• 한국자동차공학회논문집
• /
• 제7권6호
• /
• pp.279-286
• /
• 1999

Failure of spot-weld joints in car body may cause noise, vibration and safety problems. Systematic procedures for estimating fatigue strength of general spot-weld joints are developed in this paper. Fatigue test results for various spot-welded specimens are analysed using the finite element method. It is found that the maximum principal strain at the nugget boundary on the inner surface governs the fatigue failure of spot-welded joints.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.409-412
• /
• 2003

Fatigue strength. especially crack initiation behavior of high strength steel under marine water environment was investigated. Marine structures were usually constructed by lot of weld joints and were designed by basis of the fatigue strength of weld joints. This study was carried out to mini. The fatigue initiation behavior is more important rather than crack propagation behavior under the design of marine structures, because it is very difficult to find out the crack propagation phenomena and repair the damaged part of welded joints in sea water Then, the new configuration specimen for fatigue crack initiation tests was proposed. Using this new specimen, it is easy to carry out the crack initiation tests with relatively low cycling loading and clearly find out a crack initiation fatigue life.

• 대한기계학회논문집
• /
• 제6권3호
• /
• pp.232-238
• /
• 1982

The behavior of corner crack propagation by unidirectional plane bending fatigue was investigated in the butt welded joints of SS41 and SM50 steel plates including an edge through-thickness notch. The properties of fatigue crack propagation were inspected in the weld metal, heat-affected zone, and base metal of the welded joints. Main results obtained are as follows; (1) When a plate with an edge through-thickness notch is loaded by plane bending fatigue in indirection, the 2 variant corner cracks on the upper and lower edge of the plate are initiated and propagated respectively from the notch. (2) In case of a specimen containing a corner crack, it is more reasonable to estimate the crack propagation rate by area of fracture surface than by crack surface length. (3) The rate of fatigue crack propagation becomes faster in the following order; weld metal, heat-affected zone, and base metal. (4) The specimen including reinforcement shape is rapidly failed throughout bond due to effect of its shape when the repeated load exceeds a certain cycle.

• Journal of Welding and Joining
• /
• 제22권4호
• /
• pp.73-81
• /
• 2004

Failure mechanisms of welded joints under fatigue loads are interpreted that multiple collinear surface cracks initiating randomly along the weld toes propagate under the mutual interaction and coalescence of adjacent two cracks. To estimate fatigue crack propagation life for three types of the representative welded joints, i.e. non-load carrying cruciform, cover plate and longitudinal stiffener joint, the stress intensity factors at the front of the surface cracks have to be calculated, which are influenced strongly by the geometry of attachments, weld toes and the crack shapes. For the effective calculation of the stress intensity factors the Mk-factor was introduced which can be derived by a parametric study performed by FEM considering influence of the geometrical effects. The fatigue life of the cruciform joint was estimated by using the Mk-factors and the method considering the propagation mechanisms of the multiple surface cracks. Analysis results for the fatigue life had a good agreement with that of experiment.

• 대한금속재료학회지
• /
• 제49권1호
• /
• pp.64-72
• /
• 2011

The spot weldability of dissimilar metal joints between austenitic stainless steels (STS316)/IF steels and ferritic stainless steels (STS430)/IF steels was investigated. This study was aimed to determine the spot welding parameters for a dissimilar metal joint and to evaluate the dissimilar metal joint's weldability, including its welding nugget shape, tensile-shear strength, hardness, and microstructure. The comparison of these results was described in terms of fracture behavior. Compared with the weld lobe of similar metal joints, dissimilar metal joints (STS430/IF) had reduced weld current range. However, the weld lobe of STS316/IF steel joint showed increased weld current range. This is because the dilution of chemical composition in the molten weld pool suppressed the heat input being caused by Joule heat with current flow through the samples. The microstructure of the fusion zone was fully martensite and mixture of ferrite and martensite for austenitic stainless steel/IF steel and ferritic stainless steel/IF steel combination, respectively. The experimental results showed that the shape of nugget was asymmetric, in which the fusion zone of the austenitic and ferritic stainless steel sheet was larger due to the higher bulk-resistance. The predicted microstructure by using the Schaeffler diagram was well matched with experimental results. After peel test, the fracture was initiated from heat affected zone of ferritic stainless steel sheet side, however the final fracture was propagated into the IF steel sheet side due to its lower strength.

