• Journal of the Korean Ceramic Society
• /
• v.21 no.3
• /
• pp.221-230
• /
• 1984

In this study an investigation was made to determine optimum ratio between $SO_3$, MgO and $K_2O$ that maximizes $C_2S$ formation in Clinkering reaction Using response surface analysis method. It was proved that 1) Residual $K_2O$ int he clinker should be converted to $K_2SO_4$ because $K_2SO_4$ has less effect on the burnability than $K_2O$, 2) Optimum ratio if $SO_3$/K2O is 1.5, 3) Optimun balance between $CaSO_4$ and MgO is to be adjusted to such a level that w/o SO3=0.7(w/o MgO-2).4) In case of lack of $K_2O$ free CaO was minimized when $K_2SO_4$=2.3w/o and MgO=1.5w/o but if remaining $K_2O$ was 2w/o free CaI was minimized in the level that $K_2SO_4$=2.3w/o and MgO =1.5 w/o but if remaining $K_2O$ was 2 w/o free CaO was minimized in the level that $K_2SO_4$=4.5w/o and MgO =3.0 w/o.

• Journal of the Korean Ceramic Society
• /
• v.22 no.2
• /
• pp.17-24
• /
• 1985

In the composition of $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ the effect of particle size on PbO vaporization were measured, . The initial step of discontinuous vaporization of unreated PbO during the calcining process was depended on the particle size. All additives $La_2O_3Nb_2O_5$ and $Al_2O_3$ inhibited the grain growth of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ +2wt% excess PbO. The dielectric and piezoelectric properties of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ were improved by the addition of 2wt% excess PbO and proper additive. The electromechanical planar coupling factor of 0.65 and mechnical quality factor of 390 could be obtained by adding 5wt% $Nb_2O_5$ to the composition 2wt% excess PbO+$Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.753-759
• /
• 1999

The microstructure and electrical properties of ZNR that W $O_3$ is added in the range 0.5~4.0mol%, were investigated. The major part of W $O_3$ were segregated at the nodal point and W-rich phase was formed. Three crystalline phases, such as W-rich phase (W $O_3$), Bi-rich phase (B $i_2$W $O_{6}$ ), and spinel phase (Z $n_{2.33}$S $b_{0.67}$ $O_4$) were confirmed to be co-existed at the nodal point The average grain size increased in the range 15.5~29.9$\mu\textrm{m}$ with increasing W $O_3$ additive content. Consequently. W $O_3$ acted as a promotion additive of grain growth. As the W $O_3$ additive content increases. the varistor voltage and the nonlinear exponent decreased in the range 186.82~35.87V/mm and 20.90~3.34, respectively, and the leakage current increased in the range of 22.39~83.01 uh. With increasing W $O_3$ additive content, the barrier height and the density of interface states decreased in the range 1.93~0.43eV and (4.38~1.22)$\times$10$^{12}$ $\textrm{cm}^2$, respectively. W $O_3$ acted as an acceptor additive due to the donor concentration increasing in the range (1.06~0.38)$\times$10$^{18}$ /㎤with increasing W $O_3$ additive content.t.t.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.161.2-161
• /
• 2002

• Journal of the Korean Ceramic Society
• /
• v.23 no.3
• /
• pp.53-61
• /
• 1986

A gas sensor which has been made by wet process had fabricated by coating each of the mixture on alumina tube and firing at 85$0^{\circ}C$ for 3hrs. A gas concentration such $H_2$, CO, $C_3H_8$, $C_2H_2$ and $CH_4$ vs its detection voltage characteristics has been in-vestigated on $SnO_2-In_2O_3-MgO$ system doped with PdO, $La_2O_3$, $ThO_2$, NiO and $Nb_2O_5$ The optimum sensitivity composition for various gases were 90w/o $SnO_2$-9w/o $In_2O_3$-1w/o MgO for $H_2$, $C_2H_2$ CO and $C_3H_8$ and 95w/o $SnO_2$-4w/o $In_2O_3$-1w/o MgO for $CH_4$. The sample which has been made by wet process than dry process had predominated sensitivity for each gases and particle size of the sample coprecipitated with PH=9 was 0.1${\mu}{\textrm}{m}$ The $SnO_2$-In2_O_3-MgO$ system doped with 2w/o $Nb_2O_5$ and NiO was the most sensitive for $H_2$ and $C_2H_2$ gas. In $SnO_2$-In2_O_3-MgO$ system doped with $ThO_2$ the sensitivity of $H_2$ gas was decreased but CO gas was in-creased when dopant con was increased.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.3
• /
• pp.117-125
• /
• 1996

The variation of the interfacial and the electrical properties of SiO$_{2}$TiW layers as a function of anneal temperature was extensively investigated. During the deposition of SiO$_{2}$ on TiW chemical bonds such as SiO$_{2}$, TiW, WO$_{3}$, WO$_{2}$ TiO$_{2}$ Ti$_{2}$O$_{5}$ has been created at the SiO$_{2}$/TiW interface. At the anneal temperature of 300$^{\circ}C$, WO$_{3}$ and TiO$_{2}$ bonds started to break due to the reduction phenomena of W and Ti and simultaneously the metallic W and Ti bonds started to create. Above 500$^{\circ}C$, a part of Si-O bonds was broken and consequently Ti/W silicide was formed. Form the current-voltage characteristics of Al/Sico$_{2}$(220$\AA$)/TiW antifuse structure, it was found that the breakdown voltage of antifuse device wzas decreased with increasing annealing temperature for SiO$_{2}$(220$\AA$)/TiW layer. When r, the insulating property of antifuse device of the deterioration of intermetallic SiO$_{2}$ film, caused by the influw of Ti and W.W.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.392-398
• /
• 2014

