• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.2
• /
• pp.98-106
• /
• 2003

Nondestructive test (NDT) provides much information on concrete without damage of structural functions. Of NDT methods, elastic wave propagation methods, such as ultrasonic pulse velocity (UPV) method and impact-echo (IE) method, have been successfully used to estimate the strength, elastic modulus, and Poisson's ratio of concrete as well as to detect the internal microstructural change and defects. In this study, the concretes with water-binder ratio ranging from 0.27 to 0.50 and fly ash content of 20% were made and then their longitudinal wave velocities were measured by UPV and IE method, respectively. Test results showed that the UPV is greater than the longitudinal wave velocity measured by the If method, i.e., rod-wave velocity obtained from the same concrete cylinder. It was found that the difference between the two types of velocities decreased with increasing the ages of concrete and strength level. Moreover, for the empirical formula, the dynamic Poisson's ratio, static and dynamic moduli of elasticity, and velocity-strength relationship were determined. It was observed that the Poisson's ratio and the modulus of elasticity determined by the dynamic method are greater than those determined by the static test. Consequently, for the more accurate estimation of concrete properties using the elastic wave velocities, the characteristics of these velocities should be understood.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.111-118
• /
• 2014

The present study concerns the leachability of alkali ions from hardened cement paste in terms of an increase in the pH together with the rate of alkali leaching. To evaluate the influence of mix design on the leaching capacity and rate of alkali, different water-cement ratios (W/C) and binders were used to manufacture paste specimens. The cement paste was made in the form of rectangular bucket where deionised water was subsequently supplied as solvent media. Then the specimen was wrapped in polythene film to avoid contact to atmospheric conditions, which may affect the water chemistry in the bucket. The pH of media was monitored until no further change in the pH value was observed, of which value then used to calculate the leaching capacity and rate. The influence of binder on the pH of solvent is more dominant than that of water to cement ratio: OPC paste produced the highest level of alkali leaching, whilst 30% PFA and 60% GGBS pastes imposed lower level of alkali leaching. After the monitoring of the pH, the inner bucket was ground with an increment of 1.0 mm to measure the leaching influence using the suspension consisting of paste powder and deionised water. It was found that the impact zone for OPC was about 7-8 mm, whilst 30% PFA and 60% GGBS had deeper impact depth of the alkali leaching.

• Journal of the Korea Concrete Institute
• /
• v.29 no.3
• /
• pp.307-314
• /
• 2017

Concrete is a durable and cost-benefit construction material, however performance degradation occurs due to steel corrosion exposed to chloride attack. Penetration of chloride ion usually decreases due to hydrates formation and reduction of pores, and the reduced chloride behavior is considered through decreasing diffusion coefficient with time. In the work, HPC (High Performance Concrete) samples are prepared with 3 levels of W/B (water to binder) ratios of 0.37, 0.42, and 0.27 and 3 levels of replacement ratios of 0%, 30% and 50%. Several tests containing chloride diffusion coefficient, passed charge, and compressive strength are performed considering age effect of 28 days and 180 days. Chloride diffusion is more reduced in OPC concrete with lower W/B ratio and GGBFS concrete with 50% replacement ratio shows significant reduction of chloride diffusion in higher W/B ratio. At the age of 28 days, GGBFS concrete with 50% replacement ratio shows more rapid reduction of chloride diffusion than strength development, which reveals that abundant GGBFS replacement has effective resistance to chloride penetration even in the early-aged condition.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.3
• /
• pp.119-126
• /
• 2019

