• Korean Journal of Materials Research
• /
• v.23 no.6
• /
• pp.304-308
• /
• 2013

The effect of a sputter deposition sequence of Cu, Zn, and Sn metal layers on the properties of $Cu_2ZnSnS_4$ (CZTS) was systematically studied for solar cell applications. The set of Cu/Sn/Zn/Cu multi metal films was deposited on a Mo/$SiO_2$/Si wafer using dc sputtering. CZTS films were prepared through a sulfurization process of the Cu/Sn/Zn/Cu metal layers at $500^{\circ}C$ in a $H_2S$ gas environment. $H_2S$ (0.1%) gas of 200 standard cubic centimeters per minute was supplied in the cold-wall sulfurization reactor. The metal film prepared by one-cycle deposition of Cu(360 nm)/Sn(400 nm)/Zn(400 nm)/Cu(440 nm) had a relatively rough surface due to a well-developed columnar structure growth. A dense and smooth metal surface was achieved for two- or three-cycle deposition of Cu/Sn/Zn/Cu, in which each metal layer thickness was decreased to 200 nm. Moreover, the three-cycle deposition sample showed the best CZTS kesterite structures after 5 hr sulfurization treatment. The two- and three-cycle Cu/Sn/Zn/Cu samples showed high-efficient photoluminescence (PL) spectra after a 3 hr sulfurization treatment, wheres the one-cycle sample yielded poor PL efficiency. The PL spectra of the three-cycle sample showed a broad peak in the range of 700-1000 nm, peaked at 870 nm (1.425 eV). This result is in good agreement with the reported bandgap energy of CZTS.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.1
• /
• pp.58-63
• /
• 2005

PTFE (polytetrafluoroethylene) thin films were prepared from the pellets of the graphite doped PTFE via pulsed laser ablation with 1064 nm Nd:YAG laser. The graphite powder converts the absorbed photon energy into thermal energy which is transmitted to nearby PTFE. The PTFE is decomposed by thermal process. The deposited films were transparent and crystalline. SEM (scanning electron microscopy) and AFM (atomic force microscopy) analyses indicated that the film surface morphology changed to fibrous structure with increasing thickness. The fluorine to carbon ratios of the film were 1.7 and molecular axis was parallel with (100) Si-wafer substrate. These results obtained by XPS (X-ray photoelectron spectroscopy), FTIR (fourier transform infrared spectroscopy) and XRD (X-ray diffraction).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.281-281
• /
• 2010

Very low refractive index (<1.4) materials have been proved to be the key factor improving the performance of various optical components, such as reflectors, filters, photonic crystals, LEDs, and solar cell. Highly porous SiO2 are logically designed for ultralow refractive index materials because of the direct relation between porosity and index of refraction. Among them, ordered macroporous SiO2 is of potential material since their theoretically low refractive index ~1.10. However, in the conventional synthesis of ordered macroporous SiO2, the time required for the crystallization of organic nanoparticles, such as polystyrene (PS), from colloidal solution into well ordered template is typical long (several days for 1 cm substrate) due to the low interaction between particles and particle - substrate. In this study, polystyrene - polyacrylic acid (PS-AA) nanoparticles synthesized by miniemulsion polymerization method have hydrophilic polyacrylic acid tails on the surface of particles which increase the interaction between particle and with substrate giving rise to the formation of PS-AA film by simply spin - coating method. Less ordered with controlled thickness films of PS-AA on silicon wafer were successfully fabricated by changing the spinning speed or concentration of colloidal solution, as confirmed by FE-SEM. Based on these template films, a series of macroporous SiO2 films whose thicknesses varied from 300nm to ~1000nm were fabricated either by conventional sol - gel infiltration or gas phase deposition followed by thermal removal of organic template. Formations of SiO2 films consist of interconnected air balls with size ~100 nm were confirmed by FE-SEM and TEM. These highly porous SiO2 show very low refractive indices (<1.18) over a wide range of wavelength (from 200 to 1000nm) as shown by SE measurement. Refraction indices of SiO2 films at 633nm reported here are of ~1.10 which, to our best knowledge, are among the lowest values having been announced.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.37 no.1
• /
• pp.19-25
• /
• 2013

In this study, the mechanical properties of a Ti thin film are measured by a bulge test. In the bulge test, uniform pressure is applied to one side of the film. Measurement of the membrane deflection as a function of the applied pressure allows one to determine the mechanical properties of the film. Ti thin films with thicknesses of 1.0, 1.5, and $2.0{\mu}m$ were deposited on a Si wafer by using an RF magnetron sputtering system. These specimens were annealed at $600^{\circ}C$ for 150, 300, and 600 s to investigate the effect of temperature on the yield stress and mechanical properties of the Ti films. The elastic modulus, residual stress, and yield stress of these membranes are measured by a bulge test. The experimental results suggest that the yield stress is sensitive to the film thickness and annealing time.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.254-254
• /
• 2011

