• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.95-95
• /
• 2009

Zinc coatings provide the most effective and economical way of protecting steel against corrosion. There are three types of galvanizing lines typically used in production line in galvanizing industries,Galvanize (GI) coating (Zn-0.1-0.3%Al), Galfan coating (Zn-5%Al), Galvalume(GL) coating (45%Zn-Al). In continuous Galvanizing lines, the immersed bath hardware (e.g. bearings, sink, stabilizer, and corrector rolls, and also support roll arms and snout tip) are subjected to corrosion and wear failure. Understanding the reaction of these materials with the molten Zn alloy is becomes scientific and commercial interest. To investigate the reaction with molten Zn alloys, static immersion test performed for 4, 8, 16, and 24 Hr. Two different baths used for the static immersion, which are molten Zn and molten Zn-55%Al. Microstructures characterization of each of the materials and intermetallic layer formed in the reaction zone was performed using optical microscope, SEM and EDS. The thickness of the reaction layer is examined using image analysis to determine the kinetics of the reaction. The phase dominated by two distinct phase which are eutectic carbide and matrix. The morphology of the intermetallic phase formed by molten Zn is discrete phase showing high dissolution of the material, and the intermetallic phase formed by Zn-55wt%Al is continuous. Aluminum reacts readily with the materials compare to Zinc, forming iron aluminide intermetallic layer ($Fe_2Al_5$) at the interface and leaving zinc behind.

• Korean Journal of Metals and Materials
• /
• v.48 no.4
• /
• pp.297-304
• /
• 2010

The microstructure and hardness of $CO_2$ laser welds were investigated in the Ti-stabilized ferritic stainless steel 409L. The observed specimen was welded in a fully penetrated condition in which the power was 5 kW and the welding speed 5 m/min. The grain structure near the bond line of the laser welds was produced by epitaxial growth. The grain size was the largest in the fusion zone, and HAZ showed nearly the same grain size as that of the base metal. The HAZ microstructure consisted of subgrains and precipitates that were less than 100 nm in size and that were located along the subgrain boundaries. On the other hand, the hardness was the highest in the fusion zone due to the large amount of small precipitates present. These were composed of TiN, Ti(C,N) and $TiO_2$+Ti(C,N). The hardness decreased continuously from the fusion zone of the base metal. The HAZ hardness was slightly greater than that of the base metal due to the existence of subgrains and precipitates in the subgrain boundary.

• Journal of the Korean Society of Safety
• /
• v.32 no.3
• /
• pp.15-20
• /
• 2017

This study presented the strength of the materials and parts for smart distribution board fabrication, and developed a work operation process chart for smart distribution board fabrication. This work operation process chart for smart distribution board fabrication complied with SPS-KEMC regulations, and the applicable range and object are less than 1,000 V and 1,000 Hz for the AC distribution board and less than 1,500 V for the DC distribution board. The power supply is 3 phase 4 wires ($3{\Phi}$ 4W), divided into a single phase circuit and a 3 phase circuit. In addition, the circuit was configured so that the leakage current flowing through the distribution line of the load could be monitored in real time by using the sensor module installed at the rear end of the circuit breaker. Therefore, the administrator can easily find the risk factor of the load since engineer can check the leakage current of each distribution line. In addition, if a leakage current greater than standard value flows, it is possible to generate an alarm against a short circuit and cut off the leakage current. The work operation process chart for the smart distribution board fabrication consists of the following steps: raw and subsidiary materials, sheet metal work, tube making, welding, painting, busbar fabrication, assembly and wiring, product inspection, shipment, etc. Moreover, symbols, ${\Delta}$, ${\nabla}$, ${\bigcirc}$, ${\Rightarrow}$, etc. were used according to the type of work and work progress so that workers can easily understand the progress of the work.

