• Corrosion Science and Technology
• /
• v.22 no.5
• /
• pp.387-392
• /
• 2023

The objective of this study was to evaluate corrosion resistance of Zn-Al-Mg alloy coated steel in residential water with trace quantities of Cl^-. Comparative evaluations were performed using two commercial coated steel products, GI and Galvalume, as reference samples. Examination of corrosion morphology and measurement of weight loss revealed that the Zn-Al-Mg alloy coated steel exhibited higher corrosion resistance than reference samples. This finding suggests that the alloy coated steel possesses long-term corrosion resistance not only in highly Cl^- concentrated environments such as seawater, but also in environments with extremely low levels of Cl^- found in residential water. The primary factor contributing to the superior corrosion resistance of the Zn-Al-Mg alloy coated steel in residential water is the formation of an inhibiting corrosion product composed primarily of two phases: Zn₅(OH)₆(CO₃)₂ and Zn₅(OH)₈Cl₂·H₂O. The preferential dissolution of Mg from the corroded coating layer can increase alkalinity, which might enhance the thermodynamical stability of Zn₅(OH)₆(CO₃)₂.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.7
• /
• pp.1996-1998
• /
• 2014

Licochalcone C was synthesized from commercially available 2,4-dihydroxybenzaldehde by using regioselective $Al_2O_3$-mediated C-prenylation followed by conventional Claisen-Schmidt condensation in basic condition.

• Journal of Korea Water Resources Association
• /
• v.38 no.2
• /
• pp.133-142
• /
• 2005

The settling concentration of fine suspended solid particles(alumina(Al$_2$O$_3$) and quartz(SiO$_2$)) is investigated with the physico-chemical effects(initial concentration, pH and NaCl). Laboratory tests have confirmed the significant influence of increasing initial concentration and salinity which can lead to flocculation due to the intermolecular attraction. Furthermore, the influence of the pH value on the concentration-time corves of alumina has been on firmed. Besides a numerical model to predict the behaviour of cohesive deposit under still water is analyzed by solving the unsteady one-dimensional diffusion-advection equation with a explicit, implicit, Crank-Nicolson and finite difference scheme. The model predicts the existence of an equilibrium concentration. Application of the model with implicit centered difference to data from settling experiments shows a similar distribution.

• Membrane Journal
• /
• v.22 no.2
• /
• pp.135-141
• /
• 2012

This study was carried out to find the optimum coagulation conditions for ceramic microfiltration process of Y water treatment plant. When pH of raw water from Y Dam was adjusted to 7, the efficiency of coagulation was the best and the optimun dosage of coagulant was 3 mg/L(as $Al_2O_3$) for turbidity of raw water less then 10 NTU in Jar test. In mini module test, the decay rate of specific flux was the lowest when PAC (poly Aluminum Chloride) was used among coagulants and pH was adjusted to 7. The decay rate of specific flux for raw water turbidity of 10~30 NTU was greatly decreased with increase of dosage of coagulant (PAC) while the rate was not significantly decreased for turbidity more than 50 NTU. In conclusion, the optimum dosage of PAC (11% as $Al_2O_3$) was 30 and 50 mg/L for raw water turbidity of less than 10 NTU and more than 50 NTU, respectively. The dosage of PAC should be increased linearly 30 to 50 mg/L depending on raw water turbidity of 10 to 50 NTU.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2010.05a
• /
• pp.91-94
• /
• 2010

The purpose of this study is to produce artificial lightweight aggregate. The properties of aggregate are deducted by analysing the plasticity of aggregate according to the addictive contents of $CaCO_3$ and $Al_2O_3$ on constant plastic temperature($1150^{\circ}C{\sim}1160^{\circ}C$) and the specific gravity, the percentage of water absorbtion. The density on the temperature of $1150^{\circ}C{\sim}1160^{\circ}C$ which results from that the plastic temperature of pottery stone is decreased by increasing the addictive contents of $CaCO_3$ and $Al_2O_3$ manufacturing artificial light weight aggregate using pottery stone is included in the arrange of light weight aggregate density. And the percentage of water absorbtion is 4.2~14% which is similar to or lower than existing artificial light weight aggregate. The unit volume weight is in inverse proportion to density and to increase addictive contents of flux.

