• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.216-216
• /
• 2009

$(Ni_{1-x-y}Zn_xCu_y)Fe_2O_4(x=0.45,\;0{\leq}y{\leq}0.3)$ was synthesized by conventional ceramic processing, and the sintering behavior and the magnetic properties of which were studied as functions of CuO content and sintering temperature. Both the densification and the grain growth rates were significantly enhanced with the increase of CuO content, while abnormal grain growth occurred when the samples of $y{\geq}0.2$ were sintered above $950^{\circ}C$. Saturation magnetization and coercive field were mainly influenced by the densification and grain growth of the specimens, respectively.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.1033-1039
• /
• 1995

The current experiment has quantitatively investigated the effect of the content of CaO and SiO2 on the microstructure, density, electrical resistivity, power loss and initial permeability of manganese zinc ferrites. The density increased initially with CaO and SiO2 content and the further addition showed an adverse effect. The excess addition of CaO and SiO2 developed a discontinuous grain growth with numerous pores inside grains and lowered the electrical resistivity. The initial permeability decreased with increasing the content of SiO2. The samples with relatively low power loss showed that half of the total loss at 10$0^{\circ}C$, 100 kHz and 2000 Gauss was due to the eddy current loss.

• Food Science of Animal Resources
• /
• v.40 no.3
• /
• pp.338-349
• /
• 2020

The effects of organic Zn-L-selenomethionine (Zn-L-SeMet) at 0.3 ppm on carcass composition, meat characteristics, fatty acid composition, glutathione peroxidase activity, and ribonucleotide content were compared against the commercial inorganic sodium selenite (Na-Se) and the combination of the two, in commercial broilers. A total of 540 one day-old chicks were assigned at random to 3 dietary treatments : i) commercial inorganic selenium as control or T1, ii) a 1:1 ratio of inorganic and organic selenium as T2, and iii) organic selenium as T3. Carcass composition, meat characteristics, cholesterol content, fatty acid composition, and ribonucleotide content were generally unaffected by treatments. However, discrepancy were significantly observed in glutathione peroxidase activity (GSH-Px) and water holding capacity, with organic selenium showing higher glutathione peroxidase activity (p<0.01) and lower shrinkage loss (p<0.05), respectively. These findings could be explained by the contribution of organic selenium in bioavailability of GSH-Px. However, having conducted in a commercial close house system with sufficient amount of nutritional supplementation, the present study demonstrated little or no effects of organic Zn-L-SeMet on meat characteristics, fatty acid composition, and ribonucleotide content (flavor characteristic) in broiler chickens.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.106-106
• /
• 2009

Al-doped ZnO (AZO) thin films were grown on glass substrates by co-sputtering at room temperature. We made ZnO and Al target and ZnO:Al film is deposited with sputter which has two RF gun source. The Al content was controlled by varying Al RF power and effect of Al contents on the properties of ZnO:Al film was investigated. Crystallinity and orientation of the ZnO:Al films were investigated by X-ray diffraction (XRD), surface morphology of the ZnO:Al films was observed by atomic force microscope. Electrical properties of the ZnO:Al films were measured at room temperature by van der Pauw method and hall measurement. Optrical properties of ZnO:Al films were measured by UV-vis-NIR spectrometer.

• Journal of the Korean Ceramic Society
• /
• v.34 no.9
• /
• pp.949-956
• /
• 1997

With the increase of ZnO content, burnability of raw materials was improved and the formation of clinker minerals was accellerated. When ZnO was added 1wt%, the clinkering temperature was decreased about 30~5$0^{\circ}C$. As an increase of ZnO added, aluminate phase was decreased and ferrite phase was increased. When ZnO was added more than 3.0wt.%, the new phases, such as ZnO.Al2O3 and ZnO.Fe2O3 were formed. In the excess of amount of ZnO added, the decomposition of alite phase was intensed and the lamella structure in belite could not be observed due to the decomposition.

