• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.1033-1039
• /
• 1995

The current experiment has quantitatively investigated the effect of the content of CaO and SiO2 on the microstructure, density, electrical resistivity, power loss and initial permeability of manganese zinc ferrites. The density increased initially with CaO and SiO2 content and the further addition showed an adverse effect. The excess addition of CaO and SiO2 developed a discontinuous grain growth with numerous pores inside grains and lowered the electrical resistivity. The initial permeability decreased with increasing the content of SiO2. The samples with relatively low power loss showed that half of the total loss at 10$0^{\circ}C$, 100 kHz and 2000 Gauss was due to the eddy current loss.

• Journal of IKEEE
• /
• v.17 no.2
• /
• pp.182-188
• /
• 2013

Using a ceramic target ZnO:In with In doping concentration of 2%, hetero-junctions of n-ZnO:In/p-Si and p-ZnO:(In, N)/n-Si were fabricated by depositing Indium doped n - type ZnO (ZnO:In or IZO) and Indium-nitrogen co-doped p - type ZnO (ZnO:(In, N)) films on wafers of p-Si (100) and n-Si (100) by DC magnetron sputtering, respectively. These films with the best electrical and optical properties were then obtained. The micro-structural, optical and electrical properties of the n-type and p-type semiconductor thinfilms were characterized by X-ray diffraction (XRD), RBS, UV-vis; four-point probe resistance and room-temperature Hall effect measurements, respectively. Typical rectifying behaviors of p-n junction were observed by the current-voltage (I-V) measurement. It shows fairly good rectifying behavior with the fact that the ideality factor and the saturation current of diode are n=11.5, Is=1.5108.10-7 (A) for n-ZnO:In/p-Si hetero-jucntion; n=10.14, Is=3.2689.10-5 (A) for p-ZnO:(In, N)/n-Si, respectively. These results demonstrated the formation of a diode between n-type thin film and p-Si, as well as between p-type thin film and n-Si..

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.1-8
• /
• 2012

The development of martensitic grades which can be processed in continuous galvanizing lines requires the reduction of the oxides formed on the steel during the hot dip process. This reduction mechanism was investigated in detail by means of High Resolution Transmission Electron Microscopy (HR-TEM) of cross-sectional samples. Annealing of a martensitic steel in a 10% $H_2+N_2$ atmosphere with the dew point of $-35^{\circ}C$ resulted in the formation of a thin $_{C-X}MnO.SiO_{2}$ (x>1) oxide film and amorphous $_{a-X}MnO.SiO_{2}$ oxide particles on the surface. During the hot dip galvanizing in Zn-0.13%Al, the thin $_{C-X}MnO.SiO_{2}$ (x>1) oxide film was reduced by the Al. The $_{a-X}MnO.SiO_{2}$ (x<0.9) and $a-SiO_{2}$ oxides however remained embedded in the Zn coating close to the steel/coating interface. No $Fe_{2}Al_{5-X}Zn_{X}$ inhibition layer formation was observed. During hot dip galvanizing in Zn-0.20%Al, the $_{C-X}MnO.SiO_{2}$ (x>1) oxide film was also reduced and the amorphous $_{a-X}MnO.SiO_{2}$ and $a-SiO_{2}$ particles were embedded in the $Fe_{2}Al_{5-X}Zn_{X}$ inhibition layer formed at the steel/coating interface during hot dipping. The results clearly show that Al in the liquid Zn bath can reduce the crystalline $_{C-X}MnO.SiO_{2}$ (x>1) oxides but not the amorphous $_{a-X}MnO.SiO_{2}$ (x<0.9) and $a-SiO_{2}$ oxides. These oxides remain embedded in the Zn layer or in the inhibition layer, making it possible to apply a Zn or Zn-alloy coating on martensitic steel by hot dipping. The hot dipping process was also found to deteriorate the mechanical properties, independently of the Zn bath composition.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.8
• /
• pp.1135-1138
• /
• 2002

CuO/ZnO, CuO/SiO,sub>2, and CuO/ZrO2 catalysts were prepared for investigating the support effects on methanol dehydrogenation. It was found that the conversion of methanol was proportional to the copper surface area on Cu/ZnO cat alysts and was independent on that on Cu/ZrO2 and Cu/SiO2. The highest copper surface area was obtained with the Cu/ZrO2 (9/1). The unusual deactivation of the Cu/ZnO, which showed the highest selectivity among the catalysts tested, was observed. Pulse reaction with methanol indicated that the lattice oxygen in ZnO could be removed by forming CO2 in the catalytic reaction, supporting that the ZnO reduction was responsible for the severe deactivation of the Cu/ZnO.

