• The Journal of Advanced Prosthodontics
• /
• v.6 no.3
• /
• pp.224-232
• /
• 2014

PURPOSE. The purpose of the present study was to evaluate the effect of thermocycling and mechanical loading on the biaxial flexural strength and the phase transformation of one Ce-TZP/$Al_2O_3$ and two Y-TZP core materials. MATERIALS AND METHODS. Thirty disc-shaped specimens were obtained from each material. The specimens were randomly divided into three groups (control, thermocycled, and mechanically loaded). Thermocycling was subjected in distilled water for 10000 cycles. Mechanical loading was subjected with 200 N loads at a frequency of 2 Hz for 100000 times. The mean biaxial flexural strength and phase transformation of the specimens were tested. The Weibull modulus, characteristic strength, 10%, 5% and 1% probabilities of failure were calculated using the biaxial flexural strength data. RESULTS. The characteristic strengths of Ce-TZP/$Al_2O_3$ specimens were significantly higher in all groups compared with the other tested materials (P<.001). Statistical results of X-ray diffraction showed that thermocycling and mechanical loading did not affect the monoclinic phase content of the materials. According to Raman spectroscopy results, at the same point and the same material, mechanical loading significantly affected the phase fraction of all materials (P<.05). CONCLUSION. It was concluded that thermocycling and mechanical loading did not show negative effect on the mean biaxial strength of the tested materials.

• Journal of Technologic Dentistry
• /
• v.33 no.1
• /
• pp.15-23
• /
• 2011

Purpose: Thy yttria tetragonal zirconia polycrystalline(Y-TZP) is a good structural ceramic for dental restoration. But it have a problem that delamination of veneering ceramic from the Y-TZP core materials. The problem generally occur at the interface, thus this study was conducted to evaluate the interface of Y-TZP using scanning electron microscopy(SEM). Methods: To investigate this aspect, high-resolution SEM observations were made of polished and etched (HF content gel) cross-sections of the interface area. Dry and moist veneering porcelain powders were built up on the zirconia base. Results: The extent of this surface faceting is dependent upon the moisture content of the porcelain powder and the firing temperature. More moisture and higher final heating temperature accelerates the observed faceting of the Y-TZP grains at the interface to the veneering ceramic. Conclusion: These changes of the Y-TZP grains indicate that destabilization of the tetragonal phase of zirconia occurs at the interface during veneering with ceramic. It may result in a reduction of the stability of the zirconia and interface.

• Journal of Technologic Dentistry
• /
• v.42 no.3
• /
• pp.213-219
• /
• 2020

Purpose: This study aimed to identify the impact of physical surface roughing with a polishing tool onto the pre-sintering yttria-stabilized tetragonal zirconia polycrystals (TZP) core and liner treatment for chemical bonding on the bond strength of TZP core and veneering ceramic. Methods: Overall, 80 specimens were classified into two groups (non-liner, NL; and usingliner, UL ) depending on the use of liner, and these two groups were then subclassified into four groups depending on the polishing tool used. (1) Non-liner groups: NS, non-liner+stone point; NC, non-liner+carbide bur; NP, non-liner+paper cone point; NT, non-liner+silicon point. (2) Using-liner groups: US, using-liner+stone point; UC, using-liner+carbide bur; UP, usingliner+paper cone point; UT, using-liner+silicon point. The pre-sintering surface roughing values and shapes were observed, and after burning up the veneering ceramic, the shear bond strength was measured using a universal testing machine. For significance testing, a one-way analysis of variance and Tukey's multiple comparison test were conducted. An optical microscope was used to observe the fracture plane, and the following results were obtained. Results: Surface roughness NP (4.09±0.51 ㎛) represented a higher value than other groups (p<0.001). In shear bond strength, NS (35.21±1.44 MPa) of the NL group showed the highest bond strength (p<0.001). The UL group did not show a statistically significant difference between groups (p=0.612). Conclusion: Our study findings reveal that the bond strength of TZP core and veneering ceramic was improved by pre-sintering physical surface treatment than by chemical bonding with liner surface treatment.

