• 동력기계공학회지
• /
• 제15권6호
• /
• pp.81-85
• /
• 2011

Because of excellent mechanical properties, such as good friction coefficient and heat resistance characteristics, PTFE parts have been widely used in the industries. However, the poor wear resistance of PTFE has been a main problem limiting wider applications. In this study, to improve the poor wear resistance of PTFE, porous PTFE composites were prepared by mixing additives(sodium bicarbonate and graphite) with PTFE powder. The friction coefficient, wear resistance and lubricating property of porous PTFE composites were measured and the results were compared with those of untreated PTFE.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2000년도 춘계학술대회논문집
• /
• pp.163-166
• /
• 2000

The production technology of high strength and toughness wear resistance steel involves attempt to application of severe wear parts for the construction machinery. A well balanced alloy content ensures that optimum tensile properties are achieved for the high strength. After high temperature deformation like as rolling or forging it has bainite microstructure and lower yield rato(under 80%) The effectiveness of the research approach is illustrated with experimental results on good steel cleanliness(O2 :12.2 ppm, 0,004% S, 0.008%, P nonmetalic inclusion dT: 0.10) and excellent mechanical properties (TS$\geq$140kgf/mm2 El $\geq$10% IV$\geq$20j/cm2) Therefore this should be wear resistance steel which develops high strength and high toughness without heat treatment

• 한국생산제조학회지
• /
• 제21권6호
• /
• pp.860-864
• /
• 2012

The contact tip is higher the wear of resistance and the longer life are demanded to GMA welding process. In this study, four different contact tips with three different compositions by two wires were evaluated their wear resistance by measuring in every one hour the area of enlarged hole at the exit side during actual wleding. Experimental results clearly showed that the Cr-containing tips strengthened by precipitation hardening have much better resistance to wear than those made by work hardening. In addition, flux cored wire is excellent abrasion resistance test results showed. Based on these results, the domestic industry, the life of the contact tip to know will be used as basic data.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.114-116
• /
• 2003

The multi function sprayed coating is used for direct-heating, wear resistance and high bonding strength. The merits of surface direct-heating coatings are short warming time, low power consumption and better wear resistance that can be used in many organization parts. In this study, the surface direct-heating and wear resistance can be improved by spraying the proper materials on the surface $Al_2$O$_3$40%TiO$_2$ powder and Ni-20%Cr powder that had the properties of conduction and high wear resistivity are used in order to improve wear resistance, electrical properties and bonding strength.

• Structural Engineering and Mechanics
• /
• 제64권6권
• /
• pp.819-826
• /
• 2017

The effects of thermocycling procedure and material shade on the mechanical properties and wear resistance of resin-based dental restorative materials are investigated. The modulus of elasticity, hardness, plasticity index and wear resistance are determined for the conventional composite, the nanohybrid composite and the nanofilled dental composites. Disc-shape samples are prepared from each material to investigate the effects of thermocycling procedure on the mechanical properties and wear resistance of different types of dental restorative materials. In this respect, a group of samples is thermocycled and the other group is stored in ambient conditions. Then nano-indentation and nano-scratch tests are performed on the samples to measure their mechanical properties and wear resistance. Results show that the A1E shade of the dental nanocomposite possesses higher modulus of elasticity and hardness values compared to the two other shades. According to the experimental results, the mean values for the modulus of elasticity and hardness of the A1E shade of the nanocomposite are 13.71 GPa and 1.08 GPa, respectively. The modulus of elasticity and hardness of the conventional dental composite increase around 30 percent in the oral environment due to the moisture and temperature changes. The wear resistance of the dental composites is also significantly affected by moisture and temperature changes in the oral conditions. It is observed that thermocycling has no significant effect on the hardness, plasticity index and wear resistance of the nanohybrid composite and the nanocomposite dental materials.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2003년도 학술대회지
• /
• pp.64-71
• /
• 2003

In order to evaluate the effect of alloying elements (Nb and Sn) on the wear resistance of advanced Zr fuel claddings, sliding wear tests have been performed in room temperature air and water and these results were compared with those of commercial alloys such as Zircaloy-4, A and B alloys. As a result, the advanced Zr fuel claddings have a similar wear resistance compared with the commercial alloys. The wear resistance of the advanced Zr fuel claddings is closely releted to the content of Nb and Sn even though the effects of transition elements are involved in deforming wear properties. In the tested specimens with similar Sn content, wear volume became down to a minimum at $0.4\;wt\;\%$ Nb, then rapidly increased at 1.0 wt Nb. This behavior results in the variation of grain size with alloying contents. But Sn did not have a significant effect on the wear volume of advanced Zr fuel claddings below $1.1\;wt\%$. The relationship between alloying elements and wear behaviour was evaluated and discussed using material compatibility factor.