$Al_2O_3$-SiC composites reinforced with SiC whisker ($SiC_w$) were fabricated using three different methods. In the first, $Al_2O_3-SiC_w$ starting materials were used. In the second, $Al_2O_3-SiC_w$-SiC particles ($SiC_p$) were used, which was intended to enhance the mechanical properties by $SiC_p$ reinforcement. In the third method, reaction-sintering was used with mullite-Al-C-$SiC_w$ starting materials. After hot-pressing at $1750^{\circ}C$ and 30 MPa for 1 h, the composites fabricated using $Al_2O_3-SiC_w$ and $Al_2O_3-SiC_w-SiC_p$ showed strong mechanical properties, by which the effects of reinforcement by $SiC_w$ and $SiC_p$ were confirmed. On the other hand, the mechanical properties of the composite fabricated by reaction-sintering were found to be inferior to those of the other $Al_2O_3$-SiC composites owing to its relatively lower density and the presence of ${\gamma}-Al_2O_3$ and ${\gamma}-Al_{2.67}O_4$. The greatest hardness and $K_{1C}$ were 20.37 GPa for the composite fabricated using $Al_2O_3-SiC_w$, and $4.9MPa{\cdot}m^{1/2}$ using $Al_2O_3-SiC_w-SiC_p$, respectively, which were much improved over those from the monolithic $Al_2O_3$.

• Electrical & Electronic Materials
• /
• v.4 no.2
• /
• pp.150-158
• /
• 1991

본 연구에서는 0.80Pb(F $e_{1}$2/N $b_{1}$2/) $O_{3}$-(0.20-x)Pb(F $e_{2}$3/ $W_{1}$3/) $O_{3-x}$Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$ (x=0.01, 0.02, 0.03) 세라믹을 소결온도 및 시간을 각각 860~960[.deg.C], 2시간으로 하여 일반 소성법으로 제작하였다. 시편의 조성비와 소결온도에 따른 구조적, 유전적 특성을 조사하였으며 유전손실 특성의 개선을 위해 조성 0.80Pb(F $e_{1}$2/N $b_{1}$2/) $O_{3}$-0.18Pb (F $e_{2}$3/ $W_{1}$3/) $O_{3}$-0.02Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$시편에 Mn $O_{2}$를 0~1.25[wt%]로 첨가한 후 유전특성의 변화를 관찰하였다. Mn $O_{2}$의 첨가량이 증가함에 따라 결정립의 크기와 유전상수는 점차 감소하였다. 소결밀도는 900[.deg.C]에서 소결시킨 시편의 경우 최대값을 나타내었다. Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$의 양이 0.01에서 0.03[mol]로 증가함에 따라 상전이온도는 38[.deg.C]에서 2[.deg.C]로 감소하였다. 조성 0.80Pb(F $e_{1}$2/N $b_{1}$2/) $O_{3}$0.18Pb(F $e_{2}$3/ $W_{1}$3/) $O_{3}$-0.02Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$에 Mn $O_{2}$가 0.25[wt%] 첨가된 시편의 20[.deg.C]에서의 유전상수는 16,700으로 최대값을 유전손실을 1.28[%]로 최소값을 나타내었다. 또한 모든 시편은 온도 및 주파수에 따라 유전상수가 완만하게 변화하는 유전이완 특성을 나타내었다.다.

• Journal of the Korean Applied Science and Technology
• /
• v.17 no.2
• /
• pp.67-75
• /
• 2000

Cosmetic industries have recently developed sun-block products, which are composed of W/O or O/W emulsion system. It was very difficult for waterproofing product to show the stability in W/O emulsion with $TiO_{2}$. To enhance the stability of W/O emulsion, it needs to be combined with the water and oil soluble components as the gelling agents. The emulsifiers used in W/O were 3.0% of cetyl dimethicone copolyol, 2.0% of sorbitan sesquioleate as the basic emulsifiers, and 0.6% of quaternium-18 bentonite and 1.5% of dextrin palmitate as stabilizer were used. The content of titanium dioxide was optimized up to 8.0%. Titanium dioxide was used as the UV scattering powder coated with $Al_{2}O_{3}$(UV-sperse T40/TN). The sunscreen cream prepared with W/O emulsion system by using QB and DP showed higher stability than that of W/O emulsion system by using each QB and DP. W/O emulsion from Formula 3 for passing one year was very durable more than F1 and F2. Within W/O emulsion by observing F1, F2 and F3 for one year, F3 was more excellent than F2 and F3 when they were observed at RT, $4^{\circ}C$, $40^{\circ}C$, because F3 used the mixed QB and DP in W/O emulsion. The zeta potential for F1, F2, and F3 after one year were 21, 30 and 43, respectively. From these result F3 was found best stable emulsion. The in-vitro SPF value for F3 was 35 for the initial product at room temperature and also, the in-vitro SPF values of F3 was 32 for after one year. Finally, the mean in-vivo SPF value of 10 volunteers for F3 was 27.3 by the Korea cosmetic association made the rules of SPF.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1997.10a
• /
• pp.134-134
• /
• 1997