• Electrical & Electronic Materials
• /
• v.10 no.7
• /
• pp.659-667
• /
• 1997

The influence of SiO$_2$on the microstructure and electrical properties of zinc oxide varistor was investigated. Zn$_2$SiO$_4$third phase in the sintered body was found at grain boundaries, multiple grain junctions, and occasionally within ZnO grains. This phase acted as a grain growth inhibitor, which retard the grain growth of the ZnO matrix by impeding migration on the grain boundaries. As SiO$_2$ addition increases, average grain size decreased from 40.6${\mu}{\textrm}{m}$ to 26.9${\mu}{\textrm}{m}$ due to the pinning effect by Zn$_2$SiO$_4$ and drag effect by Si segregation at grain boundaries, the breakdown voltage consequently increased. When SiO$_2$ addition is increased, interface state density decreased, however, the barrier height increased by decrease of donor concentration, as a result, the nonlinear exponent increased and leakage current decreased. While, as SiO$_2$ addition increase, it was found that the apparent dielectric loss factor shows a tendency of decrease. Wholly, electrical properties of zinc oxide varistor can be said to be improved by SiO$_2$addition.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.11a
• /
• pp.100-100
• /
• 1998

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1044-1050
• /
• 2000

ZnO-Pr$_{6}$O$_{11}$-Co$_3$O$_4$-CaO 사성분계에 SiO$_2$를 0.4at%까지 첨가하여 1180, 1200 및 125$0^{\circ}C$에서 소성하여 미세구조 및 전기적인 특성을 조사하였다. 소성온도 120$0^{\circ}C$ 이상에서 치밀한 시편을 얻을 수 있었고, Si는 주로 입계에 분포하고 있으며, SiO$_2$첨가는 결정립성장을 억제하였다. 이 현상은 고상소결만이 일어나 120$0^{\circ}C$에서 소결된 시편과 액상소결이 일어난 125$0^{\circ}C$에서 소결된 시편 모두에서 관찰되었으며, SiO$_2$첨가에 의한 기공의 증가에 기인하는 것으로 판단된다. SiO$_2$의 첨가에 의해 바리스터의 비선형계수가 크게 변화하였으며, 시편의 소성과정이 고상소결인 경우 비선형계수가 증가한 반면 액상소결인 경우에는 감소하였다. 적절한 양의 SiO$_2$(약 0.3at%)를 첨가하여 액상이 형성되지 않는 120$0^{\circ}C$에서 소성하여 80 이상의 비선형계수를 갖는 바리스터를 제조할 수 있었다.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.4
• /
• pp.169-173
• /
• 2008

The objective of this study is to coat the $SiO_2$ layer uniformly on the ZnS:Cu phosphors by using Sol-Gel method. From results of SEM micrographs observation, XRD and XPS analysis, it could be confirmed that $SiO_2$ layer was relatively well coated on ZnS:Cu particles. $Ag_2S$ was used as a decoding chemical to analyze the dense and uniform coating performance of $SiO_2$ layer on phosphor particles. It could be concluded that phosphors synthesized from our two step replacement method showed strong blue peak comparing to other method and rather weak green peak also. Obtained particle size of phosphors were about 20m diameter. Luminescence properties of the phosphors were examined by photoluminescence spectra at the excitation wavelength of 270 nm.

• Journal of the Korean Ceramic Society
• /
• v.28 no.6
• /
• pp.471-477
• /
• 1991

Effects of ZnO, PbO and SiO2 on the grain growth and magnetic properties of Sr-ferrite were investigated. (1) Addition of ZnO to Sr-ferrite increased remanence, but decreased coercivity and maximum energy product. (2) Addition of PbO up to 0.5 wt% increased (B$.$H)max of Sr-ferrite, but addition more than 0.5 wt% decreased (B$.$H)mzx (3) SiO2 addition to the 0.5 wt% PbO doped Sr-ferrite decreased remanence and increased coercivity. The coercivity increase in due to the grain refinement effect of SiO2. But addition of SiO2 more than 0.5 wt% invoked a decrease of coercivity and (B$.$H)max of Sr-ferrite due to abnormal grain growth. Sr-ferrite magnet having maximum energy product of 3.7MGOe was fabricated by using the roasting product of Pyrrhotite.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.405-405
• /
• 2007

ZnO는 상온에서 3.38eV의 넓은 밴드갭을 가지는 직접천이형 반도체이며, 60meV의 큰 엑시톤 결합에너지를 가지는 UV 영역의 광소자로 응용할 수 있는 물질이다. 특히 ZnO를 이용한 LED에 대한 연구가 최근 활발히 이루어지고 있다. 그러나 n-ZnO/p-ZnO 동종접합 다이오드는 p-ZnO의 재현성이 없고, 낮은 정공농도를 보이기 때문에 n-ZnO를 기반으로 한 이종접합 다이오드의 개발이 필요하게 되었다. 특히 n-ZnO/p-Si 이종접합 다이오드는 낮은 구동전압과 제조단가가 저렴하다는 장점이 있다 또한 n-ZnO를 스퍼터링을 이용하여 증착할 경우 고온에서 성장함에도 불구하고 케리어 농도 및 이동도가 매우 낮다. 반면 MOCVD 법은 대면적 증착이 가능하고 비교적 낮은 온도에서 박막을 성장할 수 있고 전기적 특성 또한 매우 우수하다. 본 연구에서는 p-Si 기판위에 MOCVD 를 이용하여 n-ZnO를 증착하고, 이를 열처리하여 n-ZnO/p-Si 이종접합 다이오드의 특성 변화를 관찰하고자 하였다. n-ZnO/p-Si 시편을 $N_2$ 및 $O_2$ 가스 분위기에서 열처리한 후 소자의 광학적, 전기적 특성을 관찰하였다.