• Journal of Welding and Joining
• /
• 제3권2호
• /
• pp.35-41
• /
• 1985

The fracture toughness of subcritical HAZ in the hot strained weldments of two structural steels(SB 41 and SA 537) has been investigated by COD test method and metallurgical study. The obtained results are summarized as follows; 1. The hot straining embitterment of subcritical HAZ depends on the hot straining amounts of notch tip, and the transition temperature( $T_{tr}$ ) increases with the accumulated hot straining amounts(.SIGMA. vertical bar .delta.$_{t}$vertical bar). 2. The fracture toughness of subcritical HAZ depends on materials and microstructure. The transition temperature( $T_{tr}$ ) of subcritical HAZ in SB 41 is almost same as that of parent material, however in SA 537 the temperature is higher than that of parent and lower than that of transformed HAZ. 3. The subcritical HAZ in SA 537 shows a higher toughness at small amounts of hot straining (.SIGMA. vertical bar .delta. $_{t}$vertical bar<0.3mm).mm).

• Journal of Welding and Joining
• /
• 제16권4호
• /
• pp.83-91
• /
• 1998

Cracking problems which high temperature plant components suffer during long-term service, occur very often at welded locations. The crack occurs due to accumulated creep damage near fusion line or at heat affected zone (HAZ). However, most of the studies on creep crack growth behavior have been performed with matrix metal not wit welded metal due to the difficulty of interpreting the test results. In this study, creep crack growth rates were measured with C(T) specimens whose cracks were formed along the fusion line or HAZ. The measured crack growth rates were characterized by {TEX}$C_{t}${/TEX}-parameter derived for elastic-primary-secondary creeping material. Since contribution of primary creep was significant for the tested 1Cr-0.5Mo steel, its effect was carefully studied. Effects of crack tip plasticity and material aging were also discussed.

• Journal of Welding and Joining
• /
• 제18권5호
• /
• pp.41-48
• /
• 2000

Dynamic behaviors of the GMAW system are simulated using the short-circuit transfer model and the characteristic equations fir the power supply, wire system and arc. The conventional wire equation, which relates the rate change of the wire extension to the wire feed rate and melting rate, is modified to include effects of the molten drop attached at the wire tip. The modified wire equation describes behaviors of the GMAW system more precisely and provides information about the initial bridge volume for short-circuit transfer. The proposed short-circuit model predicts the variation of parameters such as the current, voltage, short-circuit frequency and time considering the effects of the surface tension and electromagnetic force due to current. The calculated results are in broad agreements with the experimental results under the argon shielding condition.

• Journal of Welding and Joining
• /
• 제7권3호
• /
• pp.55-62
• /
• 1989

Variation of the spray droplet velocity with spraying distance and the microstructural characteristics of spray deposits fromed by oxy-fuel thermal spraying with Ni-base alloy powder contained chrome boride for hard facing were examined. Measurements of spray droplet velocity as a function of distance from the nozzle tip were inexcellent agreement with computer simulated predictions. Optimum condition for thermal spray deposits in this experiment was found to be under #10kg/cm^2$ of acceleration gas pressure with 15cm of spraying distance. Fine microstructure and higher microhardness of the initial part of the deposits due to rapid solidification were found to be able to maintained in a thickness up to 0.4mm, and this initial microstructure and properties could be maintained throughout the thickness of a thick spray deposits by performing the multipass spraying with 0.4mm thickness of each pass.

• Journal of Welding and Joining
• /
• 제17권2호
• /
• pp.36-43
• /
• 1999

The effect of microstructure on the fracture toughness of multi pass weld metal has been investigated. The micromechanisms of fracture process are identified by in-situ scanning electron microscopy(SEM) fracture observation using single edge notched specimen. The notches of the in-situ fracture specimens were carefully located such that the ends of the notches were in the as-deposited top bead and the reheated weld metal respectively. The observation of in-situ fracture process for as-deposited top bead indicated that as strains are applied, microcracks are formed at the interfaces between soft proeutectoid ferrite and acicular ferrite under relatively low stress intensity factor. Then, the microcracks propagate easily along the proeutectoid ferrite phase, leading to final fracture. These findings suggest that proeutectoid ferrite plays an important role in reducing the toughness of the weld metal. On the other hand, reheated regions showed that the microcrack initiated at the notch tip grows along the localized shear bands under relatively high stress intensity factor, confirming that reheated area showing momogeneous and fine microstructure would be beneficial to the fracture resistance of weld metal.

