• Current Photovoltaic Research
• /
• v.12 no.2
• /
• pp.37-40
• /
• 2024

One of the current innovation trends in the solar industry is the increase in the size of silicon wafers. As the wafer size increases, the series resistance of the module rises, highlighting the need for research on methods for cutting and bonding solar cells. Among these, the Infrared (IR) laser scribing technique has been extensively researched. However, there is still insufficient optimization research regarding the thermal damage caused by lasers on the Transparent Conductive Oxide (TCO) layer of Heterojunction (HJT) solar cells. Therefore, in this study, we systematically varied conditions such as IR laser scribing speed, frequency, power, and the number of scribes to investigate their impact on the performance of cut cells under each condition. Additionally, we conducted a comparative analysis of thermal damage effects on the TCO layer based on varying scribing depths.

• Resources Recycling
• /
• v.22 no.2
• /
• pp.22-28
• /
• 2013

In the present study, the possibility of recovering and recycling the silicon carbide(SiC) from a silicon sludge by removing Fe and Si impurities was investigated. Si and SiC were separated from the silicon sludge using centrifugation. The separated SiC concentrate consisted of Fe, Si and SiC, in which Fe and Si were removed to recover the pure SiC. Leaching with acid/alkali solution was compared with the vapor-phase chlorination. The Fe concentration removed in the SiC was 49 ppm, and it was separated by leaching with 1 M HCl solution at $80^{\circ}C$ for 1 h. The Si concentration removed in the SiC was 860 ppm, and it was separated by leaching with 1M NaOH solution at $50^{\circ}C$ for 1 h. The SiC concentrate was chlorinated in a tubular reactor, 2.4 cm in diameter and 32 cm in length. The boat filled with SiC concentrate was located at the midpoint of the alumina tube, then, the chlorine and nitrogen gas mixture was introduced. The Fe and Si concentration removed in the SiC were 48 ppm and 405 ppm, respectively, at $500^{\circ}C$ reactor temperature, 4 h reaction time, 300 cc/min gas flow rate, and 10% $Cl_2$ gas mole fraction.

• Korean Chemical Engineering Research
• /
• v.44 no.5
• /
• pp.513-519
• /
• 2006

We developed two kinds of the microchip for application to electrophoresis based on both glass and quartz employing the MEMS fabrications. The poly-Si layer deposited onto the bonding interface apart from channel regions can play a role as the optical slit cutting off the stray light in order to concentrate the UV ray, from which it is possible to improve the signal-to-noise (S/N) ratio of the detection on a chip. In the glass chip, the deposited poly-Si layer had an important function of the etch mask and provided the bonding surface properly enabling the anodic bonding. The glass wafer including more impurities than quartz one results in the higher surface roughness of the channel wall, which affects subsequently on the microflow behavior of the sample solutions. In order to solve this problem, we prepared here the mixed etchant consisting HF and $NH_4F$ solutions, by which the surface roughness was reduced. Both the shape and the dimension of each channel were observed, and the electroosmotic flow velocities were measured as 0.5 mm/s for quartz and 0.36 mm/s for glass channel by implementing the microchip electrophoresis. Applying the optical slit with poly-Si layer provides that the S/N ratio of the peak is increased as ca. 2 times for quartz chip and ca. 3 times for glass chip. The maximum UV absorbance is also enhanced with ca. 1.6 and 1.7 times, respectively.