• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.593-596
• /
• 2003

A proposed way to prepare $YBa_2Cu_3O_y$ wires or tapes is that Ag is used as substrate and melting point of $YBa_2Cu_3O_y$ is decreased to lower than the melting point of silver ($961\;^{\circ}C$). Therefore after the deposition of $YBa_2Cu_3O_y$ film on Ag substrate, the heat treatment can be carried out below the Ag melting point. Silver (Ag) and Lead oxide(PbO) were selected to be additives for $YBa_2Cu_3O_y$. Different Ag and PbO contents were added in $YBa_2Cu_3O_y$, the melting points of which were measured by DTA. In order to guarantee that the superconductivity of $YBa_2Cu_3O_y$ was not reduced after Ag and PbO added into $YBa_2Cu_3O_y$, their superconductivities were measured. It is proved that as additives, both Ag and PbO can reduce the melting point of $YBa_2Cu_3O_y$. For Ag doped $YBa_2Cu_3O_y$, $T_c$ is about 93K and ${\Delta}Tc$ is $2{\sim}3K$. For PbO doped $YBa_2Cu_3O_y$, $T_c$ is $88K{\sim}92K$ and ${\Delta}T_c$ is $11{\sim}12K$. When 10 wt% of Ag and 10 wt% PbO were added in $YBa_2Cu_3O_y$, the melting point of the mixture of $YBa_2Cu_3O_y$ (80 wt%), Ag (10 wt%) and PbO (l0 wt%) is $943^{\circ}C$. The transition temperatures ($T_c$) of the sample is 91.8 K.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.543-546
• /
• 2004

The melting temperature and critical temperature(Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity(the transition width, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase BaPbO3 was synthesized by the simple way from both mixtures of $BaPbO_3$ and PbO, $BaPbO_3\;and\;PbO_2$. Deferent contents of $BaPbO_3$(10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there werenot reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

• 공업화학
• /
• 제7권4호
• /
• pp.639-644
• /
• 1996

원료물질인 $Y_2O_3$, $BaCO_3$, CuO 및 $AgNO_3$ 분말로부터 Y계 고온초전도체를 발화합성법으로 제조하였다 $YBa_2Cu_3O_{7-x}$와 Cu를 Ag로 부분 치환한 $YBa_2Cu_{3-y}Ag_yO_{7-x}$의 특성을 X-ray diffractometer, resistivity measuring equipment, SEM, and Vickers Hardness 등으로 분석하였다. $YBa_2Cu_3O_{7-x}$의 Tc,zero는 91K였고, 밀도는 $5.2g/cm^3$, 경도는 $590kg/mm^2$였다. Cu를 Ag로 0.15몰 이하 부분 치환한 $YBa_2Cu_{3-y}Ag_yO_{7-x}$의 경우 임계온도(Tc)는 거의 변하지 않으면서 미세구조, 밀도 및 경도가 향상되었다.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2004년도 SMICS 2004 International Symposium on Maritime and Communication Sciences
• /
• pp.57-59
• /
• 2004

The melting temperature and critical temperature (Tc) of YBa$_2$Cu$_3$Ox with deferent content impurities of PbO and BaPbO$_3$ were studied. When the PbO was used as addition in YBa$_2$Cu$_3$Ox, although the melting point could be reduced, the superconductivity (the transition wide, ΔTc) became poor. From the XRD pattern of the sintered mixture of YBa$_2$Cu$_3$Ox and PbO it was known that there is a reaction between YBa$_2$Cu$_3$Ox and PbO, and the product is BaPbO$_3$. In the process of the reaction the superconducting phase of YBa$_2$Cu$_3$Ox was decreased and in the sample BaPbO$_3$became the main phase. Therefore the superconductivity was reduced. BaPbO$_3$was chosen as the impurity for the comparative study. The single phase BaPbO$_3$was synthesized by the simple way from both mixtures of BaPbO$_3$and PbO, BaPbO$_3$and PbO$_2$. Deferent contents of BaPbO$_3$(10%, 20%, 30%) were added in the YBa$_2$Cu$_3$Ox. By the phase analysis in the XRD patterns it was proved that there were not reactions between YBa$_2$Cu$_3$Ox and BaPbO$_3$. When BaPbO$_3$was used as impurity in YBa$_2$Cu$_3$Ox the superconductivity was much better than PbO as impurity in YBa$_2$Cu$_3$Ox But the melting point of YBa$_2$Cu$_3$Ox with BaPbO$_3$could not be found when the temperature was lower than 1000 $^{\circ}C$ in the DTA measurement.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1995년도 추계 학술발표 강연 및 논문개요집
• /
• pp.74-75
• /
• 1995

