• Proceedings of the KIEE Conference
• /
• 1995.11a
• /
• pp.335-337
• /
• 1995

In this study, $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ stock solution was made and spin-coated on the $Pt/SiO_2/Si$ substrate at 4000[rpm] for 30[sec]. Coated specimens were dried at 400[$^{\circ}C$] for 10 [min]. The coating process was repeated 4 times and then heat-treated at 500$\sim$800[$^{\circ}C$], 1 hour. The final thickness of the thin films were about 3000[A]. The crystallinity and microstructure of the thin films were investigated for varing the sintering condition. The ferroelectric perovskite' phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hours. In the $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films sintered at 700[$^{\circ}C$] for 1 hour, dielectric constant and dielectric loss were 2133, 2.2[%] at room temperature, respectively. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin film capacitors having good dielectric and electrical properties are expected for the application to the dielectric material of DRAM.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.201-204
• /
• 2009

$BaTiO_3/SrTiO_3$ and $PbTiO_3/PbZrO_3$ superlattice thin films were fabricated on $Pt/Ti/SiO_2/Si$ substrate by the pulsed laser deposition process. The morphologies and physical properties of deposited films were characterized by using X-ray diffractometer, HR-SEM, and Impedance Analyzer. XRD data and SEM images of the films indicate that each layer was well deposited alternatively in the superlattice structure. The dielectric constant of $BaTiO_3/SrTiO_3$ superlattice thin film was higher than that of individual $BaTiO_3$ or $SrTiO_3$ film. Same result was obtained in the $PbTiO_3/PbZrO_3$system. The dielectric constant of a superlattice film was getting higher as the number of layer is increased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.168-170
• /
• 1994

Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were formed by spin coating method on Pt/$SiO_2$Si substrate at 4000ppm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500∼800[$^{\circ}C$] for 1 hour. The final thickness of the thin films were about 4800[A]. The ferroelectric perovskite phases precipitated under the heat-treated at 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ thin films heat-treated at 700[$^{\circ}C$] for 1 hour showed good dielectric and ferroclectric properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.153-156
• /
• 2004

The $Pb(Zr_{0.4}Ti_{0.6})O_3/Pb(Zr_{0.6}Ti_{0.4})O_3$ [PZT(4060)/(6040)] heterolayered thin films were deposited by RF sputtering method on the $Pt/TiO_2/SiO_2/Si$ substrate. The effects of the structural and dielectric properties of PZT heterolayered thin films were investigated. The MFM(Metal Ferroelectric Metal) type capacitors were made using the PZT(6040)/(4060) heterolayered thin films deposited with optimum deposition condition. An enhanced dielectric property was observed in the PZT(4060)/(6040) thin films. Investigating the dielectric constant and dielectric loss characteristics. the application for the next-generation dielectric thin films and memory devices were studied.

• Korean Journal of Materials Research
• /
• v.10 no.10
• /
• pp.684-690
• /
• 2000

In order to study effects of interfacial layers between $Pb(Zr,Til)Q_3(PZT)$ films and electrodes for Metal-Ferroelectric-MetaI(MFM) structure capacitors, we have fabricated the capacitors with the Pt/PZT/interfacial-layer/Pt/$TiO_2/SiO_2$/Si structure. $PbTiO_3(PT)$ interfacial layers were formed by sol-gel deposition and PbO, ZrO, and $TiO_2$ thin layers were deposited by reactive sputtering. $TiO_2$ interface layers result in the finest grains of PZT(crystalline Temp. $600^{\circ}C$) films compare to $PbO_2\;and\;ZrO_2$ layers. However, as the thickness of $TiO_2$ layer increases. PZT thin films become rough and electrical characteristics were deteriorated due to remained anatase phase. On the other hand. PT interface layers result in improved morphology of PZT films and do not significantly change ferroelectric properties. It is a also observed that seed layers at the middle and top of PZT films do not give significant effects on grain size but the PT seed layer at the interface between the bottom electrode and the PZT films results in the small grain size.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1454-1456
• /
• 1994

$Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were formed by spin coating method on $Pt/SiO_2/Si$ substrate at 3000rpm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500 - $800[^{\circ}C]$ for 1 hour. The final thickness of the thin films were about 4800[A]. The 100% ferroelectric perovskite phases precipitated under the heat treated at $700[^{\circ}C]$ for 1 hour. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films heat-treated at $700[^{\circ}C]$ for 1 hour showed good dielectric constant (812) property.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.14-16
• /
• 1995

Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ co-ramic thin films were formed by spin coating method on Pt/$SiO_2$/Si substrate at 4000[rpm] for 30 [sec]. Coated specimens were dried on the hot-plate at 400[$^{\circ}C$] for 10[min]. The coating process was repeated 6 times and then sintered at temperature between 500 ~ 800[$^{\circ}C$] for 1 hour. The ferroelectric perovskite phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ thin film sintered at 700[$^{\circ}C$] for 1hour showed good dielectric constant (2133) and dielectric loss (2.2[%]) Properties. The switching voltage, switching time and leakage currents density were 3.0[V], 1.7[${\mu}$sec] , 160[pA/$\textrm{cm}^2$] repectively.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.4
• /
• pp.182-185
• /
• 2010

$Pb_{0.99}[(Zr_{0.6}Sn_{0.4})_{0.9}Ti_{0.1}]_{0.98}Nb_{0.02}O_3$ (PNZST) thin films were deposited by radio frequency magnetron sputtering on a $(La_{0.5}Sr_{0.5})CoO_3$ (LSCO)/Pt/Ti/$SiO_2$/Si substrate using a PNZST target with an excess PbO of 10 mole%. The thin films deposited at the substrate temperature of $500^{\circ}C$ crystallized to a perovskite phase after rapid thermal annealing (RTA). The thin films, which annealed at $650^{\circ}C$ for 10 seconds in air, exhibited good crystal structures and ferroelectric properties. The remanent polarization and coercive field of the fabricated PNZST capacitor were approximately $20uC/cm^2$ and 50 kV/cm, respectively. The reduction of the polarization after $2.2\;{\times}\;10^9$ switching cycles was less than 10%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.547-549
• /
• 2001

The dielectric constants and dielectric losses of ZrTiO$_4$thin films deposited by DC magnetron reactive sputtering were investigated. The paraelectric properties were measured in the 100kHz range. As the deposition temperature increased (up to 67$0^{\circ}C$), the dielectric losses (tan$\delta$) decreased (down to 0.017$\pm$0.007), while the dielectric constants ($\varepsilon$) were in the range of 35$\pm$7. Post annealing at 80$0^{\circ}C$ in oxygen for 2h reduced tan$\delta$ down to 0.005$\pm$0.001, higher than those of well-sintered bulk ZrTiO$_4$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.509-512
• /
• 1999

Ferroelectric Sr$_2$(Nb, Ta)$_2$O$_{7}$(SNTO), La$_2$Ti$_2$O$_{7}$(LTO) thin films were prepared by sol-gel processes. SNTO, LTO thin films were spin-coated on Pt/TiO$_2$/SiO$_2$/Si(100). Pt/Ti/SiO$_2$/Si(100). PT/ZrO$_2$/SiO$_2$/Si(100) substrates. After multiple coating, dried thin films were heat-treated for decomposition of residual organics and crystallization. Dielectric and other relevant electrical properties were measured and the results showed a little possibility in ferroelectric gate random access memory devices.ces.