• Journal of the Korean Professional Engineers Association
• /
• v.15 no.4
• /
• pp.12-24
• /
• 1982

East Parts of Bangladesh have been benifited by low cost energy generated by domestic natural gas but West parts where energy generated by imported fuel. Bangladesh Government authority has very much concerned to transmit the low cost electricity to the West from the East for past several years. To solve such concerns, cross-country 230kv double circuits Power transmission line was proposed, however there was a big obstacle for the realization of this line to cross the Jamuna river which has 12 km long width with a deep muddy river bed. A consultant engineering firm named Merz-Mclellan anyway finalized this plan and a world-wide bid was announced on June 31, 1979. Due to the expected difficulty to construct the towers on sea like area, only three construction groups have participated. including a Korean joint venture organization of Samsung-Korean Developement corporation-Kolon Electric Machinery company. After 3 months bid evaluation, contract was awarded to Korean Consosium and KEM Co was in charge of designing steel towers with anchor bolts and base plates beside to electrical engineering field. Then KEM Co have faced and over-comed many unenpected technical difficulties such as forced eccentricity joint on base plate, distorsion issue of 60mm thick plates welding, threading anchor bolts, tad heat treatment of some anchor bolts, disagreement from Consultant Engineer on multiplying factor of leg stresses for 45$^{\circ}$ wind and on reducing O.L.F for wind loads on cables for such 1220km long spans. After spending two years long period for designing and engineering towers, base plates, and anchor bolts, first shipment of tower was finally realized on Nov. 8, 1981 and on the other hand KDD has proceeded concrete caisson work on schedule at Jamuna river site and expected to complete tower erection and stringing of cables within this year of 1982 which was original completion target.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.12
• /
• pp.1317-1323
• /
• 2014

The aim of this paper is to investigate the effects of crack orientation on fatigue crack growth behavior in friction stir welded (FSWed) Al 7075-T651. Fatigue crack growth testing was conducted on compact tension (CT) specimens machined from the friction stir welds and the base metal under constant stress intensity factor range control. Tests were performed with the crack propagating nominally perpendicular to the weld line (termed the TL specimen) and the crack propagating in a parallel direction of the weld line (termed the LT specimen), and with three different constant stress intensity factor ranges. Both these specimen orientations were found to have a considerable effect on the fatigue crack growth behavior. Paris's law was adopted for the analysis of experimental results; the exponent m of the WM-LT specimen was determined to be 3.56, which was the largest value in this experimental conditions.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.58-58
• /
• 2009

선박의 선체부분인 선수, 선미 등을 이루고 있는 곡형 외판의 제작은 강판을 원하는 형상으로 성형하기 위하여 벤딩롤러 및 유압프레스를 이용한 냉간가공과 산소-프로판가스 화염을 적용한 선상가열, 삼각가열을 이용한 열간가공으로 크게 구분할 수 있다. 선상가열을 이용한 곡면가공의 원리는 가열토치를 이용하여 강판을 가열하면 가열부는 팽창하게 되고 냉각시에는 수축하게 된다. 이 때 두께방향으로의 소성변형으로 인한 수축량의 차이로 인해 굽혀지게 된다. 최근에는 선박이 고기능 및 대형화로 인해 3차원 곡형 외판 형상이 복잡해지고, 강도를 향상시키기 위하여 합금원소(C, Nb, V, Ti)를 첨가하거나 열처리(노말라이징)를 이용한 고장력강재인 중후판의 적용이 증가하고 있다. 이러한 고강도강재를 선상가열공정으로 제작한 곡형 외판재는 가열, 냉각의 열사이클로 인해 취화되어 인성이 저하 될 수 있다. 본 연구에서는 Normalizing 열처리재인 490MPa급 강재를 이용하여, 현장에서 작업자의 미숙련으로 인해 발생 할 수 있는 최대의 가혹한 조건과 재질에 큰 영향을 미치지 않는 범위를 선정하여 선상가열시의 가열, 냉각조건에 따른 강재의 재질특성을 조사하고자 한다. 이를 위해 가열시 가열부위의 정확한 온도 측정에 역점을 두었으며, 각각 다른 선상가열 조건에 따른 시편을 제작하기 위하여 선상가열 실험장치를 제작하였다. 선상가열 실험 결과 최고가열온도 $1300^{\circ}C,\;950^{\circ}C$에서 수냉 조건인 경우 급격한 인성저하 현상이 발생하며 비록 공냉이라 하더라도 결정립 조대화로 인성 저하가 발생하였다. $800^{\circ}C$가열 후 수냉개시온도를 $700^{\circ}C$이하로 수냉한 경우에는 인성 저하 현상이 개선되고 있음을 알 수 있다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.10
• /
• pp.346-351
• /
• 2018

