• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.57-59
• /
• 2004

The melting temperature and critical temperature (Tc) of YBa$_2$Cu$_3$Ox with deferent content impurities of PbO and BaPbO$_3$ were studied. When the PbO was used as addition in YBa$_2$Cu$_3$Ox, although the melting point could be reduced, the superconductivity (the transition wide, ΔTc) became poor. From the XRD pattern of the sintered mixture of YBa$_2$Cu$_3$Ox and PbO it was known that there is a reaction between YBa$_2$Cu$_3$Ox and PbO, and the product is BaPbO$_3$. In the process of the reaction the superconducting phase of YBa$_2$Cu$_3$Ox was decreased and in the sample BaPbO$_3$became the main phase. Therefore the superconductivity was reduced. BaPbO$_3$was chosen as the impurity for the comparative study. The single phase BaPbO$_3$was synthesized by the simple way from both mixtures of BaPbO$_3$and PbO, BaPbO$_3$and PbO$_2$. Deferent contents of BaPbO$_3$(10%, 20%, 30%) were added in the YBa$_2$Cu$_3$Ox. By the phase analysis in the XRD patterns it was proved that there were not reactions between YBa$_2$Cu$_3$Ox and BaPbO$_3$. When BaPbO$_3$was used as impurity in YBa$_2$Cu$_3$Ox the superconductivity was much better than PbO as impurity in YBa$_2$Cu$_3$Ox But the melting point of YBa$_2$Cu$_3$Ox with BaPbO$_3$could not be found when the temperature was lower than 1000 $^{\circ}C$ in the DTA measurement.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.8
• /
• pp.830-834
• /
• 2004

In this study, lead-free pirzoelectric ceramics were investigated for pressure sensor applications as a function of the amount of ${La}_2{O}_3$ addition at $Bi(Na, K)Ti{O}_3-SrTi{O}_3$system. With increasing the amount of addition, the density and dielectric constant increased up to 0.9 wt% ${La}_2{O}_3$ addition and decreased above 0.9 wt% ${La}_2{O}_3$addition. Electromechanical coupling factor( $K_{P}$) showed the maximum value at 0.2 wt% ${La}_2{O}_3$addition and decreased above 0.2 wt% ${La}_2{O}_3$ addition. Electromechanical coupling $factor{(K)}_P$, density, dielectric constant$(\varepsilon_\Gamma)$, piezoelectric constant$(d_33)$ and curie temperature$(T_C)$ showed optimum value of 0.40, 5.75 g/㎤, 768, 215 pC/N and 320 $^{\circ}C$ at 0.2 wt%${La}_2{O}_3$addition, respectively.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.261-268
• /
• 1991

The dielectric properties and microstructure of SrTiO3-based grain boundary layer (GBL) capacitor were investigated, and SrTiO3 GBL capacitor was made by penetrating the Frit (PbO-Bi2O3-B2O3 system). The Nb2O5-doped SrTiO3 ceramics were fired for 4-hours, at 145$0^{\circ}C$ in H2-N2 atomsphere to get semiconductive ceramics. The grain size of SrTiO3 sintered at reduction atmosphere had increased as the amount of Nb2O5 increases and then decreased as the amount of Nb2O5 exceeded 0.2 mole%. Insulating reagents which contained PbO-Bi2O3-B2O3 system frit and oxide mixture were printed on the each semiconductive ceramics and fired at varying temperature and for different holding time. The optimum dielectric properties could be obtained by second heat treatment at 110$0^{\circ}C$ for 1 hour, when frit paste was printed. A SrTiO3-based GBLC had the apparent permitivity of about 3.2$\times$104, the dielectric loss of 0.01~0.02 and the stable temperature coefficient of capacitance. The influence of frit paste on dielectric properties was similiar to that of oxide paste but the stability of temperature property of capacitance was improved.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.3
• /
• pp.123-128
• /
• 2006

The microstructure and electrical properties of the varistors, which are composed of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-La_2O_3-based$ ceramics, were investigated for different $La_2O_3$ contents. The increase of $La_2O_3$ content led to more densified ceramics, whereas abruptly decreased the nonlinear properties by incorporating beyond 1.0 mol%. The highest nonlinearity was obtained from 0.5 mol% $La_2O_3$, with the nonlinear coefficient of 81.6 and the leakage current of $0.2{\mu}A$. The increase of sintering time and temperature greatly decreased the nonlinear properties. As the $La_2O_3$ content increased, the donor density increased from $0.64\times10^{18}/cm^3\;to\;16.89\times10^{18}/cm^3$ and the barrier height greatly decreased with increasing $La_2O_3$ content, reaching a maximum (1.47 eV) in 0.5 mol% $La_2O_3$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.667-673
• /
• 1992