• 한국해양공학회지
• /
• 제13권3호통권33호
• /
• pp.57-67
• /
• 1999

Welding is widely applicable and reliable process and is mainly adopted for fabricating heavy structures. Recently, weld metal transverse cracks in butt and fillet weld joint is a serious problem, and they must be eliminated for improving weld joint reliability. The weld metal transverse crack susceptibility of butt and fillet joint was carried out by cantilever type tensile crack testing jig and CTS test. In this view of point, this study investigated the potential factors for weld metal transverse crack. The main results obtained were as follows: 1. The content o fdiffusible hydrogen in weld metal played an important role for weld metal transverse cracks. 2. From cantilever type tensile crack tests, it was pointed out that the higher the diffusible hydrogen content and tensile restraint, the more susceptible to weld metal transverse craking. 3. The TSN(thermal severity number) and diffusible hydrogen were important factors for determining weld metal transverse cracks in fillet weld joints.

• 비파괴검사학회지
• /
• 제23권4호
• /
• pp.372-379
• /
• 2003

The problems encountered by ultrasonic testing of austenitic stainless steel weld joints are discussed in the paper. Due to low thermal conductivity and the occurrence of single phase between the melting point and the room temperature, coarse and oriented grains are formed in such weld metals more in thick sections. This leads to higher scattering at the grain boundaries and low signal to noise ratio, and extensive beam skewing. Experimental results to understand these problem are explained.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.130-132
• /
• 2006

In passenger ship building where thin plates are mainly used, conventional arc welding processes result in significant post-weld reworking due to thermal distortion of welded joints. In order to solve this problem, European shipbuilding industries introduced hybrid welding process since the 1990's. for passenger ship, first of all, stability is very important. So, in this study, we investigated effects of hybrid welding conditions on impact toughness of weld metal in passenger ship building using DH36 steel.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1996년도 특별강연 및 추계학술발표 개요집
• /
• pp.139-141
• /
• 1996

Among various welding parameters, the welding current which is inversely proportional to the tip-to-workpiece distance in GMAW is an essential parameter to monitor the GMAW process of horizontal fillet joints. For the case of weld defect such as overlap in horizontal fillet welding, therefore, the signal processing for process monitoring or automatic seam tracking should be modified by considering the weld pool surface geometry including the corresponding weld defect. In other words, the adequate signal processing algorithm is indispensible to improve the performance of the arc sensor. However, arc sensor algorithm already developed usually focus on weld seam tracing but do not considering the weld qualities. In this paper, various experiments were carried out to investigate the tendencies of the weld defects when weaving motion is added, and the experimental method based on 2$^n$ factorial design was proposed for deriving the mathematical model between the leg length and the various welding conditions. Moreover, a signal processing method based on the artificial neural network(Adaptive Resonance Theory) was proposed far discriminating the current signal of sound weld beads from that of weld beads with overlap. Finally, the algorithm for weld seam tracking combined with the mathematical modeling and the signal processing method was carried out to track the weld line in conjunction with the improvement of the weld qualities. The reliability of the proposed algorithms were evaluated through various experiments, which showed that the proposed algorithms could be effectively used for arc welding automation.

• Journal of Welding and Joining
• /
• 제13권4호
• /
• pp.65-74
• /
• 1995

The weld seam tracking sensor is indispensable to improve the flexibility of automatic arc welding systems. Among the position sensing methods available, a laser displacement sensor is one of the most prevailing methods. In this study, a laser displacement sensor was examined on detecting the weld seam of lap joints in sheet metal arc welding. The output signal of the laser displacement sensor may ontain severe fluctuation from the effect of arc light, spatters, fume, etc. So a variety of signal processing methods was applied to smooth the output signal of the sensor. And then the weld joint was determined by using the central difference method. It was revealed that the quadratic mean method plays an important role in detecting the weld seam during welding especially.