• Journal of Advanced Marine Engineering and Technology
• /
• v.27 no.1
• /
• pp.33-41
• /
• 2003

The optical properties of $ZnS_ySe_{1-\chi-y}:Te_{\chi}(\chi<0.08,y~0.11)$ alloys grown by molecular beam epitaxy (MBE) have been investigated by photoluminescence (PL) and PL-excitation (PLE) spectroscopy. Good optical properties and high crystal quality were established with lattice match condition to GaAs substrate. At room temperature, emission in the visible spectrum region from blue to green was obtained by varying the Te content of the ZnSSe:Te alloy. The efficient blue and green emission were assigned to $Te_1 and Te_n(n\geq2)$cluster bound excitons, respectively. Bright green (535 nm) and blue (462 nm) light emitting diodes (LEDs) have been developed using ZnSSe:Te system as an active layer. The turn-on voltage of 2.1 V in current-voltage characteristics is very small compared to that of commercial InGaN-based LEDs (>3.4 V), indicating the formation of a good ohmic contact due to the optimized p-ZnSe/p-ZnTe multi-quantum well (MQW) superlattice electrode layers.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.506-508
• /
• 2001

The ferrite plating with applying power ultrasound waves of 19.5 kHz and 600W enabled us to encapsulate entirely MnZn ferrite cores for transformers with Ni$\sub$x/Zn$\sub$y/Fe$\sub$3-x-y/O$_4$coating. Supplying a NH$_4$OH solution during the plating broke the limit of the solubility of Ni ions to ferrite-plated films. The electrical resistivity of the NiZn ferrite coating increased with increasing the Ni and Zn content, reaching 2.3${\times}$10$\^$5/Ωcm at the composition of Ni$\sub$0.24/Zn$\sub$0.30/Fe$\sub$2.46/O$_4$. The saturation magnetization was 540 emu/㎤. As a result, the MnZn ferrite cores were successfully encapsulated with the NiZn ferrite coatings for an insulation layer.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1455-1458
• /
• 1997

In order to promote CO gas sensitivity, $SnO_2$ added ZnO prepared. The electrical conductivities and dielectric constants decreased by increasing $SnO_2$ content in air. The electrical conductivities in 1000ppm CO atmosphere were larger than in dry air. The measured CO sensitivities were $1{\sim}15.2$ at $100^{\circ}C{\sim}480^{\circ}C$. The maximum CO sensitivity of 15mol% $SnO_2$ added ZnO was 15.2 at $305^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.188-193
• /
• 1997

ZnO thin film had been deposited on the glass 7r sputtering method, and investigated by electrical and structural properties. When the rf power was 188W and sputtering pressure was 1$\times$10$^{-3}$ Torr at room temperature, Al-doped ZnO thin film had the lowest resistivity(1$\times$10$^{-4}$ $\Omega$.cm), and then carrier concentration and Hall mobility were 6.27$\times$10$^{20}$ cm$^{-3}$ and 22.04$\textrm{cm}^2$/V.s, respectively. And undoped ZnO thin film had about 10$^{14}$ $\Omega$.cm resistivity when oxygen content was 10% or more at room temperature. The surface morphology of ZnO thin film observed by SEM was overall uniform when oxygen content was 50% below and sputtering pressure was 1.0$\times$10$^{-1}$ Torr.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1991.10a
• /
• pp.17-19
• /
• 1991

Pastes consisting of $CdZnS_{1-y}Te_{y}$ powder, 20wt/o of $CdCl_2$as a sintering aid and appropriate amount of Propylene Glycol(P.G) have been coated on glass substrates and were sintered at the temperature of $625^{\circ}C$ to find energy band gap, transmittance and electrical properties of the sintered films. The resistivity of sintered film increases with increasing Te content. X-ray diffraction patterns show that $CdZnS_{0.9}Te_{0.1}$ sintered film is in the single film in the two phase region. The transmittance of the sintered film decreases with increasing the Te content.