The memories with nano-particles are very attractive because they are promising candidates for low operating voltage, long retention time and fast program/erase speed. In recent, various nano-floating gate memories with metal-oxide nanocrystals embedded in organic and inorganic layers have been reported. Because of the carrier generation in semiconductor, induced photon pulse enhanced the program/erase speed of memory device. We studied photo-induced electrical properties of these metal-oxide nanocrystal memory devices. At first, 2~10-nm-thick Sn and In metals were deposited by using thermal evaporation onto Si wafer including a channel with $n^+$ poly-Si source/drain in which the length and width are 10 ${\mu}m$ each. Then, a poly-amic-acid (PAA) was spin coated on the deposited Sn film. The PAA precursor used in this study was prepared by dissolving biphenyl-tetracarboxylic dianhydride-phenylene diamine (BPDA-PDA) commercial polyamic acid in N-methyl-2-pyrrolidon (NMP). Then the samples were cured at 400$^{\circ}C$ for 1 hour in N atmosphere after drying at 135$^{\circ}C$ for 30 min through rapid thermal annealing. The deposition of aluminum layer with thickness of 200 nm was followed by using a thermal evaporator, and then the gate electrode was defined by photolithography and etching. The electrical properties were measured at room temperature using an HP4156a precision semiconductor parameter analyzer and an Agilent 81101A pulse generator. Also, the optical pulse for the study on photo-induced electrical properties was applied by Xeon lamp light source and a monochromator system.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.200-200
• /
• 2012

We investigated a flexible transparent film using the spinning multi-walled carbon nanotubes (MWCNTs). Spin-capable MWCNTs on iron catalyzed on a SiO2 wafer was grown by chemical vapor deposition, which was performed at $780^{\circ}C$ using C2H2 and H2 gas. The average diameter and length of MWCNTs grown on the substrate were ~15 nm and $250{\sim}300{\mu}m$, respectively. The MWCNT sheets were produced by continuously pulling out from well-aligned MWCNTs on a substrate. The MWCNT sheet films were produced simply by direct coating on the flexible film or grass. The thickness of sheet film was remarkably decreased by alcohol spraying on the surface of sheet. The alcohol splay increased transmittance and decreased electrical resistance of MWCNT sheet films. Single and double sheets were produced with sheet resistance of ~699 and ${\sim}349{\Omega}/sq$, respectively, transmittance of 81~85 % and 67~72%, respectively. The MWCNT sheet films were heated through the application of direct current power. The flexible transparent heaters showed a rapid thermal response and uniform distribution of temperature. In addition, MWCNT yarns were prepared by spinning a bundle of MWCNTs from vertically super-aligned MWCNTs on a substrate, and field emission from the tip and side of the yarns was induced in a scanning electron microscope. We found that the field emission behavior from the tip of the yarn was better than the field emission from the side. The field emission turn-on voltages from the tip and side of MWCNT yarns were 1.6 and $1.7V/{\mu}m$, respectively, after the yarn was subjected to an aging process. Both the configuration of the tip end and the body of the yarn were changed remarkably during the field emission. We also performed the field emission of the sheet films. The sheet films showed the turn on voltage of ${\sim}1.45V/{\mu}m$ during the field emission.

• Korean Journal of Materials Research
• /
• v.9 no.9
• /
• pp.890-895
• /
• 1999

The recent important issue in solar cell fabrication is to adopt thin film silicon solar cells on cheap substrates. However, thin cells demand new grid design concept that all the contacts(to the emitter and base) be located on the front surface. Hence, the aim of the investigation presented in this paper was to determine the potential and the basic limitation of the design. With this concept, an interdigitated front grid structure was realized and cells were fabricated through a set of photolithography processes. Confirmed efficiencies of up to 11.5% were achieved on bonded SOI wafers with a cell thickness of 50$\mu\textrm{m}$ in the case of finger spacing more than $\mu\textrm{m}$ and a base width of 35$\mu\textrm{m}$. It was also shown from the results that the design rules for optimizing the base fraction and reducing the shadowing fraction are noted as an important technique to realize high-efficiency thin silicon solar cells.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.77-77
• /
• 2018