The alumina-zirconia composite powders of core particle ZrO2 coated with Al2O3 were prepared by the hydrolysis-deposition of the mixed aluminum salt solution of Al2(SO4)3-Al(NO3)3-Urea. The effects of hydrolysis reaction and coating parameters on characteristics of coated powders and composites were also investigated. The degree of coating could be estimated from the ratio of tetra-/mono-ZrO2 present at the room temperature after heat-treating coated powders at 120$0^{\circ}C$ and the result of TEM observations. When the content of ZrO2 in the dispersed coating system, the coating time, and the volume ratio of water/solution were 50 mg/g, 180 min, and 5, respectively the coating efficiency was maximum (the ratio of tetra-/mono-ZrO2 was 87/13). The relative densities of coated Al2O3-ZrO2 composites sintered at 1$650^{\circ}C$ for 4 hrs were about 91~98% and the maximum ratio of tetra-/mono-ZrO2 in Al2O3-20wt% ZrO2 composites was 62/38.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.117-121
• /
• 2000

Er-doped sodiumborosilicate glass films for waveguides amplifier were fabricated by Aerosol Flame Deposition(AFD) method. Al2O3 was added to sodium borosilicate glass films to suppress the formation of crystalline phase and control the refractive index. the formation of crystalline phase was suppressed above Al2O3 of 6 wt%. As the amount of Al2O3 increased from 2 to 12 wt% the refractive index of glass films increased lineary from 1.4595 up to 1.4710. After the core of 77SiO2-15B2O3-8Na2O＋6 wt%Al2O3＋8wt%Er2O3 was coated on the buffer layer of 77SiO2-15B2O3-8Na2O＋6 wt%Al2O3, the core was etched by reactive ion etching. The absorption spectrum of 3 cm waveguide amplifier showed two peaks of 1530 and 1550 nm.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1240-1246
• /
• 1994

While sintering the Pb(Mg1/3Nb2/3)O3-PbTiO3-BaTiO3 system through solid-reaction route, pyrochlore(Pb3Nb4O13) phase while reduces the dielectric constant is inevitably formed. Substitution of Pb(Mg1/3Nb2/3)O3 with PbTiO3 and BaTiO3 can retard the occurrence of pyrochlore phase. The perovskite solid-solution without containing pyrochlore phase can be obtained when we consolidated the materials consisting of PbTiO3 and BaTiO3 at 1200℃ for 2 hours. The sintered body composed of 0.8Pb(Mg1/3Nb2/3)O3-0.1PbTiO3-0.1BaTiO3 composition showed the diffused phase transition(DPT) phenomena and the maximum value of dielectric constant at 0℃ (Tc') with the value of 1.3×104.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2000.01a
• /
• pp.95-96
• /
• 2000

The effect of $Al_2O_3$ on the dielectric constant and the coefficient of thermal expansion of lead borosilicate glasses for the application of PDP glass paste was investigated. Measurements were made theoretically by using empirical equations on the composition of the of glasses in which the $PbO/Al_2O_3$, $B_2O_3/Al_2O_3$ and $SiO_2/Al_2O_3$ ratios were systematically varied. As a result, with increasing $PbO/Al_2O_3$ the thermal expansion coefficient and the dielectric constant noticeably increased, while the change of $B_2O_3/Al_2O_3$ and $SiO_2/Al_2O_3$ ratios did not affect those properties of the glasses.

• Journal of the Korean Ceramic Society
• /
• v.28 no.3
• /
• pp.215-224
• /
• 1991

The synthesis of SrTiO3 powders having high purity and homogeneous submicron particle size was attempted by the oxalate method. The microstructure and dielectric properties of SrTiO3 based boundary layer capacitor (BLC) were investigated. Strontium titanyl oxalate[SrTiO(C2O4)2.4H2O] was prepared from the mixing solution of (Sr, Ti) using oxalic acid(H2C2O4) as a precipitating agent at 8$0^{\circ}C$. The crystalline SrTiO3 powder was obtained by thermal decomposition of the precipitate above $600^{\circ}C$. The crystalline SrTiO3 powder containing Nb2O5 as a dopant, TiO2 and SiO2 as additives was sintered at 1360~144$0^{\circ}C$ in the reducing atmosphere to get semiconductive SrTiO3. Insulating material containing PbO-Bi2O3-B2O3 frit was printed on the sintered semiconductive SrTiO3 and fired at 120$0^{\circ}C$ for 2h to get the grain boundary diffusion.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.4
• /
• pp.425-431
• /
• 2007

[ $Al_2O_3/SiC$ ]composite ceramics were sintered to evaluate the bending strength and elastic wave characteristics. The three-point bending test was carried out under room temperature. The elastic wave was detected by fracture wave detector. The crack healing behavior was investigated from 1373 K to 1723 K. The bending strength of $Al_2O_3/SiC$ composite by nanocomposite is higher than that of $Al_2O_3$ monolithic. Crack-healing behavior depended on an amount of additive powder $Y_2O_3$. In $Al_2O_3/SiC$ composite ceramics with 3 wt. % $Y_2O_3$ for additive powder, the bending strength at 1573 K is about 100% increase than that of the smooth specimens. From the result of wavelet analysis of elastic wave signal, the smooth specimen and heat treated specimen of $Al_2O_3$ monolithic and $Al_2O_3/SiC$ composite ceramics showed characteristics of frequency about 58 kHz. The strength of $Al_2O_3/SiC$ composite ceramics was a little higher than those of $Al_2O_3$ monolithic. The dominant frequencies were high with increasing of $Y_2O_3$ for additive powder. The dominant frequencies had direct connection with the bending strength.