Metal three-dimensional (3D) printing technologies are mainly classified as powder bed fusion (PBF) and direct energy deposition (DED) methods according to the method of application of a laser beam to metallic powder. The DED method can be used to fabricate fine and hard 3D metallic structures by applying a strong laser beam to a thin layer of metallic powder. The PBF method involves slicing 3D graphics to be a certain height, laminating metal powders, and making a 3D structure using a laser. While the DED method has advantages such as laser cladding and metallic welding, it causes problems with low density when 3D shapes are created. The PBF method was introduced to address the structural density issues in the DED method and makes it easier to produce relatively dense 3D structures. In this paper, thin lines were produced by using PBF 3D printers with stainless-steel powder of roughly $30{\mu}m$ in diameter with a galvano scanner and fiber-transferred Nd:YAG laser beam. Experiments were carried out to find the optimal conditions for the width of a line depending on the processing times, laser power, spot size, and scan speed. The optimal conditions were two scanning processes in one line structure with a laser power of 30 W, spot size of $28.7{\mu}m$, and scan speed of 200 mm/s. With these conditions, a minimum width of about $85.3{\mu}m$ was obtained.

• Proceedings of the KWS Conference
• /
• 1997.05a
• /
• pp.65-68
• /
• 1997

Fracture behavior of ex-serviced 1Cr-0.5Mo steel was measured at room(24$^{\circ}C$) and elevated(538$^{\circ}C$) temperature and compared with that measured with virgin 1Cr-0.5Mo steel. Compact C(T) specimens were machined from the base and welded test materials. In case of the C(T) specimens of the weld, fatigue precrack was introduced along the fusion line so that a crack growth should occur along the region of heat affected zone. It was observed that the J-R curve of the serviced material was significantly lower than that of the virgin material at room temperature. Brittle fracture was observed in the serviced material. On the other hand at elevated temperature no noticeable difference was found between the J-R curves of the virgin and the serviced material. The measured J-R curves were also compared with those of the 1.25Cr-0.5Mo steel from other literatures. Optical microscopy and SEM examination of the serviced material reveal the carbide in/along the grain boundary which shows material degradation due to long-term usage.

• Transactions of Materials Processing
• /
• v.7 no.1
• /
• pp.66-71
• /
• 1998

The present study is concerned with the hydrostatic extrusion process of copper-clad aluminium bar to investigate the bonding conditions as well as the basic flow characteristics. Considering the bonding mechanism of bi-metal contact surface as cold pressure welding the normal pressure and the contact surface expansion are selected as process parameters governing the bonding conditions, in this study the critical normal pressure required for the local extrusion-the protrusion of virgin surfaces by the surface expansion at the interface-is obtained using a slip line method and is then used as a criteron for the bonding. A rigid plastic finite element method is used to analyze the steady state extrusion process. The interface profile of bi-metal rod is predicted by tracking the paths of two particles adja-process. The interface profile of bi-metal rod is predicted by tracking the paths of two particles adja-cent to interface surface. The contact surface area ration and the normal pressure along the interface are calculated and compared to the critical normal pressure to check bonding. It is found that the model predictions are generally in good agreement with the experimental observations. The compar-isons of the extrusion pressure and interface profile by the finite element with those by experi-ments are also given.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.1
• /
• pp.127-137
• /
• 1987

The evaluation of the elastic-plastic fracture toughness $J_{1C}$ was performed on the center of weld metal(CWM), the heat affected zone (HAZ) and the base metal (BM) of API 5LB steel pipes welded by the high frequency electric resistance welding. The $J_{1C}$ was evaluated by the JSME R-Curve and JSME SZW methods using the smooth and side-grooved specimens. The results are as follows; (1) The $J_{1C}$ values by the SZW method are overestimated as compared with those by the R-curve method, because the micro-crack is formed as SZW increase with the deformation at SZ after initiation of the ductile crack. (2) The everage of $J_{1C}$ values by the the R-curve and the SZW methods in side-grooved specimens tended to decrease in comparison with smooth specimens 9.42% at CWM, 4.2% at HAZ, 23.2% at BM, respectively. (3) The boundary of the fatigue pre-crack, stretched zone, and dimple regions appeared more clearly in side-grooved specimens, for the slight change of SZW in the direction of the plate thickness, as compared with smooth specimens.