• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.2001-2003
• /
• 2005

Various organic acid were used in order to prepare new metalorganic deposition solution for high quality $REBa_2Cu_3O_{7-{\delta}}$ (RE=Y, Eu, Gd) films. Prepared fluorine free MO precursor solution was coated on single crystal (001) $LaAlO_3$ (LAO) by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature etc havebeen controlled in order to make high $J_c$ films with a good epitaxial relationship with substrate. 0.5 micron-thick film was obtained by single coating and no crack appeared after calcination. Oxygen partial pressure was varied in the range of $100{\sim}1,000 ppm$ and conversion heat treatment was carried out at the temperature of $725{\sim}765^{\circ}C$. A critical transition temperature $(T_{c0})$ of 90K and a critical transport current density $(J_c)$ of $>0.5MA/cm^2$ (77K and self-field) were demonstrated for the YBCO film on (001) oriented LAO substrates with a thickness of 0.5 micron. $I_c$ was determined by utilizing a transport measurement. SEM and XRD investigations confirmed that films were grown epitaxially onto the LAO single crystal substrate. It is thought that fluorine free new MOD solutionis promising for high quality REBCO films.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.4
• /
• pp.272-277
• /
• 2014

PURPOSE. The purpose of this study was to investigate the impact of different surface treatment methods and thermal ageing on the bond strength of autopolymerizing acrylic resin to Co-Cr. MATERIALS AND METHODS. Co-Cr alloy specimens were divided into five groups according to the surface conditioning methods. C: No treatment; SP: flamed with the Silano-Pen device; K: airborne particle abrasion with $Al_2O_3$; Co: airborne particle abrasion with silica-coated $Al_2O_3$; KSP: flamed with the Silano-Pen device after the group K experimental protocol. Then, autopolymerized acrylic resin was applied to the treated specimen surfaces. All the groups were divided into two subgroups with the thermal cycle and water storage to determine the durability of the bond. The bond strength test was applied in an universal test machine and treated Co-Cr alloys were analyzed by scanning electron microscope (SEM). Two-way analysis of variance (ANOVA) was used to determine the significant differences among surface treatments and thermocycling. Their interactons were followed by a multiple comparison' test performed uing a post hoc Tukey HSD test (${\alpha}=.05$). RESULTS. Surface treatments significantly increased repair strengths of repair resin to Co-Cr alloy. The repair strengths of Group K, and Co significantly decreased after 6,000 cycles (P<.001). CONCLUSION. Thermocycling lead to a significant decrease in shear bond strength for air abrasion with silica-coated aluminum oxide particles. On the contrary, flaming with Silano-Pen did not cause a significant reduction in adhesion after thermocycling.

• BMB Reports
• /
• v.36 no.6
• /
• pp.593-596
• /
• 2003

The effects of $N{\omega}$-nitro-L-arginine methylester (L-NAME) and L-arginine on cardiotoxicity that is induced by doxorubicin (Dox) were investigated. A single dose of Dox 15 mg/kg i.p. induced cardiotoxicity, manifested biochemically by a significant elevation of serum creatine phosphokinase (CPK) activity [EC 2.7.3.2]. Moreover, cardiotoxicity was further confirmed by a significant increase in lipid peroxides, measured as malon-di-aldehyde (MDA) in cardiac tissue homogenates. The administration of L-NAME 4 mg/kg/d p.o. in drinking water 5 days before and 3 days after the Dox injection significantly ameliorated the cardiotoxic effects of Dox, judged by the improvement in both serum CPK activity and lipid peroxides in the cardiac tissue homogenates. On the other hand, the administration of L-arginine 70 mg/kg/d p.o. did not protect the cardiac tissues against the toxicity that was induced by the Dox treatment. The findings of this study suggest that L-NAME can attenuate the cardiac dysfunction that is produced by the Dox treatment via the mechanism(s), which may involve the inhibition of the nitric oxide (NO) formation. L-NAME may, therefore, be a beneficial remedy for cardiotoxicity that is induced by Dox and can then be used to improve the therapeutic index of Dox.