In case of RC(Reinforced Concrete) structures which are constructed in coastal areas, chloride ions in sea water corrode the steel rebar in concrete. Especially in coastal areas, RC structures are affected by not only immersion of sea water, but also tidal of sea water and airborne chloride ions. In this study, marine environment exposure tests are conducted, considering 3 types of exposure environments(immersion zone, tidal zone, splash zone) and the exposure periods of 180 days, 365 days, and 730 days. Also, the concrete mixtures for this study are established, considering 3 levels of W/B(Water to Binder) ratio(0.37, 0.42, 0.47) and 2 levels of substitution rate of Fly ash(0 %, 30 %). In all exposure environments, Fly ash concrete has lower apparent chloride diffusion coefficients than OPC concrete. It is thought that fly ash's pozzolan reaction improves chloride resistance of concrete. Fly ash concrete has up to 63.5 % of decreasing rate in 180 days of exposure and up to 55.8 % of decreasing rate in 730 days of exposure, based on diffusion coefficients of OPC concrete. As a result of evaluation about effects of exposure environments, apparent chloride diffusion coefficients of fly ash concrete are evaluated in order of tidal zone, immersion zone, and splash zone. In tidal zone, It is thought that repeated cycles of wetting and drying of sea water cause the diffusion of chloride ions rapidly.

• Journal of the Korea Concrete Institute
• /
• v.21 no.3
• /
• pp.245-253
• /
• 2009

The importance of chloride ions in the corrosion of steel in concrete has led to the concept for chloride threshold level (CTL). The CTL can be defined as the content of chlorides at the steel depth that is necessary to sustain local passive film breakdown and hence initiate the corrosion process. Despite the importance of the CTL, due to the uncertainty determining the actual limits in various environments for chloride-induced corrosion, conservative values such as 0.4% by weight of cement or 1.2 kg in 1 $m^3$ concrete have been used in predicting the corrosion-free service life of reinforced concrete structures. The paper studies the CTL for blended cement concrete by comparing the resistance of cementitious binder to the onset of chloride-induced corrosion of steel. Mortar specimens were cast with centrally located steel rebar of 10 mm in diameter using cementitious mortars with ordinary Portland cement (OPC) and mixed mortars replaced with 30% pulverized fuel ash (PFA), 60% ground granulated blast furnace slag (GGBS) and 10% silica fume (SF), respectively, at 0.4 of a free W/B ratio. Chlorides were admixed in mixing water ranging 0.0, 0.2, 0.4, 0.6, 0.8, 1.0, 1.5, 2.0, 2.5 and 3.0% by weight of binder(Based on $C1^-$). Specimens were curd 28 days at the room temperature, wrapped in polyethylene film to avoid leaching out of chloride and hydroxyl ions. Then the corrosion rate was measured using the polarization resistance method and the order of CTL for binder was determined. Thus, CTL of OPC, 60%GGBS, 30%PFA and 10%SF were determined by 1.6%, 0.45%, 0.8% and 2.15%, respectively.

• Journal of the Korea Concrete Institute
• /
• v.20 no.6
• /
• pp.797-807
• /
• 2008

For this study, the semi-adiabatic temperature rising test is accomplished by using ternary system cement (OPC, BFS, FA) reducing temperature crack. Two tests are conducted; one is for the paste test, and the other is for the concrete test. As the results of paste tests, using fly ash is better to reduce hydration temperature than doing blast furnace slag. In the case of the paste mixed ternary system cement, the more fly ash is mixed and the less blast furnace slag is used, the lower the temperature is. The less the mixture ratio of blast furnace slag is and the more the mixture ratio of fly ash is, the later the temperature rising velocity and descending velocity are. Besides, the temperature is lower if water/binder ratio is high. The use of ternary system cement has the retardation effect of temperature rising because the time to reach the maximum temperature is in the order of OPC100, binary system cement, and ternary system cement. From the test, the maximum temperature of concrete used ternary system cement is $8{\sim}11^{\circ}C$ lower than that of concrete used OPC100. Moreover, temperatures rising velocity and descending velocity of ternary system cement range $47{\sim}51%$ and $37{\sim}42%$ compared with OPC100. The specimen of concrete shows remarkable low internal temperature and slow temperature rising velocity and descending velocity compared with the specimen of paste because it is that temperature loss of concrete is much more than paste specimen according to aggregates.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.195-203
• /
• 2022