• Journal of dental hygiene science
• /
• v.14 no.1
• /
• pp.29-34
• /
• 2014

The purpose of this study was to evaluate the influence of low temperature degradation (LTD) on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP). The push-shear bond test method was used to investigate the core-veneer bonding strength of industrially manufactured Y-TZP core ceramic and manufacturer recommended veneering ceramic. Four groups from ceramic-zirconia specimens (n=28; n=7 per group) were assigned into four experimental aging conditions, namely storage in an autoclave at $134^{\circ}C$ for 0, 3, 5, 10 hours. Bonding strength was obtained using a universal testing machine with crosshead speed 0.5 mm/min. Data were statistically analyzed using one-way ANOVA and Tukey's test (${\alpha}=0.05$). In bonding strength test, the group which was treated with LTD showed lower bonding strength than no treated group. The ceramic-zirconia bonding strength was affected by LTD (p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in LTD with treated Y-TZP groups.

• Journal of dental hygiene science
• /
• v.12 no.2
• /
• pp.123-129
• /
• 2012

The aim of study was to compare the color parameters and mean color difference of porcelain specimens by different veneering technique in order to examine the effect of veneering technique on esthetics of yttria-stabilized tetragonal zirconia polycrystalline(Y-TZP) all ceramic restoration. Three groups of square-shaped core ceramic specimens(14mm in diameter and 0.3, 0.5, 0.7 mm) and two groups of veneering ceramic specimen were prepared for analysis. Color parameter($L^*,a^*,b^*$) and color difference of zirconia core squares and core-veneer specimens were measured with ShadeEye $NCC^{(R)}$ spectrophotometer, respectively. Mean color difference(${\Delta}E^*$)were calculated using color difference formula. Two-way analysis of variance(ANOVA) combined with a Tukey multiple-range test were used to analysis the data(${\alpha}=0.05$). ${\Delta}E^*$ values were not significantly affected by core thickness and veneering porcelain(p=0.083). The color differences(${\Delta}E^*$) of core-veneer specimens with 0.5, 0.7 mm-A1,A2,A3.5 shade were mostly below 3.7 which was within the clinically acceptable range, while color differences between 0.3 mm-A1,A2 showed more than 3.7. All-ceramic system has color characteristics that clinicians have to consider when selecting materials. Also, manufacturers of different porcelain systems must make every effort to achieve color reproducibility.

• Journal of Technologic Dentistry
• /
• v.33 no.3
• /
• pp.193-202
• /
• 2011

Purpose: The aim of this study was to evaluate the effect of pre-treatment of core and hydrothermal treatment on the bond strength and flexural strength of ceramic veneered zirconia. Methods: 3Y-TZP specimens(KaVo Zr, $25mm{\times}3mm{\times}1mm$)were prepared by five pre-treatment methods and divided into seven groups including control two groups, subsequently the specimens veneered with the E-MAX ceram according to manufacturer's information(total specimen thickness 1.5mm). Two groups from ceramic-zirconia specimens(n=105, n=15 per group)were assigned into two experimental fatigue conditions, namely storage in an autoclave at $134^{\circ}C$ for 5h, thermo-cycling(3,000cycles, between 5 and $55^{\circ}C$, dwell time 45s, transfer time 2s). A flexural strength test was performed in a universal testing machine(crosshead speed: 0.5mm/min). Data were statistically analyzed using one-way ANOVA and Tukey's test(${\alpha}$=0.05). Results: The ceramic-zirconia bond strength value for liner application group(LLW, $27.3{\pm}3.8$) were significantly lower than those of the pre-treatment groups($30.72{\pm}5.3$). The ceramic-zirconia bond strength and zirconia flexural strength was not affected by thermo-cycling(p>0.05), whereas it was affected by storage in an autoclave at $134^{\circ}C$ for 5h(p<0.05). Conclusion: The results indicated that the ceramic-zirconia bond strength and zirconia flexural strength was affected by low temperature degradation.