• Journal of Welding and Joining
• /
• 제5권2호
• /
• pp.44-52
• /
• 1987

The fracture toughness, $J_{IC}$ of high frequency electric resistance welded steel pipe for smooth and side-grooved CT specimen was evaluated by unloading compliance method. The crack growth, .${\delta}a$ was obtained from the equation of Donald and Saxena & Hudak, and $J_{IC}$ was determined from the curve of J-${\delta}a$ relations. The crack growth on the experiment using unloading compliance method is underestimated as compared with ${\delta}a$ measured directly by the SEM, so the reliability of $J_{IC}$ from saxena & Hudak equation is large than that from Donald. The $J_{IC}$ value of side-grooved CT Specimen is estimated less than that of smooth, and this is the effect of the side-groove, the shear-lip of crack tip and the reduction of crack tunnelling phenomena.

• 대한기계학회논문집A
• /
• 제26권2호
• /
• pp.300-307
• /
• 2002

Partial penetration welding joint is defined as groove welds welded from one side, without steel backing or groove welds welded from both sides but without back gouging. So it has an unwelded portion at the root of the weld. Study of partial penetration weldment fracture behavior includes residual stress analysis and fracture analysis. The J-integral loses its path independency in residual stress field. Therefore, it is necessary to introduce a new J-integral, J, which is defined including the effect of plastic deformation and thermal strain. In this study, theoretical formulation and program were developed for the evaluation of J-integral for the crack tip located in the weldment. Evaluations of fracture behavior were performed for partial penetration multi-pass weldment of 25.4mm thick plate by J-integral. From a point of fracture in partial penetration multi-pass welding, it seemed to be better to control root face smaller than 6.35mm.

• Journal of Welding and Joining
• /
• 제21권1호
• /
• pp.72-79
• /
• 2003

Fatigue behaviour of partially penetrated butt-welded joints in high strength steel plates, in which crack-like structural defect, i.e. lack of penetration(LOP), is inevitably introduced during welding processes, was investigated. Fatigue lives of two types of welded joints, namely X-grooved and K-grooved joints, were experimentally determined first. Observed fatigue crack propagation behaviours of the partially penetrated butt-welds were interpreted through considering 3-dimensional semi-elliptical crack shape in front of the LOP. Based on such interpretation, a fracture mechanical method to estimate stress intensity factors at the crack tip was proposed. Since the fatigue lift of the partially penetrated butt-welds was strongly influenced by the ratio of size of the LOP to thickness, D/t, the D/t was used as a main parameter to calculate the fatigue lift by using the proposed method. Comparison of the fatigue lift obtained experimentally and analytically agreed well with each other. Hence it is suggested that the method used in this work to predict fatigue lift of the partially penetrated butt-welds can be applied to real cases with improved lift-prediction capability.

• 대한기계학회논문집
• /
• 제7권3호
• /
• pp.313-318
• /
• 1983

It is required in designing a spot welding to get in advance an estimated figure of nugget diameter. A method of estimating nugget diameter of low carbon steel sheets is suggested in tesms of utilizing elastic calculation in theory and of making a sectional observation of specimen of spot welding in experiment. The resultant findings are summarized as follows: 1) A contact diameter of sheet, 2.gamma.$_{o}$=d sub e/+(1.1)t, wheer de is the electrode tip diameter and t is the thickness of sheets. 2) The practical measurement of the nugget diameter reveals that $d_{n}$=(1.05) $d_{e}$+(0.9)t, and $d_{b}$ is less by 0.8-4.3% than 2.gamma.$_{o}$. 3) The more $d_{n}$ is as compared with t, the less the difference between a theoretical value and an experimental value is. 4) In the spot welding of thin steel sheets less than 3mm in thickness that are commonly used in sheet metal works, the contact diameter equals the nugget diameter. In this case, either the theoretical or experimental approach can be used for estimating the nugget diameter.meter.ter.r.

• Journal of Welding and Joining
• /
• 제21권6호
• /
• pp.77-83
• /
• 2003

The finite element analysis was performed for the cracks existing in residual stress fields in order to investigate the effects of configuration of residual stress distribution to the fatigue crack opening behaviour. And the variation of stress distributions adjacent to the crack caused by uploading was examined. The finite element model with contact elements for the crack plane and plane stress elements for the base material and the analytical method based on the superposition principle to estimate crack opening behaviour and the stress distribution adjacent to the crack subjected to uploading were used. The results of the analysis showed that crack opening behaviors and variations of stress distribution caused by uploading were changed depending on the configuration of residual stress distribution. When the crack existed in the region of compressive residual stress and the configuration of compressive residual stress distribution were inclined, a partial crack opening just behind of a crack tip occurred during uploading. Based on the above results, it was clarified that the crack opening behaviour in the residual stress field could be predicted accurately by the finite element analysis using these analytical method and model.