• Journal of Welding and Joining
• /
• v.1 no.1
• /
• pp.37-46
• /
• 1983

This paper describes a study of fillet welded joint stressed perpendicular to the weld line. The finite element method was used to determine the stress intensity factor for cruciform joint at weld toe and root cracks according to variation of H/Tp, weld angle and main plate thickness. But, in this study, weld angle was fixed at 45.deg., since the variation of weld angle affect the stress intensity factor little, also main plate thickness was fixed. Pulsating tension fatigue test was done at the second phase of experiment. The work using the concepts of the fracture mechanics on the stable crack growth, was in the correlation of the experimental fatigue stress-life behavior because the fatigue behaviors of various joint geometries are related to the stress intensity factors calculated by F.E.M. analysis. Main results obtained are summarized as follows. 1) According to the propagation of toe crack, the variation of the stress intensity factor at root crack is obvious as H/Tp is smaller. 2) According to the propagation of root cracks, the change of the stress intensity factor of the toe is very large with propagation of root crack. 3) The calculation formula of the stress intensity factor of crack propagation at the root crack was obtained. 4) The calculation formula of the stress intensity factor at the toe cracks was obtained in similar manner. 5) From the results of experiment, the velocity of fatigue crack propagation at the weld toe and root was estimated.

• International Journal of Railway
• /
• v.5 no.2
• /
• pp.89-92
• /
• 2012

Effective notch stress, as an approach to evaluate the local stress at a notch (weld toe or root), is defined as the total stress assuming linear-elastic material behavior. This method can be effectively used to evaluate the fatigue performance of welded joints. In this study, finite element analysis results using the effective notch stress method were correlated with fatigue test results of rib-to-deck welded joints in a steel orthotropic bridge deck. Effective notch stress approach provided a good correlation with the crack pattern observed in the full-scale fatigue test. A higher effective notch stress at the critical weld toe than at the weld root was consistent with the dominant crack pattern observed at the weld toe during testing. The effective notch stress at the toe on the deck plate was about 80% higher than that on the rib; no cracks at the weld toe on the rib in the testing were observed. Maximum effective notch stress at the weld root occurred on the upper side of the root notch, which indicates that cracks are more likely to propagate into the deck plate, not into the weld metal. This is also consistent with the observed crack pattern in which the crack from the root propagated upward into the deck plate. No such crack pattern, propagating into the weld metal, was observed in the testing.

• Journal of Welding and Joining
• /
• v.26 no.6
• /
• pp.97-102
• /
• 2008

It is well known that there exist two typical fatigue crack initiation locations in ship structures: one is the weld toe and the other is the weld root where partial penetration weld is performed. In particular, it is important for fillet weldments to avoid weld root cracking in order to prevent catastrophic failure particularly in ship structures. Therefore detail considerations are required for cruciform joints with partial penetration when there is a possibility of weld root crack initiation. For these reasons, fatigue tests on welded joints were performed in this study. Concept of stress intensity factor(SIF) by means of fracture mechanics is applied for predicting fatigue life of fillet welded joints.

• Journal of Welding and Joining
• /
• v.2 no.2
• /
• pp.62-69
• /
• 1984

In this study, cold crack susceptibility of high strength steel (ABS EH32 Steel) welded zone with shielded metal are welding was investigated by tensile restraint cracking test method. Effects of diffusible hydrogen content on root cracking, lower critical stress, crack initiation and fracture mode, hardness value distribution of welded zone and fractograph were mainly investigated. Following conclusions are made: 1. In the view of the lower critical stress level, wet electrode, containing much diffusible hydrogen content shows lower value than dried electrode. 2. Hardness value(Hv 5kg) in Heat Affected Zone of wet electrode is higher than that of dried electrode caused by hydrogen embrittlement. 3. In the case of wet electrode, root crack is initiated and propagated in Heat Affected Zone and then propagated to weld metal, but using of dried electrode, root crack is initiated in Heat Affected Zone and propagated to weld metal without propagating in HAZ. 4. For wet electrode, quasi-cleavage fracture mode is majorly observed on the fracture surface of HAZ and partially of weld metal due to hydrogen embrittlement.

