• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.107-114
• /
• 2011

CP steel was developed to reduce the weight and increase the strength of car body. When it was welded using state-of-the-art disk laser welding, the effected of boron on the microstructure and hardness were investigated. Welding power was fixed at 3.5kW and welding speeds were 4,8 and 12m/min. Full penetration occurred in welding speed of 12m/min and weld bead was almost unchanged with boron contents. But the welding speed increased, the upper and lower bead were narrowed. In a welding speed of more than 8m/min, underfill defects were formed on the bead bottom. The hardness of weld zone was somewhat fluctuation in fusion zone and HAZ showed the highest hardness values. The hardness of each region showed little change with the boron contents, and softening phenomenon occurred in the HAZ near the base metal regardless of the boron contents.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.8 no.3
• /
• pp.224-231
• /
• 1984

Having found by means of a tension-shear test an optimal spot welding condition under which the maximum weld strength is to be brought forth, this study made an examination of behavior of fracture concerned with behavior of stress distribution, observed around the nugget periphery of the specimens prepared under the optimal conditions, with one point spot welded mild steel sheets. The resultant findings are as follows: (1)There remarkably exists an optimal spot welding condition to indicate the maximum weld strength, and fracture of the specimens spot welded under that condition occurs outside the nugget boundary. (2)An experiment on the basis of a photoelastic model reveals that the maximum stress is distributed along the center line of the steel plate width but occurs on the region corresponding to heat affected zone of spot welds. (3)Heat affected zone of spot welds consists of coarse grains with considerably low micro Vickers hardness value and of fine grains of high micro Vickers hardness value, and in this unbalanced structure weak region are represented in coarse grain region, where fracture is initiated and continues its propagation.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1999.10a
• /
• pp.339-344
• /
• 1999

For the Tailor Welded Blank sheet used for automobile body panel, the characteristics of fatigue strength and crack propagation behavior were studied. The thickness of specimen was machined to be same (0.9mm+0.9mm) and different (0.9mm+2.0mm). As a base test, mechanical properties around welding zone were examined. The results indicated that there were no significant decreases in mechanical properties, but hardness around welding bead is 2.3 times greater than base material. The fatigue strength was the highest when the loading direction was parallel to the welding direction, which was about 85% of tensile strength of base material. It was decreased by 8.5% when the thickness of specimen and base material was different, and it is increased by 25% when pre-strain was applied. The crack propagation rate was noticeable decreased around welding line and rapidly increased as it passed by welding line. Reviewing the shape of the crack propagation, crack width around welding line was wide around the welding zone due to retardation of crack growth, but it became narrow passing welding line due to decreased toughness.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2004.10a
• /
• pp.40-48
• /
• 2004

The object of this study is to investigate the effect of joinability by using acoustic emission (AE) signals and doing a pattern recognition for weld heat affected zone (HAZ) in tensile testing. This study was carried out an SWS 490A high tension steel for electric shielded metal arc welding (SMAW), $CO_2$ gas arc welding and TIG welding. And correspondingly, the root openings are 3, 4 and 2.8mm. The results of the tensile test of weld HAZ come out electric shield arc welding > $CO_2$ gas arc welding > TIG welding in case of single welding. It is believed that this is a phenomenon where difference of its root opening or base metal thickness. Also, the technique of AE is ideally suited to study variables which control time and stress dependent fracture or damage process in metallic materials.

• Journal of Welding and Joining
• /
• v.3 no.2
• /
• pp.42-51
• /
• 1985

The dynamic fracture toughness, fracture characteristics, impact tension and tensile properties of Al-Mg-Si T5 alloy and Al-Zn-Mg T6 alloy respectively welded with filler metal of Alcan 4043 were investigated. The dynamic fracture toughness values were obtained rapidly and simply for the specimen of small size by using instrumented Chirpy impact testing machine. the testing temperatures of the specimen were a range of room temperature and-196.deg. C. The results obtained in this experiment are summarized as follows. With decreasing the testing temperatures, dynamic tensile stress and fracture load were increased, on the other hand the deflection and impact value showed decreasing tendency in order of base metal>HAZ>weld. Changes of total absorbed energy were more influenced by the crack propagation energy than the crack initiation energy. At the low temperatures, the unstable rapid fracture representing the crack propagation appeared for the specimens of Charpy press side notched in Al-Zn-Mg alloy, but it was difficult to obtain the unstable rapid fracture in Al-Mg-Si alloy. Because of the development of plastic zone at the notch root, it was difficult to obtain thevalid $K_{1d}$ value in Al-Mg-Si alloy. Therefore the fatigue cracked specimens were effective in both Al-Mg-Si and Al-Zn-Mg alloys. With decreasing the impact testing temperatures, specimens underwent a transition from dimple-type transgranular fracture to lamella surface-type intergranular fracture because of the precipitate at the grain boundaries, impurities and crystal structure of the precipitates.s.