• 한국주조공학회지
• /
• 제24권2호
• /
• pp.108-114
• /
• 2004

$Al_2O_3$, SiC reinforced Al matrix composites were fabricated by centrifugal spray casting method and their wear resistance characteristics have been studied. Particles are generally uniformly distributed in the microstructure of as-cast specimens. In order to investigate the effect of secondary deformation, hot rolling was performed for each specimen of pure Al matrix composites with a reduction of 10, 20, 30, 40 and 50% at $400{\sim}500^{\circ}C$, respectively. Microstructure of specimen showed that particle distribution density and hardness increased because of increasing of reduction ratio. Wear test with a various sliding velocity of 1.98, 2.38, 2.88 and 3.53m/sec showed that the wear resistance characterization of composite improved remarkably compared to the normal alloy and performs without reinforced particles. Microstructural observation for the worn surface of pure Al specimens without particles showed that a change in wear mechanism seemed to separate layer by surface fatigue. In other case of Al composite reinforced with $Al_2O_3$ and SiC, the grinder type of wear mechanism was shown.

• 한국주조공학회지
• /
• 제28권5호
• /
• pp.237-241
• /
• 2008

This study has been carried out to investigate the wear and heat resistant properties of durable moldwash agent for Al gravity casting according to mold washing process conditions. The wear properties of coated specimen were performed by sliding wear testing machine and heat resistance were evaluated by measuring the loss of coated moldwash agent during emerging of coated specimen in Al melts. During testing, experimental variables were mold surface temperature, moldwash agent/distilled wear, and additive concentrations. The lower additive concentration and mold temperature caused the smooth surface roughness of coated specimen, It was found that the specimen coated with moldwash/water ratio 1:3, additive concentration 9wt% and mold temperature higher than $200^{\circ}C$ showed superior wear and heat treatment. Also, these results were supported by fluidity test.

• Composites Research
• /
• 제12권5호
• /
• pp.12-22
• /
• 1999

알루미늄 기지 금속복합재료는 비강도, 비강성, 경도가 뛰어난 것으로 널리 알려져 있으며, 높은 마모 저항으로 인해 점점 중요한 재료로 인식되고 있다. 본 연구에서는 AC2B 알루미늄 합금을 기지재로 하고, 알루미나($Al_2O_3$) 및 탄소를 단섬유를 보강재로한 혼합금속복합재료를 제조하였다. 다양한 상대 마모 속도하에서의 연삭 마모 시험을 통해 금속복합재료의 상온 및 고온 마모 거동을 규명하였다. 금속복합재료의 마모 저항은 고속에서 보강재로 인해 향상되었다. 탄소 혼합 금속복합재료의 마모 저항은 탄소의 고체 윤활 효과로 인해 알루미나($Al_2O_3$) 복합재료보다 우수하였으며, 특히 고속에서의 내마모성이 가장 향상되었다. 금속복합재료의 마찰계수는 상온과 고온에서 상대 속도의 변화에도 큰 차이를 보이지 않았다.

• International Journal of Ocean System Engineering
• /
• 제2권4호
• /
• pp.244-249
• /
• 2012

In this study, a monolithic MoSi2 matrix reinforced with 20 vol% SiC particles, a SiC/MoSi2 composite matrix reinforced with 20 vol% ZrO2 particles, and a ZrO2/MoSi2 composite were fabricated using hot press sintering at $1350^{\circ}C$ for 1 h under a pressure of 30 MPa. The Vickers hardness and sliding wear resistance of the monolithic MoSi2, ZrO2/MoSi2, and SiC/MoSi2 composite were investigated at room temperature. A wear behavior test was carried out using a disk-type wear tester with a silicon nitride ball. The ZrO2/MoSi2 composite showed an average Vickers hardness value and excellent wear resistance compared with the monolithic MoSi2 and SiC/MoSi2 composite at room temperature.