• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.593-596
• /
• 2003

A proposed way to prepare $YBa_2Cu_3O_y$ wires or tapes is that Ag is used as substrate and melting point of $YBa_2Cu_3O_y$ is decreased to lower than the melting point of silver ($961\;^{\circ}C$). Therefore after the deposition of $YBa_2Cu_3O_y$ film on Ag substrate, the heat treatment can be carried out below the Ag melting point. Silver (Ag) and Lead oxide(PbO) were selected to be additives for $YBa_2Cu_3O_y$. Different Ag and PbO contents were added in $YBa_2Cu_3O_y$, the melting points of which were measured by DTA. In order to guarantee that the superconductivity of $YBa_2Cu_3O_y$ was not reduced after Ag and PbO added into $YBa_2Cu_3O_y$, their superconductivities were measured. It is proved that as additives, both Ag and PbO can reduce the melting point of $YBa_2Cu_3O_y$. For Ag doped $YBa_2Cu_3O_y$, $T_c$ is about 93K and ${\Delta}Tc$ is $2{\sim}3K$. For PbO doped $YBa_2Cu_3O_y$, $T_c$ is $88K{\sim}92K$ and ${\Delta}T_c$ is $11{\sim}12K$. When 10 wt% of Ag and 10 wt% PbO were added in $YBa_2Cu_3O_y$, the melting point of the mixture of $YBa_2Cu_3O_y$ (80 wt%), Ag (10 wt%) and PbO (l0 wt%) is $943^{\circ}C$. The transition temperatures ($T_c$) of the sample is 91.8 K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.543-546
• /
• 2004

The melting temperature and critical temperature(Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity(the transition width, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase BaPbO3 was synthesized by the simple way from both mixtures of $BaPbO_3$ and PbO, $BaPbO_3\;and\;PbO_2$. Deferent contents of $BaPbO_3$(10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there werenot reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

• Applied Chemistry for Engineering
• /
• v.7 no.4
• /
• pp.639-644
• /
• 1996

The $YBa_2Cu_{3-y}Ag_yO_{7-x}$ high-temperature superconductors were prepared by pyrophoric synthetic method from $Y_2O_3$, $BaCO_3$, CuO, and $AgNO_3$ powders. When we were partially substituted Ag for Cu in $YBa_3Cu_3O_{7-x}$, the superconducting properties of $YBa_2Cu_{3-y}Ag_yO_{7-x}$ were investigated with X-ray diffractometer, resisitivity measuring equipment, SEM, and Vickers Hardness. The Tc,zero of $YBa_2Cu_3O_{7-x}$ was 91K, the density was $5.2g/cm^3$, and the hardness was $590kg/mm^2$. When Ag was substituted below y=0.15, electrical property of $YBa_2Cu_{3-y}Ag_yO_{7-x}$ did not change but microstructure, density, and hardness were enhanced.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.57-59
• /
• 2004

The melting temperature and critical temperature (Tc) of YBa$_2$Cu$_3$Ox with deferent content impurities of PbO and BaPbO$_3$ were studied. When the PbO was used as addition in YBa$_2$Cu$_3$Ox, although the melting point could be reduced, the superconductivity (the transition wide, ΔTc) became poor. From the XRD pattern of the sintered mixture of YBa$_2$Cu$_3$Ox and PbO it was known that there is a reaction between YBa$_2$Cu$_3$Ox and PbO, and the product is BaPbO$_3$. In the process of the reaction the superconducting phase of YBa$_2$Cu$_3$Ox was decreased and in the sample BaPbO$_3$became the main phase. Therefore the superconductivity was reduced. BaPbO$_3$was chosen as the impurity for the comparative study. The single phase BaPbO$_3$was synthesized by the simple way from both mixtures of BaPbO$_3$and PbO, BaPbO$_3$and PbO$_2$. Deferent contents of BaPbO$_3$(10%, 20%, 30%) were added in the YBa$_2$Cu$_3$Ox. By the phase analysis in the XRD patterns it was proved that there were not reactions between YBa$_2$Cu$_3$Ox and BaPbO$_3$. When BaPbO$_3$was used as impurity in YBa$_2$Cu$_3$Ox the superconductivity was much better than PbO as impurity in YBa$_2$Cu$_3$Ox But the melting point of YBa$_2$Cu$_3$Ox with BaPbO$_3$could not be found when the temperature was lower than 1000 $^{\circ}C$ in the DTA measurement.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1995.11a
• /
• pp.74-75
• /
• 1995

