• Journal of the Korean Applied Science and Technology
• /
• v.31 no.2
• /
• pp.218-224
• /
• 2014

Biodegradable conductive composite films of polylactic acid(PLA) were prepared with various amounts of polyaniline(PAni) doped with dodecylbenzenesulphonic acid (DBSA) by solution blending technique to identify their mechanical and electric properties. 15 mol% of DBSA doped PAni was easily obtained by polymerizing of aniline in the presence of APS and DBSA in THF at $0^{\circ}C$. FE SEM characterization showed that PAni were well spread on the PLA domains. The tensile strength of composite film with 15 wt% of PAni was significantly decreased from $565.3kg_f/cm^2$ for PLA film itself to $309.7kg_f/cm^2$. Elongations of all PAni/PLA composite films were also decreased up to 3-6%. Electrical conductivity of $2.9{\times}10^{-3}$ S/cm could be achieved for the composite film containing 15 wt% of PAni-DBSA. Thermal stability of these composite films measured by thermogravimetric analysis(TGA) showed a slight decrease with the amount of PAni in PAni/PLA composite films at temperature lower than $300^{\circ}C$. However, the final weight of char was strongly depended with the amount of PAni in original composite films. Conclusively, PAni/PLA composite films containing more than a 15 wt% of PAni could be used for intercepting electromagnetic and preventing electrostatic applications.

• Membrane Journal
• /
• v.18 no.3
• /
• pp.198-205
• /
• 2008

A novel technology for homogeneous deposition of zeolite particles on a porous support was developed so that those particles played a seeding role for the growth of zeolite crystals. After the particles were dispersed in water, the aqueous solution was 134 through the bore of a porous tubular support. By keeping the other side of the support in a vacuum, the aqueous solution passed through the pores of the support, leading the particles to be homogeneously deposited on the support. The amount of the deposited particles was investigated by changing the following operating parameters: a particle concentration in the solution, a time for deposition, and the feeding rate of the solution. The amount of the deposited particles increased from 0.0019 g to 0.0208 g as the concentration of the particles was changed from 0.01 wt% to 0.3 wt%, while the feeding rate and the deposition time were kept to 100 mL/min and 4 min, respectively. As the deposition time was varied from 1 min to 4 min, the deposition amount increased from 0.0004g to 0.0019g at the typical condition of the rest parameters. Also, it was observed that the deposited weight increased from 0.0029 g to 0.01 g as the feeding rate increased from 100 mL/min to 300 mL/min. However, the total permeance of water and ethanol decreased through the zeolite membrane as the deposited weight increased.

• Journal of Sensor Science and Technology
• /
• v.9 no.1
• /
• pp.36-43
• /
• 2000

In oder to enhance the selectivity of TMA(trimethylamine) gas, the ZnO-based films which were doped with $Al_2O_3$, $TiO_2, $In_2O_3$ and $V_2O_5$ catalysts with various weight percents were deposited in oxygen by RF magnetron sputtering method. To improve electrical stability of sensors, the ZnO-based films were annealed in oxygen at $700^{\circ}C$ for 1 hour. The TMA selectivity of sensors was defined by the magnitude($S_{TMA}/S_{DMA}$ and $S_{TMA}/S_{NH3}$) of TMA sensitivity relative to DMA and sensitivity ammonia($NH_3$) sensitivity, respectively. The $ZnO+Al_2O_3(4\;wt.%)+TiO_2(1\;wt.%)+In_2O_3(1\;wt.%)$ sensor showed high $S_{TMA}/S_{DMA}$ of 5.9 and $S_{TMA}/S_{NH3}$ of 26 to 160 ppm at the working temperature of $300^{\circ}C$ respectively.