• Membrane and Water Treatment
• /
• v.12 no.2
• /
• pp.75-82
• /
• 2021

This study aimed to prepare a W/O nonionic microemulsion system(MEs) consisting of OP-4[polyoxyethylene(4) nonylphenol], OP-7[polyoxyethylene(7) nonylphenol], 1-hexanol, D2EHPA, kerosene and HCl solution and applied to the extraction of La(III) from chloride aqueous solution within the polysulfone hollow fiber contactor (HFC),laboratory-scale experiments were carried out to investigate the recovery of La(III) using as-prepared microemulsion from the simulation wastewater containing La(III),Al(III) and Fe(III). The right weight ratio(Rs) of OP-4 to OP-7 was firstly confirmed through determination of the solubilization capacity of HCl solution(W0,HCl) in microemulsion, the effect of several factors such as the HCl concentration, temperature and effective extraction time on the extraction efficiency of La(III) was discussed. Results showed that the acceptable Rs was 4:6 to prepare the W/O MEs. The extraction yield of La(III) increased with the increasing of HCl concentration, temperature and effective extraction time and reaches to 97.3% while using five-stage modules. The recovery yield of La(III) from simulation La-bearing wastewater was 90.6%.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.11a
• /
• pp.42-42
• /
• 2011

To evaluate the Hwangsu spring as natural mordants effect on dyeing. The natural mordants effect of Hwangsu spring were analyzed by pH, temperature, trace elements, organic matter and color fastness. Hwangsu spring having pH 2.42 and $14.4^{\circ}C$ was harvested at the end of September, in Yeongcheon (Gyeongbuk Province, Korea) and left on a $0^{\circ}C$ and $25^{\circ}C$ before use. Hwangsu spring during storage at $25^{\circ}C$ turned brown by photochemical reaction. The Result of ICP analysis, it contained Fe(414.9 ppm), Al(88.9 ppm), Mn(4.9 ppm) and observed character by water analysis. Dyeing and post-mordant procedure; Cotton(KS K 0905) were dyed with clove powder for 30 min at $70^{\circ}C$. Hwangsu spring, Aluminium Sulfate $14-18H_20(Al_2(SO_4)_3{\cdot}14-18H_2O)$, Iron Sulfate Heptahydrate($FeSO_4{\cdot}7H_2O$) were used by post mordant at the same ratio. The dyed fabrics were treated with 20% each mordant solution at $25^{\circ}C$ for 10min. Comparison with a reproduced chemical mordant, the K/S values of cotton fabrics dyed with Hwangsu sping were increased.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.599-605
• /
• 2013

CSA, a cement mineral compound that is mainly composed of $3CaO{\cdot}3Al_2O_3{\cdot}CaSO_4$, generates ettringite as a hydration product after a reaction with glass (lime), gypsum and water to speed up the hardening process and enhance the strength and degree of expansion. When used as a cement admixture, there is increased production of ettringite, which can improve the initial strength in the first three days and ameliorate the reduction in the initial strength caused by the use of fly ash in particular. In this study, a hydrate analysis was performed using XRD and SEM after substitution with fly ash (30%) and CSA (8%) with the goal of observing the effect of CSA on the initial strength of a cement mixture containing fly ash. The results of the analysis showed that an addition of CSA promoted the production of ettringite and improved the initial strength, resulting in the generation of hydrates, which can effectively enhance the long-term strength of these materials.

• Geosciences Journal
• /
• v.22 no.6
• /
• pp.989-1000
• /
• 2018

The provenance of the Central Yellow Sea Mud (CYSM) in the Yellow Sea has been attracted a great deal of attention over the last three decades, but a consensus is not yet reached. In this study, 101 surface sediment samples collected from the CYSM were investigated to determine provenance and transport mechanisms in the area using the clay minerals and major element components. The Huanghe sediments are characterized by higher smectite, but the Changjiang sediments are more abundant illite contents. Western Korean rivers contain more kaolinite and chlorite than do Chinese rivers. The Chinese rivers have higher $Fe_2O_3$, MgO, and CaO than the Korean rivers at the same $Al_2O_3$ concentration. Therefore, the clay minerals and major element concentrations can be useful indicator for the source. Based on our results, we suggest that the surface sediments in CYSM were composed mainly of Changjiang sediments, mixed a partly with sediments from the Huanghe and the western Korean rivers. Although the northwestern part of CYSM is proximate to the Huanghe, the contents of smectite and CaO were extremely low. It could be evidence that the Huanghe materials do not enter directly into the CYSM due to the Shandong Peninsula Front. Considering the oceanic circulation in the Yellow Sea, the Changjiang sediments could be transported eastward with the Changjiang Diluted Water and then mixed in CYSM via the Yellow Sea Warm Current (YSWC). Huanghe sediments could be provided by coastal currents (Shandong Coastal Current and Yellow Sea Coastal Current) and the YSWC. In addition, sediments from western Korean rivers might be supplied into the CYSM deposit via the Korean Coastal Current, Transversal Current, and YSWC.

