃ and SiO₂, layer. The external shape of the crystal shows {10-11}{10-10}(000-1) planes as expected in the PBC theory and anisotropic behavior along c-axis is obvious. As a result of etching on each plane, (000-1) and {10-11}planes were etched strongly due to the N-polarity and {10-10} plane was not affected due to the non-polarity. In the case of the crystal grown on c-plane A1₂O₃, two types of crystals were grown. They were hexagonal pyramidal-shape with {10-11}plane and hexagonal prism with basal plane. The latter might be grown by twin plane reentrant edge (TPRE) growth.
a-plane 혹은 m-plane면을 사용하는 무분극 GaN LED는 c축 방향으로 발생하는 분극의 영향을 받지 않기 때문에 분극 GaN LED에 비해 높은 내부 양자효율을 가진다. 또한 무분극 GaN는 상대적으로 고농도의 p-type 도핑이 가능하기 때문에 광효율을 높일 수 있다. 하지만 이와 같은 장점에도 불구하고 무분극 GaN는 성장모드의 비대칭으로 인해 높은 결정성과 mirror-like한 표면을 얻기가 힘들다. 본 논문에서는 Metalorganic chemical-vapor deposition (MOCVD) 장비를 사용하여 r-plane 사파이어 기판위에 a-plane GaN을 성장시켰다. 일반적으로 사용하는 저온에서의 nucleation layer 성장 대신 $1050^{\circ}$의 고온에서 성장 시킨후 일반적으로 사용하는 two-step 성장방법으로 그위에 5.5um정도의 GaN을 성장시켰다. 성장시 Trimethylgallium(TMGa)와 암모니아를 각각 Ga과 N 소스로 이용하였고 캐리어 가스는 수소를 사용하였다. 비대칭 결정성을 줄이기 위해 3D island growth mode에서의 성장조건을 바꾸어 c축과 m축 방향으로의 X-ray 결정성(FWHM) 차이가 564 arcsec에서 206 arcsec로 변화 시켰다. Normarski 현미경으로 표면을 관찰한 결과 v-defect이 없고 a-plane GaN에서 볼 수 있는 전형적인 줄무늬 패턴을 가지는 표면을 얻었으며 광학적 특성을 보기 위해 Photoluminescence (PL)을 측정하였다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.