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.35 no.6
• /
• pp.622-625
• /
• 2022

YBa₂Cu₃O_7-y bulk as a high temperature oxide superconducting conductor has the high critical temperature of 92 K. YBa₂Cu₃O_7-y bulk superconductors have been fabricated by a seeded melting growth. Magnetic properties were studied by using superconductor of melted YBa₂Cu₃O_7-y oxides. It was demonstrated that Y₂BaCuO₅ particles acts as a pinning center which plays an important role on the magnetic properties. The thickness of the upper and lower pellets of the YBa₂Cu₃O_7-y bulk was formed at 40 mm with 55 g of the composition, and the YBa₂Cu₃O_7-y superconductor was manufactured through a heat treatment process. Manufacturing the superconducting bulk, it is possible to improve the pore density of the superconducting bulk by providing a path through which oxygen could be emitted.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.341-344
• /
• 2004

The superconducting properties of $YBa_2Cu_3O_x$ with different content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as an additive in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and $BaPbO_3$ would be the main phase in the sample. Therefore, $BaPbO_3$ was chosen as the impurity additive for the comparative study. The single phase of $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Different contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the Phase analysis in the XRD patterns it was proved that there was no reaction between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as an impurity additive in $YBa_2Cu_3O_x$.

• Journal of the Speleological Society of Korea
• /
• no.78
• /
• pp.17-22
• /
• 2007

The melting temperature and critical temperature (Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity (the transition wide, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Deferent contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there were not reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.15 no.8
• /
• pp.1771-1776
• /
• 2011

In this paper, as an attempt to improve the preparation conditions of $YBa_2Cu_3Ox$ superconducting bulk samples, the properties of $YBa_2Cu_3Ox$ superconductor depending on the particle size of YBCO powder and $BaPbO_3$ as an additive have been investigated, and a study on the effects of additive to the density, grain alignment, and porosity of samples that affect the critical current of superconductor has been performed. In order to prepare superconductor, $YBa_2Cu_3Ox$ powder synthesized by sol-gel method, showing a size distribution of 0.2~1 ${\mu}m$ was used. The $BaPbO_3$ added to promote grain growth and to decrease porosities and weak links between grain boundaries of $YBa_2Cu_3Ox$ superconductors. In the samples prepared by sol-gel synthesized powder with 10, 20, and 30 wt% conductive $BaPbO_3$ additives, the sample with 20 wt% $BaPbO_3$ obtained the highest critical current of 4.74 A, showing 20 wt% higher critical current than that with solid state synthesized powder.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.366-369
• /
• 2003

High T$_{c}$ superconducting lines will be applied as key materials in the areas of power transmission line; magnetic levitation of vehicle; magnetic separation; magnetic energy storage and marine propulsion. A combination method of electrophoresis deposition and zone-melting for preparation of YBaCuO tape is proposed. The submicron particle powder of YBaCuO made by sol-gel method is used in the electrophoresis process. A 40~50${\mu}{\textrm}{m}$ thickness of YBaCuO film on Ag plate could be deposited in about three minutes. After deposition the film is rolled and heat treated in order to increase the density and the adhesion of the film to the Ag plate. Silver(Ag) and lead oxide(PbO) were added in the YBaCuO powder in order to reduce its melting point. The YBaCuO coating with controlled Ag and PbO contents was preliminarily zone-melted at about 945$^{\circ}C$.>.