• Economic and Environmental Geology
• /
• v.31 no.5
• /
• pp.389-398
• /
• 1998

The Au-Ag deposit of the Oknam mine occurs as gold-silver-bearing rhodochrosite veins in biotite schist and phyllite of the Precambriam Yulri Group. Five stages of ore deposition are recognized, each showing a definite mineral assemblage. General mineral parageneses in veins (stage III) associated with gold and silver vary inwardly from the vein margin: arsenopyrite + pyrite $\Rightarrow$ sphalerite+chalcopyrite+galena+gold $\Rightarrow$ ga1ena+Ag-bearing minerals. Fluid inclusion data indicate that temperature and salinity of ore fluids overally decreased with time: $345^{\circ}{\sim}240^{\circ}C$ and 3.4~7.8 wt. % NaCl equiv during stage I (quartz vein mineralization), $313^{\circ}{\sim}207^{\circ}C$ and 2.3~8.7 wt.% NaCl equiv during manganese-bearing carbonate stages (II and III), and $328^{\circ}{\sim}213^{\circ}C$ and 3.6-5.4 wt.% NaCl equiv during stage IV (quartz vein mineralization). The ore fluids probably evolved through repeated pulses of boiling and later mixing with cooler and more dilute meteoric waters. Fluid inclusion data and geologic arguments indicate that pressures during the mineralization were in the range of 90 to 340 bars. Gold occurs as silver-rich electrums (21 to 29 atom. % Au) and was deposited at temperatures between $300^{\circ}$ and $240^{\circ}C$. Thermochemical calculations suggest that gold was deposited as a combined result of increase in pH and decreases in temperature, $fs_2$ and $fo_2$.

• Restorative Dentistry and Endodontics
• /
• v.36 no.4
• /
• pp.313-323
• /
• 2011

Objectives: This study investigated the optimal combination of 3-component photoinitiation system, consisting of CQ, p-octyloxy-phenyl-phenyl iodonium hexafluoroantimonate (OPPI), and 2-dimethylaminoethyl methacrylate (DMAEMA) to increase the degree of conversion of resin monomers, and analyze the effect of the ratio of the photoinitiator to the co-initiator. Materials and Methods: Each photoinitiators (CQ and OPP) and co-initiator (DMAEMA) were mixed in three levels with 0.2 wt.% (low concentration, L), 1.0 wt.% (medium concentration, M), and 2.0 wt.% (high concentration, H). A total of nine groups using the Taguchi method were tested according to the following proportion of components in the photoinitiator system: LLL, LMM, LHH, MLM, MMH, MHL, HLH, HML, HHM. Each monomer was polymerized using a quartz-tungsten-halogen curing unit (Demetron 400, USA) for 5, 20, 40, 60, 300 sec and the degree of conversion (DC) was determined at each exposure time using FTIR. Results: Significant differences were found for DC values in groups. MMH group and HHM group exhibited greater initial DC than the others. No significant difference was found with the ratio of the photoinitiators (CQ, OPPI) to the co-initiator (DMAEMA). The concentrations of CQ didn't affect the DC values, but those of OPPI did strongly. Conclusions: MMH and HHM groups seem to be best ones to get increased DC. MMH group is indicated for bright, translucent color and HHM group is good for dark, opaque colored-resin.

• Journal of Sensor Science and Technology
• /
• v.6 no.4
• /
• pp.265-273
• /
• 1997

The TMA gas sensors are fabricated with the ZnO-based thin films grown by a RF magnetron sputtering method. We investigate the surface carrier concentration, Hall electron mobility, electrical resistivity and sensitivity according to temperature variation and TMA gas concentration. The ZnO-based thin film sensors prepared by sputtering in oxygen showed higher surface carrier concentration, higher Hall mobility, higher sensitivity, and lower electrical resistivity than sensors prepared by sputtering in argon. The doping ZnO-based thin film sensors showed the same electrical properties in comparison with nondoping sensors. In case of sputtering on the oxygen gaseous atmosphere, the ZnO-based thin film sensors doped with 4.0 wt.% $Al_{2}O_{3}$, 1.0 wt.% $TiO_{2}$, and 0.2 wt.% $V_{2}O_{3}$ showed the highest surface carrier concentration of $5.95{\times}10^{20}cm^{-3}$, Hall electron mobility of $177\;cm^{2}/V{\cdot}s$, lowest electrical resistivity of $0.59{\times}10^{-4}{\Omega}{\cdot}cm$ and highest sensitivity of 12.1(working temperature, $300^{\circ}C$, TMA gas, 8 ppm).