• Journal of Technologic Dentistry
• /
• v.35 no.1
• /
• pp.19-27
• /
• 2013

Purpose: The aim of this research was to evaluate the shear bond strength of different zirconia veneering ceramics with and without liner glass materials to yttria partially-stabilized tetragonal zirconia polycrystalline(Y-TZP). Methods: Five co mmercial zirconia veneering ceramics were used in this study, E-Max(EM), Creation ZI(CR), Cercon ceram kiss(CE), Triceram(TR) and Zirkonzahn ICE(ZI). All samples were prepared according to manufacturer's instructions. Experimental industrially manufactured Y-TZP ceramic blocks(diameter: 2.7 mm; height: 13.5 mm) were used in this study. Shear bond strength between zirconia ceramic coping and zirconia veneering ceramics were evaluated by the push-shear bond test. The fracture load data were analyzed using ANOVA and Scheffe's test(${\alpha}$=0.05). The fractured surfaces of zirconia core ceraimc and zirconia veneering ceramics were observed using a scanning electron microscope(SEM). Results: The mean shear bond strengths ranged from 20 MPa ($20.12{\pm}6.34$ MPa) to 66.6 MPa ($66.62{\pm}10.01$ MPa). The Triceram(TRG) showed the highest value and Creation ZI(CR) showed the lowest value. In all groups, Zirconia liner and glass material groups was significantly higher shear bond strength than without liner(P<0.05), with the exception of Cercon ceram kiss(CE)groups. Conclusion: Zirconia bonding materials may have the advantage of improved bond strength between zirconia ceramic core and veneering ceramics.

• Journal of dental hygiene science
• /
• v.13 no.3
• /
• pp.290-295
• /
• 2013

The purpose of this study was to investigate the shear bond strength between various commercial all-ceramic system core and veneering ceramics, and evaluate the clinical stability by comparing the conventional metal ceramic system. The test samples were divided into three groups: Ni-Cr alloy (metal bond), yttria-stabilized, tetragonal zirconia polycrystal (Y-TZP) (zirconia bond), lithium disilicate (lithium disilicate bond). The veneering porcelain recommended by the manufacturer for each type of material was fired to the core. After firing, the specimens were subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.50 mm/min until failure. Average shear strengths (mega pascal) were analyzed with a one-way analysis of variance and the Tukey test (${\alpha}$=0.05). The mean shear bond strength${\pm}$SD in MPa was $44.79{\pm}2.31$ in the Ni-Cr alloy group, $28.32{\pm}4.41$ in the Y-TZP group, $15.91{\pm}1.39$ in the Lithium disilicate group. The ANOVA showed a significant difference among groups (p<0.05). None of the all-ceramic system core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.5
• /
• pp.415-422
• /
• 2014

PURPOSE. The purpose of this study was to evaluate and compare the translucency of shaded zirconia allceramic systems. MATERIALS AND METHODS. Translucency of 3 different zirconia all-ceramic systems colored by different techniques was compared with a lithium disilicate glass-ceramic (IPS e.max Press). Square-shaped specimens with 0.5 mm thickness were fabricated from In-Ceram YZ, ICE Zirkon and Katana systems in A1, A2 and A3.5 shades according to Vitapan Classical shade tab (n=11). Specimens were then veneered and glazed with corresponding veneer ceramic recommended by each zirconia system manufacturer and the total thickness was set to 1.5 mm. Translucency measurements were performed with VITA Easyshade Compact spectrophotometer after each stage and translucency parameter was calculated. Data were statistically analyzed with repeated measures ANOVA and Tukey multiple comparison test. RESULTS. The control group was significantly more translucent than the zirconia systems (P<.05). ICE Zirkon cores showed the least translucency; neither In-Ceram YZ nor Katana systems were superior to each other in terms of translucency. Translucency of all specimens was decreased after veneering, and the translucency rankings were changed. CONCLUSION. Coloring technique did not have a significant effect on translucency of zirconia cores. Although zirconia systems were less translucent than lithium disilicate glass ceramic, they had partial translucency and there were translucency differences among the zirconia systems. Chroma affected the translucency of precolored zirconia cores.

• The Journal of the Korea Contents Association
• /
• v.15 no.9
• /
• pp.384-394
• /
• 2015

The purpose of this study was to evaluate the push-shear bond strength between five commercial zirconia veneering ceramics and zirconia core cylinder, and to investigate the effect of biaxial flexural strength and zirconia liner glass treatments. The biaxial flexural strengths of the veneering ceramics were evaluated by a piston-on-three-ball test. The bond strengths between the Y-TZP cylinder and zirconia veneering ceramics were evaluated using the push-shear bond strength test. The data was analyzed using two-way ANOVA and Scheffe's test. The biaxial flexural strength of Cercon ceram kiss (CE) was higher than those of the other groups. The glass-treated and Triceram zirconia groups showed the highest value and the Creation ZI(CR) showed the lowest. In all groups, the liner glass treatment groups showed significantly higher push-shear bond strength than those without(P<0.05). The liner glass treatments of zirconia can improve the bond strength between the zirconia ceramic core and veneering ceramics.