• Journal of environmental and Sanitary engineering
• /
• v.13 no.1
• /
• pp.57-68
• /
• 1998

This study was surveyed to examine the removable ability of residual aluminum with the coagulants(LAS, PAC) and the auxiliary coagulants(Loess, R-calmont) on raw water. The leaching test of the auxiliary coagulant showed that the loess contained a lot of Al, Fe and Mn. On the reverse, the R-calmont was a little. Most of the loess were composed of $SiO_{2}$ 53.25%, $Al_{2}O_{3}$ 29.28%, $Fe_{2}O_{3}$ 10.73% and Si/Al ratio was 3.08. In using both LAS vs. loess and PAC vs. loess as the coagulated material, the removal of residual aluminum was the highest as 96.3%, 96.6% respectively, and that of the residual turbidity was 95.0% when PAC vs. R-calmont was dosed 0.2mg/L. Also, loess showed better than R-calmont in the removable efficiency of aluminum and turbidity. When the setting time of auxiliary coagulant was input ar the same time with coagulant, the removal aluminum was the highest as 93.3% to 96.6%.

• Journal of the Korean Chemical Society
• /
• v.19 no.5
• /
• pp.317-324
• /
• 1975

The adsorptions of gaseous $H_2O\;and\;D_2O\;on\;Na^+-,\;Ca^{2+}-,\;and\;Al^{3+}$ montmorillonites at various temperatures were undertaken. Break down of ir hydroxyl stretching bands into four Gaussian components was made by means of manual technique. Resonance theory of water to form silanol hydroxyl group was supported by $3625cm^{-1}$ band for OH and $2680cm^{-1}$ band for OD which depend on amounts of water adsorbed. The broad bands at about $3400 cm^{-1}\;and\;2475cm^{-1}$ were assigned to stretching band of silanol OH hydrogen bonded to adsorbed water. The prominent $3230 cm^{-1}$ band together with component around $2345 cm^{-1}$ were attributed to adsorbed $H_2O\;and\;D_2O$ respectively. The chemical nature of the hydrogen bonding between adsorbed water and neighboring surface OH was explained adequately in terms of electrostatic interaction.

• 한국가스학회:학술대회논문집
• /
• 2005.10a
• /
• pp.83-87
• /
• 2005

The kinetics of the direct synthesis of DME was studied under different conditions over a temperature range of $220\~280^{\circ}C$, syngas ratio $1.2\~ 3.0$ All experiment were carried out over hybrid catalyst, composed to a methanol synthesis catalyst (Cu/ZnO/$Al_2O_3$) and a dehydration Catalyst ($\gamma$-Al_2O_3$) The observed reaction rate qualitatively follows a Langmiur-Hinshellwood type of reaction mechanism. Such a mechanism is considered with three reaction, methanol synthesis, methanol dehydration and water gas shift reaction. From a surface reaction with dissociative adsorption of hydrogen, methanol and water, individual reaction rate was determined

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.1
• /
• pp.92-99
• /
• 2021

CaO-based by-products composed of CaO, SO3, Al2O3, etc. are generally used as raw materials for CaO compounds. When applied to the recovered water of ready-mixed concrete, the hydration reaction of the powder material is accelerated and concrete performance can be improved. In this study, activated sludge was prepared to apply to the recovered water of ready-mixed concrete by mixing CaO-based hot-rolled slag(C12A7) in the recycling water of ready-m ixed concrete. Cem ent paste setting time and mortar compressive strength performance tests confirmed the effect on the hydration reaction. Therefore, the possibility of concrete application using activated sludge was confirmed.

• Journal of the Korean Society of Combustion
• /
• v.11 no.2
• /
• pp.7-14
• /
• 2006

Catalytic combustion is one of the suitable methods for micro power source due to high energy density and it can be applied to micro structured chamber without consideration of quenching since it is flameless combustion. Catalyst loading in the micro structured combustion chamber is one of the most important issues in the development of micro catalytic combustors. In this research, to coat catalyst on the chamber wall, two methods were investigated. First, $Al_2O_3$ was selected as a support of Pt and $Pt/Al_2O_3$ was synthesized through the alumina sol-gel procedure. To improve the coating thickness and adhesion between catalyst and substrate, heat resistant and water solvable organic-inorganic hybrid binder was used. Porous silicon was also investigated as a catalyst support for platinum. Through the parametric studies of current density and etching time, fabrication process of $1{\sim}2{\mu}m$ of diameter and about $25{\mu}m$ depth pores was confirmed. Coated substrates were test in the micro channel combustor which was fabricated by the wet etching and machining of SUS 304. Using $Pt/Al_2O_3$ coated substrate and Pt coated porous silicon substrate, conversion rate of fuel was over 95 % for $H_2/Air$ premixed gas.