In this paper, the effects of the bottom ash aggregate sizes and compaction levels on the thermal conductivity of porous concrete were investigated. In this experimental study, bottom ash was used as aggregates after identifying the aggregate characteristics. SA mixtures included hybrid aggregates, and DA contained only one particle size. The water-binder ratio was fixed at 0.30, and the compaction levels were applied to the concrete specimens at 0.5, 1.5, and 3.0 MPa. Unit weight, total void ratio, and thermal conductivity were measured and analyzed. As the compaction level increased, the unit weight and thermal conductivity increased in the SA mixtures, but the total void ratio decreased. In addition, the thermal conductivity of the specimens under oven-dried condition were lower than that of the specimens under air-dried condition. The correlation between the unit weight, total porosity, and thermal conductivity of porous concrete was analyzed. The thermal conductivity-unit weight correlation was proportional, while the thermal conductivity-total void ratio correlation was inversely proportional.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.55-61
• /
• 2023

This study aims to develop CLSM fill material for emergency restoration using landfill coal ash. As a result of examining physical properties such as particle size distribution and fines content of landfill coal ash, bottom ash, fly ash, and general soil were mixed, and SP was found to have a density of 2.03 and a residual particle pass rate of 7.8 %. CLSM materials that secure fluidity in unit quantities without using chemical admixtures such as glidants and water reducing agents have a high risk of material separation due to bleeding. As a result of this experiment, it was found that the bleeding ratio did not satisfy the standard in the case of the specimen with a large amount of fly ash and a lot of addition of mixing water. As a result of the compressive strength test, the strength development of 0.5 MPa or more for 4 hours was found to be satisfactory for the specimens using hemihydrate gypsum with a unit binder amount of 200 or more, and the remaining gypsum showed poor strength development. Although it is judged that landfill coal ash can be used as a CLSM material, it is necessary to identify and apply the physical and chemical characteristics of coal ash buried in the ash treatment plant of each power generation company.

• KIEAE Journal
• /
• v.15 no.4
• /
• pp.45-52
• /
• 2015

Purpose: Foam concrete is the concrete that contains large amount of air voids inside. In general, the density of foam concrete depends on parameters like water/binder ratio, foam volume, aggregate and pozzolan content, etc. Method: In this study, the effect of foam volume and fly ash content on dry density is investigated intensively in order to find the relationship between each parameter and their abilities to counteract with each other. According to the above information, though there are quite a number of studies on the effect micro fiber on foam concrete at low volume fractions, there is still lack of information especially on the high fiber content side. The objective of the second study is to investigate further on the use of micro fiber at higher volume fraction and fill in the lacking information. Beside from this study, the investigation of the effect of micro-fiber (polypropylene) to enhance the properties of foam concrete is also carried out. Result: Of the two variables that are investigated in this study, the foam volume and the fly ash content, show significant effect on the properties of foam concrete. The foam volume tends to decrease the density and strength of foam concrete. In the second part of our study, a large fibre volume fraction is proved to be able to evidently increase the flexural strength of foam concrete up to about 40% due to the effect of fibre bridging over the crack and a significant number of fibres that intercepts the crack surfaces. However, the compressive strength is found to decrease severely due to the occurrence of large pores as the result of fibre being added into concrete mixture.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.12-20
• /
• 2017

This report presents the results of an investigation on the fundamental properties of mortars high fluidity high volume slag cement(HVSC) activated with sodium silicate($Na_2SiO_3$). The ordinary Portland cement(OPC) was replaced by ground granulated blast furnace slag(GGBFS) from 40% to 80% and calcium sulfoaluminate(CSA) was 2.5% or 5.0% mass. The $Na_2SiO_3$ was added at 2% and 4% by total binder(OPC+GGBFS+CSA) weight. A constant water-to-binder ratio(w/b)=0.35 was used for all mixtures. The research carried out the mini slump, V-funnel, setting time, compressive strength and drying shrinkage. The experimental results showed that the contents of superplasticizer, V-funnel, setting time and drying shrinkage increased as the contents of CSA and $Na_2SiO_3$ increase. The compressive strength increases with and an increase in CSA and $Na_2SiO_3$. One of the major reason for these results is the accelerated reactivity of GGBFS with CSA and $Na_2SiO_3$. The maximum performance was CSA 5.0% + $Na_2SiO_3$ 4% specimens.