Panel level packaging (PLP) 공정은 차세대 반도체 패키징 기술로써 wafer level packaging 대비 net die 면적이 넓어 생산 단가 절감에 유리하다. PLP 공정에 적용되는 구리 재배선 층 (RDL, redistribution layer)은 두께 불균일도에 의해 전기 저항의 유동이 민감하게 변화하기 때문에 RDL의 두께를 균일하게 형성하는 것은 신뢰성 측면에서 매우 중요하다. 구리 RDL은 주로 도금 공정을 통해 형성되며, 균일한 도금막 형성을 위해 도금조에 평탄제를 첨가하여 도금 속도를 균일하게 한다. 도금막에 대한 흡착은 주로 평탄제의 imine 작용기에 포함된 질소 원자가 관여하며, imine 작용기의 4차화에 의한 평탄제의 흡착 정도를 제어하여 평탄제 성능을 개선할 수 있다. 본 연구에서는 도금 평탄제에 포함된 imine 작용기의 질소 원자를 4차화하여 구리 RDL의 도금 두께 불균일도를 제어하고자 하였다. 유기첨가제와 4차화 반응을 위해 알킬화제로써 dimethyl sulfate의 비율을 조절하여 각각 0, 50, 100 %로 4차화 반응을 진행하였다. 평탄제의 4차화 여부를 확인하기 위해 gel permeation chromatography (GPC) 분석을 실시하였다. 도금은 20 ~ 200 um의 다양한 배선 폭을 갖는 구리 RDL 미세패턴에서 진행하였으며, 4차화 평탄제를 첨가하여 광학 현미경과 공초점 레이저 현미경을 통해 도금막 표면과 두께에 대한 분석을 실시하였다. GPC 분석을 통해 4차화 반응 후 알킬화제에 의해 나타나는 GPC peak이 감소한 것을 확인하였다. 광학 현미경 및 공초점 레이저 현미경 분석 결과, 4차화된 질소 원자가 존재하지 않는 평탄제의 경우, 도금 시 도금막의 두께가 불균일하였으며 단면 분석 시 dome 형태가 관찰되었다. 또한 100 % 4차화를 실시한 평탄제를 첨가하여 도금 한 경우 마찬가지로 두께가 불균일한 dish 형태의 도금막이 형성되었다. 반면, 50 % 4차화를 적용한 평탄제를 첨가한 경우, 도금막 단면의 형태는 평평한 모습을 보였으며 매우 양호한 균일도를 가지는 것으로 확인되었다. 이로 인해 imine 작용기를 포함한 평탄제의 4차화 반응을 통해 구리 RDL의 단면 형상 및 불균일도가 제어되는 것을 확인하였으며, 4차화된 imine 작용기의 비율을 조절하여 높은 균일도를 갖는 구리 RDL 도금이 가능한 것으로 판단되었다.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.04a
• /
• pp.105-110
• /
• 2011

The doping procedure in crystalline silicon solar cell fabrication usually contains oxygen injection during drive-in process and removal of phosphorous silicate glass(PSG). In this paper, we studied the effect of oxygen injection and PSG on conversion efficiency of solar cell. The mono crystalline silicon wafers with $156{\times}156mm^2$, $200{\mu}m$, $0.5-3.0{\Omega}{\cdot}cm$ and p-type were used. After etching $7{\mu}m$ of the surface to form the pyramidal structure, the P(phosphorous) was injected into silicon wafer using diffusion furnace to make the emitter layer. After then, the silicon nitride was deposited by the PECVD with 80 nm thickness and 2.1 refractive index. The silver and aluminium electrodes for front and back sheet, respectively, were formed by screen-printing method, followed by firing in 400-425-450-550-$880^{\circ}C$ five-zone temperature conditions to make the ohmic contact. Solar cells with four different types were fabricated with/without oxygen injection and PSG removal. Solar cell that injected oxygen during the drive-in process and removed PSG after doping process showed the 17.9 % conversion efficiency which is best in this study. This solar cells showed $35.5mA/cm^2$ of the current density, 632 mV of the open circuit voltage and 79.5 % of the fill factor.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.51-55
• /
• 2011

In this paper, the optimized doping condition of crystalline silicon solar cells with 156 ${\times}$ 156 mm2 area was studied. To optimize the drive-in condition in the doping process, the other conditions except drive-in temperature and time were fixed. After etching 7 ${\mu}m$ of the surface to form the pyramidal structure, the silicon nitride deposited by the PECVD had 75~80 nm thickness and 2 to 2.1 for a refractive index. The silver and aluminium electrodes for front and back sheet, respectively, were formed by screen-printing method, followed by firing in $400-425-450-550-850^{\circ}C$ five-zone temperature conditions to make the ohmic contact. Drive-in temperature was changed in range of $828^{\circ}C$ to $860^{\circ}C$ and time was from 3 min to 40 min. The sheet resistance of wafer was fixed to avoid its effect on solar cell. The solar cell fabricated with various conditions showed the similar conversion efficiency of 17.4%. This experimental result showed the drive-in temperatures and times little influence on solar cell characteristics.