• The Korean Journal of Ceramics
• /
• v.2 no.3
• /
• pp.125-130
• /
• 1996

Hematite iron ore and waste iron oxide sludge containing about 3-5 wt% $SiO_2$ were purified by three types of method developed on the basis of the Bayer process which is known as the purification process of bauxite ore. The basic principle of the developed methods lies in the fact that the impurities contained in the iron oxides, such as $SiO_2$ and $Al_2O_3$ are soluble in the alkaline reagents. Reaction of the raw materials with KOH was done in pressure vessel, at atmospheric pressure, and by both of these two. By the pressure vessel method $SiO_2$ content was reduced to below 0.5 wt% in the waste iron oxide sludge, while, in iron ore, $SiO_2$ remained at 2-3 wt%. The atmospheric pressure reaction rendered the waste iron oxide sludge $SiO_2$ content below 0.5wt% when the reaction temperature increased to above 90$0^{\circ}C$. The combined method of two previous methods was the most effective process and rendered the refined iron oxide about 300-400ppm of $SiO_2$. Using some refined iron oxides, Ba-ferrite was produced and magnetic properties were measured. The highest quality of magnetic properties obtained in this study were Br=2.09 G, bHc=1.99 KOe, iHc=4.54 KOe, $(BH)_{max}$=1.06 MGOe. Effect of sintering condition and chemical composition will be discussed.

• Korean Journal of Materials Research
• /
• v.25 no.9
• /
• pp.468-474
• /
• 2015

Evaluations of the microstructure and mechanical properties of age hardenable Cu-2.0wt%Be alloy are performed in order to determine whether it can be used as a welding electrode for projection welding. The microstructure examinations, hardness measurements, and tensile tests of selective aging conditions are conducted. The results indicate that the aging treatment with the fine-grained microstructure exhibits better hardness and high tensile properties than those of the coarse-grained microstructure. The highest hardness value and high tensile strength are obtained from the aged condition of $300^{\circ}C$ for 360 min due to the presence of the metastable ${\dot{\gamma}}$ precipitates on the grain boundaries. The values of the highest hardness and tensile strength are measured as 374 Hv and 1236.2 MPa, respectively. The metastable ${\dot{\gamma}}$ precipitates are transferred to the equilibrium ${\gamma}$ precipitates due to the over-aged treatment. The presence of the ${\gamma}$ precipitates appears as nodule-like precipitates decorated around the grain boundaries. The welding electrode with the best aging treated condition exhibits better welding performance for electrodes than those of electrodes used previously.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.3
• /
• pp.107-112
• /
• 2007

Aluminum doped zinc oxide (AZO) films were deposited on non-alkali glass substrate by DC magnetron sputtering with 3 types of AZO targets (doped with 1.0 wt%, 2.0 wt%, 3.0 wt% $Al_2O_3$). Electrical, optical properties and microstructure of AZO films have been investigated by Hall effect measurements, UV/VIS/NIR spectrophotometer, and XRD, respectively. Crystallinity of AZO films increased with increasing substrate temperature ($T_s$) and doping ratio of Al. Resistivity and optical transmittance in visible light were $8.8{\times}10^{-4}{\Omega}cm$ and above 85%, respectively, for the AZO film deposited using AZO target (doped with 3.0 wt% $Al_2O_3$) at $T_s$ of $300^{\circ}C$. On the other hand, transmittance of AZO films in near-infrared region decreased with increasing $T_s$ and doping ratio of Al, which could be attributed to the increase of carrier density.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.300-303
• /
• 2003

[ $0.91(PSN-PZT)-0.05BF-0.04PNW+0.3wt%MnO_2+0.6wt%CuO+xwt%CeO_2$ ] ceramics were fabricated with the variations of $CeO_2$ addition at the sintering temperature of $950^{\circ}C$ and their microstructure and dielectric and piezoelectric characteristics were investigated. As the amount of $CeO_2$ addition increased, the grain size, density and electromechanical coupling factor(kp) were increased and the mechanical quality factor(Qm) was decreased. At the $0.3wt%CeO_2$, density, grain size and electromechanical factor(kp) showed the maximum value of $7.87g/cm^3$, $3.22{\mu}m$ and 0.5, respectively. However, mechanical quality factor(Qm) showed the minimum value of 807 at the $0.5wt%CeO_2$.