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.4
• /
• pp.212-219
• /
• 2001

The fatigue test was carried out to evaluate the fatigue characteristics of fire resistance steel for frame structure and heat affected zone (HAZ) by the one side Gas Metal Arc Welding (GMAW). In this paper, the fatigue crack growth behavior was investigated with the compact tension specimen of base metal and the HAZ according to chemical composition and rolling end temperature, respectively. And the acoustic emission signals obtained from the fatigue test were analyzed by the time-frequency analysis method as a nondestructive evaluation. Main results obtained are summarized as follows; The hardness was appeared softening phenomenon that weld metal and HAZ are lower than that of base metal. Fatigue life of welded specimen was longer than that of base metal. m was 3~4.5 in base metal and 3.8~5.8 in HAZ. The main frequency range of acoustic emission signal analyzed from time-frequency method is different with the range by noise and crack. Also, it could be classified that it was also generated by fracture mechanics of dimple, inclusion etc.

• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.294-299
• /
• 2010

Two types of welding methods were performed on austenitic 304 stainless steel: laser welding and TIG welding. The differences of the corrosion characteristics of the welded zones from the two welding methods were investigated with electrochemical methods, such as measurement of the corrosion potential, polarization curves, cyclic voltammogram, etc. The vickers hardness of all laser-welded zones (WM:Weld Metal, HAZ:Heat Affected Zone, BM:Base Metal) was relatively higher while their corrosion current densities exhibited a comparatively lower value than those which were TIG welded. In particular, the corrosion current density of the TIG-welded HAZ had the highest value among all other welding zones, which suggests that chromium depletion due to the formation of chromium carbide occurs in the HAZ, which is in the sensitization temperature range, thus it can easily be corroded with an active anode. Intergrenular corrosion was also observed at the TIG-welded HAZ and WM zones. Consequently, we can see that corrosion resistance of all austenitic 304 stainless steel welding zones can be improved via the use of laser welding.

• Journal of Welding and Joining
• /
• v.28 no.2
• /
• pp.60-65
• /
• 2010

Although two dimensional axi-symmetric modeling is useful for calculating the residual stresses of a cylindrical weldment such as a core barrel, this conventional axi-symmetric modeling can not express the behavior of shrinkage well in the locally heated weld zone. New technique of two dimensional axi-symmetric modeling using a virtual fixture is suggested to simulate the behavior of dimensional changes in the weld zone during the heating period of the welding. The virtual fixture in the model has a role to restrain the expansion of the high temperature heated region, which simulates equivalent intrinsic restraint effect of the weldment. In the restraint condition of the virtual fixture above the critical yield strength, the calculated shrinkages by using the suggested axi-symmetric model agreed well with those measured in a welded mock-up. The calculated residual stresses by using the suggested axi-symmetric model also agreed well with those calculated by using conventional axi-symmetric model which has beenused for calculating residual stresses in the weldment.

• Transactions of Materials Processing
• /
• v.27 no.5
• /
• pp.296-300
• /
• 2018

T-type and H-type section steels were generally used in shipbuilding and offshore plants and were produced by welding technology. These section steels were produced by handwork, and the supplying amounts can't satisfy the demand amounts of the fabrication companies. In case of fillet welding, there are some gaps in weld-joint region due to no groove preparation processing and it can occur crack initiation in the welded region. It is important to evaluate the microstructural and mechanical properties of welded zone to solve these problems. To satisfy the demand amounts of T-bar parts, automatic welding technology was introduced and several conditions as a function of welding speeds were carried out to improve the manufacturing speed. Heat-affected zone may be affected by variation of heat input and cooling rate through automatic welding speed and welding speed is necessary to be optimized. In this study, fusion zone and heat-affected zone were investigated by microstructural and mechanical analysis and were evaluated whether the welded parts were sound or not.

• Journal of Welding and Joining
• /
• v.23 no.5
• /
• pp.61-68
• /
• 2005

Dissimilar joining of Al 6013-T4 alloys and austenite stainless steel was carried out using friction stir welding technique. Microstructures near the weld zone and mechanical properties of the joint have been investigated. Microstructures in the stainless steel side were composed of the heat affected zone and the plastically deformed zone, while those in the Al alloy side were composed of the recrystallized zone including stainless steel particles, the thermo-mechanically affected zone and the heat affected zone. TEM micrographs revealed that the interface region was composed of the mixed layers of elongated stainless steel and ultra-fine grained Al alloy with lamella structure and intermetallic compound layer. Thickness of the intermetallic layer was approximately 300nm and was identified as the A14Fe with hexagonal close packed structure. Mechanical properties, such as tensile and fatigue strengths were lower than those of 6013 Al alloy base metal, because tool inserting location was deviated to Al alloy from the butt line, which resulted in the lack of the stirring.