• KSBB Journal
• /
• v.10 no.4
• /
• pp.441-448
• /
• 1995

Optimized fermentation medium and cultural conditions for the production or exopolysaccharide KS-1 with Bacillus polymyxa KS-1 was following as; 30g g1ucose, 2.59g yeast extract, $2.5g KH_2PO_4, 0.5g NaCl, 0.3g MgSO_4.7H_20, 0.1g CaC0_3 0.05g, FeSO_4.7H_2O, and 0.05g MnS0_4 . 4H_20in 1 liter distilled water. The exopolysaccharide production was influenced by the by the temperature and pH, the optimal conditions for the production of exopolysaccharide KS-1 seemed to be $30^{\circ}C$ and pH 7.0, respectively. About $10.3g/\ell$ of maximum exopolysaccharide was obtained al the initial pH 7.0, $30^{\circ}C$, 2vvm of aeration rate and 400 rpm of impeller speed in a jar fermentor.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.406-406
• /
• 2016

To get high efficiency n-type crystalline silicon solar cells, passivation is one of the key factor. Tunnel oxide (SiO2) reduce surface recombination as a passivation layer and it does not constrict the majority carrier flow. In this work, the passivation quality enhanced by different chemical solution such as HNO3, H2SO4:H2O2 and DI-water to make thin tunnel oxide layer on n-type crystalline silicon wafer and changes of characteristics by subsequent annealing process and firing process after phosphorus doped amorphous silicon (a-Si:H) deposition. The tunneling of carrier through oxide layer is checked through I-V measurement when the voltage is from -1 V to 1 V and interface state density also be calculated about $1{\times}1012cm-2eV-1$ using MIS (Metal-Insulator-Semiconductor) structure . Tunnel oxide produced by 68 wt% HNO3 for 5 min on $100^{\circ}C$, H2SO4:H2O2 for 5 min on $100^{\circ}C$ and DI-water for 60 min on $95^{\circ}C$. The oxide layer is measured thickness about 1.4~2.2 nm by spectral ellipsometry (SE) and properties as passivation layer by QSSPC (Quasi-Steady-state Photo Conductance). Tunnel oxide layer is capped with phosphorus doped amorphous silicon on both sides and additional annealing process improve lifetime from $3.25{\mu}s$ to $397{\mu}s$ and implied Voc from 544 mV to 690 mV after P-doped a-Si deposition, respectively. It will be expected that amorphous silicon is changed to poly silicon phase. Furthermore, lifetime and implied Voc were recovered by forming gas annealing (FGA) after firing process from $192{\mu}s$ to $786{\mu}s$. It is shown that the tunnel oxide layer is thermally stable.

• Advances in concrete construction
• /
• v.5 no.6
• /
• pp.639-658
• /
• 2017

Very limited studies have been accomplished concerning the historical structures around Harran area. Collected mortar samples from the historic structures in the area were tested to explore their mechanical, chemical and mineralogical properties. Mortar samples from three different points of each historical structure were taken and specified in accordance with the related standards taking into consideration their mechanical, chemical and mineralogical properties. By means of SEM-EDX the presence of organic fibres and calcite, quartz, plagioclase and muscovite minerals has been examined. Additionally, by means of XRF analysis, oxide ($SiO_2$, $Al_2O_3$, and $Fe_2O_3$) percentages of mortar ingredients have been specified, also. According to the test results obtained, it was confirmed that the mortars had densities ranging between $1.51-2.10g/cm^3$, porosity values ranging between 8.89-35.38% and compressive strengths ranging between 5.02-5.90 MPa. Specimen HU, which has the highest durability and lowest water absorption and porosity, was the mortar taken from the most intact building in the mosque complex. This result is most likely due to the very little fine aggregate content of HU. In contrast, HUC mortars with a small amount of fine particles and brick contents yielded slightly lower compressive strengths. The interesting point of this study is the mineralogical analysis results and especially the presence of ettringite in these historic mortars linked to the use of pozzolanic materials. Survival of these historic structures in Harran Area through centuries of use and, also, having been subjected to many earthquakes can probably be explained by these properties of the mortars.