• International journal of steel structures
• /
• v.18 no.5
• /
• pp.1589-1597
• /
• 2018

Fatigue tests and numerical analysis were carried out to evaluate the fatigue performance at the U-rib to deck welded joint in steel box girder. Twenty specimens were tested corresponding to different penetration rates (80 and 100%) under fatigue bending load, and the fatigue strength was investigated based on hot spot stress (HSS) method. The detailed stress distribution at U-rib to deck welded joint was analyzed by the finite element method, as well as the stress intensity factor of weld root. The test results show that the specimens with fully penetration rate have longer crack propagation life due to the welding geometry, resulting in higher fatigue failure strength. The classification of FAT-90 is reasonable for evaluating fatigue strength by HSS method. The penetration rate has effect on crack propagation angle near the surface, and the 1-mm stress below weld toe and root approves to be more suitable for fatigue stress assessment, because of its high sensitivity to weld geometry than HSS.

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.240-242
• /
• 2004

Effect of post treatment on the fatigue strength of a box weldment was investigated in order to improve fatigue life of the weldment. The post treatment applied were the smooth grinding of weld bead, weld toe grinding and hammer peening at the weld toe. The fatigue strength of the weldment after post treatment clearly increased, compared with that of the weldment in as-welded condition. After smooth grinding of weld bead, fatigue crack initiated at the root of the weldment, while fatigue crack initiated at the weld toe for the other methods.

• Journal of Korean Society of Steel Construction
• /
• v.12 no.3 s.46
• /
• pp.231-238
• /
• 2000

There was extreme improvement in the processing result of weld toe, but there is possibility that the fatigue failure occurs from the weld root part where the fatigue strength became low relatively. This study did the fatigue test at the cross rib specimens which implemented a partial penetration weld to improve the fatigue strength of the weld root part. As a result of the fatigue test of the partial penetration weld and the fillet weld specimens, almost the same fatigue strength appeared. Because the fatigue failure began from toe, there was not a reinforcement effect in the weld root part by the partial penetration weld. So, it examined fatigue strength at the partial penetration welding specimens which processed toe to stop the fatigue failure of toe part. As a result, there was big fatigue strength improvement from the partial penetration weld than the fillet weld. Therefore, if fatigue crack occurrence can be restrained from toe, it thinks that the fatigue strength of the root part can improve by the partial penetration weld, after all, it thinks that the overall fatigue life can improve.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.200-205
• /
• 2000

Fatigue failure modes of load-carrying cruciform weld joints are dependent on the characteristics of the fatigue crack initiation and propagation from the weld toe or the weld root. In this study, constant amplitude fatigue tests on load-carrying fillet welded specimen carried out, and fatigue strengths were evaluated. Also, an attempt is made to develop a new analytical model with more accuracy to predict the fatigue crack propagation life of fillet welded cruciform joints of SWS 490B steels containing lack of penetration defects. From the result of this study, fatigue crack growth characteristics of load-carrying fillet welded cruciform joints, containing lack of penetration defects are found to be affected by the weld geometry, stress range and microstructures of the weld zone.

• Steel and Composite Structures
• /
• v.26 no.1
• /
• pp.103-113
• /
• 2018

To study the effects of corner braces on fatigue performance of the U-rib and roof weld in steel bridge decks, the fatigue experiment was carried out to compare characteristics of the crack shape with and without corner braces. The improvement of fatigue life and stress variation after setting corner braces were also analysed. Different parameters of corner brace sizes, arrangements, and detail types were considered in the FEM models to obtain stress distribution and variation at the weld. Furthermore, enhancement of the fatigue performance by corner braces was evaluated. The results demonstrated that the corner brace could improve the fatigue life of the U-rib and roof weld, which exerted even no influence on the crack shape. Moreover, stress of the roof weld was decreased and the crack position was transferred from the root weld to U-rib and corner brace weld. It was suggested no weld scallop should be drilled on the corner brace. A transverse rib with lower height which was set between U-ribs was favourable for improvement of fatigue performance.

• Nuclear Engineering and Technology
• /
• v.55 no.11
• /
• pp.4112-4119
• /
• 2023

This study employs the microshear test method to examine the local mechanical properties of narrow-gap welded joints, revealing the mechanical inhomogeneity by evaluating the microshear strength, stress-strain curves, and failure strain. On this basis, the influence of weld joints micromechanical inhomogeneity on the crack tip opening displacement (CTOD) fracture toughness is investigated. From the root weld layer to the cover weld layer, the fracture toughness at the center of the weld seam demonstrates an increasing trend, with the experimental and calculated CTOD values showing a good correspondence. The microproperties of the welded joints significantly impact the load-bearing capacity and fracture toughness. During the deformation process of the "low-matching" microregions, the plastic zone expansion is hindered by the surrounding microregion strength constraints, thus reducing the fracture toughness. In contrast, during the deformation of the "high-matching" microregions, the surrounding microregions absorb some of the loading energy, partially releasing the concentrated stress at the crack tip, which in turn increases the fracture toughness.