• 한국전기전자재료학회논문지
• /
• 제35권6호
• /
• pp.622-625
• /
• 2022

YBa₂Cu₃O_7-y bulk as a high temperature oxide superconducting conductor has the high critical temperature of 92 K. YBa₂Cu₃O_7-y bulk superconductors have been fabricated by a seeded melting growth. Magnetic properties were studied by using superconductor of melted YBa₂Cu₃O_7-y oxides. It was demonstrated that Y₂BaCuO₅ particles acts as a pinning center which plays an important role on the magnetic properties. The thickness of the upper and lower pellets of the YBa₂Cu₃O_7-y bulk was formed at 40 mm with 55 g of the composition, and the YBa₂Cu₃O_7-y superconductor was manufactured through a heat treatment process. Manufacturing the superconducting bulk, it is possible to improve the pore density of the superconducting bulk by providing a path through which oxygen could be emitted.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.341-344
• /
• 2004

The superconducting properties of $YBa_2Cu_3O_x$ with different content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as an additive in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and $BaPbO_3$ would be the main phase in the sample. Therefore, $BaPbO_3$ was chosen as the impurity additive for the comparative study. The single phase of $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Different contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the Phase analysis in the XRD patterns it was proved that there was no reaction between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as an impurity additive in $YBa_2Cu_3O_x$.

• 동굴
• /
• 제78호
• /
• pp.17-22
• /
• 2007

The melting temperature and critical temperature (Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity (the transition wide, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Deferent contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there were not reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

• 한국정보통신학회논문지
• /
• 제15권8호
• /
• pp.1771-1776
• /
• 2011

미세 입자 크기를 갖는 $YBa_2Cu_3Ox$(YBCO) 초전도 분말을 이용하여 $BaPbO_3$ 첨가에 따른 $YBa_2Cu_3Ox$ 초전도 벌크의 임계전류를 향상시키는 요소인 시편의 밀도와 결정들의 정렬 상태를 향상시키고, 기공도를 감소시키기 위한 연구를 수행하였다. 졸겔법으로 미세 크기를 갖는 $YBa_2Cu_3Ox$ 초전도 분말을 합성하여 입자의 크기가 0.2~1 ${\mu}m$의 미세한 분포를 갖는 초전도 분말을 사용하고, $YBa_2Cu_3Ox$ 초전도 시편의 입자 성장을 촉진시키고, 기공과 입계간의 약연접을 감소시키기 위하여 금속 물질 및 구조 화합물인 $BaPbO_3$를 10~30 wt%를 첨가하여 시편을 제작하고 특성을 관찰하였다. 나노 크기를 갖는 YBCO 분말과 $BaPbO_3$ 20 wt%를 첨가하여 제작한 $YBa_2Cu_3Ox$ 초전도 시편은 일반적인 벌크 제작법으로 제작된 시편과 비교하여 임계전류가 20% 향상된 4.74A를 얻었다.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2003년도 춘계종합학술대회
• /
• pp.366-369
• /
• 2003

High T$_{c}$ superconducting lines will be applied as key materials in the areas of power transmission line; magnetic levitation of vehicle; magnetic separation; magnetic energy storage and marine propulsion. A combination method of electrophoresis deposition and zone-melting for preparation of YBaCuO tape is proposed. The submicron particle powder of YBaCuO made by sol-gel method is used in the electrophoresis process. A 40~50${\mu}{\textrm}{m}$ thickness of YBaCuO film on Ag plate could be deposited in about three minutes. After deposition the film is rolled and heat treated in order to increase the density and the adhesion of the film to the Ag plate. Silver(Ag) and lead oxide(PbO) were added in the YBaCuO powder in order to reduce its melting point. The YBaCuO coating with controlled Ag and PbO contents was preliminarily zone-melted at about 945$^{\circ}C$.>.